Process for forming thin films by plasma CVD for use in the production of semiconductor devices
Assignee: Fujitsu Ltd
•
Filing: 1993-11-19
•
Granted: 1996-06-11
•
Expires: 2013-11-19
Abstract
Abstract A silicon oxide film is formed by a CVD process, with the use of a silane group gas and water as a main feed gas. Further, a film including silanol is formed by the plasma CVD process with a specific plasma energy, using the silane group gas and water as the main feed gas. The specific plasma energy is selected at 40 (Wx DEG C./cm2) or below. By annealing this film including silanol, or by performing the oxygen plasma process or the ammonia plasma process, the oxide film or the nitride film is formed.
Inventors
- 👤 Takashi Kato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 19:23
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/401; C23C16/402; C23C16/56; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/65; H10P14/6516; H10P14/6518; H10P14/6524; H10P14/6526; H10P14/6529; H10P14/6532; H10P14/6548; H10P14/66; H10P14/662; H10P14/6923; H10P14/6927; H10P95/00; H10P14/6336; H10P14/668; H10P14/6681; H10P14/6682; H10P14/69215; Y; Y10; Y10S; Y10S438/00; Y10S438/935
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
85 words
A process for producing of a semiconductor device, comprising: a first step of forming a film comprising an inorganic silanol by performing a plasma CVD at a plasma energy value of no greater than 40 (W·°C./cm 2 ) and using a silane group gas and water as a feed gas; and a second step of treating the film under conditions sufficient to anneal said film or to plasma irradiate said film under conditions sufficient to convert said film to a film comprising a silicon oxide.
Claim 2
Dependent Claim
85 words
A process for producing of a semiconductor device, comprising: a first step of forming a film comprising an inorganic silanol by performing a plasma CVD at a plasma energy value of no greater than 40 (W·°C./cm 2 ) and using a silane group gas and water as a feed gas; and a second step of treating the film under conditions sufficient to anneal said film or to plasma irradiate said film under conditions sufficient to convert said film to a film comprising a silicon oxide.
Claim 3
Dependent Claim
29 words
A process for producing of a semiconductor device according to claim 1, wherein the plasma discharge of the feed gas is caused by applying an exciting electric power intermittently.
Claim 4
Dependent Claim
41 words
A process as claimed in claim 1, wherein said CVD process is carried out under low power conditions sufficient to provide substantially all of the hydrogen in said film in the form of inorganic silanols of the formula: Si-(OH) x .
Claim 5
Dependent Claim
84 words
A process for producing of a semiconductor device comprising: a first step of forming a film comprising an inorganic silanol by performing a plasma CVD at an energy value of not more than 40 (W·°C./cm 2 ) using a silane group gas and H 2 O as a feed gas; and a second step of transforming the film comprising said inorganic silanol, to a nitride film by treating said film with an ammonia plasma under conditions sufficient to form a nitride in said film.
Claim 6
Dependent Claim
84 words
A process for producing of a semiconductor device comprising: a first step of forming a film comprising an inorganic silanol by performing a plasma CVD at an energy value of not more than 40 (W·°C./cm 2 ) using a silane group gas and H 2 O as a feed gas; and a second step of transforming the film comprising said inorganic silanol, to a nitride film by treating said film with an ammonia plasma under conditions sufficient to form a nitride in said film.
Claim 7
Dependent Claim
26 words
A process for producing of a semiconductor device according to claim 4, wherein the feed gas is plasma discharged by impressing an exciting electric power intermittently.
Claim 8
Dependent Claim
41 words
A process as claimed in claim 4, wherein said CVD process is carried out under low power conditions sufficient to provide substantially all of the hydrogen in said film in the form of inorganic silanols of the formula: Si-(OH) x .
Claim 9
Dependent Claim
133 words
A process for producing of a semiconductor device comprising: a first step of forming a SiO 2 film without a silanol by a plasma CVD process, using a silane group gas and water as a feed gas, a second step of forming a second film, comprising an inorganic silanol, by a further plasma CVD process with a plasma energy value of no greater than 40 (W·°C./cm 2 ), using a silane group gas and H 2 O as a feed gas, on said SiO 2 film; and a third step of transforming the second film comprising an inorganic silanol to a film comprising a nitride by stopping the supply of said silane group gas and water to said further plasma CVD process and feeding an ammonia plasma into contact with said second film.
Claim 10
Dependent Claim
133 words
A process for producing of a semiconductor device comprising: a first step of forming a SiO 2 film without a silanol by a plasma CVD process, using a silane group gas and water as a feed gas, a second step of forming a second film, comprising an inorganic silanol, by a further plasma CVD process with a plasma energy value of no greater than 40 (W·°C./cm 2 ), using a silane group gas and H 2 O as a feed gas, on said SiO 2 film; and a third step of transforming the second film comprising an inorganic silanol to a film comprising a nitride by stopping the supply of said silane group gas and water to said further plasma CVD process and feeding an ammonia plasma into contact with said second film.
Claim 11
Dependent Claim
42 words
A process as claimed in claim 7, wherein said second CVD process is carried out under low power conditions sufficient to provide substantially all of the hydrogen in said film in the form of inorganic silanols of the formula: Si-(OH) x .
References Cited (Backward Citations)
US4002512A
Cited
US4196232A
Cited
US4732761A
Cited
US4999314A
Cited
US4937094A
Cited
US4877641A
Cited
US5314724A
Cited
JPH05121568A
Cited
US5424253A
Cited
US5429995A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-06-11 | 1999-12-11 | 2000-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-06-11 | 2003-12-11 | 2004-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-06-11 | 2007-12-11 | 2008-06-11 | $7700.00 | Window Closed / Lapsed |