Conductive paste compound for via hole filling, printed circuit board which uses the conductive paste, and method of manufacturing the same
Assignee: Dowa Holdings Co Ltd
•
Filing: 1996-05-17
•
Granted: 1999-06-22
•
Expires: 2016-05-17
Abstract
Abstract A conductive paste compound for via hole filling includes a conductive filler at 80 to 92 weight percent with an average particle size of from 0.5 to 20 mu m and specific surface of from 0.1 to 1.5 m2/g, a liquid epoxy resin at 4.5 to 20 weight percent containing 2 or more epoxy groups with room temperature viscosity of 15 Paxsec or less, and a hardener at 0.5 to 5 weight percent, wherein the viscosity is 2,000 Paxsec or less and the volatile amount is 2.0 weight percent or less. A filling paste and a printed circuit board with use thereof are provided which can conduct an inner-via-hole connection between electrode layers without using a through-hole plating technique. The conductive paste comprises a metallic particle such as copper, an epoxy resin, a hardener, and if necessary, a dispersant. The paste having low viscosity and low volatility under high shear is used to fill holes disposed in a laminated substrate. Then, this substrate is heated and pressurized together with copper foil on both sides to attain a printed circuit board where both sides are electrically inner-via-hole connected.
Inventors
- 👤 Kouji Kawakita
- 👤 Seiichi Nakatani
- 👤 Tatsuo Ogawa
- 👤 Masatoshi Suehiro
- 👤 Kouichi Iwaisako
- 👤 Hideo Akiyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 20:36
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K1/095; H01; H01B; H01B1/00; H01B1/20; H01B1/22; H05K3/00; H05K3/40; H05K3/4038; H05K3/4053; H05K3/4069; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0355; H05K2201/10; H05K2201/10227; H05K2201/10378; H05K2203/00; H05K2203/14; H05K2203/1461; H05K3/46; H05K3/4611; H05K3/4614; H05K3/462; H05K3/4623; H05K3/4644; H05K3/4652; H10; H10W; H10W72/00; H10W72/30; H10W72/321; H10W72/325; H10W72/351; H10W72/352; H10W72/353; H10W72/354; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/25
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
119 words
A via hole filling conductive paste compound consisting essentially of (a) a conductive filler in an amount of 80 to 92 weight percent having an average particle size of 0.5 to 20 μm and a specific surface area of 0.1 to 1.5 m 2 /g, (b) a liquid epoxy resin in an amount of 4.5 to 17.0 weight percent which contains two or more epoxy groups which comprises glycidyl esterified dimer acids and has a room temperature viscosity of 15 Pa·s or less, and (c) a hardener in an amount of 0.5 to 5 weight percent, wherein the conductive paste compound has a viscosity of 2,000 Pa·s or less, and contains 2.0 weight percent or less of volatile components.
Claim 2
Dependent Claim
119 words
A via hole filling conductive paste compound consisting essentially of (a) a conductive filler in an amount of 80 to 92 weight percent having an average particle size of 0.5 to 20 μm and a specific surface area of 0.1 to 1.5 m 2 /g, (b) a liquid epoxy resin in an amount of 4.5 to 17.0 weight percent which contains two or more epoxy groups which comprises glycidyl esterified dimer acids and has a room temperature viscosity of 15 Pa·s or less, and (c) a hardener in an amount of 0.5 to 5 weight percent, wherein the conductive paste compound has a viscosity of 2,000 Pa·s or less, and contains 2.0 weight percent or less of volatile components.
Claim 3
Dependent Claim
37 words
The conductive paste compound used for filling via holes as claimed in claim 1, further including a dispersant in an amount of 0.01 to 1.5 weight percent against 100 weight parts of said components (a) to (c).
Claim 4
Dependent Claim
37 words
The conductive paste compound used for filling via holes as in claim 1, wherein said conductive filler comprises at least one fine grain selected from the group consisting of gold, silver, palladium, copper, nickel, tin, and lead.
Claim 5
Dependent Claim
32 words
The conductive paste compound used for filling via holes as in claims 1 or 2, wherein said conductive filler comprises copper with a surface oxygen concentration of 1.0 weight percent or less.
Claim 6
Dependent Claim
50 words
The conductive paste compound used for filling via holes as claimed in claim 1, wherein said epoxy resin comprises at least one liquid epoxy resin selected from the group consisting of bisphenol A epoxy resin, bisphenol F epoxy resin, alicyclic epoxy resin, amine epoxy resin, and glycidyl esterified epoxy resin.
Claim 7
Dependent Claim
57 words
The conductive paste compound used for filling via holes as claimed in claim 1, wherein said liquid epoxy resin contains 10 weight percent or more of an epoxy resin which comprises glycidyl esterified dimer acids, the weight percent of said epoxy containing glycidyl esterified dimer acids being based on the total amount of said liquid epoxy resin.
Claim 8
Dependent Claim
72 words
The conductive paste compound used for filling via holes as claimed in claim 1 or 2, wherein said liquid epoxy resin is a compound comprising 50 weight percent or less of one epoxy resin selected from the group consisting of bisphenol A and bisphenol F, and further comprising 50 weight percent or more of epoxy resin composed of glycidyl esterified dimer acids with an epoxy equivalent of from 300 to 600 g/eq.
Claim 9
Dependent Claim
38 words
The conductive paste compound used for filling via holes as in claim 1, wherein said hardener is at least one hardener selected from the group consisting of amine hardeners, urea hardeners, acid anhydride hardeners, and aromatic amine hardeners.
Claim 10
Dependent Claim
23 words
The conductive paste compound used for filling via holes as claimed in claim 1 or 2, wherein said hardener is a latent hardener.
Claim 11
Dependent Claim
38 words
The conductive paste compound used for filling via holes as claimed in claim 2, wherein said dispersant comprises at least one dispersant selected from the group consisting of nonionic dispersants, anionic dispersants, and a ammonium salt cationic dispersant.
References Cited (Backward Citations)
GB974919A
Cited
US3983075A
Cited
US4383363A
Cited
US4634623A
Cited
US4598037A
Cited
US4747968A
Cited
US4937148A
Cited
EP0279979A1
Cited
US4967314A
Cited
US5055374A
Cited
US5326636A
Cited
US5043102A
Cited
US5242511A
Cited
US4999699A
Cited
US5204025A
Cited
DE4125879A1
Cited
US5346750A
Cited
US5652042A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-06-21 | 2002-12-21 | 2003-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-06-21 | 2006-12-21 | 2007-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-06-21 | 2010-12-21 | 2011-06-22 | $7700.00 | Window Closed / Lapsed |