Abstract
Abstract A corrosion-resistant metal strip and method for making the same which is essentially lead free and is not highly reflective. The coating on the metal strip is a metallic coating comprised of tin and a very low weight percentage of lead. The coating alloy may also include antimony, bismuth, copper, zinc to improve the coating process and/or improve the properties of the tin coating. A metal layer may also applied to the surface of the metal strip prior to applying the metallic alloy coating.
Inventors
- 👤 II Jay F. Carey
- 👤 Mehrooz Zamanzadeh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:26
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/18; C; C23; C23C; C23C2/00; C23C2/003; C23C2/0034; C23C2/00342; C23C2/00344; C23C2/0035; C23C2/0036; C23C2/0038; C23C2/02; C23C2/022; C23C2/024; C23C2/026; C23C2/04; C23C2/08; C23C28/00; C23C28/02; C23C28/021; C23C28/023; C23C28/025; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/939; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12708; Y10T428/12715; Y10T428/12722; Y10T428/12771; Y10T428/12785; Y10T428/12792; Y10T428/12799; Y10T428/12806; Y10T428/12826; Y10T428/12847; Y10T428/12854; Y10T428/12861; Y10T428/12903; Y10T428/1291; Y10T428/12951; Y10T428/12972; Y10T428/12979
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
112 words
A thin metal strip of a metal selected from the group consisting of carbon steel, stainless steel, copper, nickel alloys, tin, titanium, coated in a continuous, hot-dip process having an ultra-thin intermediate metal layer of a metal selected from the group consisting of nickel, chromium, zinc, copper or tin applied to the surface of said strip and a coating of corrosive-resistant metallic coating coated onto said intermediate metal barrier layer, said coating comprising at least about 15 weight percent tin, at least about 10 weight percent zinc, less than 1.0 weight percent lead and an effective amount of metallic stabilizer selected from the group consisting of antimony, bismuth, copper and mixtures thereof.
Claim 2
Dependent Claim
112 words
A thin metal strip of a metal selected from the group consisting of carbon steel, stainless steel, copper, nickel alloys, tin, titanium, coated in a continuous, hot-dip process having an ultra-thin intermediate metal layer of a metal selected from the group consisting of nickel, chromium, zinc, copper or tin applied to the surface of said strip and a coating of corrosive-resistant metallic coating coated onto said intermediate metal barrier layer, said coating comprising at least about 15 weight percent tin, at least about 10 weight percent zinc, less than 1.0 weight percent lead and an effective amount of metallic stabilizer selected from the group consisting of antimony, bismuth, copper and mixtures thereof.
Claim 3
Dependent Claim
54 words
A coated metal strip as defined in claim 1, wherein said coating is a two phase alloy of tin and zinc with the zinc in a tin rich matrix comprising: ______________________________________
Tin 15-90
Zinc 10-85
Magnesium
0.0-5
Nickel 0.0-5
Copper 0.0-5
Titanium
0.0-1
Aluminum
0.0-5
Antimony
0.0-7.5
Bismuth 0.0-1.7
Iron 0.0-1.0
Lead 0.0-0.5.
______________________________________
Claim 4
Dependent Claim
39 words
A coated metal strip as defined in claim 2, wherein said coating includes at least one metal additive selected from the group consisting of nickel, magnesium, titanium, aluminum, manganese, silicon, cadmium, lead, copper, iron, antimony, bismuth and mixtures thereof.
Claim 5
Dependent Claim
23 words
A coated metal strip as defined in claim 3, wherein the lead content of said coating is not more than 0.01 weight percent.
Claim 6
Dependent Claim
28 words
A coated metal strip as defined in claim 4, wherein said ultra-thin intermediate metal layer on said strip is heated prior to said strip being hot dip coated.
Claim 7
Dependent Claim
16 words
A coated metal strip as defined in claim 5, wherein said ultrathin intermediate layer is tin.
Claim 8
Dependent Claim
20 words
A coated metal strip as defined in claim 2, wherein the thickness of said coating is at least 0.0001 inch.
