Fabrication process for semiconductor device
Assignee: NEC Corp
•
Filing: 1996-10-25
•
Granted: 1999-06-22
•
Expires: 2016-10-25
Abstract
Abstract A Fabrication process for a semiconductor device, in which an element separation region and a gate insulation layer are formed on a surface of a silicon layer of a semiconductor substrate. Then, a gate electrode wiring is formed on the surface of the silicon layer and an insulation layer spacer is formed at the side surface of the gate electrode wiring. Diffusion layers to be a source and drain regions are formed in a predetermined region on the surface of the silicon layer. At least the surface of the diffusion region is converted into an uneven surface. Then, a refractory metal (e.g. titanium layer) is deposited on the entire surface, a refractory metal silicide layer is selectively formed on at least one of the surfaces of the diffusion layers by annealing, and a non-reacted refractory metal layer is selectively removed. Thus, in advance of deposition of titanium layer, unevenness is formed on the exposed surfaces of the diffusion layers and the upper surface of the polycrystalline silicon layer. This allows a MOS transistor of the salicide structure to be formed without increasing sheet resistance even when high temperature annealing is performed.
Inventors
- 👤 Michiko Yamanaka
- 👤 Naoharu Nishio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 08:06
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; H10D30/00; H10D30/01; H10D30/021; H10D30/0212; H10D30/0223; H10D30/0227; H10D64/011; H10D64/0111; H10D64/0112; H10D64/20; H10D64/23; H10D64/251; H10D64/258; H10D64/259; H10D64/27; H10D64/311; H10D64/411; H10D64/511; H10D64/517; H10D64/60; H10D64/66; H10D64/661; H10D64/662; H10D64/663
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
141 words
A fabrication process for semiconductor device comprising the steps of: forming a diffusion layer on the surface of a silicon layer; converting a surface of said diffusion layer into an uneven surface having an unevenness of a predetermined size with primary exposed surface consisting of (111) surface; depositing refractory metal onto at least said uneven surface; and forming through annealing a refractory metal suicide layer having a grain growth restricted by said predetermined size of said unevenness of said uneven surface, to eliminate deformation and agglomeration of grain of said refractory metal suicide layer and to produce a substantially lower resistance in said refractory metal silicide layer, wherein the step of converting the surface of said diffusion layer into the surface having the unevenness includes selectively depositing amorphous silicon or polycrystalline silicon at least on the surface of said diffusion layer.
Claim 2
Dependent Claim
141 words
A fabrication process for semiconductor device comprising the steps of: forming a diffusion layer on the surface of a silicon layer; converting a surface of said diffusion layer into an uneven surface having an unevenness of a predetermined size with primary exposed surface consisting of (111) surface; depositing refractory metal onto at least said uneven surface; and forming through annealing a refractory metal suicide layer having a grain growth restricted by said predetermined size of said unevenness of said uneven surface, to eliminate deformation and agglomeration of grain of said refractory metal suicide layer and to produce a substantially lower resistance in said refractory metal silicide layer, wherein the step of converting the surface of said diffusion layer into the surface having the unevenness includes selectively depositing amorphous silicon or polycrystalline silicon at least on the surface of said diffusion layer.
Claim 3
Dependent Claim
16 words
A process as set forth in claim 1, wherein said refractory metal is titanium or cobalt.
Claim 4
Dependent Claim
52 words
A process as set forth in claim 1, wherein said silicon layer is a polycrystalline silicon layer, and said semiconductor substrate has a laminated structure of a single crystal silicon substrate, an insulation layer covering the surface of said single crystal silicon substrate and said polycrystalline silicon layer covering said insulation layer.
