US5693578A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of forming thin silicon oxide film with high dielectric breakdown and hot carrier resistance
Assignee: Fujitsu Semiconductor Ltd
•
Filing: 1996-02-26
•
Granted: 1997-12-02
•
Expires: 2016-02-26
Abstract
Abstract A method of forming a silicon oxide film by setting a silicon wafer in a chamber capable of introducing oxidizing gas and being evacuated and by heating the silicon wafer in an oxidizing atmosphere. The method includes the steps of: transporting the silicon wafer into the chamber without contacting the silicon wafer with air; introducing an ozone containing gas into the chamber and setting the interior of the chamber to a predetermined pressure; and heating the silicon wafer to a predetermined temperature and oxidizing the surface of the silicon wafer. The predetermined pressure is preferably between 200 Torr and 0.1 Torr. Ozone may be generated from oxygen by applying ultraviolet rays to the upper space of a silicon wafer. The temperature of ozone to be introduced is preferably low. It is preferable to incorporate infrared heating in order not to excessively heat ozone and to heat a silicon wafer to a high temperature.
Inventors
- 👤 Toshiro Nakanishi
- 👤 Yasuhisa Sato
- 👤 Masaki Okuno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:48
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/10; H10P70/12; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
153 words
A method of forming a silicon oxide film, comprising the steps of: (a) transporting a silicon wafer not having an oxide film intentionally formed on a surface of active regions thereof into an evacuated chamber without contacting said silicon wafer with air, after a preparatory process including oxide removal; (b) introducing gas which contains oxygen and 0.01 volume % to 0.04 volume % ozone into said chamber and setting the interior of said chamber to a pressure capable of causing oxidation of the silicon wafer, said pressure capable of causing oxidation being atmospheric pressure or a lower pressure; and (c) heating said silicon wafer to a temperature in a range from approximately 700° C. to approximately 1100° C. while introducing gas in step (b), thereby thermally oxidizing the surface of said silicon wafer, the silicon wafer being heated after step (a) without an intervening oxidation step at a temperature below approximately 700° C.
Claim 2
Independent Claim
153 words
A method of forming a silicon oxide film, comprising the steps of: (a) transporting a silicon wafer not having an oxide film intentionally formed on a surface of active regions thereof into an evacuated chamber without contacting said silicon wafer with air, after a preparatory process including oxide removal; (b) introducing gas which contains oxygen and 0.01 volume % to 0.04 volume % ozone into said chamber and setting the interior of said chamber to a pressure capable of causing oxidation of the silicon wafer, said pressure capable of causing oxidation being atmospheric pressure or a lower pressure; and (c) heating said silicon wafer to a temperature in a range from approximately 700° C. to approximately 1100° C. while introducing gas in step (b), thereby thermally oxidizing the surface of said silicon wafer, the silicon wafer being heated after step (a) without an intervening oxidation step at a temperature below approximately 700° C.
Claim 3
Dependent Claim
20 words
A method according to claim 1, wherein said pressure capable of causing oxidation is between 200 Torr and 0.1 Torr.
Claim 4
Dependent Claim
17 words
A method according to claim 1, wherein in step (c), water vapor is introduced into said chamber.
Claim 5
Dependent Claim
23 words
A method according to claim 1, wherein in step (c), one of hydrogen chloride gas and chlorine gas is introduced into said chamber.
Claim 6
Dependent Claim
28 words
A method according to claim 1, wherein step (c) further includes a substep of cooling said gas which contains ozone before said gas is introduced into said chamber.
Claim 7
Dependent Claim
30 words
A method according to claim 5, wherein said substep of cooling cools said gas which contains ozone to a temperature in the range from liquid nitrogen temperature to room temperature.
Claim 8
Dependent Claim
20 words
A method according to claim 6, wherein said pressure capable of causing oxidation is between 200 Torr and 0.1 Torr.
Claim 9
Dependent Claim
19 words
A method according to claim 1, wherein in step (c) said silicon wafer is heated by an infrared lamp.
Claim 10
Dependent Claim
39 words
A method according to claim 8, wherein said gas which contains oxygen and 0.01 volume % to 0.04 volume % ozone is introduced in step (b) from a gas supply tube directed to the surface of said silicon wafer.
Claim 11
Dependent Claim
16 words
A method according to claim 8, wherein said pressure capable of causing oxidation is atmospheric pressure.
Claim 12
Independent Claim
131 words
A method of forming a silicon oxide film, comprising the steps of: (a) transporting a silicon wafer not having an oxide film intentionally formed on a surface of active regions thereof into an evacuated chamber without contacting said silicon wafer with air, after a preparatory process including oxide removal; (b) introducing oxygen gas into said chamber and setting the interior of said chamber to a pressure capable of causing oxidation on the silicon wafer; and (c) applying ultraviolet radiation to said oxygen gas introduced into said chamber to generate ozone at a concentration in a range from 0.01 volume % to 0.04 volume %, and heating said silicon wafer to a temperature in a range from approximately 700° C. to 1100° C., thereby thermally oxidizing the surface of said silicon wafer.
