N2 O nitrided-oxide trench sidewalls and method of making isolation structure
Assignee: Intel Corp
•
Filing: 1996-12-31
•
Granted: 1998-07-14
•
Expires: 2016-12-31
Abstract
Abstract A method of forming an isolation structure in a semiconductor substrate is described. A trench is first etched into a semiconductor substrate. A first oxide layer is then formed with the trench. The first oxide layer is subjected to a nitrogen-oxide gas ambient and is annealed to form an oxy-nitride surface on the first oxide layer and a silicon-oxynitride interface between the first oxide layer and the semiconductor substrate. A second oxide layer is then deposited over the oxy-nitride surface of the first oxide layer. The method and isolation structure of the present invention prevents dopant outdiffusion, reduces trench stresses, allows more uniform growth of thin gate oxides, and permits the use of thinner gate oxides.
Inventors
- 👤 Reza Arghavani
- 👤 Robert S. Chau
- 👤 Simon Yang
- 👤 John Graham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:03
CPC Classifications
H; H10; H10W; H10W10/00; H10P; H10P95/00; H10P95/06; H10P95/062; H10W10/01; H10W10/011; H10W10/014; H10W10/0145; H10W10/0147; H10W10/10; H10W10/17
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
85 words
A method of forming an isolation structure in a semiconductor substrate comprising the steps of: a) etching a trench in said semiconductor substrate; b) forming a first oxide layer within said trench; c) subjecting said first oxide layer to a nitrogen-oxide (N 2 O) gas ambient to form an oxy-nitride surface on said first oxide layer and a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate; and d) depositing a second oxide layer over said oxy-nitride surface of said first oxide layer.
Claim 2
Independent Claim
85 words
A method of forming an isolation structure in a semiconductor substrate comprising the steps of: a) etching a trench in said semiconductor substrate; b) forming a first oxide layer within said trench; c) subjecting said first oxide layer to a nitrogen-oxide (N 2 O) gas ambient to form an oxy-nitride surface on said first oxide layer and a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate; and d) depositing a second oxide layer over said oxy-nitride surface of said first oxide layer.
Claim 3
Dependent Claim
32 words
The method of claim 1 further comprising the step of performing a trench preclean after said step of etching said trench and prior to said step of forming said first oxide layer.
Claim 4
Dependent Claim
29 words
The method of claim 1 further comprising the step of performing a chemical mechanical polishing (CMP) etch-back step to isolate said first and second oxide layers within said trench.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said first oxide layer is formed by a method including growing a thermal oxide within said trench.
Claim 6
Dependent Claim
19 words
The method of claim 1 wherein said second oxide layer is deposited by a chemical vapor deposition (CVD) process.
Claim 7
Independent Claim
132 words
A method of forming an isolation structure in a semiconductor substrate comprising the steps of: a) etching a trench in said semiconductor substrate; b) growing a thermal oxide within said trench to form a first oxide layer; c) subjecting said first oxide layer to a nitrogen-oxide (N 2 O) gas ambient to form an oxy-nitride surface on said first oxide layer and a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate, wherein said N 2 O gas ambient treatment step consumes some of said semiconductor substrate and rounds the top corners of said trench; d) depositing a second oxide layer over said oxy-nitride surface of said first oxide layer; and e) performing a chemical mechanical polishing etch-back step to isolate said first and second oxide layers within said trench.
Claim 8
Independent Claim
132 words
A method of forming an isolation structure in a semiconductor substrate comprising the steps of: a) etching a trench in said semiconductor substrate; b) growing a thermal oxide within said trench to form a first oxide layer; c) subjecting said first oxide layer to a nitrogen-oxide (N 2 O) gas ambient to form an oxy-nitride surface on said first oxide layer and a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate, wherein said N 2 O gas ambient treatment step consumes some of said semiconductor substrate and rounds the top corners of said trench; d) depositing a second oxide layer over said oxy-nitride surface of said first oxide layer; and e) performing a chemical mechanical polishing etch-back step to isolate said first and second oxide layers within said trench.
Claim 9
Dependent Claim
16 words
The method of claim 6 wherein said second oxide layer is a substantially undoped oxide layer.
Claim 10
Dependent Claim
33 words
The method of claim 6 wherein said second oxide layer is a doped oxide selected from a group consisting of borosilicate glass (BSG), phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), and any combination thereof.
Claim 11
Dependent Claim
19 words
The method of claim 6 wherein said second oxide layer is deposited by a chemical vapor deposition (CVD) process.
Claim 12
Dependent Claim
21 words
The method of claim 9 wherein the CVD process is a low pressure CVD (LPCVD) process performed using a TEOS chemistry.
Claim 13
Independent Claim
229 words
A method of forming an isolation structure in a semiconductor substrate comprising the steps of: a) forming a pad oxide layer above said semiconductor substrate; b) forming a polish stop layer above said pad oxide layer; c) patterning and etching said polish stop layer and said pad oxide layer; d) etching a trench in said semiconductor substrate; e) performing a trench preclean step; f) forming a first oxide layer within said trench to form a first trench oxide layer; g) subjecting said first oxide layer to a nitrogen-oxide (N 2 O) gas ambient to form an oxy-nitride surface on said first oxide layer and a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate, wherein said N 2 O gas ambient treatment step consumes some of said semiconductor substrate and rounds the top corners of said trench; h) depositing a second trench oxide layer over said oxy-nitride surface of said first trench oxide layer; i) polishing said second trench oxide layer in order to remove the portion of said second trench oxide layer above said polish stop layer; j) removing said polish stop layer; k) performing a chemical mechanical polishing etch-back step to isolate said first and second oxide layers within said trench; and l) forming a thin gate oxide layer over said semiconductor substrate and said trench for use in the formation of a semiconductor device.