Claim 5
Dependent Claim
222 words
A fabrication process for semiconductor device comprising the steps of: forming an element separation region and a gate insulation layer on a surface of a silicon layer which constitute at least a surface of a semiconductor substrate, forming a gate electrode wiring on the surface of said silicon layer and further forming an insulation layer spacer at the side surface of said gate electrode wiring; forming diffusion layers to be source and drain regions in a predetermined region on the surface of said silicon layer; converting at least the surfaces of said diffusion layers into uneven surfaces having an unevenness of a predetermined size with primary exposed surface consisting of (111) surface; and depositing refractory metal on at least the uneven surfaces; selectively forming through annealing a refractory metal silicide layer having grain growth restricted by said predetermined unevenness of said uneven; and selectively removing non-reacted refractory metal layer, wherein formation of said refractory metal silicide layer on the uneven surfaces eliminates deformation and agglomeration of grain of said refractory metal silicide layer and produces said refractory metal silicide layer with a substantially lower resistance, and wherein the step of converting at least the surfaces of said diffusion layers into the surface having the unevenness includes selectively depositing amorphous silicon or polycrystalline silicon at least on the surfaces of said diffusion layers.
Claim 6
Dependent Claim
222 words
A fabrication process for semiconductor device comprising the steps of: forming an element separation region and a gate insulation layer on a surface of a silicon layer which constitute at least a surface of a semiconductor substrate, forming a gate electrode wiring on the surface of said silicon layer and further forming an insulation layer spacer at the side surface of said gate electrode wiring; forming diffusion layers to be source and drain regions in a predetermined region on the surface of said silicon layer; converting at least the surfaces of said diffusion layers into uneven surfaces having an unevenness of a predetermined size with primary exposed surface consisting of (111) surface; and depositing refractory metal on at least the uneven surfaces; selectively forming through annealing a refractory metal silicide layer having grain growth restricted by said predetermined unevenness of said uneven; and selectively removing non-reacted refractory metal layer, wherein formation of said refractory metal silicide layer on the uneven surfaces eliminates deformation and agglomeration of grain of said refractory metal silicide layer and produces said refractory metal silicide layer with a substantially lower resistance, and wherein the step of converting at least the surfaces of said diffusion layers into the surface having the unevenness includes selectively depositing amorphous silicon or polycrystalline silicon at least on the surfaces of said diffusion layers.
Claim 7
Dependent Claim
16 words
A process as set forth in claim 4, wherein said refractory metal is titanium or cobalt.
Claim 8
Dependent Claim
51 words
A process as set forth in claim 5, wherein said silicon layer has a predetermined surface orientation and is directly formed on another single crystal silicon layer having a same surface orientation as said predetermined surface orientation, said silicon layer and said another single crystal silicon layer constituting said semiconductor substrate.
Claim 9
Dependent Claim
52 words
A process as set forth in claim 5, wherein said silicon layer is a polycrystalline silicon layer, and said semiconductor substrate has a laminated structure of a single crystal silicon substrate, an insulation layer covering the surface of said single crystal silicon substrate and said polycrystalline silicon layer covering said insulation layer.
Claim 10
Dependent Claim
57 words
A process as set forth in claim 4, wherein said silicon layer is a single crystal silicon layer having a predetermined surface orientation and is directly formed on another single crystal silicon layer having a same surface orientation as said predetermined surface orientation, said silicon layer and said another single crystal silicon layer constituting said semiconductor substrate.
Claim 11
Dependent Claim
51 words
A process as set forth in claim 4, wherein said silicon layer has a predetermined surface orientation and is directly formed on another single crystal silicon layer having a same surface orientation as said predetermined surface orientation, said silicon layer and said another single crystal silicon layer constituting said semiconductor substrate.
Claim 12
Dependent Claim
52 words
A process as set forth in claim 4, wherein said silicon layer is a polycrystalline silicon layer, and said semiconductor substrate has a laminated structure of a single crystal silicon substrate, an insulation layer covering the surface of said single crystal silicon substrate and said polycrystalline silicon layer covering said insulation layer.
References Cited (Backward Citations)
US3753774A
Cited
US4458410A
Cited
US4498223A
Cited
US4555301A
Cited
US4701349A
Cited
US4873205A
Cited
GB2214708A
Cited
US4965213A
Cited
US4966868A
Cited
JPH02290018A
Cited
JPH0346323A
Cited
US5344793A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-06-21 | 2002-12-21 | 2003-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-06-21 | 2006-12-21 | 2007-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-06-21 | 2010-12-21 | 2011-06-22 | $7700.00 | Window Closed / Lapsed |