Assignee: Vanguard International Semiconductor Corp
•
Filing: 1995-10-27
•
Granted: 1998-01-06
•
Expires: 2015-10-27
Abstract
Abstract A process, to fill small diameter contact holes with tungsten, without deleterious attack of contact hole liner materials, during the tungsten deposition, has been developed. The process consists of using a titanium nitride barrier layer, overlying a titanium adhesive layer. However the barrier characteristics of titanium nitride are enhanced by subjecting this layer to an anneal cycle in an nitrogen ambient. The annealing produces a more robust barrier in terms of incorporating additional nitrogen into the deposited titanium nitride layer, as well as forming titanium nitride on any underlying titanium, that may be exposed due to defects in the deposited titanium nitride layer.
Inventors
- 👤 Haw Yen
- 👤 Shaw-Tzeng Hsia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:19
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/041; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10W20/033; H10W20/047; H10W20/048; H10W20/056; H10W20/071; H10W20/081
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
242 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole, lined with adhesive and barrier layers, and filled with a metal, to provide electrical contact between an active device region in said semiconductor substrate, and an overlying interconnect metallization, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region in said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element, to create said active device region; surface cleaning of said active device region; deposition of an adhesive layer on said dielectric layer, on sides of said contact hole, and on surface of said active device region; deposition of a barrier layer on said adhesive layer; annealing in an nitrogen ambient, at a temperature between about 550° to 650° C., for a time between about 45 to 75 min; depositing metal, on said barrier layer, completely filling said contact hole; etch back of said metal to form a metal plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form metal interconnect structure.
Claim 2
Independent Claim
242 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole, lined with adhesive and barrier layers, and filled with a metal, to provide electrical contact between an active device region in said semiconductor substrate, and an overlying interconnect metallization, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region in said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element, to create said active device region; surface cleaning of said active device region; deposition of an adhesive layer on said dielectric layer, on sides of said contact hole, and on surface of said active device region; deposition of a barrier layer on said adhesive layer; annealing in an nitrogen ambient, at a temperature between about 550° to 650° C., for a time between about 45 to 75 min; depositing metal, on said barrier layer, completely filling said contact hole; etch back of said metal to form a metal plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form metal interconnect structure.
Claim 3
Dependent Claim
20 words
The method of claim 1, wherein said device element in said semiconductor substrate, is an N type, field effect transistor.
Claim 4
Dependent Claim
36 words
The method of claim 1, wherein said dielectric layer is silicon oxide, deposited using LPCVD or PECVD processing, at a temperature between about 500° to 750° C., to a thickness between about 8000 to 15000 Angstroms.
Claim 5
Dependent Claim
20 words
The method of claim 1, wherein said contact hole is formed via anisotropic reactive ion etching, using CHF 3 .
Claim 6
Dependent Claim
35 words
The method of claim 1, wherein said first conductivity imparting dopant is phosphorous, ion implanted at an energy between about 50 to 80 KEV., at a dose between about 1E15 to 5E15 atoms/cm 2 .
Claim 7
Dependent Claim
46 words
The method of claim 1, wherein surface cleaning of said active device region is performed using a solution of about 200 parts water, to one part hydrofluoric acid, at a temperature between about 20° to 25° C., for a time between about 75 to 105 seconds.
Claim 8
Dependent Claim
24 words
The method of claim 1, wherein said adhesive layer is titanium, deposited using r.f. sputtering, to a thickness between about 250 to 350 Angstroms.
Claim 9
Dependent Claim
26 words
The method of claim 1, wherein said barrier layer is titanium nitride, deposited via direct r.f. sputtering, to a thickness between about 600 to 1000 Angstroms.
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein said barrier layer is titanium nitride, deposited via reactive r.f. sputtering, using a nitrogen containing ambient, to a thickness between about 600 to 1000 Angstroms.
Claim 11
Dependent Claim
124 words
The method of claim 1, wherein annealing of said barrier layer is performed by; loading of samples in furnace at a temperature between about 275° to 325° C., in a nitrogen flow of between about 25 to 30 liters/min., ramp up and stabilization at a temperature between about 550° to 650° C., for a time between about 100 to 120 min., in an nitrogen flow between about 25 to 30 liters/min., annealing at a temperature between about 550° to 650° C., in an nitrogen flow between about 25 to 30 liters/min., for a time between about 45 to 75 min., and ramp down and unload at a temperature between about 275° to 325° C., in a nitrogen flow between about 25 to 30 liters/min.
