Surface treatment process for steels and article
Assignee: Bpifrance Financement SA
•
Filing: 1975-08-01
•
Granted: 1977-04-05
•
Expires: 1995-08-01
Abstract
Abstract A process for treating a steel surface, comprising the steps of immersing the surface in a bath of molten tin at a temperature and for a period of time suitable to cause a layer of tin containing diffused iron to adhere to the surface and, after removal of the surface from the bath, removing a surface layer in which iron and tin accord substantially with the formula of Fe Sn 2 so as to expose a layer in which iron and tin accord substantially to the formula Fe Sn.
Inventors
- 👤 Jacques Galland
- 👤 Dominique Boutard nee Gabillet
- 👤 Jacques Chene
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 02:30
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/44; C23C; C23C2/00; C23C2/04; C23C2/08; C23F1/10; C23F1/14; C23F1/16; C23F1/30; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12708; Y10T428/12722
Claims Analysis
Total Claims: 36
Claim 1
Independent Claim
171 words
A method of providing a hard and corrosion resistant layer comprising iron and tin on a surface of a steel substrate which comprises: immersing a surface of a steel substrate in a bath of molten tin maintained at a temperature of from 400° to 700° C for a period of time sufficient to cause a tin-containing layer containing diffused iron to adhere to said surface, said tin-containing layer comprising a first, inner, portion adjacent the steel substrate containing iron and tin in amounts corresponding substantially to the formula FeSn, a second portion adjacent said first portion containing iron and steel in amounts corresponding substantially to the formula FeSn 2 , and a third, outer, portion of tin adjacent said second portion; removing said surface bearing said tin-containing layer from said bath; and removing said third portion and said second portion of said tin-containing layer to provide said surface of said steel substrate with a hard and corrosion resistant layer containing iron and tin in amounts corresponding substantially to the formula FeSn.
Claim 2
Independent Claim
171 words
A method of providing a hard and corrosion resistant layer comprising iron and tin on a surface of a steel substrate which comprises: immersing a surface of a steel substrate in a bath of molten tin maintained at a temperature of from 400° to 700° C for a period of time sufficient to cause a tin-containing layer containing diffused iron to adhere to said surface, said tin-containing layer comprising a first, inner, portion adjacent the steel substrate containing iron and tin in amounts corresponding substantially to the formula FeSn, a second portion adjacent said first portion containing iron and steel in amounts corresponding substantially to the formula FeSn 2 , and a third, outer, portion of tin adjacent said second portion; removing said surface bearing said tin-containing layer from said bath; and removing said third portion and said second portion of said tin-containing layer to provide said surface of said steel substrate with a hard and corrosion resistant layer containing iron and tin in amounts corresponding substantially to the formula FeSn.
Claim 3
Dependent Claim
25 words
A method according to claim 1 wherein said time is sufficient to provide a tin-containing layer having a thickness of about 100 to 200 microns.
Claim 4
Dependent Claim
19 words
A method according to claim 2 wherein the thickness of said first portion is about 50 to 100 microns.
Claim 5
Dependent Claim
16 words
A method according to claim 1 wherein said bath temperature is from 400° to 650° C.
Claim 6
Dependent Claim
33 words
A method according to claim 1 wherein said steel substrate contains a metal selected from the group consisting of nickel and chromium and wherein said hard and corrosion resistant layer contains said metal.
Claim 7
Dependent Claim
36 words
A method according to claim 5 wherein the amounts of nickel and chromium present in said hard and corrosion resistant layer are, respectively, about 0.5 to 3.5% by weight and about 3 to 7% by weight.
Claim 8
Dependent Claim
36 words
A method according to claim 1 wherein said bath of molten tin contains a metal selected from the group consisting of nickel, chromium and magnesium and wherein said hard and corrosion resistant layer contains said metal.
Claim 9
Dependent Claim
22 words
A method according to claim 7 wherein said bath of molten tin contains nickel in an amount of about 6% by weight.
Claim 10
Dependent Claim
24 words
A method according to claim 7 wherein said bath of molten tin contains magnesium in an amount of about 5 to 10% by weight.
Claim 11
Dependent Claim
14 words
A method according to claim 7 wherein said steel substrate is a carbon steel.
Claim 12
Dependent Claim
25 words
A method according to claim 1 wherein said steel substrate contains nickel and chromium and wherein said bath of molten tin contains nickel and chromium.
