US4753818A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for photochemical vapor deposition of oxide layers at enhanced deposition rates
Assignee: Raytheon Co
•
Filing: 1986-07-25
•
Granted: 1988-06-28
•
Expires: 2006-07-25
Abstract
Abstract A process for depositing an oxide layer on a substrate by exposing the substrate to a selected vapor phase reactant, a chosen oxygen-containing precursor, and a selected physical quenching gas, in the presence of radiation of a selected wavelength. The radiation causes the direct dissociation of the oxygen-containing precursor to form neutral oxygen atoms in an excited electronic state. The quenching gas physically interacts with the oxygen atoms in the excited electronic state to form oxygen atoms in the unexcited electronic state. The latter then react with the vapor phase reactant to form the oxide, which deposits as a layer on the substrate. The rate of reaction to form and deposit the oxide layer is enhanced by the conversion of the excited electronic state oxygen atoms to unexcited electronic state oxygen atoms by the physical quenching gas.
Inventors
- 👤 Harvey N. Rogers, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:46
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/48; C23C16/482; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/402
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
154 words
A photochemical vapor deposition process for depositing a layer of an oxide of a chosen material on the surface of a selected substrate comprising the steps of: (a) providing said substrate; and (b) exposing said substrate to a selected vapor phase reactant comprising silane, a chosen oxygen-containing precursor comprising nitrous oxide, and a selected physical quenching gas comprising neopentane, in the presence of radiation having a wavelength of about 1849 angstroms to cause the direct dissociation of said oxygen-containing precursor to form neutral oxygen atoms in an excited electronic state wherein said quenching gas physically interacts with said oxygen atoms in said excited electronic state to form oxygen atoms in the unexcited electronic state and said oxygen atoms in said unexcited electronic state react with said vapor phase reactant to form said oxide comprising predominantly silicon dioxide, which deposits as said layer on said surface of said substrate at an enhanced rate of deposition.
Claim 2
Dependent Claim
154 words
A photochemical vapor deposition process for depositing a layer of an oxide of a chosen material on the surface of a selected substrate comprising the steps of: (a) providing said substrate; and (b) exposing said substrate to a selected vapor phase reactant comprising silane, a chosen oxygen-containing precursor comprising nitrous oxide, and a selected physical quenching gas comprising neopentane, in the presence of radiation having a wavelength of about 1849 angstroms to cause the direct dissociation of said oxygen-containing precursor to form neutral oxygen atoms in an excited electronic state wherein said quenching gas physically interacts with said oxygen atoms in said excited electronic state to form oxygen atoms in the unexcited electronic state and said oxygen atoms in said unexcited electronic state react with said vapor phase reactant to form said oxide comprising predominantly silicon dioxide, which deposits as said layer on said surface of said substrate at an enhanced rate of deposition.
Claim 3
Dependent Claim
94 words
The process of claim 1 wherein: (a) the flow rate of said silane is 0.2 to 1.5 standard cubic centimeters per minute (sccm); (b) the flow rate of said nitrous oxide is 50 to 200 sccm; (c) the flow rate of said neopentane is about 2 to 10 sccm; and (d) the pressure at which said process is performed is within the range of about 2.5 to 5.5 torr (332 to 732 pascals); and (e) the rate of deposition of said oxide is within the range of about 34 to 63 angstroms per minute.
Claim 4
Dependent Claim
26 words
The process of claim 1 wherein the flow rate of said neopentane is within the range of about 2 to 15 standard cubic centimeters per minute.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-28 | 1991-12-28 | 1992-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-28 | 1995-12-28 | 1996-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-28 | 1999-12-28 | 2000-06-28 | $7700.00 | Window Closed / Lapsed |