Fabrication method for a semiconductor device on a semiconductor on insulator substrate using a two stage threshold adjust implant
Assignee: NXP USA Inc
•
Filing: 1995-11-03
•
Granted: 1998-02-17
•
Expires: 2015-11-03
Abstract
Abstract A two stage threshold adjust implantation process is performed after field oxidation to avoid the effects of dopant redistribution and segregation. At any of several steps in a manufacturing process, only routine implant energy and dose adjustments are required to create a first and a second dopant profile (110, 120) that result in the reduction of edge leakage and threshold voltage sensitivity to device layer thickness of a semiconductor device on a semiconductor on insulator substrate.
Inventors
- 👤 Marco Racanelli
- 👤 Wen-Ling M. Huang
- 👤 Bor-Yuan C. Hwang
- 👤 Juergen A. Foerstner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:16
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/60; H10D30/67; H10D30/6757; H10D30/01; H10D30/021; H10D30/031; H10D30/0321; H10D30/0323; H10D30/6704; H10D30/6706; H10D30/674; H10D62/00; H10D62/10; H10D62/17; H10D62/213; H10D62/221; H10D62/235; H10D62/314; H10D30/6713; H10D30/6715
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
162 words
A method of fabricating a semiconductor device on a semiconductor on insulator substrate comprising the steps of: providing said semiconductor on insulator substrate, wherein said semiconductor on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming an active area on said semiconductor on insulator substrate, wherein said active area is within the semiconductor material and adjacent a field oxide region; forming a sacrificial layer overlying said active area; forming a first dopant profile, wherein said first dopant profile has a peak dopant concentration in a portion of said active area adjacent said field oxide region and the interface between the semiconductor material and the insulator material; and forming a second dopant profile, wherein said second dopant profile has a peak dopant concentration in a channel region of said active area, wherein a concentration of the first dopant profile is greater than a concentration of the second dopant profile.
Claim 2
Independent Claim
162 words
A method of fabricating a semiconductor device on a semiconductor on insulator substrate comprising the steps of: providing said semiconductor on insulator substrate, wherein said semiconductor on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming an active area on said semiconductor on insulator substrate, wherein said active area is within the semiconductor material and adjacent a field oxide region; forming a sacrificial layer overlying said active area; forming a first dopant profile, wherein said first dopant profile has a peak dopant concentration in a portion of said active area adjacent said field oxide region and the interface between the semiconductor material and the insulator material; and forming a second dopant profile, wherein said second dopant profile has a peak dopant concentration in a channel region of said active area, wherein a concentration of the first dopant profile is greater than a concentration of the second dopant profile.
Claim 3
Dependent Claim
39 words
The method of claim 1 wherein the step of providing the semiconductor on insulator substrate further comprises providing a bulk substrate having thereon a buried insulation layer, and further having a semiconductor device layer overlying said buried insulation layer.
Claim 4
Dependent Claim
46 words
The method of claim 1 wherein the step of providing the semiconductor on insulator substrate further comprises providing a bulk substrate having thereon a buried insulation layer comprised of silicon oxide, and further having a semiconductor device layer, comprised of silicon, overlying said buried insulation layer.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein the step of forming a first dopant profile comprises implanting boron, phosphorus or arsenic into said active area.
Claim 6
Dependent Claim
24 words
The method of claim 1 wherein the step of forming a second dopant profile comprises implanting boron, phosphorus or arsenic into said active area.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein the step of forming a sacrificial layer further comprises forming a sacrificial layer comprised of silicon oxide.
Claim 8
Independent Claim
147 words
A method of adjusting threshold voltage in a semiconductor device fabricated on a semiconductor on insulator substrate comprising the steps of: providing the semiconductor on insulator substrate, wherein said semiconductor on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming an active area in said semiconductor on insulator substrate, wherein said active area is within the semiconductor material and adjacent a field oxide region; forming a gate oxide layer on said active area; depositing a polysilicon layer overlying said gate oxide layer; forming a first dopant profile, wherein said first dopant profile has a peak dopant concentration in a portion of said active area adjacent said field oxide region; and forming a second dopant profile, wherein said second dopant profile has a peak dopant concentration in a channel region of said active area.
Claim 9
Independent Claim
147 words
A method of adjusting threshold voltage in a semiconductor device fabricated on a semiconductor on insulator substrate comprising the steps of: providing the semiconductor on insulator substrate, wherein said semiconductor on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming an active area in said semiconductor on insulator substrate, wherein said active area is within the semiconductor material and adjacent a field oxide region; forming a gate oxide layer on said active area; depositing a polysilicon layer overlying said gate oxide layer; forming a first dopant profile, wherein said first dopant profile has a peak dopant concentration in a portion of said active area adjacent said field oxide region; and forming a second dopant profile, wherein said second dopant profile has a peak dopant concentration in a channel region of said active area.
Claim 10
Dependent Claim
46 words
The method of claim 7 wherein the step of providing the semiconductor on insulator substrate further comprises providing a bulk substrate having thereon a buried insulation layer comprised of silicon oxide, and further having a semiconductor device layer, comprised of silicon, overlying said buried insulation layer.
Claim 11
Dependent Claim
54 words
The method of claim 7 wherein the step of forming a gate oxide layer further comprises forming the gate oxide layer with a thickness between approximately 5 and 40 nm, and the step of forming a polysilicon layer further comprises forming the polysilicon layer with a thickness between approximately 20 nm and 400 nm.