Claim 12
Dependent Claim
36 words
The method of claim 1, wherein annealing of said barrier layer results in the formation of a titanium disilicide layer, at the bottom of said contact hole, to a thickness between about 100 to 200 Angstroms.
Claim 13
Dependent Claim
37 words
The method of claim 1, wherein said metal is tungsten, deposited using LPCVD processing, at a temperature between about 450° to 475° C., to a thickness between about 6000 to 8000 Angstroms, using a tungsten hexafluoride source.
Claim 14
Independent Claim
254 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole lined with titanium for adhesive purposes, lined with titanium nitride for barrier purposes, and filled with tungsten, to provide electrical contact between an active device region and an overlying interconnect metallization, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region in said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element to create a heavily doped N type region; surface cleaning of said heavily doped N type region; deposition of a titanium layer on said dielectric layer, on sides of said contact hole, and on said heavily doped N type region; deposition of a titanium nitride barrier layer on said titanium layer; annealing in an nitrogen ambient, at a temperature between about 550° to 650° C., for a time between about 45 to 75 min; deposition of a tungsten on said titanium nitride barrier layer, completely filling said contact hole; etch back of said tungsten to form a tungsten plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form metal interconnect structure.
Claim 15
Independent Claim
254 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole lined with titanium for adhesive purposes, lined with titanium nitride for barrier purposes, and filled with tungsten, to provide electrical contact between an active device region and an overlying interconnect metallization, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region in said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element to create a heavily doped N type region; surface cleaning of said heavily doped N type region; deposition of a titanium layer on said dielectric layer, on sides of said contact hole, and on said heavily doped N type region; deposition of a titanium nitride barrier layer on said titanium layer; annealing in an nitrogen ambient, at a temperature between about 550° to 650° C., for a time between about 45 to 75 min; deposition of a tungsten on said titanium nitride barrier layer, completely filling said contact hole; etch back of said tungsten to form a tungsten plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form metal interconnect structure.
Claim 16
Dependent Claim
20 words
The method of claim 13, wherein said device element in said semiconductor substrate, is an N type field effect transistor.
Claim 17
Dependent Claim
36 words
The method of claim 13, wherein said dielectric layer is silicon oxide, deposited using LPCVD or PECVD processing, at a temperature between about 500° to 750° C., to a thickness between about 8000 to 15000 Angstroms.
Claim 18
Dependent Claim
35 words
The method of claim 13, wherein said first conductivity imparting dopant is phosphorous, ion implanted at an energy between about 50 to 80 Kev., at a dose between about 1E15 to 5E15 atoms/cm 2 .
Claim 19
Dependent Claim
24 words
The method of claim 13, wherein said titanium adhesion layer is deposited using r.f. sputtering, to a thickness between about 250 to 350 Angstroms.
Claim 20
Dependent Claim
26 words
The method of claim 13, wherein said titanium nitride barrier layer is deposited via direct r.f. sputtering, to a thickness between about 600 to 1000 Angstroms.
Claim 21
Dependent Claim
31 words
The method of claim 13, wherein said titanium nitride barrier layer is deposited via reactive r.f. sputtering, using a nitrogen containing ambient, to a thickness between about 600 to 1000 Angstroms.
Claim 22
Dependent Claim
100 words
The method of claim 13, wherein annealing of said titanium nitride barrier layer is performed using a nitrogen flow between about 25 to 30 liters/min.; initially to load the wafers at a temperature between about 275° to 325° C., followed by a ramp up and stabilization step at a temperature between about 550° to 650° C., for a time between about 100 to 120 min., an anneal at a temperature between about 550° to 650° C., for a time between about 45 to 75 min., and a ramp down and unload at a temperature between about 275° to 325° C.
Claim 23
Dependent Claim
51 words
The method of claim 13, wherein annealing of said titanium nitride barrier layer results in the creation of a titanium disilicide layer, at the bottom of said contact hole, from the reaction of said titanium and said heavily doped N type region, to a thickness between about 100 to 200 Angstroms.
Claim 24
Dependent Claim
37 words
The method of claim 13, wherein said tungsten is deposited using LPCVD processing, at a temperature between about 450° to 475° C., to a thickness between about 6000 to 8000 Angstroms, using tungsten hexafluoride as a source.
References Cited (Backward Citations)
US5244835A
Cited
US5236852A
Cited
US5286675A
Cited
US5492863A
Cited
US5587338A
Cited
US5599736A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-05 | 2001-07-07 | 2002-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-05 | 2005-07-07 | 2006-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-05 | 2009-07-07 | 2010-01-06 | $7700.00 | Window Closed / Lapsed |