High dielectric constant thin film structure method for forming high dielectric constant thin film and apparatus for forming high dielectric contact thin film
Assignee: Mitsubishi Electric Corp
•
Filing: 1996-10-01
•
Granted: 1998-11-10
•
Expires: 2016-10-01
Abstract
Abstract There is provided a (Ba, Sr) TiO3 film of higher dielectric constant and less leakage current for serving as a dielectric thin film of a capacitor in a semiconductor memory. DPM (dipivaloylmethanato) compounds of Ba, Sr and Ti are dissolved in THF (tetrahydrofuran) to obtain Ba(DPM)2/THF, Sr(DPM)2/THF and TiO(DPM)2/THF solutions which are used as source material solutions. A (Ba, Sr) TiO3 film is formed by a CVD method while increasing a relative percentage of a Ti source material flow rate to a sum of Ba source material flow rate and Sr source material flow rate. The film formation is carried out in multiple steps, and annealing is applied in each step after deposition of the film.
Inventors
- 👤 Takaaki Kawahara
- 👤 Mikio Yamamuka
- 👤 Tetsuro Makita
- 👤 Tsuyoshi Horikawa
- 👤 Akimasa Yuuki
- 👤 Teruo Shibano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:11
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6938; H10P14/69398; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/409; C23C16/44; C23C16/448; C23C16/4481; C23C16/4485; C23C16/52; C23C16/56; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/682; H10D1/684; H10D64/00; H10D64/01; H10D64/013; H10P14/40; H10P14/42; H10P14/43; H10P14/66; H10P14/668; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6342; H10P14/65; H10P14/6502; H10P14/6506; H10P14/6516; H10P14/6529; H10P14/6544; Y; Y10; Y10S; Y10S427/00; Y10S427/101
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
119 words
A method for forming a dielectric film by CVD, said method comprising the steps of: providing two or more organometallic compounds; depositing, by CVD, metal oxide on a substrate concurrently using said two or more organometallic compounds as source materials for corresponding metallic elements to be deposited in said dielectric film; and varying a surface temperature of said substrate, during said deposition step, to change a composition ratio, in the film thickness direction, of said metallic elements in said dielectric film; wherein said deposition of said metal oxide is by decomposition of at least one of said organometallic compounds, and said decomposition of said at least one of said organometallic compounds depends on said surface temperature of said substrate.
Claim 2
Independent Claim
119 words
A method for forming a dielectric film by CVD, said method comprising the steps of: providing two or more organometallic compounds; depositing, by CVD, metal oxide on a substrate concurrently using said two or more organometallic compounds as source materials for corresponding metallic elements to be deposited in said dielectric film; and varying a surface temperature of said substrate, during said deposition step, to change a composition ratio, in the film thickness direction, of said metallic elements in said dielectric film; wherein said deposition of said metal oxide is by decomposition of at least one of said organometallic compounds, and said decomposition of said at least one of said organometallic compounds depends on said surface temperature of said substrate.
Claim 3
Independent Claim
169 words
A method for forming a dielectric film, said method comprising: providing two or more organometallic compounds; depositing, by CVD, metal oxide on a substrate using said two or more organometallic compounds as source materials for corresponding metallic elements to be deposited in said dielectric film; and varying a surface temperature of said substrate, during said deposition step, to change a composition ratio, in the film thickness direction, of said metallic elements in said thin film; wherein said deposition of said metal oxide is by decomposition of at least one of said organometallic compounds, and said decomposition of said at least one of said organometallic compounds depends on said surface temperature of said substrate; wherein said organometallic compounds comprise a Ba dipivaloylmethanato compound, a Sr dipivaloylmethanato compound, and a Ti dipivaloylmethanato compound; wherein said at least one of said organometallic compounds is said Ti dipivaloylmethanato compound; and wherein said deposition of said metal oxide by said decomposition of said Ti dipivaloylmethanato compound depends on said surface temperature of said substrate.
Claim 4
Independent Claim
169 words
A method for forming a dielectric film, said method comprising: providing two or more organometallic compounds; depositing, by CVD, metal oxide on a substrate using said two or more organometallic compounds as source materials for corresponding metallic elements to be deposited in said dielectric film; and varying a surface temperature of said substrate, during said deposition step, to change a composition ratio, in the film thickness direction, of said metallic elements in said thin film; wherein said deposition of said metal oxide is by decomposition of at least one of said organometallic compounds, and said decomposition of said at least one of said organometallic compounds depends on said surface temperature of said substrate; wherein said organometallic compounds comprise a Ba dipivaloylmethanato compound, a Sr dipivaloylmethanato compound, and a Ti dipivaloylmethanato compound; wherein said at least one of said organometallic compounds is said Ti dipivaloylmethanato compound; and wherein said deposition of said metal oxide by said decomposition of said Ti dipivaloylmethanato compound depends on said surface temperature of said substrate.
