Method for forming a titanium nitride barrier layer
Assignee: Intel Corp
•
Filing: 1992-06-03
•
Granted: 1993-08-03
•
Expires: 2012-06-03
Abstract
Abstract Two methods for substantially improving the integrity of a TiN barrier layer are disclosed. The first method allows an atmospheric anneal in a conventional semiconductor furnace. The atmospheric anneal substantially seals the exposed TiN surface preventing subsequent metal layers from migrating through the barrier layer. The second method involves a reaction within a plasma reactor using a plasma gas. The plasma gas reacts with titanium within the TiN film to form a desired titanium compound. The gas is adsorbed onto the TiN grains at the grain boundaries within the TiN film thus filling the grain boundaries and thus substantially preventing subsequent metal layers from migrating though the TiN barrier layer. The second method allows the deposition of TiN, the plasma reaction, and subsequent metal depositions to take place on the same equipment using the same evacuation cycle.
Inventors
- 👤 Huei-Min Ho
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 03:55
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/074; H10W20/076; H10W20/031; H10W20/032; H10W20/033; H10W20/047; H10W20/048; Y; Y10; Y10S; Y10S257/00; Y10S257/915
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
82 words
A method of forming metalized interconnects on a semiconductor substrate comprising the steps of: (a) depositing a titanium nitride barrier layer onto said substrate; (b) after depositing said titanium nitride barrier layer exposing said titanium nitride barrier layer to a plasma gas to react said plasma gas with titanium within said titanium nitride barrier layer and to fill grain boundaries within said titanium nitride barrier layer; and (c) depositing at least one metal layer over said plasma reacted titanium nitride barrier layer.
Claim 2
Independent Claim
82 words
A method of forming metalized interconnects on a semiconductor substrate comprising the steps of: (a) depositing a titanium nitride barrier layer onto said substrate; (b) after depositing said titanium nitride barrier layer exposing said titanium nitride barrier layer to a plasma gas to react said plasma gas with titanium within said titanium nitride barrier layer and to fill grain boundaries within said titanium nitride barrier layer; and (c) depositing at least one metal layer over said plasma reacted titanium nitride barrier layer.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein all steps take place during at least one evacuation cycle.
Claim 4
Dependent Claim
17 words
The method of claim 1, wherein all steps take place in at least one piece of equipment.
Claim 5
Dependent Claim
23 words
The method of claim 1, wherein said barrier layer is exposed to said plasma gas for a time no greater than 60 seconds.
Claim 6
Dependent Claim
28 words
The method of claim 1, wherein said barrier layer is exposed to said plasma gas at a temperature in a range of approximately 20° C. through 300° C.
Claim 7
Dependent Claim
28 words
The method of claim 1, wherein said barrier layer is exposed to said plasma gas at a pressure in a range of approximately 5 mT through 20 mT.
Claim 8
Dependent Claim
29 words
The method of claim 1, wherein said barrier layer is exposed to said plasma gas at a RF power in a range of approximately 8 watts through 100 watts.
Claim 9
Dependent Claim
21 words
The method of claim 1, wherein said plasma gas comprises a gas selected from the group consisting of oxygen and nitrogen.
Claim 10
Independent Claim
117 words
A method of forming metalized interconnects on a semiconductor substrate comprising the steps of: (a) depositing a titanium nitride barrier layer onto said substrate: (b) exposing said titanium nitride barrier layer to a plasma gas to react said plasma gas with titanium within said titanium nitride barrier layer and to fill grain boundaries within said titanium nitride barrier layer wherein said titanium nitride barrier layer is exposed to said plasma gas for a time of approximately 60 seconds, at a temperature of approximately 300° C., at a pressure of approximately 20 mT, and at a RF power of approximately 20 watts: and (c) depositing at least one metal layer over said plasma reacted titanium nitride barrier layer.
Claim 11
Independent Claim
117 words
A method of forming metalized interconnects on a semiconductor substrate comprising the steps of: (a) depositing a titanium nitride barrier layer onto said substrate: (b) exposing said titanium nitride barrier layer to a plasma gas to react said plasma gas with titanium within said titanium nitride barrier layer and to fill grain boundaries within said titanium nitride barrier layer wherein said titanium nitride barrier layer is exposed to said plasma gas for a time of approximately 60 seconds, at a temperature of approximately 300° C., at a pressure of approximately 20 mT, and at a RF power of approximately 20 watts: and (c) depositing at least one metal layer over said plasma reacted titanium nitride barrier layer.
References Cited (Backward Citations)
US4965656A
Cited
US4782380A
Cited
US4897709A
Cited
US4976839A
Cited
US5070036A
Cited
US5094981A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-08-02 | 1997-02-01 | 1997-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-08-02 | 2001-02-01 | 2001-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-08-02 | 2005-02-01 | 2005-08-03 | $7700.00 | Window Closed / Lapsed |