Integrated circuit structure having floating electrode with discontinuous phase of metal silicide formed on a surface thereof and process for making same
Assignee: LSI Corp
•
Filing: 1994-05-06
•
Granted: 1996-03-12
•
Expires: 2014-05-06
Abstract
Abstract A process is disclosed for forming an integrated circuit device, such as an EPROM device, with a floating gate electrode with a discontinuous phase of metal silicide formed on a surface thereof is described. The process for forming such a discontinuous phase of metal silicide on the surface of a polysilicon floating gate electrode for the device comprises the steps of depositing a first polysilicon layer over a substrate, and preferably over a thin oxide layer on the substrate capable of functioning as a gate oxide; then forming a very thin layer of a silicide-forming metal over the polysilicon layer; and heating the structure sufficiently to cause all of the silicide-forming metal to react with the underlying polysilicon layer to form metal silicide and to coalesce the metal silicide into a discontinuous phase on the surface of the polysilicon layer. When an EPROM device is to be constructed, the process includes the further steps of forming an first insulation layer over the structure; forming a second polysilicon layer over the first insulation layer; and then forming a second insulation layer over the second polysilicon layer. The structure is then patterned to form a dual gate electrode structure with a floating gate and a control gate. After doping of the underlying substrate to form the source and drain regions, a further oxide layer may be formed over the entire structure and contact openings may be cut to the source and drain regions and control gate electrode, thus completing formation of an EPROM device with a floating gate having a discontinuous phase of metal silicide on a surface thereof facing the control gate.
Inventors
- 👤 Ashok K. Kapoor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 08:09
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0411; H10B; H10B41/00; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0112
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
93 words
A process for forming an integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over a substrate; b) forming over said polysilicon layer a layer of a metal silicide sufficiently thin to result in coalescence of said metal silicide into a discontinuous phase upon subsequent heating thereof; and c) heating said structure sufficiently to cause said metal silicide to coalesce into a discontinuous phase on the surface of said underlying polysilicon layer.
Claim 2
Dependent Claim
93 words
A process for forming an integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over a substrate; b) forming over said polysilicon layer a layer of a metal silicide sufficiently thin to result in coalescence of said metal silicide into a discontinuous phase upon subsequent heating thereof; and c) heating said structure sufficiently to cause said metal silicide to coalesce into a discontinuous phase on the surface of said underlying polysilicon layer.
Claim 3
Dependent Claim
59 words
The process of claim 1 wherein said step of forming said layer of metal silicide over said layer of polysilicon further comprises the steps of forming a thin layer of silicide-forming metal over said polysilicon layer and then heating said structure to cause said silicide-forming metal to react with said underlying polysilicon layer to form said metal silicide layer.
Claim 4
Dependent Claim
66 words
The process of claim 2 wherein said step of heating said structure to form said metal silicide and said step of heating said structure sufficiently to cause said metal silicide to coalesce to form said discontinuous phase of metal silicide are carried out in one continuous step by heating said structure to a temperature sufficient to cause said metal silicide to coalesce after it is formed.
Claim 5
Dependent Claim
33 words
The process of claim 1 wherein said step of forming said layer of metal silicide over said layer of polysilicon further comprises depositing a thin layer of metal silicide over said polysilicon layer.
Claim 6
Dependent Claim
112 words
A process for forming an integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over a substrate; b) then forming over said polysilicon layer a layer of a silicide-forming metal sufficiently thin to permit formation of a metal silicide layer which will coalesce into a discontinuous phase upon subsequent heating; and c) heating said structure sufficiently to cause all of said silicide-forming metal to react with said underlying polysilicon layer to form a metal silicide and to cause said metal silicide to coalesce into a discontinuous phase on said polysilicon layer.
Claim 7
Dependent Claim
112 words
A process for forming an integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over a substrate; b) then forming over said polysilicon layer a layer of a silicide-forming metal sufficiently thin to permit formation of a metal silicide layer which will coalesce into a discontinuous phase upon subsequent heating; and c) heating said structure sufficiently to cause all of said silicide-forming metal to react with said underlying polysilicon layer to form a metal silicide and to cause said metal silicide to coalesce into a discontinuous phase on said polysilicon layer.
