Carbonated hydroxyapatite compositions and uses
Assignee: Norian Corp
•
Filing: 1996-06-27
•
Granted: 1999-05-04
•
Expires: 2016-06-27
Abstract
Abstract Carbonated hydroxyapatite compositions and their preparation are described. The compositions are biologically resorbable and are prepared as flowable masses which can be administered by syringe to set in situ to serve as a support structure, filler, prosthesis or the like. Optionally the compositions may include proteins or serve as a depot for compositions of phrarmacological interest.
Inventors
- 👤 Brent R. Constantz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:05
CPC Classifications
A; A61; A61L; A61L24/00; A61L24/02; A61K; A61K6/00; A61K6/60; A61K6/69; A61K6/70; A61K6/71; A61K6/74; A61K6/75; A61L27/00; A61L27/02; A61L27/12; A61L27/40; A61L27/44; A61L27/46; A61L27/50; A61L27/58; C; C01; C01B; C01B25/00; C01B25/16; C01B25/26; C01B25/32; C01B25/322; C01B25/327; C01B25/455; A61F; A61F2/00; A61F2/02; A61F2/28; A61F2002/2817; A61F2/30; A61F2002/30001; A61F2002/30003; A61F2002/3006; A61F2002/30062; A61F2210/00; A61F2210/0004; A61F2310/00; A61F2310/00005; A61F2310/00179; A61F2310/00293
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
174 words
A two-part calcium phosphate cement formulation that, when mixed, is capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1,33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, and which two-part calcium phosphate cement formulation contains: as the first part dry ingredients comprising a partially neutralized phosphoric acid, a calcium phosphate source, and calcium carbonate in an amount ranging front about 9.33 to 70 wt % of said dry ingredients; and as the second part a physiologically acceptable aqueous lubricant solution selected from the group consisting of 0.01 to 2M sodium phosphate solution at pH 6 to 11 and 0.01 to 2M sodium carbonate solution at pH 6 to 11, wherein said aqueous lubricant solution is present in an amount ranging from about 15 to 50 wt % of the two-part calcium phosphate cement formulation.
Claim 2
Dependent Claim
174 words
A two-part calcium phosphate cement formulation that, when mixed, is capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1,33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, and which two-part calcium phosphate cement formulation contains: as the first part dry ingredients comprising a partially neutralized phosphoric acid, a calcium phosphate source, and calcium carbonate in an amount ranging front about 9.33 to 70 wt % of said dry ingredients; and as the second part a physiologically acceptable aqueous lubricant solution selected from the group consisting of 0.01 to 2M sodium phosphate solution at pH 6 to 11 and 0.01 to 2M sodium carbonate solution at pH 6 to 11, wherein said aqueous lubricant solution is present in an amount ranging from about 15 to 50 wt % of the two-part calcium phosphate cement formulation.
Claim 3
Dependent Claim
23 words
The cement according to claim 1, wherein said partially neutralized phosphoric acid source is Ca(H 2 PO 4 ) 2 .H 2 O.
Claim 4
Dependent Claim
14 words
The cement according to claim 1, wherein said calcium phosphate source is tricalcium phosphate.
Claim 5
Dependent Claim
173 words
A two-part calcium phosphate cement formulation that, when mixed, is capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, and which two-part calcium phosphate cement formulation contains: as the first part dry ingredients comprising a partially neutralized phosphoric acid, a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 40 wt % of said dry ingredients; and as the second part a physiologically acceptable aqueous lubricant solution selected from the group consisting of 0.01 to 2M sodium phosphate solution at pH 6 to 11 and 0.01 to 2M sodium carbonate solution at pH 6 to 11, wherein said aqueous lubricant solution is present in an amount ranging from about 15 to 50 wt % of the two-part calcium phosphate cement formulation.
Claim 6
Dependent Claim
173 words
A two-part calcium phosphate cement formulation that, when mixed, is capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, and which two-part calcium phosphate cement formulation contains: as the first part dry ingredients comprising a partially neutralized phosphoric acid, a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 40 wt % of said dry ingredients; and as the second part a physiologically acceptable aqueous lubricant solution selected from the group consisting of 0.01 to 2M sodium phosphate solution at pH 6 to 11 and 0.01 to 2M sodium carbonate solution at pH 6 to 11, wherein said aqueous lubricant solution is present in an amount ranging from about 15 to 50 wt % of the two-part calcium phosphate cement formulation.
