Annealing of titanium - titanium nitride in contact hole
Assignee: Vanguard International Semiconductor Corp
•
Filing: 1995-10-27
•
Granted: 1997-01-07
•
Expires: 2015-10-27
Abstract
Abstract A process has been developed in which small diameter contact holes can be filled with chemically vapor deposited tungsten, without severe attack of the contact hole liner materials. An adhesive layer of titanium, and a barrier layer of titanium nitride are used for the contact hole liner, and are deposited prior to tungsten process. A process consisting of subjecting the barrier layer of titanium nitride to a rapid thermal anneal, in an ammonia ambient, results in enhanced barrier characteristics. The robust titanium nitride layer is now able to survive the tungsten deposition process, and attack form fluorine ions, produced during the decomposition of the tungsten source, tungsten hexafluoride.
Inventors
- 👤 Ching-Ying Lee
- 👤 Shaw-Tzeng Hsia
- 👤 Haw Yen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:26
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/041; H10W20/033; H10W20/047; H10W20/048; H10W20/056
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
250 words
A method for fabricating a MOSFET device on a semiconductor substrate, using a contact hole, lined with an adhesive and barrier layers and filled with a metal, to provide electrical contact between an active device region in said semiconductor substrate, and an overlying metal interconnect structure, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element, to create said active device region; surface cleaning of said active device region; deposition of an adhesive layer on said dielectric layer, on sides of said contact hole, and on surface of said active device region; deposition of a barrier comprising a metal nitride layer on said adhesive layer; after the deposition of the barrier layer, rapid thermal annealing in a nitrogen containing ambient thereby nitriding a portion of the adhesive layer; deposition of said metal, on said barrier layer, completely filling said contact hole; etchback of said metal to form a metal plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form said metal interconnect structure.
Claim 2
Independent Claim
250 words
A method for fabricating a MOSFET device on a semiconductor substrate, using a contact hole, lined with an adhesive and barrier layers and filled with a metal, to provide electrical contact between an active device region in said semiconductor substrate, and an overlying metal interconnect structure, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant into said specific region of said device element, to create said active device region; surface cleaning of said active device region; deposition of an adhesive layer on said dielectric layer, on sides of said contact hole, and on surface of said active device region; deposition of a barrier comprising a metal nitride layer on said adhesive layer; after the deposition of the barrier layer, rapid thermal annealing in a nitrogen containing ambient thereby nitriding a portion of the adhesive layer; deposition of said metal, on said barrier layer, completely filling said contact hole; etchback of said metal to form a metal plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form said metal interconnect structure.
Claim 3
Dependent Claim
21 words
The method of claim 1, wherein said device element in said semiconductor substrate , is an N type, field effect transistor.
Claim 4
Dependent Claim
36 words
The method of claim 1, wherein said dielectric layer is silicon oxide, deposited using LPCVD or PECVD processing, at a temperature between about 400° and 800° C., to a thickness between about 6000 and 14000 Angstroms.
Claim 5
Dependent Claim
35 words
The method of claim 1, wherein said contact hole is formed via anisotropic RIE processing, using CHF 3 +CF 4 + argon, with said contact hole having a diameter between about 0.3 and 0.7 μm.
Claim 6
Dependent Claim
35 words
The method of claim 1, wherein said first conductivity imparting dopant is arsenic, ion implanted at an energy between about 20 and 50 Key., at a dose between about 1E15 and 5E15 atoms/cm 2 .
Claim 7
Dependent Claim
41 words
The method of claim 1, wherein surface cleaning of said active device region is performed using a solution of water and hydrofluoric acid, at a temperature between about 20° and 25° C., for a time between about 75 and 105 seconds.
Claim 8
Dependent Claim
24 words
the method of claim 1, wherein said adhesive layer is titanium, deposited via r.f. sputtering, to a thickness between about 250 and 500 Angstroms.
Claim 9
Dependent Claim
30 words
The method of claim 1, wherein said barrier layer is titanium nitride, deposited using r.f. sputtering, using a titanium nitride target, to a thickness between about 800 and 1800 Angstroms.
Claim 10
Dependent Claim
35 words
The method of claim 1, wherein said barrier layer is titanium nitride, deposited using reactive r.f. sputtering, using a titanium target in a nitrogen containing ambient, to a thickness between about 800 and 1800 Angstroms.
Claim 11
Dependent Claim
119 words
The method of claim 1, wherein said rapid thermal annealing of said barrier layer is performed by; loading of wafers in rapid thermal anneal furnace at a temperature between about 350° and 450° C., in a nitrogen flow of about 20 liters/min., ramp up and stabilization an a temperature between about 575° and 625° C., for about 60 seconds in an ammonia flow of between about 2 and 5 liters/min., ramp up and stabilization at a temperature between about 700° and 740° C., for about 20 seconds in a ammonia flow between about 2 and 5 liters/min., and ramp down and unload at a temperature between about 350° and 430° C., in a nitrogen flow of about 20 liters/min.
Claim 12
Dependent Claim
38 words
The method of claim 1, wherein said rapid thermal annealing of said barrier layer is performed in an ammonia ambient, at a temperature between about 700° and 740° C., for a time between about 10 and 60 seconds.
Claim 13
Dependent Claim
44 words
The method of claim 1, wherein rapid thermal annealing of said barrier layer is performed in a nitrogen flow between about 2 and 5 liters/min., at a stabilization temperature between about 650° and 800° C., for a time between about 30 and 90 seconds.
Claim 14
Dependent Claim
40 words
The method of claim 1 in wherein said rapid thermal annealing of said barrier layer results in the formation of a titanium disilicide layer at the bottom of said contact hole, to a thickness between about 100 and 300 Angstroms.
