Method of heat-treating a glass substrate
Assignee: Semiconductor Energy Laboratory Co Ltd
•
Filing: 1994-09-23
•
Granted: 1997-10-07
•
Expires: 2014-09-23
Abstract
Abstract A method of heat-treating a glass substrate where the substrate is thermally treated (such as the formation of films, growth of films, and oxidation) around or above its strain point. After thermally treating the substrate around or above its strain point the glass substrate may be slowly cooled at a rate of 0.01 DEG to 0.5 DEG C./min to achieve maximum shrinkage of the substrate. Following further thermal treatments the substrate may be quickly cooled at a rate of 10 DEG C./min to 300 DEG C./sec to suppress shrinkage of the glass substrate. The substrate can have films such as aluminum nitrate films, silicon oxide films, silicon films, insulating films, semiconductor films, etc. Film formation can occur either before or after thermal treatment of the substrate around or above its strain point and before further thermal treatments.
Inventors
- 👤 Takeshi Fukada
- 👤 Mitsunori Sakama
- 👤 Satoshi Teramoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 02:55
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3429; C03C17/3482; C03B; C03B25/00; C03B32/00; C03C17/001; C03C17/22; C03C17/225; C03C2217/00; C03C2217/20; C03C2217/28; C03C2217/281; C03C2217/282; C03C2218/00; C03C2218/30; C03C2218/32; Y; Y02; Y02P; Y02P40/00; Y02P40/50; Y02P40/57
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
59 words
A method for heat-treating a glass substrate having a strain point comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; and heat-treating said glass substrate at a temperature lying within 50° C. from the strain point of said glass substrate, wherein said film contains oxygen at 0.001 to 10 atomic %.
Claim 2
Independent Claim
59 words
A method for heat-treating a glass substrate having a strain point comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; and heat-treating said glass substrate at a temperature lying within 50° C. from the strain point of said glass substrate, wherein said film contains oxygen at 0.001 to 10 atomic %.
Claim 3
Independent Claim
73 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; and heat-treating said glass substrate at a temperature lying within 50° C. from the strain point of said glass substrate in an ambient atmosphere of nitrogen or a mixture of nitrogen and oxygen, wherein said aluminum nitride contains 0.01 to 20 atomic % of oxygen.
Claim 4
Independent Claim
73 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; and heat-treating said glass substrate at a temperature lying within 50° C. from the strain point of said glass substrate in an ambient atmosphere of nitrogen or a mixture of nitrogen and oxygen, wherein said aluminum nitride contains 0.01 to 20 atomic % of oxygen.
Claim 5
Dependent Claim
30 words
The method of claim 2 further comprising the step of, after said step of heat-treating said glass substrate, cooling said glass substrate at a rate of 0.01° to 0.5° C./min.
Claim 6
Dependent Claim
59 words
The method of claim 2 wherein after said step of heat-treating said glass substrate, a second heat treatment step is carried out at a temperature lower than the temperature of said step of heat-treating said glass substrate, and wherein after the second heat treatment step, the substrate is rapidly cooled at a rate of 10° C./min to 300° C./sec.
Claim 7
Independent Claim
69 words
A method of heat-treating a glass substrate comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; and heat-treating said glass substrate in an ambient atmosphere selected from the group consisting of N 2 , N 2 O, NH 3 and mixtures thereof and simultaneously annealing said film comprising aluminum nitride, wherein said film contains oxygen at 0.001 to 10 atomic %.
Claim 8
Independent Claim
69 words
A method of heat-treating a glass substrate comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; and heat-treating said glass substrate in an ambient atmosphere selected from the group consisting of N 2 , N 2 O, NH 3 and mixtures thereof and simultaneously annealing said film comprising aluminum nitride, wherein said film contains oxygen at 0.001 to 10 atomic %.
Claim 9
Dependent Claim
32 words
The method of claim 5 further comprising a step of cooling said glass substrate in an ambient atmosphere containing N 2 , N 2 O, or NH 3 after said heat-treating step.
Claim 10
Independent Claim
89 words
A method of heat-treating a glass substrate comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; first heat-treating said glass substrate in an ambient atmosphere selected from the group consisting of N 2 , N 2 O, NH 3 and mixtures thereof; slowly cooling said glass substrate after said first heat-treating step; second heat-treating said glass substrate at a temperature lower than a temperature used in said first heat-treating step; and rapidly cooling said glass substrate after said second heat-treating step.