Claim 7
Dependent Claim
24 words
The cement according to claim 4, wherein said aqueous lubricant solution is a 0.01 to 2M sodium phosphate solution at pH 6 to 11.
Claim 8
Dependent Claim
22 words
The cement according to claim 4, wherein said partially neutralized phosphoric acid is Ca(H 2 PO 4 ) 2 .H 2 O.
Claim 9
Dependent Claim
150 words
A two-part calcium phosphate cement formulation that, when mixed, is capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) and is biocompatible, and which two-part calcium phosphate cement formulation contains: as the first part dry ingredients comprising Ca(H 2 PO 4 ) 2 . H 2 O, a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 18 wt % of said dry ingredients; and as the second part a 0.01 to 2M sodium phosphate solution at pH 6 to 11 present in an amount ranging from about 15 to 50 wt % of the two-part calcium phosphate cement formulation.
Claim 10
Dependent Claim
150 words
A two-part calcium phosphate cement formulation that, when mixed, is capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) and is biocompatible, and which two-part calcium phosphate cement formulation contains: as the first part dry ingredients comprising Ca(H 2 PO 4 ) 2 . H 2 O, a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 18 wt % of said dry ingredients; and as the second part a 0.01 to 2M sodium phosphate solution at pH 6 to 11 present in an amount ranging from about 15 to 50 wt % of the two-part calcium phosphate cement formulation.
Claim 11
Dependent Claim
180 words
A kit for use in the preparation of a composition capable of hardening and forming air integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, said kit comprising: dry ingredients comprising a partially neutralized phosphoric acid, a calcium phosphate source, and calcium carbonate in an amount ranging from about 9.33 to 70 wt % of said dry ingredients; and a physiologically acceptable aqueous lubricant solution selected from the group consisting of 0.01 to 2M sodium phosphate solution at pH 6 to 11 and 0.01 to 2M sodium carbonate solution at pH 6 to 11, wherein said aqueous lubricant solution is physically separated from the dry ingredients of said kit and is present in an amount ranging from about 15 to 50 wt % of the total weight of said dry ingredients and said aqueous lubricant of said kit.
Claim 12
Dependent Claim
180 words
A kit for use in the preparation of a composition capable of hardening and forming air integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, said kit comprising: dry ingredients comprising a partially neutralized phosphoric acid, a calcium phosphate source, and calcium carbonate in an amount ranging from about 9.33 to 70 wt % of said dry ingredients; and a physiologically acceptable aqueous lubricant solution selected from the group consisting of 0.01 to 2M sodium phosphate solution at pH 6 to 11 and 0.01 to 2M sodium carbonate solution at pH 6 to 11, wherein said aqueous lubricant solution is physically separated from the dry ingredients of said kit and is present in an amount ranging from about 15 to 50 wt % of the total weight of said dry ingredients and said aqueous lubricant of said kit.
Claim 13
Dependent Claim
22 words
The kit according to claim 8, wherein said partially neutralized phosphoric acid is Ca(H 2 PO 4 ) 2 .H 2 O.
Claim 14
Dependent Claim
14 words
The kit according to claim 9, wherein said calcium phosphate source is tricalcium phosphate.
Claim 15
Dependent Claim
24 words
The kit according to claim 8, wherein said aqueous lubricant solution is a 0.01 to 2M sodium phosphate solution at pH 6 to 11.
Claim 16
Dependent Claim
16 words
The kit according to claim 8, wherein at least two of said dry ingredients are combined.
Claim 17
Dependent Claim
161 words
A kit for use in the preparation of a composition capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, said kit comprising: dry ingredients comprising Ca(H 2 PO 4 ) 2 .H 2 O, a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 40 wt % of said dry ingredients; and a 0.01 to 2M sodium phosphate solution at pH 6 to 11, wherein said sodium phosphate solution is physically separated from the dry ingredients of said kit and is present in an amount ranging from about 15 to 50 wt % of the total weight of said dry ingredients and said sodium phosphate solution of said kit.
