Method of providing a dielectric structure for semiconductor devices
Assignee: National Semiconductor Corp
•
Filing: 1994-12-23
•
Granted: 1997-11-18
•
Expires: 2014-12-23
Abstract
Abstract A dielectric structure on a substrate includes a primary dielectric layer on the substrate, the primary dielectric being a metal oxide, such as tantalum pentoxide, having a high dielectric constant, and a secondary dielectric layer, such as an oxide or nitride of silicon, on the primary dielectric layer. In one embodiment, a multi-layer structure includes a second primary dielectric layer disposed on the secondary dielectric layer, and a second secondary dielectric layer disposed on the second primary dielectric layer, each primary dielectric layer being in a first crystalline state characterized by low leakage current for a given applied electrical field. A method of forming a dielectric structure on a substrate includes forming a layer of a primary dielectric, which is a metal oxide having a high dielectric constant, forming a secondary dielectric layer on the primary dielectric layer, and annealing the primary dielectric layer.
Inventors
- 👤 Euisik Yoon
- 👤 Ronald P. Kovacs
- 👤 Michael E. Thomas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:49
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6938; H10P14/6939; H10P14/69393; H10P95/00; H10D; H10D1/00; H10D1/60; H10D1/68; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/0134; H10D64/01342; H10D64/01344; H10D64/60; H10D64/66; H10D64/68; H10D64/681; H10D64/685; H10D64/691; H10D64/693; H10P14/65; H10P14/6516; H10P14/6529; H10P14/6544; H10P14/6921; H10P14/69215; H10P14/694; H10P14/6943; H10P14/69433; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/66; H10P14/662; H10P14/69391; H10P14/69394; Y; Y10; Y10S; Y10S148/00; Y10S148/014
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
157 words
A method of providing a dielectric structure on a substrate, comprising the steps of: (a) providing a first layer of a primary dielectric on the substrate, said primary dielectric being a metal oxide having a high dielectric constant selected from the group consisting of Ta 2 O 5 , TiO 2 , Nb 2 O 5 and Al 2 O 3 ; (b) providing a first secondary dielectric layer on said first primary dielectric layer; (c) annealing said first primary dielectric layer in an oxygen-bearing ambient: (d) providing a second layer of said primary dielectric on said first secondary dielectric layer; (e) providing a second layer of said secondary dielectric on said second primary dielectric layer; and (f) annealing said second layer of said primary dielectric; wherein after said step of annealing each of said layers of said primary dielectric has a polycrystalline structure characterized by mean surface roughness of less than about 5 to 7 Angstroms.
Claim 2
Independent Claim
157 words
A method of providing a dielectric structure on a substrate, comprising the steps of: (a) providing a first layer of a primary dielectric on the substrate, said primary dielectric being a metal oxide having a high dielectric constant selected from the group consisting of Ta 2 O 5 , TiO 2 , Nb 2 O 5 and Al 2 O 3 ; (b) providing a first secondary dielectric layer on said first primary dielectric layer; (c) annealing said first primary dielectric layer in an oxygen-bearing ambient: (d) providing a second layer of said primary dielectric on said first secondary dielectric layer; (e) providing a second layer of said secondary dielectric on said second primary dielectric layer; and (f) annealing said second layer of said primary dielectric; wherein after said step of annealing each of said layers of said primary dielectric has a polycrystalline structure characterized by mean surface roughness of less than about 5 to 7 Angstroms.
Claim 3
Dependent Claim
28 words
A method as recited in claim 1, further comprising the step of providing an interface secondary dielectric layer on the substrate and below said first primary dielectric layer.
Claim 4
Dependent Claim
31 words
A method as recited in claim 1, further comprising the step of forming an oxide layer on said substrate and below said first primary dielectric layer simultaneously with said step (c).
Claim 5
Dependent Claim
35 words
A method as recited in claim 1, wherein each of said steps of providing a secondary dielectric layer comprises providing a secondary dielectric layer having a thickness between approximately 10 Angstroms and approximately 50 Angstroms.
Claim 6
Dependent Claim
48 words
A method as recited in claim 1, wherein each of said steps of providing a secondary dielectric layer comprises providing a layer of a substance selected from the group consisting of SiO 2 , Si 3 N 4 , TiO 2 , and Al 2 O 3 .
Claim 7
Dependent Claim
28 words
A method as recited in claim 1, further comprising the step of providing an interface secondary dielectric layer on the substrate and below said first primary dielectric layer.
Claim 8
Dependent Claim
31 words
A method as recited in claim 1, further comprising the step of forming an oxide layer on said substrate and below said first primary dielectric layer simultaneously with said step (c).
Claim 9
Independent Claim
123 words
A method of providing a dielectric structure on a substrate, comprising the steps of: (a) providing a first layer of a primary dielectric on the substrate, said primary dielectric being Ta 2 O 5 ; (b) providing a first secondary dielectric layer on said first primary dielectric layer; (c) annealing said first primary dielectric layer in an oxygen-bearing ambient; (d) providing a second layer of said primary dielectric on said first secondary dielectric layer; (e) providing a second layer of said secondary dielectric on said second primary dielectric layer; and (f) annealing said second layer of said primary dielectric; wherein each of said steps of providing a primary dielectric layer comprises forming a layer having a thickness of less than approximately 200 Angstroms.
