Self-setting calcium phosphate cements and methods for preparing and using them
Assignee: American Dental Association
•
Filing: 1993-09-24
•
Granted: 1996-06-11
•
Expires: 2013-09-24
Abstract
Abstract The invention includes methods and compositions relating to calcium phosphate cements, which self-harden substantially to hydroxyapatite at ambient temperature when in contact with an aqueous medium. More specifically the cements comprise a combination of one or more sparingly soluble calcium phosphates other than tetracalcium phosphate with an aqueous solution adjusted with a base to maintain a pH of about 12.5 or above and having sufficient dissolved phosphate salt to yield a solution mixture with phosphate concentration equal to or greater than about 0.2 mol/L.
Inventors
- 👤 Laurence C. Chow
- 👤 Shozo Takagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 01:47
CPC Classifications
A; A61; A61L; A61L24/00; A61L24/02; A61K; A61K6/00; A61K6/50; A61K6/54; A61K6/60; A61K6/69; A61K6/80; A61K6/831; A61K6/838; A61K6/849; A61K6/864; A61K6/873; A61K6/876; A61L27/00; A61L27/02; A61L27/12; A61F; A61F2310/00; A61F2310/00005; A61F2310/00179; A61F2310/00293
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
108 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising (1) preparing an aqueous solution of phosphate having a concentration of about 0.2 mol/L or above and adjusting the pH of the solution with base to about 12.5 or above, and (2) combining the aqueous solution with a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, and with an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, in the absence of solid crystalline phosphoric acid.
Claim 2
Independent Claim
108 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising (1) preparing an aqueous solution of phosphate having a concentration of about 0.2 mol/L or above and adjusting the pH of the solution with base to about 12.5 or above, and (2) combining the aqueous solution with a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, and with an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, in the absence of solid crystalline phosphoric acid.
Claim 3
Independent Claim
100 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising preparing a mixture of a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water, a non-calcium containing phosphate salt at a concentration of about 0.2 mols/L or above and base effective to adjust the pH to about 12.5 or above, in the absence of solid crystalline phosphoric acid.
Claim 4
Independent Claim
100 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising preparing a mixture of a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water, a non-calcium containing phosphate salt at a concentration of about 0.2 mols/L or above and base effective to adjust the pH to about 12.5 or above, in the absence of solid crystalline phosphoric acid.
Claim 5
Independent Claim
69 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising combining a calcium phosphate salt consisting essentially of dicalcium phosphate or dicalcium phosphate dihydrate, with an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide and an aqueous solution adjusted with base to maintain a pH of about 12.5 or above.
Claim 6
Independent Claim
69 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising combining a calcium phosphate salt consisting essentially of dicalcium phosphate or dicalcium phosphate dihydrate, with an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide and an aqueous solution adjusted with base to maintain a pH of about 12.5 or above.
Claim 7
Independent Claim
68 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising preparing a mixture of a calcium phosphate salt consisting essentially of dicalcium phosphate or dicalcium phosphate dihydrate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water and base effective to maintain a pH of about 12.5 or above.
Claim 8
Independent Claim
68 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising preparing a mixture of a calcium phosphate salt consisting essentially of dicalcium phosphate or dicalcium phosphate dihydrate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water and base effective to maintain a pH of about 12.5 or above.
Claim 9
Independent Claim
102 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising (1) preparing an aqueous solution of a non-calcium containing salt of phosphoric acid having a concentration of phosphate of about 0.2 mols/L or above, and (2) combining the aqueous solution with a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, and with an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, in the absence of solid crystalline phosphoric acid.
Claim 10
Independent Claim
102 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising (1) preparing an aqueous solution of a non-calcium containing salt of phosphoric acid having a concentration of phosphate of about 0.2 mols/L or above, and (2) combining the aqueous solution with a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, and with an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, in the absence of solid crystalline phosphoric acid.
Claim 11
Independent Claim
93 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising preparing a mixture of a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water and a non-calcium containing salt of phosphoric acid at a concentration of phosphate of about 0.2 mols/L or above, in the absence of solid crystalline phosphoric acid.
Claim 12
Independent Claim
93 words
A method for making a calcium phosphate cement which self-sets to hydroxyapatite as the predominant product at ambient temperatures comprising preparing a mixture of a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water and a non-calcium containing salt of phosphoric acid at a concentration of phosphate of about 0.2 mols/L or above, in the absence of solid crystalline phosphoric acid.