Claim 8
Dependent Claim
92 words
The process of claim 5 wherein said step of forming over said polysilicon layer said layer of a silicide-forming metal sufficiently thin to permit formation of a metal silicide layer which will coalesce into a discontinuous phase upon subsequent heating further comprises forming a silicide-forming metal layer not exceeding about 10 -8 meters (100 Angstroms) in thickness, whereby all of said silicide-forming metal will subsequently react with said underlying polysilicon to form said metal silicide during said heating step, and said metal silicide will coalesce into a discontinuous phase upon further heating.
Claim 9
Dependent Claim
29 words
The process of claim 6 wherein said heating step further comprises forming from about 25×10 -10 meters (25 Angstroms) to about 250×10 -10 meters (250 Angstroms) of metal silicide.
Claim 10
Dependent Claim
38 words
The process of claim 5 wherein said step of forming said layer of silicide-forming metal further comprises forming a layer of a metal selected from the group consisting of titanium, tungsten, tantalum, niobium, hafnium, molybdenum, cobalt, and nickel.
Claim 11
Dependent Claim
66 words
The process of claim 8 which comprises the further steps of: a) forming an first insulation layer over the structure; b) forming a second polysilicon layer over said first insulation layer; c) then forming a second insulation layer over said second polysilicon layer; and d) then patterning said structure to form a dual gate electrode structure comprising a floating gate electrode and a control gate electrode.
Claim 12
Dependent Claim
77 words
The process of claim 9 which comprises the further steps of: a) doping said substrate to form source and drain regions; b) forming a further oxide layer over the entire structure; and c) forming contact openings through said further oxide layer to said source and drain regions and said control gate electrode; to thereby form an EPROM device with said floating gate having a discontinuous phase of metal silicide on a surface thereof facing said control gate.
Claim 13
Dependent Claim
238 words
A process for forming an EPROM integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide form on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over an oxide layer on a substrate capable of functioning as a gate oxide; b) then forming a very thin layer of a silicide-forming metal over said first polysilicon layer; c) heating said structure sufficiently to cause all of said silicide-forming metal to react with said underlying first polysilicon layer to form metal silicide and to cause said metal silicide to coalesce into a discontinuous phase on the underlying surface of said first polysilicon layer; d) forming an first insulation layer over said structure; e) forming a second polysilicon layer over said first insulation layer; f) then forming a second insulation layer over said second polysilicon layer; g) then patterning said structure to form a dual gate electrode structure with a floating gate electrode and a control gate electrode; h) doping said substrate to form source and drain regions; i) forming a third insulation layer over said entire structure; and j) then forming contact openings through said third insulation layer to said source and drain regions and said control gate electrode; to thereby form an EPROM device with a floating gate electrode having a discontinuous phase of metal silicide on the surface of said floating gate facing said control gate electrode.
Claim 14
Dependent Claim
238 words
A process for forming an EPROM integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide form on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over an oxide layer on a substrate capable of functioning as a gate oxide; b) then forming a very thin layer of a silicide-forming metal over said first polysilicon layer; c) heating said structure sufficiently to cause all of said silicide-forming metal to react with said underlying first polysilicon layer to form metal silicide and to cause said metal silicide to coalesce into a discontinuous phase on the underlying surface of said first polysilicon layer; d) forming an first insulation layer over said structure; e) forming a second polysilicon layer over said first insulation layer; f) then forming a second insulation layer over said second polysilicon layer; g) then patterning said structure to form a dual gate electrode structure with a floating gate electrode and a control gate electrode; h) doping said substrate to form source and drain regions; i) forming a third insulation layer over said entire structure; and j) then forming contact openings through said third insulation layer to said source and drain regions and said control gate electrode; to thereby form an EPROM device with a floating gate electrode having a discontinuous phase of metal silicide on the surface of said floating gate facing said control gate electrode.
Claim 15
Dependent Claim
57 words
The process of claim 11 wherein said step of forming said very thin layer of silicide-forming metal over said polysilicon layer further comprises forming a metal layer not exceeding about 10 -8 meters (100 Angstroms) in thickness, whereby all of said silicide-forming metal will react with said underlying polysilicon during said step of forming said metal silicide.