Claim 14
Independent Claim
229 words
A method of forming an isolation structure in a semiconductor substrate comprising the steps of: a) forming a pad oxide layer above said semiconductor substrate; b) forming a polish stop layer above said pad oxide layer; c) patterning and etching said polish stop layer and said pad oxide layer; d) etching a trench in said semiconductor substrate; e) performing a trench preclean step; f) forming a first oxide layer within said trench to form a first trench oxide layer; g) subjecting said first oxide layer to a nitrogen-oxide (N 2 O) gas ambient to form an oxy-nitride surface on said first oxide layer and a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate, wherein said N 2 O gas ambient treatment step consumes some of said semiconductor substrate and rounds the top corners of said trench; h) depositing a second trench oxide layer over said oxy-nitride surface of said first trench oxide layer; i) polishing said second trench oxide layer in order to remove the portion of said second trench oxide layer above said polish stop layer; j) removing said polish stop layer; k) performing a chemical mechanical polishing etch-back step to isolate said first and second oxide layers within said trench; and l) forming a thin gate oxide layer over said semiconductor substrate and said trench for use in the formation of a semiconductor device.
Claim 15
Dependent Claim
11 words
The method of claim 11 wherein said semiconductor substrate comprises silicon.
Claim 16
Dependent Claim
14 words
The method of claim 11 wherein said polish stop layer comprises a nitride layer.
Claim 17
Dependent Claim
20 words
The method of claim 11 wherein said trench preclean step is performed using a chemical comprising: SC1, SC2, and HF.
Claim 18
Dependent Claim
15 words
The method of claim 11 wherein said first trench oxide layer comprises a thermal oxide.
Claim 19
Dependent Claim
33 words
The method of claim 12 wherein said N 2 O gas ambient treatment step consumes some of said silicon to form a silicon oxy-nitride surface and rounds the top corners of said trench.
Claim 20
Dependent Claim
19 words
The method of claim 11 wherein said second oxide layer is deposited by a chemical vapor deposition (CVD) process.
Claim 21
Dependent Claim
17 words
The method of claim 11 wherein said second trench oxide layer is a substantially undoped oxide layer.
Claim 22
Dependent Claim
33 words
The method of claim 11 wherein said second oxide layer is a doped oxide selected from a group consisting of borosilicate glass (BSG), phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), and any combination thereof.
Claim 23
Dependent Claim
19 words
The method of claim 11 wherein said thin gate oxide layer has a thickness of less than 32 Å.
Claim 24
Dependent Claim
68 words
An isolation structure formed in a semiconductor substrate, said isolation structure comprising: a trench in said semiconductor substrate; a first oxide layer lining said trench, said first oxide layer having an oxy-nitride surface; a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate; and a second oxide layer within said trench, said second oxide layer disposed directly on said oxy-nitride surface of said first oxide layer.
Claim 25
Dependent Claim
68 words
An isolation structure formed in a semiconductor substrate, said isolation structure comprising: a trench in said semiconductor substrate; a first oxide layer lining said trench, said first oxide layer having an oxy-nitride surface; a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate; and a second oxide layer within said trench, said second oxide layer disposed directly on said oxy-nitride surface of said first oxide layer.
Claim 26
Dependent Claim
15 words
The isolation structure of claim 21 wherein said trench is a shallow trench isolation structure.
Claim 27
Dependent Claim
15 words
The isolation structure of claim 21 wherein said first oxide layer is a thermal oxide.
Claim 28
Dependent Claim
16 words
The isolation structure of claim 21 wherein said second oxide layer is a substantially undoped oxide.
Claim 29
Dependent Claim
34 words
The isolation structure of claim 21 wherein said second oxide layer is a doped oxide selected from a group consisting of: borosilicate glass (BSG), phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), and any combination thereof.
Claim 30
Dependent Claim
101 words
A semiconductor device comprising: an isolation structure formed in a semiconductor substrate, said isolation structure comprising: a trench in said semiconductor substrate; a first oxide layer lining said trench, said first oxide layer having an oxy-nitride surface; a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate; and a second oxide layer within said trench, said second oxide layer disposed directly on said oxy-nitride surface of said first oxide layer; and a transistor formed adjacent said isolation structure, said transistor comprising: a thin gate oxide layer, said thin gate oxide layer having a thickness of less than 32 Å.
Claim 31
Dependent Claim
101 words
A semiconductor device comprising: an isolation structure formed in a semiconductor substrate, said isolation structure comprising: a trench in said semiconductor substrate; a first oxide layer lining said trench, said first oxide layer having an oxy-nitride surface; a silicon-oxy-nitride interface between said first oxide layer and said semiconductor substrate; and a second oxide layer within said trench, said second oxide layer disposed directly on said oxy-nitride surface of said first oxide layer; and a transistor formed adjacent said isolation structure, said transistor comprising: a thin gate oxide layer, said thin gate oxide layer having a thickness of less than 32 Å.
Claim 32
Dependent Claim
15 words
The isolation structure of claim 26 wherein said trench is a shallow trench isolation structure.
Claim 33
Dependent Claim
15 words
The isolation structure of claim 26 wherein said first oxide layer is a thermal oxide.
Claim 34
Dependent Claim
16 words
The isolation structure of claim 26 wherein said second oxide layer is a substantially undoped oxide.
Claim 35
Dependent Claim
34 words
The isolation structure of claim 26 wherein said second oxide layer is a doped oxide selected from a group consisting of: borosilicate glass (BSG), phosphosilicate glass (PSG), borophosphosilicate glass (BPSG), and any combination thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-07-13 | 2002-01-12 | 2002-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-07-13 | 2006-01-12 | 2006-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-07-13 | 2010-01-12 | 2010-07-14 | $7700.00 | Window Closed / Lapsed |