Method for fabricating a MOS transistor with two-layer inverse-T tungsten gate structure
Assignee: International Business Machines Corp
•
Filing: 1994-11-22
•
Granted: 1997-02-04
•
Expires: 2014-11-22
Abstract
Abstract The present invention is directed to a unique method for fabricating a silicon based MOS transistor having an inverse-T refractory metal gate structure. The gate fabricated according to this invention comprises a main CVD tungsten portion and a lower sputtered tungsten portion outwardly extending from the bottom of the CVD portion such that a cross section of the gate appears as an inverted "T". A Cl 2 /O 2 plasma etch is used to etch the CVD tungsten layer and a chemical etch is used to etch the sputtered tungsten layer to form the gate electrode. It has been discovered that sputtered tungsten is more resistant to Cl 2 /O 2 reactive ion etch than is CVD tungsten. The sputtered tungsten layer acts as a shield to protect the underlying gate oxide layer from ion damage throughout the fabrication process.
Inventors
- 👤 Fernand Dorleans
- 👤 Liang-Choo Hsia
- 👤 Louis L. C. Hsu
- 👤 Gerald R. Larsen
- 👤 Geraldine C. Schwartz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:33
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01316; H10D64/01324; H10D64/021; H10P; H10P32/00; H10P32/10; H10P32/14; H10P32/1408; H10P32/141; H10P32/1412; H10P32/17; H10P32/171; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/60; H10P50/66; H10P50/663; H10P50/667
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
104 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of refractory metal having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of refractory metal having a second density on said first layer of refractory metal; wherein said first density is lower than said second density; etching said second layer to form an upper gate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion.
Claim 2
Independent Claim
104 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of refractory metal having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of refractory metal having a second density on said first layer of refractory metal; wherein said first density is lower than said second density; etching said second layer to form an upper gate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion.
Claim 3
Dependent Claim
24 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 1 wherein said refractory metal is molybdenum.
Claim 4
Dependent Claim
24 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 1 wherein said refractory metal is tungsten.
Claim 5
Independent Claim
129 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of refractory metal having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of refractory metal having a second density on said first layer of refractory metal; wherein said first density is lower than said second density, wherein said first layer of refractory metal is deposited by sputter deposition and said second layer of refractory metal is deposited by chemical vapor deposition; etching said second layer to form an upper gate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion.
Claim 6
Independent Claim
129 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of refractory metal having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of refractory metal having a second density on said first layer of refractory metal; wherein said first density is lower than said second density, wherein said first layer of refractory metal is deposited by sputter deposition and said second layer of refractory metal is deposited by chemical vapor deposition; etching said second layer to form an upper gate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion.
Claim 7
Independent Claim
128 words
A method for fabricating a tungsten gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of tungsten having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of tungsten having a second density on said first layer of tungsten metal; wherein said first density is lower than said second density; etching said second layer to form an upper gate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion, wherein said second tungsten layer is etched by Cl 2 /O 2 plasma, said first tungsten layer acting to stop said Cl 2 /O 2 plasma etch.
Claim 8
Independent Claim
128 words
A method for fabricating a tungsten gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of tungsten having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of tungsten having a second density on said first layer of tungsten metal; wherein said first density is lower than said second density; etching said second layer to form an upper gate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion, wherein said second tungsten layer is etched by Cl 2 /O 2 plasma, said first tungsten layer acting to stop said Cl 2 /O 2 plasma etch.
Claim 9
Independent Claim
111 words
A method for fabricating a tungsten gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of tungsten having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of tungsten having a second density on said first layer of tungsten metal; wherein said first density is lower than said second density; etching said second layer to form an uppergate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion, wherein said first tungsten layer is etched by wet chemical etch.
Claim 10
Independent Claim
111 words
A method for fabricating a tungsten gate electrode for a MOS transistor, comprising the steps of: depositing a first layer of tungsten having a first density on a gate oxide layer formed on a silicon substrate; depositing a second layer of tungsten having a second density on said first layer of tungsten metal; wherein said first density is lower than said second density; etching said second layer to form an uppergate electrode portion; and, partially etching a thickness of said first layer to form a lower portion of said gate electrode that extends laterally beyond said upper gate electrode portion, wherein said first tungsten layer is etched by wet chemical etch.
Claim 11
Dependent Claim
33 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 6 wherein said wet chemical etch comprises KH 2 PO 4 /KOH/K 3 Fe(CN) 6 .
Claim 12
Dependent Claim
73 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 1, further comprising the steps of: implanting impurity ion dopants into a portion of said first layer using said upper gate electrode as a mask, said dopants being contained within said first layer during said implanting step; annealing said silicon substrate to drive-in said dopant to form a shallow source region and a shallow drain region.
Claim 13
Dependent Claim
66 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 1, further comprising the steps of: forming a first sidewall spacer about said upper gate electrode portion, said first sidewall spacer extending over a portion of said lower gate electrode portion; forming a second sidewall spacer about said first sidewall spacer after said step of etching said first layer.
Claim 14
Dependent Claim
58 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 9, further comprising the steps of: forming a silicide over said source region and said drain region; implanting dopant into said silicide; driving said dopant into said source region and said drain region, said dopant for reducing contact and series resistance.
Claim 15
Dependent Claim
28 words
A method for fabricating a refractory metal gate electrode for a MOS transistor, as recited in claim 1, wherein said first layer is thinner than said second layer.
References Cited (Backward Citations)
US4319932A
Cited
US4356623A
Cited
US4356623B1
Cited
US4901128A
Cited
JPS6342173A
Cited
US4963504A
Cited
JPH01206667A
Cited
US5049514A
Cited
US4906589A
Cited
US4984042A
Cited
US5217923A
Cited
US5140403A
Cited
US5306655A
Cited
US5162884A
Cited
US5182619A
Cited
US5304504A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-04 | 2000-08-05 | 2001-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-04 | 2004-08-05 | 2005-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-04 | 2008-08-05 | 2009-02-04 | $7700.00 | Window Closed / Lapsed |