Claim 10
Independent Claim
123 words
A method of providing a dielectric structure on a substrate, comprising the steps of: (a) providing a first layer of a primary dielectric on the substrate, said primary dielectric being Ta 2 O 5 ; (b) providing a first secondary dielectric layer on said first primary dielectric layer; (c) annealing said first primary dielectric layer in an oxygen-bearing ambient; (d) providing a second layer of said primary dielectric on said first secondary dielectric layer; (e) providing a second layer of said secondary dielectric on said second primary dielectric layer; and (f) annealing said second layer of said primary dielectric; wherein each of said steps of providing a primary dielectric layer comprises forming a layer having a thickness of less than approximately 200 Angstroms.
Claim 11
Dependent Claim
31 words
A method as recited in claim 1, wherein each of said steps of providing a primary dielectric layer comprises providing a layer having a thickness of less than approximately 100 Angstroms.
Claim 12
Independent Claim
133 words
A method of forming a capacitor on a substrate wherein the substrate serves as a first electrode, comprising the steps of: (a) providing a first layer of a primary dielectric on the substrate, said primary dielectric being a metal oxide having a high dielectric constant; (b) providing a first secondary dielectric layer on said first primary dielectric layer; (c) providing a second layer of said primary dielectric on said first secondary dielectric layer; (d) providing a second secondary dielectric layer on said second primary dielectric layer; (e) annealing each of said primary dielectric layers so that each of said primary dielectric layers has a polycrystalline structure characterized by mean surface roughness of less than about 5 to 7 Angstroms; and (f) forming a second electrode on a final layer of said secondary dielectric.
Claim 13
Independent Claim
133 words
A method of forming a capacitor on a substrate wherein the substrate serves as a first electrode, comprising the steps of: (a) providing a first layer of a primary dielectric on the substrate, said primary dielectric being a metal oxide having a high dielectric constant; (b) providing a first secondary dielectric layer on said first primary dielectric layer; (c) providing a second layer of said primary dielectric on said first secondary dielectric layer; (d) providing a second secondary dielectric layer on said second primary dielectric layer; (e) annealing each of said primary dielectric layers so that each of said primary dielectric layers has a polycrystalline structure characterized by mean surface roughness of less than about 5 to 7 Angstroms; and (f) forming a second electrode on a final layer of said secondary dielectric.
Claim 14
Dependent Claim
36 words
A method as recited in claim 10, wherein said primary dielectric is selected from the group consisting of Ta 2 O 5 , TiO 2 , Nb 2 O 5 and Al 2 O 5 .
Claim 15
Dependent Claim
45 words
A method as recited in claim 11, wherein said primary dielectric is Ta 2 O 5 , and each of said steps of providing a primary dielectric layer comprises forming a Ta 2 O 5 layer having a thickness of less than approximately 200 Angstroms.
Claim 16
Dependent Claim
35 words
A method as recited in claim 11, wherein each of said steps of providing a primary dielectric layer comprises forming a Ta 2 O 5 layer having a thickness of less than approximately 100 Angstroms.
Claim 17
Dependent Claim
35 words
A method as recited in claim 10, wherein each of said steps of providing a secondary dielectric layer comprises providing a secondary dielectric layer having a thickness between approximately 10 Angstroms and approximately 50 Angstroms.
Claim 18
Dependent Claim
35 words
A method as recited in claim 14, wherein each of said steps of providing a primary dielectric layer comprises forming a Ta 2 O 5 layer having a thickness of less than approximately 100 Angstroms.
Claim 19
Dependent Claim
24 words
A method as recited in claim 15, wherein each of said steps of annealing comprises the step of annealing in an oxygen bearing ambient.
Claim 20
Dependent Claim
48 words
A method as recited in claim 10, wherein each of said steps of providing a secondary dielectric layer comprises providing a layer of a substance selected from the group consisting of SiO 2 , Si 3 N 4 , TiO 2 , and Al 2 O 3 .
Claim 21
Dependent Claim
27 words
A method as recited in claim 10, wherein each of said annealed layers of said primary dielectric has a crystalline structure characterized by relatively small grain size.
References Cited (Backward Citations)
US3668004A
Cited
US3730766A
Cited
US3967310A
Cited
JPS5258490A
Cited
US4335391A
Cited
US4495219A
Cited
US4636833A
Cited
US4659606A
Cited
US4690846A
Cited
JPS61145854A
Cited
US4937650A
Cited
JPS62209832A
Cited
JPS62219659A
Cited
JPS62242331A
Cited
US4891684A
Cited
US5072269A
Cited
US4989056A
Cited
US5091761A
Cited
US5111355A
Cited
JPH04184932A
Cited
US5225286A
Cited
US5173835A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-11-17 | 2001-05-19 | 2001-11-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-11-17 | 2005-05-19 | 2005-11-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-11-17 | 2009-05-19 | 2009-11-18 | $7700.00 | Window Closed / Lapsed |