Claim 13
Independent Claim
131 words
A method of forming a silicon oxide film, comprising the steps of: (a) transporting a silicon wafer not having an oxide film intentionally formed on a surface of active regions thereof into an evacuated chamber without contacting said silicon wafer with air, after a preparatory process including oxide removal; (b) introducing oxygen gas into said chamber and setting the interior of said chamber to a pressure capable of causing oxidation on the silicon wafer; and (c) applying ultraviolet radiation to said oxygen gas introduced into said chamber to generate ozone at a concentration in a range from 0.01 volume % to 0.04 volume %, and heating said silicon wafer to a temperature in a range from approximately 700° C. to 1100° C., thereby thermally oxidizing the surface of said silicon wafer.
Claim 14
Dependent Claim
22 words
A method according to claim 11, wherein said pressure capable of causing oxidation on the silicon wafer is atmospheric pressure or lower.
Claim 15
Dependent Claim
17 words
A method according to claim 11, wherein in step (c), water vapor is introduced into said chamber.
Claim 16
Dependent Claim
23 words
A method according to claim 11, wherein in step (c), one of hydrogen chloride gas and chlorine gas is introduced into said chamber.
Claim 17
Dependent Claim
17 words
A method according to claim 11, wherein step (b) introduces ozone gas together with said oxygen gas.
Claim 18
Dependent Claim
26 words
A method according to claim 15, wherein step (b) includes a substep of cooling said ozone gas before said ozone gas is introduced into said chamber.
Claim 19
Dependent Claim
28 words
A method according to claim 16, wherein said substep of cooling cools said ozone gas to a temperature in the range from liquid nitrogen temperature to room temperature.
Claim 20
Dependent Claim
24 words
A method according to claim 11, wherein said pressure capable of causing oxidation on the silicon wafer is between 200 Torr and 0.1 Torr.
Claim 21
Independent Claim
187 words
A method of forming a silicon oxide film, comprising the steps of: (a) transporting a silicon wafer not having an oxide film intentionally formed on a surface of active regions thereof into an evacuated chamber without contacting said silicon wafer with air, after a preparatory process including oxide removal, said chamber having an upper hot zone and a lower cool zone, the wafer being first introduced into said lower cool zone; (b) introducing gas which contains ozone at a concentration in a range from 0.1 ppm to 2.5 volume % into said chamber and setting the interior of said chamber to a pressure capable of causing oxidation of the silicon wafer; and (c) elevating said silicon wafer from said lower cool zone to said upper hot zone in the gas which contains ozone, to heat the silicon wafer to a temperature in a range from approximately 700° C. to approximately 1100° C., thereby thermally oxidizing the surface of said silicon wafer without using a plasma, the silicon wafer being heated after steps (a) and (b) without an intervening oxidation step at a temperature below approximately 700° C.
Claim 22
Independent Claim
187 words
A method of forming a silicon oxide film, comprising the steps of: (a) transporting a silicon wafer not having an oxide film intentionally formed on a surface of active regions thereof into an evacuated chamber without contacting said silicon wafer with air, after a preparatory process including oxide removal, said chamber having an upper hot zone and a lower cool zone, the wafer being first introduced into said lower cool zone; (b) introducing gas which contains ozone at a concentration in a range from 0.1 ppm to 2.5 volume % into said chamber and setting the interior of said chamber to a pressure capable of causing oxidation of the silicon wafer; and (c) elevating said silicon wafer from said lower cool zone to said upper hot zone in the gas which contains ozone, to heat the silicon wafer to a temperature in a range from approximately 700° C. to approximately 1100° C., thereby thermally oxidizing the surface of said silicon wafer without using a plasma, the silicon wafer being heated after steps (a) and (b) without an intervening oxidation step at a temperature below approximately 700° C.
Claim 23
Dependent Claim
23 words
A method according to claim 19, wherein said upper hot zone is heated with a resistance heater disposed around said upper hot zone.
Claim 24
Dependent Claim
18 words
A method according to claim 19, wherein the heating in step (c) is done with a lamp heater.
Claim 25
Dependent Claim
16 words
A method according to claim 20, wherein the chamber has an interior wall made of quartz.
Claim 26
Dependent Claim
26 words
A method according to claim 19, wherein the gas introduced in step (b) has an ozone concentration in a range from 0.01 to 0.04 vol. %.
References Cited (Backward Citations)
US4341592A
Cited
US4409260A
Cited
US4906595A
Cited
US4872947A
Cited
JPH01290758A
Cited
JPH01297827A
Cited
JPH01305526A
Cited
JPH02189920A
Cited
JPH03134153A
Cited
US5057463A
Cited
US5089441A
Cited
JPH0439931A
Cited
US5229334A
Cited
US5330935A
Cited
JPH04306824A
Cited
US5294571A
Cited
US5316981A
Cited
JPH06132279A
Cited
US5360769A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-12-01 | 2001-06-02 | 2001-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-12-01 | 2005-06-02 | 2005-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-12-01 | 2009-06-02 | 2009-12-02 | $7700.00 | Window Closed / Lapsed |