Claim 13
Dependent Claim
85 words
A calcium phosphate composition which self-hardens to hydroxyapatite as the predominant product at ambient temperature comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, and an aqueous phosphate solution of pH about 12.5 or above with phosphate concentration of about 0.2 mol/L or above, in the absence of solid crystalline phosphoric acid.
Claim 14
Dependent Claim
85 words
A calcium phosphate composition which self-hardens to hydroxyapatite as the predominant product at ambient temperature comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, and an aqueous phosphate solution of pH about 12.5 or above with phosphate concentration of about 0.2 mol/L or above, in the absence of solid crystalline phosphoric acid.
Claim 15
Dependent Claim
88 words
A calcium phosphate composition which self-hardens to hydroxyapatite as the predominant product at ambient temperature comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water, phosphate salt at a concentration of about 0.2 mols/L or above and base effective to maintain the pH at 12.5 or above, in the absence of solid crystalline phosphoric acid.
Claim 16
Dependent Claim
88 words
A calcium phosphate composition which self-hardens to hydroxyapatite as the predominant product at ambient temperature comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water, phosphate salt at a concentration of about 0.2 mols/L or above and base effective to maintain the pH at 12.5 or above, in the absence of solid crystalline phosphoric acid.
Claim 17
Dependent Claim
58 words
A calcium phosphate composition, which self-hardens to hydroxyapatitc as the predominant product at ambient temperature, comprising a calcium phosphate consisting essentially of dicalcium phosphate or dicalcium phosphate dihydrate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide and an aqueous solution having a pH of about 12.5 or above.
Claim 18
Dependent Claim
58 words
A calcium phosphate composition, which self-hardens to hydroxyapatitc as the predominant product at ambient temperature, comprising a calcium phosphate consisting essentially of dicalcium phosphate or dicalcium phosphate dihydrate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide and an aqueous solution having a pH of about 12.5 or above.
Claim 19
Dependent Claim
60 words
A calcium phosphate composition, which self-hardens to hydroxyapatite as the predominant product at ambient temperature, comprising a calcium phosphate consisting essentially of elicalcium phosphate or dicalcium phosphate dihidrate, an additional source of calcium selected from the group consisting of calcium carbonate calcium oxide and calcium hydroxide, water and a base effective to adjust the pH to about 12.5 or above.
Claim 20
Dependent Claim
60 words
A calcium phosphate composition, which self-hardens to hydroxyapatite as the predominant product at ambient temperature, comprising a calcium phosphate consisting essentially of elicalcium phosphate or dicalcium phosphate dihidrate, an additional source of calcium selected from the group consisting of calcium carbonate calcium oxide and calcium hydroxide, water and a base effective to adjust the pH to about 12.5 or above.
Claim 21
Dependent Claim
88 words
A calcium phosphate composition, which self-hardens to hydroxyapatite as the predominant product at ambient temperature, comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the the group consisting of calcium carborate, calcium oxide and calcium hydroxide, and an aqueous phosphate solution of a non-calcium containing salt of phosphoric acid with phosphate concentration of about 0.2 mols/L or above in the absence of solid crystalline phosphoric acid.
Claim 22
Dependent Claim
88 words
A calcium phosphate composition, which self-hardens to hydroxyapatite as the predominant product at ambient temperature, comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the the group consisting of calcium carborate, calcium oxide and calcium hydroxide, and an aqueous phosphate solution of a non-calcium containing salt of phosphoric acid with phosphate concentration of about 0.2 mols/L or above in the absence of solid crystalline phosphoric acid.
Claim 23
Dependent Claim
83 words
A calcium phosphate composition, which self-hardens to hydroxyapatite as the predominant product at ambient temperature, comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water and a non-calcium containing salt of phosphoric acid at a concentration of about 0.2 mols/L or above in the absence of solid crystalline phosphoric acid.
Claim 24
Dependent Claim
83 words
A calcium phosphate composition, which self-hardens to hydroxyapatite as the predominant product at ambient temperature, comprising a calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, water and a non-calcium containing salt of phosphoric acid at a concentration of about 0.2 mols/L or above in the absence of solid crystalline phosphoric acid.
Claim 25
Dependent Claim
84 words
A self-setting calcium phosphate bone cement comprising a mixture of (1) calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, (2) an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, and (3) an aqueous phosphate solution of pH of about 12.5 or above with a concentration of phosphate of about 0.2 mols/L or above, in the absence of solid crystalline phosphoric acid.
Claim 26
Dependent Claim
84 words
A self-setting calcium phosphate bone cement comprising a mixture of (1) calcium phosphate salt having a calcium to phosphorus molar ratio of less than 5 to 3 which is other than tetracalcium phosphate, (2) an additional source of calcium selected from the group consisting of calcium carbonate, calcium oxide and calcium hydroxide, and (3) an aqueous phosphate solution of pH of about 12.5 or above with a concentration of phosphate of about 0.2 mols/L or above, in the absence of solid crystalline phosphoric acid.
