Self-aligned contact structures using high selectivity etching
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-01-12
•
Granted: 1999-02-16
•
Expires: 2018-01-12
Abstract
Abstract A self-aligned structure and method of etching contact holes in the self-aligned structure are described. The dielectric materials, etching methods, and etchants are chosen to provide high selectivity etching. The structure comprises an electrode with a silicon oxy-nitride cap and silicon oxy-nitride spacers on the sidewalls of the electrode and the cap. An etch stop layer of silicon nitride is deposited over the substrate covering the spacers and cap. A layer of silicon oxide is deposited over the etch stop layer. Etching methods and etchants are used which provide a ratio of the etching rate of silicon oxide to the etching rate of silicon nitride or silicon oxy-nitride of at least eight and a ratio of the etching rate of silicon nitride to the etching rate of silicon oxy-nitride of at least two.
Inventors
- 👤 Li-chih Chao
- 👤 Jhon-Jhy Liaw
- 👤 Yuan-Chang Huang
- 👤 Jin-Yuan Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:32
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/069; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; Y; Y10; Y10S; Y10S257/00; Y10S257/90
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
229 words
A method of forming a contact structure, comprising the steps of: providing a substrate having devices formed therein and an electrode formed thereon, wherein said electrode has a top and sidewalls; forming a first dielectric cap on said top of said electrode, wherein said first dielectric cap has sidewalls; forming spacers of said first dielectric on said sidewalls of said electrode and said sidewalls of said first dielectric cap; depositing a layer of second dielectric on said substrate thereby covering said first dielectric cap and said first dielectric spacers; depositing a layer of third dielectric on said layer of second dielectric; forming a photoresist contact hole mask; etching a contact hole in said layer of third dielectric using said photoresist contact hole mask and a first etching means, wherein said first etching means provides a ratio of the etching rate of said third dielectric to the etching rate of said first dielectric of at least eight and a ratio of the etching rate of said third dielectric to the etching rate of said second dielectric of at least eight; removing said photoresist contact hole mask; and etching said contact hole in said layer of second dielectric using a second etching means wherein said second etching means provides a ratio of the etching rate of said second dielectric to the etching rate of said first dielectric of at least two.
Claim 2
Independent Claim
229 words
A method of forming a contact structure, comprising the steps of: providing a substrate having devices formed therein and an electrode formed thereon, wherein said electrode has a top and sidewalls; forming a first dielectric cap on said top of said electrode, wherein said first dielectric cap has sidewalls; forming spacers of said first dielectric on said sidewalls of said electrode and said sidewalls of said first dielectric cap; depositing a layer of second dielectric on said substrate thereby covering said first dielectric cap and said first dielectric spacers; depositing a layer of third dielectric on said layer of second dielectric; forming a photoresist contact hole mask; etching a contact hole in said layer of third dielectric using said photoresist contact hole mask and a first etching means, wherein said first etching means provides a ratio of the etching rate of said third dielectric to the etching rate of said first dielectric of at least eight and a ratio of the etching rate of said third dielectric to the etching rate of said second dielectric of at least eight; removing said photoresist contact hole mask; and etching said contact hole in said layer of second dielectric using a second etching means wherein said second etching means provides a ratio of the etching rate of said second dielectric to the etching rate of said first dielectric of at least two.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein said first dielectric is silicon oxy-nitride.
Claim 4
Dependent Claim
22 words
The method of claim 1 wherein said second dielectric is silicon nitride having a thickness of between about 100 and 800 Angstroms.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said third dielectric is silicon oxide having a thickness of between about 1000 and 20,000 Angstroms.
Claim 6
Dependent Claim
47 words
The method of claim 1 wherein said first dielectric is silicon oxy-nitride, said second dielectric is silicon nitride, said third dielectric is silicon oxide and said first etching means uses dry anisotropic etching and an etchant comprising C 4 F 8 , CH 3 F, and Ar.
Claim 7
Dependent Claim
34 words
The method of claim 5 wherein said dry anisotropic etching uses a source power of between about 1200 watts and 1600 watts and a bias power of between about 1200 watts and 1600 watts.
Claim 8
Dependent Claim
51 words
The method of claim 5 wherein said etchant comprises C 4 F 8 at a flow rate of between about 10 and 15 sccm, CH 3 F at a flow rate of between about 5 and 15 sccm, and Ar at a flow rate of between about 50 and 100 sccm.
Claim 9
Dependent Claim
40 words
The method of claim 1 wherein said first dielectric is silicon oxy-nitride, said second dielectric is silicon nitride, and said first etching means uses a dry anisotropic etching and an etchant comprising CH 3 F, O 2 , and Ar.
Claim 10
Dependent Claim
32 words
The method of claim 8 wherein said dry anisotropic etching uses a source power of between about 1800 and 2200 watts and a bias power of between about 100 and 300 watts.
Claim 11
Dependent Claim
49 words
The method of claim 8 wherein said etchant comprises CH 3 F at a flow rate of between about 10 and 20 sccm, O 2 at a flow rate of between about 5 and 20 sccm, and Ar at a flow rate of between about 50 and 100 sccm.
Claim 12
Dependent Claim
39 words
The method of claim 1 wherein a fourth dielectric is formed between said electrode and said substrate, said fourth dielectric has sidewalls, and said spacers of said first dielectric are also formed on said sidewalls of said fourth dielectric.
Claim 13
Dependent Claim
12 words
The method of claim 1 wherein said substrate is a silicon substrate.
Claim 14
Dependent Claim
12 words
The method of claim 1 wherein said electrode is a polysilicon electrode.
Claim 15
Dependent Claim
19 words
The method of claim 1 wherein said removing said photoresist contact hole mask is accomplished using an oxygen plasma.
References Cited (Backward Citations)
US4455737A
Cited
US4954867A
Cited
US5352621A
Cited
US5286667A
Cited
US5691246A
Cited
US5716862A
Cited
US5364804A
Cited
US5578524A
Cited
US5741719A
Cited
US5674787A
Cited
US5668039A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-02-15 | 2002-08-17 | 2003-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-02-15 | 2006-08-17 | 2007-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-02-15 | 2010-08-17 | 2011-02-16 | $7700.00 | Window Closed / Lapsed |