Claim 12
Dependent Claim
34 words
The method of claim 7 wherein the step of forming a first dopant profile further comprises forming the first dopant profile with a dopant selected from the group consisting of boron, phosphorus and arsenic.
Claim 13
Dependent Claim
34 words
The method of claim 7 wherein the step of forming a second dopant profile further comprises forming the second dopant profile with a dopant selected from the group consisting of boron, phosphorus and arsenic.
Claim 14
Independent Claim
174 words
A method of adjusting threshold voltage and reducing edge leakage in a semiconductor device fabricated on a silicon on insulator substrate, comprising the steps of: providing the silicon on insulator substrate comprising a device layer, wherein said silicon on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming at least one field oxide region in said device layer to define an active area within the semiconductor material; forming a gate oxide layer on said active area; forming a polysilicon layer overlying said gate oxide layer; patterning said polysilicon layer to form a gate electrode; forming a source region and a drain region in said active area, wherein said source region and said drain region are self-aligned to said gate electrode; performing a first threshold adjust implant, wherein a first dopant profile is formed in said silicon on insulator substrate; and performing a second threshold voltage adjust implant, wherein a second dopant profile is formed in said silicon on insulator substrate.
Claim 15
Independent Claim
174 words
A method of adjusting threshold voltage and reducing edge leakage in a semiconductor device fabricated on a silicon on insulator substrate, comprising the steps of: providing the silicon on insulator substrate comprising a device layer, wherein said silicon on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming at least one field oxide region in said device layer to define an active area within the semiconductor material; forming a gate oxide layer on said active area; forming a polysilicon layer overlying said gate oxide layer; patterning said polysilicon layer to form a gate electrode; forming a source region and a drain region in said active area, wherein said source region and said drain region are self-aligned to said gate electrode; performing a first threshold adjust implant, wherein a first dopant profile is formed in said silicon on insulator substrate; and performing a second threshold voltage adjust implant, wherein a second dopant profile is formed in said silicon on insulator substrate.
Claim 16
Dependent Claim
34 words
The method of claim 12, wherein the step of providing the silicon on insulator substrate comprises providing a bulk substrate having thereon a buried insulator layer, underlying said device layer, comprised of silicon oxide.
Claim 17
Dependent Claim
17 words
The method of claim 12, further comprising the step of forming sidewall spacers adjacent said gate electrode.
Claim 18
Dependent Claim
30 words
The method of claim 12, wherein the step of forming a source region and a drain region, include forming LDD regions, self-aligned to said gate electrode, in said active area.
Claim 19
Dependent Claim
27 words
The method of claim 12, wherein the steps of performing a first threshold adjust implant and a second threshold adjust implant further comprise implanting boron or phosphorus.
Claim 20
Dependent Claim
43 words
The method of claim 12, wherein the step of forming a first dopant profile further comprises implanting a dopant at a first implant energy and the step of forming a second dopant profile further comprises implanting a dopant at a second implant energy.
Claim 21
Dependent Claim
42 words
The method of claim 12, wherein the step of forming a first dopant profile in said silicon on insulator substrate further comprises forming a peak dopant concentration in a portion of said active area adjacent said at least one field oxide region.
Claim 22
Dependent Claim
39 words
The method of claim 12, wherein the step of forming a second dopant profile in said silicon on insulator substrate further comprises forming a peak dopant concentration in a channel region of said active area underlying said gate electrode.
Claim 23
Independent Claim
131 words
A method of fabricating a semiconductor device on a semiconductor on insulator substrate comprising the steps of: providing the semiconductor on insulator substrate, wherein said semiconductor on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming at least one field oxide region on said semiconductor on insulator substrate, wherein said at least one field oxide region defines an active area within the semiconductor material; doping said semiconductor substrate wherein a first dopant profile having a peak dopant concentration in a portion of said active area adjacent said field oxide region is formed; and doping said semiconductor substrate wherein a second dopant profile having a peak dopant concentration in a channel region of said active area is formed.
Claim 24
Independent Claim
131 words
A method of fabricating a semiconductor device on a semiconductor on insulator substrate comprising the steps of: providing the semiconductor on insulator substrate, wherein said semiconductor on insulator substrate includes a semiconductor material disposed on an insulator material, and an interface between the semiconductor material and the insulator material; forming at least one field oxide region on said semiconductor on insulator substrate, wherein said at least one field oxide region defines an active area within the semiconductor material; doping said semiconductor substrate wherein a first dopant profile having a peak dopant concentration in a portion of said active area adjacent said field oxide region is formed; and doping said semiconductor substrate wherein a second dopant profile having a peak dopant concentration in a channel region of said active area is formed.
References Cited (Backward Citations)
US4402761A
Cited
US4649629A
Cited
US5081052A
Cited
US5028552A
Cited
US4845047A
Cited
US5384279A
Cited
US4948745A
Cited
US5091328A
Cited
US5185280A
Cited
US5283200A
Cited
US5248627A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-02-16 | 2001-08-18 | 2002-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-02-16 | 2005-08-18 | 2006-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-02-16 | 2009-08-18 | 2010-02-17 | $7700.00 | Window Closed / Lapsed |