Claim 5
Independent Claim
475 words
A method for forming a barium strontium titanate (Ba, Sr) TiO 3 film (BST film), comprising: (a) obtaining accumulated data with respect to a plurality of sample film operations, including: (a-1) determining a constant Ba flow rate for Ba source material and a constant Sr flow rate for Sr source material; (a-2) performing a sample film operation, including: (a-2-i) providing a sample with a sample substrate comprising a sample substrate material having a sample substrate thickness, (a-2-ii) providing said sample with a sample coating material at a sample coating material thickness, said sample coating material coating a respective percentage of said sample substrate, (a-2-iii) selecting a heating temperature, (a-2-iv) selecting a Ti flow rate for Ti source material, (a-2-v) depositing a sample BST film on said sample using said selected heating temperature, said selected Ti flow rate, said constant Ba flow rate, and said constant Sr flow rate, (a-2-vi) measuring a sample composition ratio of Ti, Ba, and Sr in said sample BST film, and (a-2-vii) recording, as said accumulated data, a sample parameter set including respective sample values for: said sample coating material, said percentage of said sample substrate coated by said sample coating material, said sample coating material thickness, said sample substrate thickness, said selected heating temperature, said selected Ti flow rate, and said sample composition ratio; (a-3) performing said sample film operation a plurality of times, including varying at least one of: said sample coating material, said percentage of said sample substrate coated by said sample coating material, said sample coating material thickness, said sample substrate thickness, said selected heating temperature, and said selected Ti flow rate; (b) providing and measuring a target to be coated, including: (b-1) providing a target substrate comprising a target substrate material having a target substrate thickness, (b-2) providing on said target a target coating material at a target coating material thickness, said target coating material coating a respective percentage of said target substrate, (b-3) selecting a target composition ratio of Ti, Ba, and Sr for a target BST film, (b-4) measuring said target substrate thickness, said target coating material thickness, and said respective percentage of said target substrate coated by said target coating material, and (b-5) selecting a target heating temperature; (c) using said accumulated data to determine a target Ti flow rate based on one of said plurality of sample film operations having said sample parameter set with said respective sample values substantially similar to values for said target coating material, said percentage of said target substrate coated by said target coating material, said target coating material thickness, said target substrate thickness, said selected target heating temperature, and said target composition ratio; and (d) forming said target BST film on said target using said selected target heating temperature, said determined target Ti flow rate, said constant Ba flow rate, and said constant Sr flow rate.
Claim 6
Independent Claim
475 words
A method for forming a barium strontium titanate (Ba, Sr) TiO 3 film (BST film), comprising: (a) obtaining accumulated data with respect to a plurality of sample film operations, including: (a-1) determining a constant Ba flow rate for Ba source material and a constant Sr flow rate for Sr source material; (a-2) performing a sample film operation, including: (a-2-i) providing a sample with a sample substrate comprising a sample substrate material having a sample substrate thickness, (a-2-ii) providing said sample with a sample coating material at a sample coating material thickness, said sample coating material coating a respective percentage of said sample substrate, (a-2-iii) selecting a heating temperature, (a-2-iv) selecting a Ti flow rate for Ti source material, (a-2-v) depositing a sample BST film on said sample using said selected heating temperature, said selected Ti flow rate, said constant Ba flow rate, and said constant Sr flow rate, (a-2-vi) measuring a sample composition ratio of Ti, Ba, and Sr in said sample BST film, and (a-2-vii) recording, as said accumulated data, a sample parameter set including respective sample values for: said sample coating material, said percentage of said sample substrate coated by said sample coating material, said sample coating material thickness, said sample substrate thickness, said selected heating temperature, said selected Ti flow rate, and said sample composition ratio; (a-3) performing said sample film operation a plurality of times, including varying at least one of: said sample coating material, said percentage of said sample substrate coated by said sample coating material, said sample coating material thickness, said sample substrate thickness, said selected heating temperature, and said selected Ti flow rate; (b) providing and measuring a target to be coated, including: (b-1) providing a target substrate comprising a target substrate material having a target substrate thickness, (b-2) providing on said target a target coating material at a target coating material thickness, said target coating material coating a respective percentage of said target substrate, (b-3) selecting a target composition ratio of Ti, Ba, and Sr for a target BST film, (b-4) measuring said target substrate thickness, said target coating material thickness, and said respective percentage of said target substrate coated by said target coating material, and (b-5) selecting a target heating temperature; (c) using said accumulated data to determine a target Ti flow rate based on one of said plurality of sample film operations having said sample parameter set with said respective sample values substantially similar to values for said target coating material, said percentage of said target substrate coated by said target coating material, said target coating material thickness, said target substrate thickness, said selected target heating temperature, and said target composition ratio; and (d) forming said target BST film on said target using said selected target heating temperature, said determined target Ti flow rate, said constant Ba flow rate, and said constant Sr flow rate.
References Cited (Backward Citations)
US4775203A
Cited
US5372850A
Cited
US5406445A
Cited
JPH07268634A
Cited
US5527567A
Cited
US5618761A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-09 | 2002-05-11 | 2002-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-09 | 2006-05-11 | 2006-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-09 | 2010-05-11 | 2010-11-10 | $7700.00 | Window Closed / Lapsed |