Claim 11
Independent Claim
89 words
A method of heat-treating a glass substrate comprising the steps of: forming a film comprising aluminum nitride on a surface of said glass substrate; first heat-treating said glass substrate in an ambient atmosphere selected from the group consisting of N 2 , N 2 O, NH 3 and mixtures thereof; slowly cooling said glass substrate after said first heat-treating step; second heat-treating said glass substrate at a temperature lower than a temperature used in said first heat-treating step; and rapidly cooling said glass substrate after said second heat-treating step.
Claim 12
Dependent Claim
21 words
The method of claim 7 wherein said slowly cooling step is carried out at a rate of 0.01° to 0.5° C./min.
Claim 13
Dependent Claim
22 words
The method of claim 7 wherein said rapidly cooling step is carried out at a rate of 10° C./min to 300° C./sec.
Claim 14
Independent Claim
54 words
A method of heat-treating a glass substrate comprising the steps of: forming a film comprising aluminum nitride on top and bottom surfaces of said glass substrate; and heat-treating said glass substrate having said film formed thereon in an ambient atmosphere containing nitrogen, wherein said aluminum nitride contains 0.01 to 20 atomic % of oxygen.
Claim 15
Independent Claim
54 words
A method of heat-treating a glass substrate comprising the steps of: forming a film comprising aluminum nitride on top and bottom surfaces of said glass substrate; and heat-treating said glass substrate having said film formed thereon in an ambient atmosphere containing nitrogen, wherein said aluminum nitride contains 0.01 to 20 atomic % of oxygen.
Claim 16
Dependent Claim
36 words
The method of claim 10 wherein said step of forming said film comprising aluminum nitride is carried out by a method selected from the group consisting of positive column plasma CVD, plasma CVD and thermal CVD.
Claim 17
Dependent Claim
26 words
The method of claim 10 wherein said substrate is heated to a temperature higher than a strain point of said glass substrate by said heat-treating step.
Claim 18
Dependent Claim
17 words
The method of claim 10 wherein said glass substrate is maintained substantially horizontally in said heat-treating step.
Claim 19
Independent Claim
106 words
A method of heat-treating a glass substrate on which a semiconductor device is to be formed, said method comprising the steps of: forming a film comprising aluminum nitride at least on a surface of said glass substrate on which said semiconductor device is to be formed; heat-treating said glass substrate; slowly cooling said glass substrate at a rate of 0.01° to 0.5° C./min in an ambient atmosphere containing nitrogen; and then forming said semiconductor device on said glass substrate, wherein the step of heat-treating is carried out at a temperature higher than any process temperature at which said semiconductor device is formed on said glass substrate.
Claim 20
Independent Claim
106 words
A method of heat-treating a glass substrate on which a semiconductor device is to be formed, said method comprising the steps of: forming a film comprising aluminum nitride at least on a surface of said glass substrate on which said semiconductor device is to be formed; heat-treating said glass substrate; slowly cooling said glass substrate at a rate of 0.01° to 0.5° C./min in an ambient atmosphere containing nitrogen; and then forming said semiconductor device on said glass substrate, wherein the step of heat-treating is carried out at a temperature higher than any process temperature at which said semiconductor device is formed on said glass substrate.
Claim 21
Dependent Claim
12 words
The method of claim 14 wherein said semiconductor device comprises a transistor.
Claim 22
Independent Claim
68 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: heat-treating said glass substrate above said strain point; slowly cooling said glass substrate after said heat-treating step; forming a film comprising aluminum nitride at least on one surface of said glass substrate; and heat-treating said glass substrate and said film in an ambient atmosphere containing nitrogen to anneal said film comprising aluminum nitride.
Claim 23
Independent Claim
68 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: heat-treating said glass substrate above said strain point; slowly cooling said glass substrate after said heat-treating step; forming a film comprising aluminum nitride at least on one surface of said glass substrate; and heat-treating said glass substrate and said film in an ambient atmosphere containing nitrogen to anneal said film comprising aluminum nitride.
Claim 24
Independent Claim
120 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: first heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said first heat-treating step at a rate of 0.01° C./min. to 0.5° C./min.; second heat-treating said glass substrate after said first cooling step at a temperature lower than said strain point; and second cooling said glass substrate after said second heat-treating step at a rate of 10° C./min. to 300° C./sec., wherein said method comprises a further step of forming a film on said glass substrate either before or after performing the step of said first heat-treating and before performing the step of said second heat-treating.
Claim 25
Independent Claim
120 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: first heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said first heat-treating step at a rate of 0.01° C./min. to 0.5° C./min.; second heat-treating said glass substrate after said first cooling step at a temperature lower than said strain point; and second cooling said glass substrate after said second heat-treating step at a rate of 10° C./min. to 300° C./sec., wherein said method comprises a further step of forming a film on said glass substrate either before or after performing the step of said first heat-treating and before performing the step of said second heat-treating.