Claim 9
Dependent Claim
30 words
A coated metal strip as defined in claim 2, wherein said ultra-thin metal intermediate layer is plated onto said metal strip and has a thickness of up to 3 microns.
Claim 10
Dependent Claim
16 words
A coated metal strip as defined in claim 2, wherein said ultra-thin intermediate layer is copper.
Claim 11
Dependent Claim
16 words
A coated metal strip as defined in claim 2, wherein said ultra-thin intermediate layer is chromium.
Claim 12
Dependent Claim
40 words
A coated metal strip as defined in claim 1, wherein said coating includes at least one metal additive selected from the group consisting of nickel, magnesium, titanium, aluminum, manganese, silicon, cadmium, lead, copper, iron, zinc, antimony, bismuth and mixtures thereof.
Claim 13
Dependent Claim
23 words
A coated metal strip as defined in claim 1, wherein the lead content of said coating is not more than 0.01 weight percent.
Claim 14
Dependent Claim
30 words
A coated metal strip as defined in claim 12, wherein said ultra-thin metal intermediate layer is plated onto said metal strip and has a thickness of up to 3 microns.
Claim 15
Dependent Claim
20 words
A coated metal strip as defined in claim 1, wherein the thickness of said coating is at least 0.0001 inch.
Claim 16
Dependent Claim
30 words
A coated metal strip as defined in claim 1, wherein said ultra-thin metal intermediate layer is plated onto said metal strip and has a thickness of up to 3 microns.
Claim 17
Dependent Claim
40 words
A coated metal strip as defined in claim 1, wherein metal strip is an alloy of iron with an alloying metal selected from the group consisting of chromium, nickel, carbon, molybdenum, silicon, manganese, titanium, boron, copper, aluminum and mixtures thereof.
Claim 18
Dependent Claim
34 words
A coated metal strip as defined in claim 1, including an intermetallic layer formed between the surface of said strip and said hot dip coating, said intermetallic layer having a thickness of 1-10 microns.
Claim 19
Dependent Claim
30 words
A coated metal strip as defined in claim 1, wherein said ultra-thin metal intermediate layer is plated onto said metal strip and has a thickness of up to 3 microns.
Claim 20
Dependent Claim
28 words
A coated metal strip as defined in claim 18, wherein said ultra-thin intermediate metal layer on said strip is heated prior to said strip being hot dip coated.
Claim 21
Dependent Claim
16 words
A coated metal strip as defined in claim 19, wherein said ultra-thin intermediate layer is tin.
Claim 22
Dependent Claim
16 words
A coated metal strip as defined in claim 1, wherein said ultra-thin intermediate layer is copper.
Claim 23
Dependent Claim
16 words
A coated metal strip as defined in claim 1, wherein said ultra-thin intermediate layer is chromium.
Claim 24
Dependent Claim
190 words
A coated metal strip having a thickness of 0.005-0.2 inch and supplied from a coil and plated with an intermediate metal layer of up to 3 microns thick, and coating said plated strip by continuously passing said plated strip in a longitudinal direction at a speed through a molten bath of metal alloy having a temperature of at least 449° F. such that the residence time of said plated strip in said molten bath is 0.166-10 minutes to deposit an impervious layer of said metal alloy on the surface of said plated strip and form an intermetallic layer between said strip surface and said coating, said coating having a generally uniform thickness of 0.0001-0.05 inch along the length of said strip and including at least about 15 weight percent tin, at least about 10 weight percent zinc and an effective amount of metallic stabilizer selected from the group consisting of antimony, bismuth, copper and mixtures thereof, said intermetallic layer having a thickness of 1-10 microns and comprising a heat created multi-phase interface alloy created from a mixture of said metal strip, said intermediate metal barrier layer and said metal alloy.
