Method of manufacturing a semiconductor device, in which a silicon wafer is provided at its surface with field oxide regions
Assignee: US Philips Corp
•
Filing: 1989-07-21
•
Granted: 1990-03-06
•
Expires: 2009-07-21
Abstract
Abstract A method of manufacturing a semiconductor device, in which a surface (1) of a silicon wafer (2) is locally provided with an oxidation mask (3), whereupon the wafer is subjected to an oxidation treatment by heating it in an oxidizing gas mixture. According to the invention, the wafer is heated during the treatment in the oxidizing gas mixture to a temperature of 950° to 1050° C. Water is then added to the oxidizing gas mixture. The quantity of added water is initially less than 30% by volume and later larger. Thus, in a comparatively short time a comparatively thick layer of oxide can be formed without defects being formed in silicon lying under the oxide.
Inventors
- 👤 Paulus A. van der Plas
- 👤 Wilhelmina C. E. Snels
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:54
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10P14/61; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/0126; H10W10/0127; H10W10/10; H10W10/13; H10P14/6322; Y; Y10; Y10S; Y10S148/00; Y10S148/117; Y10S148/118
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
175 words
A method of manufacturing semiconductor devices having defect free areas below field oxide layers comprising the steps of forming an oxidation preventing mask locally on a surface of a silicon wafer, and oxidizing unmasked portions of said silicon wafer by carrying out in sequence the steps of heating said silicon wafer to a temperature range of 950° C. to 1050° C., initially passing a wet oxidizing gas mixture over said silicon wafer in said temperature range to initially oxidize said unmasked portions of said silicon wafer to a thickness of up to at least 50 nm, said wet oxidizing gas mixture having a water content of at most 30% by volume to prevent defects from forming in the underlying silicon wafer, then adding additional water to said oxidizing gas mixture in said temperature range to bring said water content to an amount of more than 30% by volume, and continuing passing said oxidizing gas mixture with the added water over said silicon wafer until a desired thickness of oxide is formed on said silicon wafer.
Claim 2
Independent Claim
175 words
A method of manufacturing semiconductor devices having defect free areas below field oxide layers comprising the steps of forming an oxidation preventing mask locally on a surface of a silicon wafer, and oxidizing unmasked portions of said silicon wafer by carrying out in sequence the steps of heating said silicon wafer to a temperature range of 950° C. to 1050° C., initially passing a wet oxidizing gas mixture over said silicon wafer in said temperature range to initially oxidize said unmasked portions of said silicon wafer to a thickness of up to at least 50 nm, said wet oxidizing gas mixture having a water content of at most 30% by volume to prevent defects from forming in the underlying silicon wafer, then adding additional water to said oxidizing gas mixture in said temperature range to bring said water content to an amount of more than 30% by volume, and continuing passing said oxidizing gas mixture with the added water over said silicon wafer until a desired thickness of oxide is formed on said silicon wafer.
Claim 3
Dependent Claim
32 words
A method according to claim 1, wherein said step of passing said oxidizing gas mixture is carried out to initially oxidize said silicon wafer to a thickness of 50 to 200 nm.
Claim 4
Dependent Claim
26 words
A method according to claim 1, wherein said step of adding water is carried out to bring said water content to more than 80% by volume.
Claim 5
Dependent Claim
32 words
A method according to claim 3, wherein said step of passing said oxidizing gas mixture is carried out to initially oxidize said silicon wafer to a thickness of 50 to 200 nm.
Claim 6
Dependent Claim
33 words
A method according to claim 1 or claim 3 or claim 4, wherein said step of adding water is carried out by reacting hydrogen and oxygen in the area of said silicon wafer.
Claim 7
Dependent Claim
53 words
A method according to claim 1 or claim 3 or claim 4, wherein said step of forming said oxidation preventing mask is carried out by depositing a base layer of silicon oxynitride having a refractive index of 1.6 to 1.8 and then depositing a top layer of silicon nitride on said base layer.
Claim 8
Dependent Claim
34 words
A method according to claim 6, wherein said base layer is deposited to a thickness of 30 to 50 nm, and said top layer is deposited to a thickness of 75 to 150 nm.
Claim 9
Dependent Claim
14 words
A method according to claim 7, wherein said desired thickness is approximately 800 nm.
Claim 10
Dependent Claim
20 words
A method according to claim 1 or claim 3 or claim 4, wherein said desired thickness is approximately 800 nm.
Claim 11
Dependent Claim
39 words
A method according to claim 1 or claim 3 or claim 4, wherein said step of initially passing a wet oxidizing gas mixture over said silicon wafer is carried out with said water content being about 15% by volume.
Claim 12
Dependent Claim
28 words
A method according to claim 10, wherein said step of initially passing a wet oxidizing gas mixture over said silicon wafer is carried out for about 20 minutes.
Claim 13
Dependent Claim
22 words
A method according to claim 11, wherein said desired thickness of oxide is 800 nm and is obtained in about 4 hours.
References Cited (Backward Citations)
US2930722A
Cited
US3380852A
Cited
US3583685A
Cited
US4139658A
Cited
JPS54125966A
Cited
US4267205A
Cited
US4363868A
Cited
JPS5762545A
Cited
US4376796A
Cited
JPS59181540A
Cited
JPS60122799A
Cited
JPS6116531A
Cited
US4551910A
Cited
US4599247A
Cited
JPS6210018A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-05 | 1993-09-04 | 1994-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-05 | 1997-09-04 | 1998-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-05 | 2001-09-04 | 2002-03-06 | $7700.00 | Window Closed / Lapsed |