Claim 18
Dependent Claim
161 words
A kit for use in the preparation of a composition capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, said kit comprising: dry ingredients comprising Ca(H 2 PO 4 ) 2 .H 2 O, a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 40 wt % of said dry ingredients; and a 0.01 to 2M sodium phosphate solution at pH 6 to 11, wherein said sodium phosphate solution is physically separated from the dry ingredients of said kit and is present in an amount ranging from about 15 to 50 wt % of the total weight of said dry ingredients and said sodium phosphate solution of said kit.
Claim 19
Dependent Claim
162 words
A kit for use in the preparation of a composition capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, said kit comprising: dry ingredients comprising Ca(H 2 PO 4 ) 2 .H 2 O , a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 18 wt % of said dry ingredients; and a 0.01 to 2M sodium phosphate solution at pH 6 to 11, wherein said sodium phosphate solution is physically separated from the dry ingredients of said kit and is present in an amount ranging front about 15 to 50 wt % of the total weight of said dry ingredients and said sodium phosphate solution of said kit.
Claim 20
Dependent Claim
162 words
A kit for use in the preparation of a composition capable of hardening and forming an integral mass, wherein said integral mass is substantially pure 2 to 10 wt % carbonate-substituted hydroxyapatite that (i) has a calcium/phosphate molar ratio of about 1.33 to 2.0, (ii) is not sintered or hydrothermally prepared, (iii) has a compressive strength ranging from about 5620 to 11794 psi, and (iv) is biocompatible, said kit comprising: dry ingredients comprising Ca(H 2 PO 4 ) 2 .H 2 O , a tricalcium phosphate, and calcium carbonate in an amount ranging from about 9.33 to 18 wt % of said dry ingredients; and a 0.01 to 2M sodium phosphate solution at pH 6 to 11, wherein said sodium phosphate solution is physically separated from the dry ingredients of said kit and is present in an amount ranging front about 15 to 50 wt % of the total weight of said dry ingredients and said sodium phosphate solution of said kit.
References Cited (Backward Citations)
US33221A
Cited
US33161A
Cited
US3647371A
Cited
FR2096886A1
Cited
US4139599A
Cited
US4048300A
Cited
US3873327A
Cited
US3913229A
Cited
AU518908B2
Cited
GB1487181A
Cited
US4170658A
Cited
US4321042A
Cited
US4097935A
Cited
JPS53111000A
Cited
US4279661A
Cited
US4335086A
Cited
EP0026090A2
Cited
US4429691A
Cited
JPS5770216A
Cited
US4324772A
Cited
JPS5889288A
Cited
US4481174A
Cited
US4518430A
Cited
USRE33161E
Cited
USRE33221E
Cited
JPS5956676A
Cited
JPS59192365A
Cited
US4612053A
Cited
US4917702A
Cited
JPS624637A
Cited
US4959104A
Cited
JPS62193482A
Cited
JPS63252913A
Cited
WO1988009769A1
Cited
JPS6474591A
Cited
JPH01130423A
Cited
US5180426A
Cited
JPH01203801A
Cited
JPH01266235A
Cited
US5336264A
Cited
JPH01310544A
Cited
WO1990000892A1
Cited
JPH02117445A
Cited
JPH02117444A
Cited
JPH02255082A
Cited
US5092888A
Cited
JPH03123609A
Cited
JPH03174349A
Cited
JPH03283213A
Cited
US5536575A
Cited
US5569490A
Cited
GB2248232A
Cited
US5152836A
Cited
US5322675A
Cited
US5149368A
Cited
US5262166A
Cited
JPH04348754A
Cited
JPH04348755A
Cited
US5782971B1
Cited
US5782971A
Cited
JPH059383A
Cited
JPH0523386A
Cited
GB2260977A
Cited
US5338356A
Cited
EP0543765A1
Cited
US5320844A
Cited
JPH05319891A
Cited
FR2693716A1
Cited
JPH0645494A
Cited
EP0625490B1
Cited
US5580623A
Cited
EP0639366A1
Cited
WO1995008304A1
Cited
US5525148A
Cited
WO1995008319A1
Cited
CA2143733A1
Cited
US5683496A
Cited
US5571493A
Cited
US5709742A
Cited
WO1996029144A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-05-03 | 2002-11-02 | 2003-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-05-03 | 2006-11-02 | 2007-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-05-03 | 2010-11-02 | 2011-05-04 | $7700.00 | Window Closed / Lapsed |