Method for producing a transparent conductive ZnO film by incorporating a boron or aluminum containing material
Assignee: YKK Corp
•
Filing: 1995-04-04
•
Granted: 1996-08-13
•
Expires: 2015-04-04
Abstract
Abstract The formation of a transparent conductive ZnO film on a substrate in accordance with the chemical vapor deposition process is accomplished herein by a method characterized by feeding purified water and an organic metal material for Zn as separately entrained by a carrier gas into a vacuum chamber having a reduced inner pressure, adjusting the gas pressure inside the vacuum chamber to a level in the range of from 1 to 30 Torrs, supplying diborane gas or a compound containing boron or aluminum into the vacuum chamber, heating a substrate disposed inside the chamber to a prescribed temperature, and performing the ensuant formation of a film under the adjusted gas pressure mentioned above. Preferably, the formation of the film on the substrate disposed inside the vacuum chamber is carried out while the substrate is kept irradiated with ultraviolet light. This method enables the transparent conductive ZnO film possessing a textured surface form, exhibiting low resistivity, and particularly befitting adoption as a transparent conductive film in a thin-film solar cell to be produced at a relatively high film-forming rate.
Inventors
- 👤 Akira Yamada
- 👤 Shinichiro Yoshida
- 👤 Masahiro Yoshino
- 👤 Kiyoshi Takahashi
- 👤 Akira Omura
- 👤 Makoto Konagai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:02
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/48; C23C16/482; C23C16/22; C23C16/30; C23C16/40; C23C16/407; H; H10; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2922; H10P14/34; H10P14/3402; H10P14/3424; H10P14/3426; H10P14/3438; H10P14/3441
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
181 words
A method for the production of a transparent conductive ZnO film having a textured surface, the method comprising the preparatory steps of reducing a pressure in a vacuum chamber, heating a substrate disposed inside said vacuum chamber to a temperature in the range of from about 120° C. to about 270° C., feeding purified water as entrained by an inert carrier gas into said vacuum chamber, and adjusting the gas pressure inside said chamber to a level in the range of from 1 to 30 Torrs and the film-forming steps of supplying an organozinc compound as entrained by a carrier gas in conjunction with at least one compound selected from the group consisting of diborane, trimethyl boron, triethyl boron, triethyl aluminum, triisobutyl aluminum and dimethyl aluminum hydride into said vacuum chamber, irradiating the substrate with ultraviolet light having a wavelength of not more than 254 nm so as to be consumed at a rate of at least 1 mW/cm 2 , and continuing the ensuing formation of said ZnO film having a textured surface under the adjusted gas pressure mentioned above.
Claim 2
Independent Claim
181 words
A method for the production of a transparent conductive ZnO film having a textured surface, the method comprising the preparatory steps of reducing a pressure in a vacuum chamber, heating a substrate disposed inside said vacuum chamber to a temperature in the range of from about 120° C. to about 270° C., feeding purified water as entrained by an inert carrier gas into said vacuum chamber, and adjusting the gas pressure inside said chamber to a level in the range of from 1 to 30 Torrs and the film-forming steps of supplying an organozinc compound as entrained by a carrier gas in conjunction with at least one compound selected from the group consisting of diborane, trimethyl boron, triethyl boron, triethyl aluminum, triisobutyl aluminum and dimethyl aluminum hydride into said vacuum chamber, irradiating the substrate with ultraviolet light having a wavelength of not more than 254 nm so as to be consumed at a rate of at least 1 mW/cm 2 , and continuing the ensuing formation of said ZnO film having a textured surface under the adjusted gas pressure mentioned above.
Claim 3
Dependent Claim
16 words
A method according to claim 1, wherein said organozinc compound is dimethyl zinc or diethyl zinc.
Claim 4
Independent Claim
182 words
A method for the production of a transparent conductive ZnO film having a textured surface on a substrate by a chemical vapor deposition process, the method comprising reducing a pressure in a vacuum chamber, entraining purified water and an organozinc compound into separate flows of a carrier gas and feeding the flows into a vacuum chamber having a reduced inner gas pressure, adjusting the inner gas pressure in said vacuum chamber to a level in the range of from 1 to 30 Torrs, supplying at least one compound selected from the group consisting of diborane, trimethyl boron, triethyl boron, triethyl aluminum, triisobutyl aluminum and dimethyl aluminum hydride into said vacuum chamber, and heating a substrate disposed inside said vacuum chamber to a temperature in the range of from about 120° C. to about 270° C. while irradiating the substrate with ultraviolet light having a wavelength of not more than 254 nm so as to be consumed at a rate of at least 1 mW/cm 2 to deposit said ZnO film having a textured surface on the substrate under said adjusted gas pressure.
Claim 5
Independent Claim
182 words
A method for the production of a transparent conductive ZnO film having a textured surface on a substrate by a chemical vapor deposition process, the method comprising reducing a pressure in a vacuum chamber, entraining purified water and an organozinc compound into separate flows of a carrier gas and feeding the flows into a vacuum chamber having a reduced inner gas pressure, adjusting the inner gas pressure in said vacuum chamber to a level in the range of from 1 to 30 Torrs, supplying at least one compound selected from the group consisting of diborane, trimethyl boron, triethyl boron, triethyl aluminum, triisobutyl aluminum and dimethyl aluminum hydride into said vacuum chamber, and heating a substrate disposed inside said vacuum chamber to a temperature in the range of from about 120° C. to about 270° C. while irradiating the substrate with ultraviolet light having a wavelength of not more than 254 nm so as to be consumed at a rate of at least 1 mW/cm 2 to deposit said ZnO film having a textured surface on the substrate under said adjusted gas pressure.
Claim 6
Dependent Claim
16 words
A method according to claim 3, wherein said organozinc compound is dimethyl zinc or diethyl zinc.
References Cited (Backward Citations)
US3907616A
Cited
US4751149A
Cited
US4631199A
Cited
JPS62154411A
Cited
US4798808A
Cited
US4753818A
Cited
US4888203A
Cited
US4873118A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-08-13 | 2000-02-12 | 2000-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-08-13 | 2004-02-12 | 2004-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-08-13 | 2008-02-12 | 2008-08-13 | $7700.00 | Window Closed / Lapsed |