Claim 25
Dependent Claim
190 words
A coated metal strip having a thickness of 0.005-0.2 inch and supplied from a coil and plated with an intermediate metal layer of up to 3 microns thick, and coating said plated strip by continuously passing said plated strip in a longitudinal direction at a speed through a molten bath of metal alloy having a temperature of at least 449° F. such that the residence time of said plated strip in said molten bath is 0.166-10 minutes to deposit an impervious layer of said metal alloy on the surface of said plated strip and form an intermetallic layer between said strip surface and said coating, said coating having a generally uniform thickness of 0.0001-0.05 inch along the length of said strip and including at least about 15 weight percent tin, at least about 10 weight percent zinc and an effective amount of metallic stabilizer selected from the group consisting of antimony, bismuth, copper and mixtures thereof, said intermetallic layer having a thickness of 1-10 microns and comprising a heat created multi-phase interface alloy created from a mixture of said metal strip, said intermediate metal barrier layer and said metal alloy.
Claim 26
Dependent Claim
22 words
A coated metal strip as defined in claim 23, wherein said residence time in said molten alloy is less than one minute.
Claim 27
Dependent Claim
17 words
A coated metal strip as defined in claim 23, wherein said intermetallic layer includes iron and tin.
Claim 28
Dependent Claim
35 words
A coated strip as in claim 23, wherein said continuous hot dipped procedure has an operation line speed such that the residence time of said strip in said molten bath is less than one minute.
Claim 29
Dependent Claim
15 words
A coated metal strip as defined in claim 23, wherein said strip is stainless steel.
Claim 30
Dependent Claim
16 words
A coated metal strip as defined in claim 27, wherein said intermediate metal layer is chromium.
Claim 31
Dependent Claim
16 words
A coated metal strip as defined in claim 27, wherein said intermediate metal layer is copper.
Claim 32
Dependent Claim
16 words
A coated metal strip as defined in claim 27, wherein said intermediate metal layer is tin.
Claim 33
Dependent Claim
14 words
A coated metal strip as defined in claim 23, wherein said strip is copper.
Claim 34
Dependent Claim
16 words
A coated metal strip as defined in claim 31, wherein said intermediate metal layer is chromium.
Claim 35
Dependent Claim
16 words
A coated metal strip as defined in claim 31, wherein said intermediate metal layer is copper.
Claim 36
Dependent Claim
16 words
A coated metal strip as defined in claim 31, wherein said intermediate metal layer is tin.
Claim 37
Dependent Claim
16 words
A coated metal strip as defined in claim 23, wherein said intermediate metal layer is chromium.
Claim 38
Dependent Claim
16 words
A coated metal strip as defined in claim 23, wherein said intermediate metal layer is copper.
Claim 39
Dependent Claim
16 words
A coated metal strip as defined in claim 23, wherein said intermediate metal layer s tin.
Claim 40
Dependent Claim
272 words
A coated metal strip formed of a metal strip selected from the group consisting of carbon steel, stainless steel, copper, nickel alloys, tin, aluminum, bronze and titanium, said metal strip having a thickness of about 0.005-0.2 inch and supplied from a coil and plated with an intermediate metal layer of at least about 1 micron thick and of a metal selected from the group consisting of chromium, copper, nickel, tin or zinc, said metal strip and said ultra-thin intermediate layer heated prior to hot dip coating said metal strip, and coating said heated plated metal strip by continuously passing said heated plated strip in a longitudinal direction at a speed through a molten bath of metal alloy having a temperature of at least about 449° F. such that the residence time of said heated plated metal strip in said molten bath is about 0.166-10 minutes to deposit an impervious layer of said metal alloy on the surface of said heated plated strip and forming an intermetallic layer between said strip surface and said coating, said coating having a generally uniform thickness of at least about 0.0001 inch along the length of said strip, said intermetallic layer having a thickness of about 1-10 microns and comprising a heat created multi-phase interface alloy created from a mixture of said metal strip, said intermediate metal layer and said metal alloy, said coating comprising at least about 15 weight percent tin, at least about 10 weight percent zinc, up to about 1.0 weight percent lead, and at least an effective amount of metallic stabilizer selected from the group consisting of antimony, bismuth, copper or mixtures thereof.
