Blanket tungsten etchback process using disposable spin-on-glass
Assignee: Industrial Technology Research Institute
•
Filing: 1993-04-14
•
Granted: 1994-02-15
•
Expires: 2013-04-14
Abstract
Abstract A new method of completing a tungsten contact is described. An insulator layer is formed over device structures in and on a semiconductor substrate. The insulator layer is flowed to planarize the layer. The insulator layer is covered with a spin-on-glass layer which is baked and cured. Contact openings are formed through the insulator and spin-on-glass layers to the device structures and to the substrate. A nucleation layer is formed over the spin-on-glass layer and within the contact openings. A layer of tungsten is deposited over the nucleation layer. The tungsten layer is etched back, thereby leaving the tungsten layer within the contact openings and leaving some of the tungsten layer as residue overlying the spin-on-glass layer. The spin-on-glass layer is removed, thereby removing any tungsten layer residue overlying the spin-on-glass layer. The contacts are completed by an aluminum metalization.
Inventors
- 👤 Kuang-Chao Chen
- 👤 Shaw-Tzeng Hsia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:39
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/063; H10W20/056; H10W20/059
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
182 words
The method of completing tungsten contacts in an integrated circuit comprising: providing semiconductor device structures in and on a semiconductor substrate; providing at least one patterned conductive layer for contacting the active elements of said device structures; the surface of said patterned conductive layer structure is irregular with horizontal and vertical components; depositing and flowing an insulator layer over said irregular structure patterned conductive layer; covering said insulator with a spin-on-glass layer and baking said spin-on-glass layer; defining contact openings through said insulator and spin-on-glass layers to said device structures and to said substrate; depositing a nucleation layer over said spin-on-glass layer and within said contact openings; depositing a layer of tungsten over said nucleation layer; etching back said tungsten layer and said nucleation layer thereby leaving said tungsten layer within said contact openings and leaving some of said tungsten layer as residue overlying said spin-on-glass layer; removing said spin-on-glass layer and thereby removing any said tungsten layer residue overlying said spin-on-glass layer; and depositing a layer of metal to complete said contacts to said device structures and to said silicon substrate.
Claim 2
Independent Claim
182 words
The method of completing tungsten contacts in an integrated circuit comprising: providing semiconductor device structures in and on a semiconductor substrate; providing at least one patterned conductive layer for contacting the active elements of said device structures; the surface of said patterned conductive layer structure is irregular with horizontal and vertical components; depositing and flowing an insulator layer over said irregular structure patterned conductive layer; covering said insulator with a spin-on-glass layer and baking said spin-on-glass layer; defining contact openings through said insulator and spin-on-glass layers to said device structures and to said substrate; depositing a nucleation layer over said spin-on-glass layer and within said contact openings; depositing a layer of tungsten over said nucleation layer; etching back said tungsten layer and said nucleation layer thereby leaving said tungsten layer within said contact openings and leaving some of said tungsten layer as residue overlying said spin-on-glass layer; removing said spin-on-glass layer and thereby removing any said tungsten layer residue overlying said spin-on-glass layer; and depositing a layer of metal to complete said contacts to said device structures and to said silicon substrate.
Claim 3
Dependent Claim
44 words
The method of claim 1 wherein said insulator layer is composed of borophosphosilicate glass deposited to a thickness of between about 3000 to 6000 Angstroms and flowed at conditions 800° to 900° C. in nitrogen, Argon, or steam ambient for 1 to 2 hours.
Claim 4
Dependent Claim
24 words
The method of claim 1 wherein said spin-on-glass layer has a thickness of between about 500 to 3000 Angstroms and is of siloxane type.
Claim 5
Dependent Claim
24 words
The method of claim 1 wherein said spin-on-glass layer has a thickness of between about 500 to 3000 Angstroms and is of silicate type.
Claim 6
Dependent Claim
26 words
The method of claim 1 wherein said spin-on-glass layer is baked with conditions 80°-100°-150°-200°-250°-300° C. for a duration of 1 to 2 minutes for each stage.
Claim 7
Dependent Claim
24 words
The method of claim 1 wherein said nucleation layer is composed of Ti/TiN and has a thickness of between about 800 to 2000 Angstroms.
Claim 8
Dependent Claim
24 words
The method of claim 1 wherein said nucleation layer is composed of Ti/TiW and has a thickness of between about 800 to 2000 Angstroms.
Claim 9
Dependent Claim
24 words
The method of claim 1 wherein said nucleation layer is composed of Ti/TiWN and has a thickness of between about 800 to 2000 Angstroms.
Claim 10
Dependent Claim
24 words
The method of claim 1 wherein said nucleation layer is composed of TiN and has a thickness of between about 800 to 2000 Angstroms.
Claim 11
Dependent Claim
35 words
The method of claim 1 wherein said tungsten layer is deposited by chemical vapor deposition at a temperature of between about 400° to 500° C. to a thickness of between about 3500 to 5000 Angstroms.
Claim 12
Dependent Claim
79 words
The method of claim 1 wherein said etching back of said tungsten layer uses SF 6 , Ar, and He gases in a three step process wherein the first step is timed to etch away more than half of said tungsten thickness and wherein the second step uses same said gases and has an etching endpoint at said nucleation layer and wherein the third step uses the same said gases in a timed etch depending on said tungsten thickness.