Claim 26
Dependent Claim
21 words
The method of claim 17 wherein said first heat-treating step is carried out in an ambient atmosphere containing N 2 .
Claim 27
Independent Claim
138 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: first heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said first heat-treating step at a rate of 0.01° C./min to 0.5° C./min.; second heat-treating said glass substrate after said first cooling step at a temperature higher than said strain point; and second cooling said glass substrate after said second heat-treating step at a rate of 10° C./min. to 300° C./sec, wherein said first heat-treating step is carried out at a temperature higher than said second heat-treating step, and wherein said method comprises a further step of forming a film on said glass substrate either before or after performing the step of said first heat-treating and before performing the step of said second heat-treating.
Claim 28
Independent Claim
138 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: first heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said first heat-treating step at a rate of 0.01° C./min to 0.5° C./min.; second heat-treating said glass substrate after said first cooling step at a temperature higher than said strain point; and second cooling said glass substrate after said second heat-treating step at a rate of 10° C./min. to 300° C./sec, wherein said first heat-treating step is carried out at a temperature higher than said second heat-treating step, and wherein said method comprises a further step of forming a film on said glass substrate either before or after performing the step of said first heat-treating and before performing the step of said second heat-treating.
Claim 29
Dependent Claim
21 words
The method of claim 19 wherein said first heat-treating step is carried out in an ambient atmosphere containing N 2 .
Claim 30
Independent Claim
131 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: first heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said first heat-treating step at a rate of 0.01° C./min. to 0.5° C./min.; second heat-treating said glass substrate after said first cooling step at a temperature higher than said strain point and lower than said temperature at which said first heat-treating is conducted; and second cooling said glass substrate after said second heat-treating step at a rate of 2° to 200° C./sec. wherein said method comprises a further step of forming a film on said glass substrate either before or after performing the step of said first heat-treating and before performing the step of said second heat-treating.
Claim 31
Independent Claim
131 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: first heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said first heat-treating step at a rate of 0.01° C./min. to 0.5° C./min.; second heat-treating said glass substrate after said first cooling step at a temperature higher than said strain point and lower than said temperature at which said first heat-treating is conducted; and second cooling said glass substrate after said second heat-treating step at a rate of 2° to 200° C./sec. wherein said method comprises a further step of forming a film on said glass substrate either before or after performing the step of said first heat-treating and before performing the step of said second heat-treating.
Claim 32
Dependent Claim
21 words
The method of claim 21 wherein said first heat-treating step is carried out in an ambient atmosphere containing N 2 .
Claim 33
Independent Claim
114 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said heat-treating step at a rate of 0.01° C./min. to 0.5° C./min.; forming an insulating film on said glass substrate; forming a silicon film on said insulating film after said first cooling step; crystallizing said silicon film formed on said insulating film; and second cooling said silicon film formed on said insulating film after said crystallizing step at a rate of 10° C./min. to 300° C./sec., wherein said crystallizing step is carried out at a temperature lower than said heat-treating step.
Claim 34
Independent Claim
114 words
A method of heat-treating a glass substrate having a strain point comprising the steps of: heat-treating said glass substrate at a temperature higher than said strain point; first cooling said glass substrate after said heat-treating step at a rate of 0.01° C./min. to 0.5° C./min.; forming an insulating film on said glass substrate; forming a silicon film on said insulating film after said first cooling step; crystallizing said silicon film formed on said insulating film; and second cooling said silicon film formed on said insulating film after said crystallizing step at a rate of 10° C./min. to 300° C./sec., wherein said crystallizing step is carried out at a temperature lower than said heat-treating step.
Claim 35
Dependent Claim
21 words
The method of claim 23 wherein said first heat-treating step is carried out in an ambient atmosphere containing N 2 .
Claim 36
Dependent Claim
12 words
The method of claim 23 wherein said insulating film comprises silicon oxide.
References Cited (Backward Citations)
US4116658A
Cited
US4100330A
Cited
US4399015A
Cited
JPS58114037A
Cited
US4824712A
Cited
US5165972A
Cited
US5094966A
Cited
US4959136A
Cited
US5252140A
Cited
JPH01319682A
Cited
JPH02102150A
Cited
US5254208A
Cited
US5262654A
Cited
US5163220A
Cited
US5296653A
Cited
US5372860A
Cited
US5492843A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-10-06 | 2001-04-07 | 2001-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-10-06 | 2005-04-07 | 2005-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-10-06 | 2009-04-07 | 2009-10-07 | $7700.00 | Window Closed / Lapsed |