Claim 15
Dependent Claim
39 words
The method of claim 1, wherein said metal is tungsten, deposited using LPCVD processing, at a temperature between about 400° and 500° C., to a thickness between about 5000 and 9000 Angstroms, using tungsten hexafluoride as a source material.
Claim 16
Independent Claim
248 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole lined with titanium, for adhesion purposes, titanium nitride, for barrier purposes, and filled with tungsten, to provide electrical contact between an active device region and an overlying metal interconnect structure, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant, into said specific region of said device element, to create a doped N type region; surface cleaning of said doped N type region; deposition of said titanium layer, on said dielectric layer, on sides of said contact hole, and on said doped N type region; deposition of said titanium nitride layer on said titanium layer; after the deposition of said titanium nitride layer, rapid thermal annealing in an ammonia ambient thereby nitriding a portion of said titanium layer; deposition of said tungsten on said titanium nitride layer, completely filling said contact hole; etchback of said tungsten to form a tungsten plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form said metal interconnect structure.
Claim 17
Independent Claim
248 words
A method for fabricating a MOSFET device, on a semiconductor substrate, using a contact hole lined with titanium, for adhesion purposes, titanium nitride, for barrier purposes, and filled with tungsten, to provide electrical contact between an active device region and an overlying metal interconnect structure, comprising the steps of: providing device elements on said semiconductor substrate; deposition of a dielectric layer on said semiconductor substrate, including deposition on said device elements; photolithographic processing to open a region in photoresist, exposing said dielectric layer, directly over a specific region of said device element; anisotropic etching of said dielectric layer, in opened region of said photoresist, to create a contact hole to said specific region of said device element; ion implanting a first conductivity imparting dopant, into said specific region of said device element, to create a doped N type region; surface cleaning of said doped N type region; deposition of said titanium layer, on said dielectric layer, on sides of said contact hole, and on said doped N type region; deposition of said titanium nitride layer on said titanium layer; after the deposition of said titanium nitride layer, rapid thermal annealing in an ammonia ambient thereby nitriding a portion of said titanium layer; deposition of said tungsten on said titanium nitride layer, completely filling said contact hole; etchback of said tungsten to form a tungsten plug in said contact hole; deposition of an interconnect metallization layer; and patterning of said interconnect metallization layer to form said metal interconnect structure.
Claim 18
Dependent Claim
20 words
The method of claim 15, wherein said device element in said semiconductor substrate, is an N type field effect transistor.
Claim 19
Dependent Claim
36 words
The method of claim 15, wherein said dielectric layer is silicon oxide, deposited using LPCVD or PECVD processing, at a temperature between about 400° and 800° C., to a thickness between about 6000 and 14000 Angstroms.
Claim 20
Dependent Claim
35 words
The method of claim 15, wherein said first conductivity imparting dopant is arsenic, ion implanted at an energy between about 20 and 50 Kev., at a dose between about 1E15 and 5E15 atoms/cm 2 .
Claim 21
Dependent Claim
23 words
The method of claim 15, wherein said titanium layer is deposited using r.f. sputtering, to a thickness between about 250 and 500 Angstroms.
Claim 22
Dependent Claim
29 words
The method of claim 15, wherein said titanium nitride layer is deposited via r.f. sputtering, using a titanium nitride target, to a thickness between about 800 and 1800 Angstroms.
Claim 23
Dependent Claim
29 words
The method of claim 15, wherein said titanium nitride layer is deposited via reactive r.f sputtering, using a titanium target, to a thickness between about 800 and 1800 Angstroms.
Claim 24
Dependent Claim
125 words
The method of claim 15, wherein said rapid thermal annealing of said titanium nitride layer is performed by; initially loading wafers into rapid thermal anneal furnace at a temperature between about 350° and 450° C., in a nitrogen flow of about 20 liters/min., ramp up and stabilization at a temperature between about 575° and 625° C., for a time of about 60 seconds, in an ammonia flow between about 2 and 5 liters/min., ramp up and stabilization at a temperature between about 700° and 740° C., for a time of about 20 seconds, in an ammonia flow between about 2 and 5 liters/min., and ramp down and unload at a temperature between about 350° and 450° C., in a nitrogen flow of about 20 liters/min.
Claim 25
Dependent Claim
39 words
The method of claim 15, wherein said rapid thermal annealing of said titanium nitride layer is performed in an ammonia ambient, at a temperature between about 700° to 740° C., for a time between about 10 and 60 seconds.
Claim 26
Dependent Claim
47 words
The method of claim 15, wherein said rapid thermal annealing of said titanium nitride layer is performed in a nitrogen flow of between about 2 and 5 liters/min., at a stabilization temperature between about 650° and 800° C., for a time between about 30 and 90 seconds.
Claim 27
Dependent Claim
53 words
The method of claim 15, wherein said rapid thermal annealing, of said titanium nitride layer, results in the creation of a titanium disilicide layer, at the bottom of said contact hole, from the reaction of said titanium layer and said doped N type region, to a thickness between about 100 and 300 Angstroms.
Claim 28
Dependent Claim
36 words
The method of claim 15, wherein said tungsten is deposited using LPCVD processing, at a temperature between about 400° and 500° C., to a thickness between about 5000 and 9000 Angstroms, using a tungsten hexafluoride source.
References Cited (Backward Citations)
JPH01220824A
Cited
US4994410A
Cited
US5232871A
Cited
JPH0529316A
Cited
US5434044A
Cited
US5525543A
Cited
US5275715A
Cited
JPH06275559A
Cited
US5286675A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-07 | 2000-07-08 | 2001-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-07 | 2004-07-08 | 2005-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-07 | 2008-07-08 | 2009-01-07 | $7700.00 | Window Closed / Lapsed |