Process for low-temperature surface layer oxidation of a semiconductor substrate
Assignee: Raytheon Co
•
Filing: 1982-06-28
•
Granted: 1983-10-11
•
Expires: 2002-06-28
Abstract
Abstract The specification discloses a process for forming a coherent, uniform oxide layer on the surface of a selected semiconductor material by heating a wafer of the selected semiconductor material at a temperature of about 750° C. or lower in the presence of a chosen oxygen-containing precursor and a chosen gas phase halogen-containing molecular reactant which reacts with the oxygen-containing precursor to form atomic oxygen. The substrate is heated in the presence of these reactants for a period of time sufficient to enable the atomic oxygen to react with the surface atoms of the wafer and thus form the coherent uniform oxide layer. The temperature of about 750° C. is sufficiently low to avoid adverse effects, such as dopant migration, on the wafer. In a preferred embodiment of the present invention, a coherent, uniform layer of silicon dioxide is formed on the surface of a silicon wafer.
Inventors
- 👤 Ricardo C. Pastor
- 👤 Remedios K. Chew
- 👤 Luisa E. Gorre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:23
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; C; C23; C23C; C23C8/00; C23C8/06; C23C8/08; C23C8/10; C23C8/12; C23C8/14; H10P14/6322; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
111 words
A process for forming a coherent, uniform oxide layer on the surface of a selected semiconductor material which comprises: (a) providing a wafer of said semiconductor material; and (b) heating said wafer to a temperature of about 750° C. or lower in the presence of a selected oxygen-containing precursor and a chosen gas phase halogen-containing molecular reactant capable of reacting with said oxygen-containing precursor at said temperature to form atomic oxygen, for a period of time sufficient to enable said atomic oxygen to react with the surface atoms of said wafer and thereby form said coherent, uniform oxide layer, said temperature being sufficiently low to avoid adverse effects on said wafer.
Claim 2
Dependent Claim
111 words
A process for forming a coherent, uniform oxide layer on the surface of a selected semiconductor material which comprises: (a) providing a wafer of said semiconductor material; and (b) heating said wafer to a temperature of about 750° C. or lower in the presence of a selected oxygen-containing precursor and a chosen gas phase halogen-containing molecular reactant capable of reacting with said oxygen-containing precursor at said temperature to form atomic oxygen, for a period of time sufficient to enable said atomic oxygen to react with the surface atoms of said wafer and thereby form said coherent, uniform oxide layer, said temperature being sufficiently low to avoid adverse effects on said wafer.
Claim 3
Dependent Claim
37 words
The process as set forth in claim 1 wherein said semiconductor material is selected from the group consisting of silicon, germanium, and an oxidizable semiconductor material capable of withstanding said temperature of about 750° C. or lower.
Claim 4
Dependent Claim
40 words
The process as set forth in claim 1 wherein said wafer is doped with impurities to a predetermined concentration and in a predetermined profile, whereby said temperature is sufficiently low to suppress movement of said dopants in said semiconductor material.
Claim 5
Dependent Claim
40 words
The process set forth in claim 1 wherein said oxygen-containing precursor is selected from the group consisting of water (H 2 O), hydrogen peroxide (H 2 O 2 ), nitrous oxide (N 2 O), and nitrogen dioxide (NO 2 ).
Claim 6
Dependent Claim
50 words
The process set forth in claim 1 wherein said gas phase halogen-containing molecular reactant is selected from the group consisting of Cl 2 , Br 2 , I 2 , CF 4 , CCl 4 CHCl 3 , CBr 4 , CHBr 3 , CI 4 and CHI 3 .
Claim 7
Dependent Claim
89 words
A process for forming an oxide layer on a chosen semiconductor substrate which comprises exposing a surface of said substrate at a temperature of about 750° C. to a mixture of a selected oxygen-containing precursor and a gas phase halogen-containing molecular reactant which is capable of being dissociated by heat to produce atomic halogen that reacts with said oxygen-containing precursor to dissociate off atomic oxygen at said temperature which does not adversely affect said chosen semiconductor substrate, to thereby form said oxide layer on said surface of said substrate.
Claim 8
Dependent Claim
89 words
A process for forming an oxide layer on a chosen semiconductor substrate which comprises exposing a surface of said substrate at a temperature of about 750° C. to a mixture of a selected oxygen-containing precursor and a gas phase halogen-containing molecular reactant which is capable of being dissociated by heat to produce atomic halogen that reacts with said oxygen-containing precursor to dissociate off atomic oxygen at said temperature which does not adversely affect said chosen semiconductor substrate, to thereby form said oxide layer on said surface of said substrate.
Claim 9
Dependent Claim
18 words
The process defined in claim 4 wherein said substrate is silicon and said oxide is substantially silicon dioxide.
Claim 10
Dependent Claim
24 words
The process defined in claim 5 wherein said substrate is heated at a pressure of about one atmosphere for about five hours or more.
References Cited (Backward Citations)
US2802760A
Cited
DE1521950A1
Cited
USRE28385E
Cited
US3692571A
Cited
US4109030A
Cited
US4176206A
Cited
US4139658A
Cited
US4232057A
Cited
US4267205A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |