Method of making a semiconductor laser device
Assignee: Fujifilm Business Innovation Corp
•
Filing: 1996-07-29
•
Granted: 1997-07-15
•
Expires: 2016-07-29
Abstract
Abstract A semiconductor laser device in which semiconductor layers of an n-type cladding layer, a quantum well active layer 106, a p-type cladding layer, and an intermediate layer are formed on an n-type GaAs substrate in successive order, and a mixed-crystal is formed in a region except the semiconductor layers of the contact layer and the lower part of the contact layer by diffusing Si into the structure from above the intermediate layer, characterized in that the contact layer and the intermediate layer are made of n-type or nonconductive semiconductor material, and a p-type low-resistance region, formed by diffusing Zn into the structure from above the contact layer, is profiled so as not to overlap with the mixed-crystal region formed by Si diffusion.
Inventors
- 👤 Hiromi Otoma
- 👤 Nobuaki Ueki
- 👤 Hideki Fukunaga
- 👤 Hideo Nakayama
- 👤 Yasuji Seko
- 👤 Mario Fuse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:56
CPC Classifications
B; B82; B82Y; B82Y20/00; H; H01; H01S; H01S5/00; H01S5/20; H01S5/04; H01S5/042; H01S5/0421; H01S5/2054; H01S5/2059; H01S5/30; H01S5/32; H01S5/3206; H01S5/321; H01S5/323; H01S5/32308; H01S5/32325; H01S5/34; H01S5/343; H01S5/34326
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
258 words
A method for manufacturing a semiconductor laser device, comprising the steps of: a) forming a first cladding layer made of semiconductor of a first conductivity type on a substrate; b) forming a quantum well active layer made of semiconductor on said first cladding layer; c) forming a second cladding layer layered on said quantum well active layer, said second cladding layer being made of semiconductor material of a second conductivity type that is opposite to said first conductivity type; d) forming an intermediate layer on said second cladding layer, said intermediate layer being made of semiconductor material of said first conductivity type or nonconductive type semiconductor; e) forming a contact layer on a part of said intermediate layer, said contact layer being made of semiconductor material of said first conductivity type or nonconductive type semiconductor; f) forming a first impurity layer at a location deviated sideways from said contact layer, said first impurity layer being made of a first impurity for forming a mixed crystal of said second conductivity type by diffusing said first impurity into said second cladding layer; g) forming a mixed-crystal by diffusing the first impurity into the structure up to said quantum well active layer after said first impurity layer is formed; and h) forming a low resistance region of a second conductivity type by diffusing a second impurity, said low resistance region being extended over a range from said contact layer, through said intermediate layer, to part of said second cladding layer, and being isolated from said mixed-crystal region by said intermediate layer.
Claim 2
Independent Claim
258 words
A method for manufacturing a semiconductor laser device, comprising the steps of: a) forming a first cladding layer made of semiconductor of a first conductivity type on a substrate; b) forming a quantum well active layer made of semiconductor on said first cladding layer; c) forming a second cladding layer layered on said quantum well active layer, said second cladding layer being made of semiconductor material of a second conductivity type that is opposite to said first conductivity type; d) forming an intermediate layer on said second cladding layer, said intermediate layer being made of semiconductor material of said first conductivity type or nonconductive type semiconductor; e) forming a contact layer on a part of said intermediate layer, said contact layer being made of semiconductor material of said first conductivity type or nonconductive type semiconductor; f) forming a first impurity layer at a location deviated sideways from said contact layer, said first impurity layer being made of a first impurity for forming a mixed crystal of said second conductivity type by diffusing said first impurity into said second cladding layer; g) forming a mixed-crystal by diffusing the first impurity into the structure up to said quantum well active layer after said first impurity layer is formed; and h) forming a low resistance region of a second conductivity type by diffusing a second impurity, said low resistance region being extended over a range from said contact layer, through said intermediate layer, to part of said second cladding layer, and being isolated from said mixed-crystal region by said intermediate layer.
Claim 3
Dependent Claim
49 words
The method of manufacturing a semiconductor laser device of claim 1, further comprising: a step of forming a diffusion/protective layer with an opening layered on said contact layer, and in said low resistance region forming step, said second impurity being supplied through said opening, from above said diffusion/protective layer.
Claim 4
Dependent Claim
78 words
The method of manufacturing a semiconductor laser device of claim 2, wherein the size of said opening of said diffusion/protective layer, and the thickness of said contact layer and said intermediate layer are selected such that the diffusion of said second impurity, which is supplied through said opening of said diffusion/protective layer, reaches said second cladding layer through said contact layer and said intermediate layer, and terminates before reaching said mixed crystal region made of said first impurity.
Claim 5
Dependent Claim
195 words
The method of manufacturing a semiconductor laser device of claim 2, wherein the size of said opening of said diffusion/protective layer, and the thickness of said contact layer, said intermediate layer and the impurities diffusion condition determining diffusion length of l 1 and 1 2 are selected so as to satisfy the following inequalities: l.sub.1 +l.sub.2 <l d<c where l 1 : length of the diffusion of said first impurity in a direction parallel to the surface of said intermediate layer, as measured from the end of said impurity layer closer to said contact layer l 2 : length of the diffusion of said second impurity in a direction parallel to the surface of said intermediate layer, as measured from the side wall of said opening of said diffusion/protective layer l: distance between a side wall of said opening of said diffusion/protective layer and the end of said impurity layer closer to said contact layer c: length of the diffusion of the second impurity in a direction vertical to the surface of said intermediate layer, as measured from the surface of said contact layer d: total thickness of said contact layer and said intermediate layer.
References Cited (Backward Citations)
US5047366A
Cited
US5219785A
Cited
US5460984A
Cited
JPH04219989A
Cited
US5253265A
Cited
US5275969A
Cited
US5232867A
Cited
US5256596A
Cited
JPH0653605A
Cited
JPH0653604A
Cited
US5567646A
Cited
US5376583A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-07-14 | 2001-01-13 | 2001-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-07-14 | 2005-01-13 | 2005-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-07-14 | 2009-01-13 | 2009-07-15 | $7700.00 | Window Closed / Lapsed |