Claim 41
Dependent Claim
272 words
A coated metal strip formed of a metal strip selected from the group consisting of carbon steel, stainless steel, copper, nickel alloys, tin, aluminum, bronze and titanium, said metal strip having a thickness of about 0.005-0.2 inch and supplied from a coil and plated with an intermediate metal layer of at least about 1 micron thick and of a metal selected from the group consisting of chromium, copper, nickel, tin or zinc, said metal strip and said ultra-thin intermediate layer heated prior to hot dip coating said metal strip, and coating said heated plated metal strip by continuously passing said heated plated strip in a longitudinal direction at a speed through a molten bath of metal alloy having a temperature of at least about 449° F. such that the residence time of said heated plated metal strip in said molten bath is about 0.166-10 minutes to deposit an impervious layer of said metal alloy on the surface of said heated plated strip and forming an intermetallic layer between said strip surface and said coating, said coating having a generally uniform thickness of at least about 0.0001 inch along the length of said strip, said intermetallic layer having a thickness of about 1-10 microns and comprising a heat created multi-phase interface alloy created from a mixture of said metal strip, said intermediate metal layer and said metal alloy, said coating comprising at least about 15 weight percent tin, at least about 10 weight percent zinc, up to about 1.0 weight percent lead, and at least an effective amount of metallic stabilizer selected from the group consisting of antimony, bismuth, copper or mixtures thereof.
References Cited (Backward Citations)
US84205A
Cited
US1989925A
Cited
FR746337A
Cited
US2258327A
Cited
GB528558A
Cited
US2210593A
Cited
GB546179A
Cited
US2374926A
Cited
GB581604A
Cited
US2533048A
Cited
GB626826A
Cited
US2703766A
Cited
GB709163A
Cited
US2806622A
Cited
US3012310A
Cited
GB796128A
Cited
US3058856A
Cited
US3105022A
Cited
GB1008316A
Cited
GB1074852A
Cited
US3231127A
Cited
GB1040916A
Cited
FR1457769A
Cited
GB1143107A
Cited
GB1194751A
Cited
GB1178816A
Cited
FR2052324A5
Cited
GB1277523A
Cited
US3630792A
Cited
US3728144A
Cited
GB1361942A
Cited
US3791801A
Cited
JPS4954230A
Cited
GB1439774A
Cited
US3962501A
Cited
US3966564A
Cited
US4015950A
Cited
US3860438A
Cited
GB1513002A
Cited
FR2281995A1
Cited
GB1517454A
Cited
US4049481A
Cited
US4202921A
Cited
US4152471A
Cited
US4216250A
Cited
GB1588808A
Cited
US4177326A
Cited
DE2713196A1
Cited
GB2005307A
Cited
US4184928A
Cited
US4190504A
Cited
GB2022158A
Cited
US4330574A
Cited
US4330574B1
Cited
US4357027A
Cited
GB2055402A
Cited
US4321289A
Cited
GB2087931A
Cited
GB2099857A
Cited
JPS5848694A
Cited
GB2117414A
Cited
JPS58221283A
Cited
JPS5941430A
Cited
JPS5996238A
Cited
US4814049A
Cited
FR2554831A1
Cited
JPS60208465A
Cited
US4883723A
Cited
US4778733A
Cited
EP0261078A1
Cited
US4862825A
Cited
US4969980A
Cited
US4999258A
Cited
US4758407A
Cited
US4806309A
Cited
JPH01259153A
Cited
US5023113A
Cited
US4879096A
Cited
US4934120A
Cited
US4987716A
Cited
US5114799A
Cited
EP0480122A2
Cited
US5203985A
Cited
US5202002A
Cited
US5175026A
Cited
GB2265389A
Cited
US5314758A
Cited
US5354624A
Cited
GB2276887A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-02-12 | 1999-08-14 | 2000-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-02-12 | 2003-08-14 | 2004-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-02-12 | 2007-08-14 | 2008-02-13 | $7700.00 | Window Closed / Lapsed |