Claim 27
Dependent Claim
33 words
The method of claim 1 wherein the calcium phosphate salt is selected from the group consisting of dicalcium phosphate anhydrous, dicaleium phosphate dihydrate, α-tricalcium phosphate, amorphous calcium phosphate, octacalcium phosphate and β-tricalcium phosphate.
Claim 28
Dependent Claim
24 words
The method of claim 1 wherein the base employed to adjust the pH of the solution to about 12.5 or above is sodium hydroxide.
Claim 29
Dependent Claim
31 words
The composition of claim 7 further including fluoride containing compounds such that the fluoride content of the composition is in an amount sufficient to increase the rate of formation of hydroxyapatite.
Claim 30
Dependent Claim
34 words
The composition of claim 16 wherein the fluoride compounds are selected from the group consisting of NaF, CaF 2 , SnF 2 , Na 2 PO 3 F, and Na 2 SiF 6 .
Claim 31
Dependent Claim
17 words
The composition of claim 16 wherein the fluoride content in the composition is about 3.8% by weight.
Claim 32
Dependent Claim
31 words
The composition in claim 7 further including a seed crystal compound from the group consisting of HA and fluorapatite in an amount sufficient to reduce the setting time of the cement.
Claim 33
Dependent Claim
20 words
A calcium phosphate cement that is a tissue substitute having as a calcium phosphate component the composition of claim 7.
Claim 34
Dependent Claim
20 words
A calcium phosphate cement that is a tissue substitute having as a calcium phosphate component the composition of claim 9.
Claim 35
Dependent Claim
20 words
A calcium phosphate cement that is a tissue substitute having as a calcium phosphate component the composition of claim 11.
Claim 36
Dependent Claim
29 words
A calcium phosphate bone cement which self-sets to hydroxyapatite at ambient temperature and is substantially resorbable when implanted in contact with living bone comprising the composition of claim 7.
Claim 37
Dependent Claim
29 words
A calcium phosphate bone cement which self-sets to hydroxyapatite at ambient temperature and is substantially resorbable when implanted in contact with living bone comprising the composition of claim 7.
Claim 38
Dependent Claim
29 words
A calcium phosphate bone cement which self-sets to hydroxyapatite at ambient temperature and is substantially resorbable when implanted in contact with living bone comprising the composition of claim 11.
Claim 39
Dependent Claim
33 words
The composition of claim 7 further comprising an additive selected from the group consisting of medicaments, filler materials, crystal adjustors, viscosity modifiers, pore forming agents, osteoinductive factors, bone morphogenic proteins and other proteins.
Claim 40
Dependent Claim
9 words
The composition of claim 26 further including gelling agents.
Claim 41
Dependent Claim
23 words
The composition of claim 27 wherein the gelling agents are selected from the group consisting of hydroxypropyl methylcellulose, carboxyl methylcellulose, starch, proteoglycans, glycoproteins.
Claim 42
Dependent Claim
24 words
The composition of claim 7 further including medicaments such that the medicaments are released into the suffounding living tissue over a period of time.
Claim 43
Dependent Claim
19 words
The composition of claim 7 which includes filler materials in sufficient amounts to increase the strength of the cement.
Claim 44
Dependent Claim
25 words
The composition of claim 30 wherein the filler materials are selected from the group of non-toxic biocompatible natural or synthetic polymers and non-toxic biocompatible metal.
Claim 45
Dependent Claim
26 words
The composition of claim 7 further including pore forming agents that form pores of a diameter effective to cause vascularization of tissue which infiltrates the composition.
Claim 46
Dependent Claim
39 words
The composition of claim 32 wherein the pore forming agents are materials that are sufficiently insoluble in the cement and can be removed by dissolution in physiological fluids, removed by solvents or heating after the hardening of the cement.
References Cited (Backward Citations)
US3679360A
Cited
US3787900A
Cited
US3929971A
Cited
US3913229A
Cited
US4097935A
Cited
US4599085A
Cited
US4497075A
Cited
USRE33161E
Cited
USRE33221E
Cited
US4880610A
Cited
US5047031A
Cited
US5053212A
Cited
US5129905A
Cited
US5034059A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-06-11 | 1999-12-11 | 2000-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-06-11 | 2003-12-11 | 2004-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-06-11 | 2007-12-11 | 2008-06-11 | $7700.00 | Window Closed / Lapsed |