Planarization method for intermetal dielectrics between multilevel interconnections on integrated circuits
Assignee: Industrial Technology Research Institute
•
Filing: 1997-04-11
•
Granted: 1998-06-02
•
Expires: 2017-04-11
Abstract
Abstract An improved method for making a planar intermetal dielectric layer (IMD) for multilevel electrical interconnections on ULSI circuits is achieved. The method involves forming metal lines on which is deposited a conformal PECVD oxide. A multilayer of spin-on glass, composed of at least four layers, is deposited and baked at elevated temperatures and long times after each layer to minimize the poisoned via problem on product with minimum feature sizes greater than 0.35 um. A multilayer of a low dielectric constant polymer can also be used to reduce the RC time delay on product having minimum feature sizes less than 0.35 um. After depositing a SiO2 on the SOG, or depositing a Fluorine-doped Silicon Glass (FSG) on the low k polymer, the layer is partially chemical/mechanically polished to provide the desired more global planar IMD. This eliminates the necessity of polishing back the SOG or polymer, which is difficult to achieve with the current technologies. Via holes are then etched in the IMD, and a FSG insulating layer is deposited and etched back to form sidewall spacers in the via holes to prevent outgassing from the SOG or low k polymer, and the next level of metal interconnections are formed. The method can be repeated to achieve a multilevel of planar metal interconnections for ULSI circuits.
Inventors
- 👤 Chine-Gie Lou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:58
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/092; H10P; H10P95/00; H10P95/06; H10P95/062
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
257 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices in and on said substrate; b. depositing a first insulating layer over said devices, and further having contact openings in said first insulating layer for electrical contacts to said devices; c. forming a metal barrier layer on said insulating layer and in said contact openings; d. depositing a first conductive layer for contacting said devices in said contact openings; e. patterning said first conductive layer and said metal barrier layer to form first metal lines as interconnections for said devices; f. depositing a second insulating layer on said patterned first conductive layer; g. depositing a spin-on glass (SOG) multilayer composed of at least four layers, each layer of said multilayer being baked after spin coating, thereby forming an essentially planar surface over said first metal lines; h. curing said spin-on-glass multilayer; i. depositing a third insulating layer on said spin-on-glass multilayer, and partially chemical/mechanically polishing back said third insulating to form a more global planar surface; j. etching via holes through said third insulating layer, said spin-on-glass multilayer, and said second insulating layer to said first metal lines; k. depositing a fourth insulating layer and anisotropically plasma etching back to form sidewall spacers on the sidewalls of said via holes; l. depositing a second conductive layer on said third insulating layer and in said via holes; m. patterning said second conductive layer to form the next level of metal interconnections.
Claim 2
Independent Claim
257 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices in and on said substrate; b. depositing a first insulating layer over said devices, and further having contact openings in said first insulating layer for electrical contacts to said devices; c. forming a metal barrier layer on said insulating layer and in said contact openings; d. depositing a first conductive layer for contacting said devices in said contact openings; e. patterning said first conductive layer and said metal barrier layer to form first metal lines as interconnections for said devices; f. depositing a second insulating layer on said patterned first conductive layer; g. depositing a spin-on glass (SOG) multilayer composed of at least four layers, each layer of said multilayer being baked after spin coating, thereby forming an essentially planar surface over said first metal lines; h. curing said spin-on-glass multilayer; i. depositing a third insulating layer on said spin-on-glass multilayer, and partially chemical/mechanically polishing back said third insulating to form a more global planar surface; j. etching via holes through said third insulating layer, said spin-on-glass multilayer, and said second insulating layer to said first metal lines; k. depositing a fourth insulating layer and anisotropically plasma etching back to form sidewall spacers on the sidewalls of said via holes; l. depositing a second conductive layer on said third insulating layer and in said via holes; m. patterning said second conductive layer to form the next level of metal interconnections.
Claim 3
Dependent Claim
22 words
The method of claim 1, wherein said barrier layer is composed of titanium/titanium nitride and prevents aluminum from reacting with said devices.
Claim 4
Dependent Claim
32 words
The method of claim 1, wherein said second insulating layer is deposited by plasma enhanced chemical vapor deposition using tetraethosiloxane (TEOS) and having a thickness of between about 500 and 2500 Angstroms.
Claim 5
Dependent Claim
89 words
The method of claim 1, wherein each said layer of said spin-on-glass multilayer is a siloxane having a thickness of between about 900 and 2100 Angstroms and is baked sequentially at a temperature of between about 120° and 140° C. for about 2 minutes, a temperature of between about 180° and 220° C. for about 2 minutes, and at a temperature of between about 280° and 310° C. for about 2 minutes, thereby minimizing outgassing of moisture from said spin-on glass in said via holes and preventing via poisoning.
Claim 6
Dependent Claim
31 words
The method of claim 1, wherein said curing is carried out by electron beam curing at a temperature of between about 150° and 250° C. for about 7 to 10 minutes.
Claim 7
Dependent Claim
34 words
The method of claim 1, wherein said third insulating layer is deposited by plasma enhanced chemical vapor deposition (PECVD) using TEOS, and is deposited to a thickness of between about 7000 and 12000 Angstroms.
Claim 8
Dependent Claim
56 words
The method of claim 1, wherein said third insulating layer is a low dielectric constant insulator deposited by high-density plasma chemical vapor deposition (HDP-CVD) using a mixture of carbon tetrafluoride, oxygen, argon, and hydrogen and deposited to a thickness of between about 7000 and 12000 Angstroms, and having a dielectric constant of about 3.0 to 3.5.