Claim 16
Dependent Claim
45 words
The process of claim 12 wherein said step of forming said very thin layer of silicide-forming metal over said polysilicon layer further comprises forming a silicide-forming metal layer ranging in thickness from about 10 -9 meters (10 Angstroms) to about 5×10 -9 meters (50 Angstroms).
Claim 17
Dependent Claim
45 words
The process of claim 12 wherein said step of forming said very thin layer of silicide-forming metal over said polysilicon layer further comprises forming a silicide-forming metal layer ranging in thickness from about 10 -9 meters (10 Angstroms) to about 3×10 -9 meters (30 Angstroms).
Claim 18
Dependent Claim
40 words
The process of claim 12 wherein said step of forming said very thin layer of silicide-forming metal further comprises forming a layer of a metal selected from the group consisting of titanium, tungsten, tantalum, niobium, hafnium, molybdenum, cobalt, and nickel.
Claim 19
Dependent Claim
49 words
The process of claim 12 wherein said step of heating said structure to form said metal silicide and to coalesce said metal silicide into a discontinuous phase on the surface of said polysilicon layer is performed prior to said step of forming said first insulation layer over said structure.
Claim 20
Dependent Claim
43 words
The process of claim 12 wherein said structure is heated to a temperature of at least 50° C. above the minimum temperature required to form said metal silicide to thereby coalesce said metal silicide into a discontinuous phase over said first polysilicon layer.
Claim 21
Dependent Claim
41 words
The process of claim 17 wherein said structure is heated to a temperature of from about 500° C. to about 1000° C. to form said metal silicide and coalesce said metal silicide into a discontinuous phase over said first polysilicon layer.
Claim 22
Dependent Claim
167 words
A process for forming an integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over a substrate; b) then forming over said polysilicon layer a layer of a silicide-forming metal sufficiently thin to permit formation of a metal silicide layer which will coalesce into a discontinuous phase upon subsequent heating; c) heating said structure sufficiently to cause all of said silicide-forming metal to react with said underlying polysilicon layer to form a metal silicide and to cause said metal silicide to coalesce into a discontinuous phase on said polysilicon layer; d) then forming an first insulation layer over said structure; e) forming a second polysilicon layer over said first insulation layer; f) then forming a second insulation layer over said second polysilicon layer; and g) then patterning said structure to form a dual gate electrode structure comprising a floating gate electrode and a control gate electrode.
Claim 23
Dependent Claim
167 words
A process for forming an integrated circuit structure with a floating gate electrode having a discontinuous phase of metal silicide on a surface thereof which includes the steps of: a) depositing a first polysilicon layer over a substrate; b) then forming over said polysilicon layer a layer of a silicide-forming metal sufficiently thin to permit formation of a metal silicide layer which will coalesce into a discontinuous phase upon subsequent heating; c) heating said structure sufficiently to cause all of said silicide-forming metal to react with said underlying polysilicon layer to form a metal silicide and to cause said metal silicide to coalesce into a discontinuous phase on said polysilicon layer; d) then forming an first insulation layer over said structure; e) forming a second polysilicon layer over said first insulation layer; f) then forming a second insulation layer over said second polysilicon layer; and g) then patterning said structure to form a dual gate electrode structure comprising a floating gate electrode and a control gate electrode.
Claim 24
Dependent Claim
38 words
The process of claim 19 wherein said step of forming said layer of silicide-forming metal further comprises forming a layer of a metal selected from the group consisting of titanium, tungsten, tantalum, niobium, hafnium, molybdenum, cobalt, and nickel.
References Cited (Backward Citations)
US4735919A
Cited
US5001527A
Cited
US5017505A
Cited
US5087583A
Cited
US4957777A
Cited
US5081066A
Cited
US5057447A
Cited
US5182232A
Cited
US5223081A
Cited
US5110752A
Cited
US5245206A
Cited
US5320880A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-12 | 1999-09-11 | 2000-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-12 | 2003-09-11 | 2004-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-12 | 2007-09-11 | 2008-03-12 | $7700.00 | Window Closed / Lapsed |