Claim 13
Dependent Claim
55 words
The method of claim 1 wherein said etchback of said nucleation layer uses Cl 2 and Ar gases in a two step etching process wherein the first step has an etch rate of 2000 to 2500 Angstroms/minute and wherein the second step uses the same said gases at an etch rate of about 600 Angstroms/minute.
Claim 14
Dependent Claim
22 words
The method of claim 1 wherein said spin-on-glass layer is removed using buffered hydrofluoric acid for between about 30 to 120 seconds.
Claim 15
Independent Claim
192 words
The method of completing electrical contacts in an integrated circuit using a disposable spin-on-glass layer comprising: providing semiconductor device structures in and on a semiconductor substrate; providing at least one patterned conductive layer for contacting the active elements of said device structures; the surface of said patterned conductive layer structure is irregular with horizontal and vertical components; depositing and flowing an insulator layer over said irregular structure patterned conductive layer; covering said insulator with a spin-on-glass layer and baking said spin-on-glass layer; defining contact openings through said insulator and spin-on-glass layers to said device structures and to said substrate; depositing a nucleation layer over said spin-on-glass layer and within said contact openings; depositing a layer of conductive metal over said nucleation layer; etching back said conductive metal layer and said nucleation layer thereby leaving said conductive metal layer within said contact openings and leaving some of said conductive metal layer as residue overlying said spin-on-glass layer; removing said spin-on-glass layer and thereby removing any said conductive metal layer residue overlying said spin-on-glass layer; and depositing a layer of metal to complete said contacts to said device structures and to said silicon substrate.
Claim 16
Independent Claim
192 words
The method of completing electrical contacts in an integrated circuit using a disposable spin-on-glass layer comprising: providing semiconductor device structures in and on a semiconductor substrate; providing at least one patterned conductive layer for contacting the active elements of said device structures; the surface of said patterned conductive layer structure is irregular with horizontal and vertical components; depositing and flowing an insulator layer over said irregular structure patterned conductive layer; covering said insulator with a spin-on-glass layer and baking said spin-on-glass layer; defining contact openings through said insulator and spin-on-glass layers to said device structures and to said substrate; depositing a nucleation layer over said spin-on-glass layer and within said contact openings; depositing a layer of conductive metal over said nucleation layer; etching back said conductive metal layer and said nucleation layer thereby leaving said conductive metal layer within said contact openings and leaving some of said conductive metal layer as residue overlying said spin-on-glass layer; removing said spin-on-glass layer and thereby removing any said conductive metal layer residue overlying said spin-on-glass layer; and depositing a layer of metal to complete said contacts to said device structures and to said silicon substrate.
Claim 17
Dependent Claim
45 words
The method of claim 14 wherein said insulator layer is composed of borophosphosilicate glass deposited to a thickness of between about 3000 to 6000 Angstroms and flowed at conditions 800° to 900° C. in a nitrogen, argon, or steam ambient for 1 to 2 hours.
Claim 18
Dependent Claim
24 words
The method of claim 14 wherein said spin-on-glass layer has a thickness of between about 500 to 3000 Angstroms and is of siloxane type.
Claim 19
Dependent Claim
24 words
The method of claim 14 wherein said spin-on-glass layer has a thickness of between about 500 to 3000 Angstroms and is of silicate type.
Claim 20
Dependent Claim
26 words
The method of claim 14 wherein said spin-on-glass layer is baked with conditions 80°-100°-150°-200°-250°-300° C. for a duration of 1 to 2 minutes for each stage.
Claim 21
Dependent Claim
24 words
The method of claim 14 wherein said nucleation layer is composed of Ti/TiN and has a thickness of between about 800 to 2000 Angstroms.
Claim 22
Dependent Claim
24 words
The method of claim 14 wherein said nucleation layer is composed of Ti/TiW and has a thickness of between about 800 to 2000 Angstroms.
Claim 23
Dependent Claim
24 words
The method of claim 14 wherein said nucleation layer is composed of Ti/TiWN and has a thickness of between about 800 to 2000 Angstroms.
Claim 24
Dependent Claim
24 words
The method of claim 14 wherein said nucleation layer is composed of TiN and has a thickness of between about 800 to 2000 Angstroms.
Claim 25
Dependent Claim
39 words
The method of claim 14 wherein said conductive metal layer is tungsten and is deposited by chemical vapor deposition at a temperature of between about 400° to 500° C. to a thickness of between about 3500 to 5000 Angstroms.
Claim 26
Dependent Claim
84 words
The method of claim 14 wherein said etching back of said conductive metal layer uses SF 6 , Ar, and He gases in a three step process wherein the first step is timed to etch away more than half of said conductive metal layer thickness and wherein the second step uses the same said gases with an etching endpoint at said nucleation layer and wherein the third step uses the same said gases in a timed etch depending on said conductive metal layer thickness.
Claim 27
Dependent Claim
55 words
The method of claim 14 wherein said etchback of said nucleation layer uses Cl 2 and Ar gases in a two step etching process wherein the first step has an etch rate of 2000 to 2500 Angstroms/minute and wherein the second step uses the same said gases at an etch rate of about 600 Angstroms/minute.
References Cited (Backward Citations)
US4833519A
Cited
US4960732A
Cited
US4879257A
Cited
US5091340A
Cited
US4952528A
Cited
US5006485A
Cited
US5164330A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-14 | 1997-08-16 | 1998-02-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-14 | 2001-08-16 | 2002-02-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-14 | 2005-08-16 | 2006-02-15 | $7700.00 | Window Closed / Lapsed |