Claim 9
Dependent Claim
18 words
The method of claim 1, wherein said spin-on glass is doped with fluorine to reduce the dielectric constant.
Claim 10
Dependent Claim
21 words
The method of claim 1, wherein said fourth insulating layer is composed of a high-density plasma fluorine-doped silicon oxide glass (HDP-FSG).
Claim 11
Independent Claim
265 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices in and on said substrate; b. depositing a first insulating layer over said devices, and further having contact openings in said first insulating layer for electrical contacts to said devices; c. forming a metal barrier layer on said first insulating layer and in said contact openings; d. depositing a first conductive layer for contacting said devices in said contact openings; e. patterning said first conductive layer and said metal barrier layer to form first metal lines as interconnections for said devices; f. depositing a second insulating layer on said patterned first conductive layer; g. depositing a low dielectric polymer multilayer composed of at least four layers, each layer of said multilayer being baked after spin coating, thereby forming an essentially planar surface over said first metal lines; h. curing said low dielectric polymer multilayer; i. depositing a low dielectric constant insulator on said polymer multilayer and partially chemical/mechanically polishing back said low dielectric constant insulator to form a more global planar surface; j. etching via holes through said low dielectric constant insulator, said polymer multilayer, and said second insulating layer to said first metal lines; k. depositing a fourth insulating layer and anisotropically plasma etching back to form sidewall spacers on the sidewalls of said via holes; l. depositing a second conductive layer on said low dielectric constant insulator and in said via holes; m. patterning said second conductive layer to form the next level of metal interconnections.
Claim 12
Independent Claim
265 words
A method for fabricating multilevel metal interconnections having low dielectric constant insulators on a substrate comprising the steps of: a. providing a semiconductor substrate having semiconductor devices in and on said substrate; b. depositing a first insulating layer over said devices, and further having contact openings in said first insulating layer for electrical contacts to said devices; c. forming a metal barrier layer on said first insulating layer and in said contact openings; d. depositing a first conductive layer for contacting said devices in said contact openings; e. patterning said first conductive layer and said metal barrier layer to form first metal lines as interconnections for said devices; f. depositing a second insulating layer on said patterned first conductive layer; g. depositing a low dielectric polymer multilayer composed of at least four layers, each layer of said multilayer being baked after spin coating, thereby forming an essentially planar surface over said first metal lines; h. curing said low dielectric polymer multilayer; i. depositing a low dielectric constant insulator on said polymer multilayer and partially chemical/mechanically polishing back said low dielectric constant insulator to form a more global planar surface; j. etching via holes through said low dielectric constant insulator, said polymer multilayer, and said second insulating layer to said first metal lines; k. depositing a fourth insulating layer and anisotropically plasma etching back to form sidewall spacers on the sidewalls of said via holes; l. depositing a second conductive layer on said low dielectric constant insulator and in said via holes; m. patterning said second conductive layer to form the next level of metal interconnections.
Claim 13
Dependent Claim
22 words
The method of claim 10, wherein said barrier layer is composed of titanium/titanium nitride and prevents aluminum from reacting with said devices.
Claim 14
Dependent Claim
33 words
The method of claim 10, wherein said second insulating layer is deposited by plasma enhanced chemical vapor deposition (PECVD) using tetraethosiloxane (TEOS) and having a thickness of between about 400 and 2000 Angstroms.
Claim 15
Dependent Claim
80 words
The method of claim 10, wherein each layer of said low dielectric polymer multilayer is a polymer containing fluorine and each said layer is deposited to a thickness of between about 900 and 2100 Angstroms and is baked sequentially at a temperature of between about 190° and 210° C. for about 2 minutes, a temperature of between about 220° and 240° C. for about 2 minutes, and at a temperature of between about 280° and 310° C. for about 2minutes.
Claim 16
Dependent Claim
23 words
The method of claim 10, wherein said low dielectric polymer multilayer is doped with fluorine having a reduced dielectric constant of about 2.7.
Claim 17
Dependent Claim
31 words
The method of claim 10, wherein said curing is carried out by electron beam curing at a temperature of between about 150° and 270° C. for about 8 to 12 minutes.
Claim 18
Dependent Claim
55 words
The method of claim 10, wherein said low dielectric constant insulator is a fluorine-doped silicon glass (FSG) deposited by high-density plasma chemical vapor deposition (HDP-CVD) using a mixture of carbon tetrafluoride, oxygen, argon, and hydrogen, to a thickness of between about 7000 and 12000 Angstroms, and having a dielectric constant of about 3.0 to 3.5.
Claim 19
Dependent Claim
35 words
The method of claim 10, wherein said low dielectric polymer multilayer is comprised of a polymer selected from a group consisting of polyimide, polysilsequioxane, benzocyclobutene (BCB), parylene N, fluorinated polyimide, parylene F, and amorphous Teflon.
Claim 20
Dependent Claim
18 words
The method of claim 10, wherein said low dielectric polymer multilayer is synthesized from perfluorobiphenyl with aromatic bisphenols.
Claim 21
Dependent Claim
21 words
The method of claim 10, wherein said fourth insulating layer is composed of a high-density plasma fluorine-doped silicon oxide glass (HDP-FSG).
References Cited (Backward Citations)
US5219792A
Cited
US5393708A
Cited
US5312512A
Cited
US5371046A
Cited
US5413963A
Cited
US5616519A
Cited
US5663108A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-01 | 2001-12-01 | 2002-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-01 | 2005-12-01 | 2006-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-01 | 2009-12-01 | 2010-06-02 | $7700.00 | Window Closed / Lapsed |