US4139658A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for manufacturing a radiation hardened oxide
Assignee: RCA Corp
•
Filing: 1976-06-23
•
Granted: 1979-02-13
•
Expires: 1996-06-23
Abstract
Abstract A pyrogenic oxide is grown on a silicon wafer in a furnace by oxidizing hydrogen in the presence of an excess amount of oxygen as well as anhydrous hydrogen chloride to produce steam within the furnace. After growing a suitable pyrogenic oxide layer, the hydrogen and hydrogen chloride flows are turned off while the oxygen flow is continued to grow a dry oxide. A nitrogen anneal while the wafer is slowly pulled from the furnace completes the hybrid, radiation hard oxide layer.
Inventors
- 👤 Seymour H. Cohen
- 👤 Joseph J. Fabula
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:53
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/6322; Y; Y10; Y10S; Y10S148/00; Y10S148/003; Y10S257/00; Y10S257/906; Y10S438/00; Y10S438/953
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
121 words
A process for manufacturing oxides for semiconductor devices comprising the steps of: (a) placing a silicon wafer into a furnace whose temperature is between 800° C. and 1200° C. and into which only oxygen gas, hydrogen gas and an anhydrous hydrogen halide gas are being injected there being an excess of oxygen gas with respect to hydrogen gas such that between 5% and 95% of the oxygen gas injected into the furnace does not combine with hydrogen gas; (b) growing a pyrogenic oxide layer; (c) turning off said hydrogen and hydrogen halide flows and growing a dry oxide layer; (d) turning off said oxygen flow; and (e) injecting an inert gas into said furnace while removing said wafer from said furnace.
Claim 2
Dependent Claim
121 words
A process for manufacturing oxides for semiconductor devices comprising the steps of: (a) placing a silicon wafer into a furnace whose temperature is between 800° C. and 1200° C. and into which only oxygen gas, hydrogen gas and an anhydrous hydrogen halide gas are being injected there being an excess of oxygen gas with respect to hydrogen gas such that between 5% and 95% of the oxygen gas injected into the furnace does not combine with hydrogen gas; (b) growing a pyrogenic oxide layer; (c) turning off said hydrogen and hydrogen halide flows and growing a dry oxide layer; (d) turning off said oxygen flow; and (e) injecting an inert gas into said furnace while removing said wafer from said furnace.
Claim 3
Dependent Claim
24 words
The process of claim 1 in which said hydrogen halide is selected from the group consisting of hydrogen chloride, hydrogen bromide, and hydrogen iodide.
Claim 4
Dependent Claim
17 words
The process of claim 2 wherein said pyrogenic oxide layer is grown for at least 5 minutes.
Claim 5
Dependent Claim
17 words
The process of claim 2 wherein said dry oxide layer is grown for at least 5 minutes.
Claim 6
Dependent Claim
13 words
The process of claim 2 wherein said silicon wafer has N type conductivity.
Claim 7
Dependent Claim
19 words
The process of claim 5 wherein the surface of said crystal is oriented parallel to the (100) crystallographic plane.
Claim 8
Dependent Claim
19 words
The process of claim 2 wherein said pyrogenic oxide layer is grown for between 25 minutes and 50 minutes.
Claim 9
Dependent Claim
18 words
The process of claim 1 wherein said dry oxide layer is grown for between 25 and 50 minutes.
Claim 10
Dependent Claim
18 words
The process of claim 2 wherein the temperature of said furnace is between 850° C. and 1000° C.
Claim 11
Dependent Claim
16 words
The process of claim 1 in which said hydrogen halide is selected to be hydrogen chloride.
Claim 12
Dependent Claim
21 words
The process of claim 10 wherein said hydrogen chloride concentration is between 0.5% and 3.0% of the volume of said furnace.
Claim 13
Dependent Claim
11 words
The process of claim 2 wherein said inert gas is nitrogen.
Claim 14
Dependent Claim
19 words
The process of claim 12 wherein said step of removing takes place over a period of about 5 minutes.
Claim 15
Dependent Claim
21 words
The process of claim 13 wherein the ambient temperature around said wafer varies from said furnace temperature to about 20° C.
References Cited (Backward Citations)
US3258359A
Cited
US3336661A
Cited
USRE28385E
Cited
US3666546A
Cited
US3692571A
Cited
US4010290A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-12 | 1982-08-14 | 1983-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-12 | 1986-08-14 | 1987-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-12 | 1990-08-14 | 1991-02-13 | $7700.00 | Window Closed / Lapsed |