Claim 13
Dependent Claim
17 words
A method according to claim 1 wherein said period of time is about 48 to 100 hours.
Claim 14
Dependent Claim
21 words
A method according to claim 1 wherein said second and third portions of said tin-containing layer are removed by chemical descaling.
Claim 15
Dependent Claim
31 words
A method according to claim 13 wherein the surface is immersed in a descaling bath consisting essentially of a substantially 35% concentration nitric acid solution to which hexamethylenetetramine has been added.
Claim 16
Dependent Claim
18 words
A method according to claim 13 wherein the hexamethylenetetramine is added in an amount of about 1 g/liter.
Claim 17
Dependent Claim
29 words
A method according to claim 13 wherein tin is liberated during the descaling in the form of a precipitate of hydrated stannic oxide and wherein said tin is recovered.
Claim 18
Dependent Claim
34 words
A method according to claim 16 wherein the tin is recovered by direct reduction of salts in an acid medium using a reducing agent selected from the group consisting of Zn, Al and Mg.
Claim 19
Dependent Claim
27 words
A method according to claim 16 wherein the tin is recovered by cathodic reduction after a prior conversion, by hydrochloric acid, of stannic sulphate into stannic chloride.
Claim 20
Dependent Claim
16 words
A method according to claim 1 wherein the FeSn 2 layer is removed by chemical descaling.
Claim 21
Dependent Claim
21 words
A method according to claim 1 wherein said second and third portions of said tin-containing layer are removed by electrochemical descaling.
Claim 22
Dependent Claim
38 words
A method according to claim 20 wherein the descaling is carried out by immersing the surface in a substantially 1N sulphuric acid solution and applying a constant voltage (with respect to a sulphate electrode) of about -550 mV.
Claim 23
Dependent Claim
36 words
A method according to claim 21 wherein the voltage varies in an alternating manner over a range of the order of -900 to +300 mV, at a rate of a few hundreds of mV per minute.
Claim 24
Dependent Claim
32 words
A method according to claim 20 wherein the surface is immersed in a substantially 1N solution of sulphuric acid and a cyclically variable voltage (with respect to a sulphate electrode) is applied.
Claim 25
Dependent Claim
36 words
A method according to claim 20 wherein said steel substrate contains nickel and chromium and wherein electrochemical descaling is stopped when a very weak passivity current results from the appearance of the compound Fe(Cr Ni Sn).
Claim 26
Dependent Claim
36 words
A method according to claim 1 wherein after the immersion a slow cooling of the surface is carried out to prevent fissuration due to the difference in coefficients of expansion of steel and said tin-containing layer.
Claim 27
Dependent Claim
19 words
A method according to claim 1 wherein said second and third portions of said tin-containing layer are removed mechanically.
Claim 28
Dependent Claim
16 words
A method according to claim 26 wherein said second and third portions are removed by grinding.
Claim 29
Dependent Claim
44 words
A steel substrate having a surface bearing a hard and corrosion resistant layer having a thickness of about 50 to 100 microns, containing iron and tin in amounts corresponding substantially to the formula FeSn and being made according to the process of claim 1.
Claim 30
Dependent Claim
27 words
A steel substrate according to claim 28 wherein said hard and corrosion resistant layer contains a metal selected from the group consisting of Cr, Ni, and Mg.
Claim 31
Dependent Claim
18 words
A steel substrate according to claim 29 wherein said hard and corrosion resistant layer contains Cr and Ni.
Claim 32
Dependent Claim
47 words
A steel substrate according to claim 30 wherein said hard and corrosion resistant layer includes an inner region adjacent the surface of said steel substrate in which Cr and Ni are present in amounts, respectively, of 3 to 7% by weight and 0.5 to 3.5% by weight.
Claim 33
Dependent Claim
17 words
A steel substrate according to claim 31 wherein said region has a thickness of about 10-20 microns.
Claim 34
Dependent Claim
23 words
A steel substrate according to claim 28 wherein said hard and corrosion resistant layer has a hardness of from 400 to 750 Vickers.
Claim 35
Dependent Claim
35 words
A steel substrate having a surface bearing a hard and corrosion resistant layer having a thickness of about 50 to 100 microns, and containing iron and tin in amounts corresponding substantially to the formula FeSn.
Claim 36
Dependent Claim
35 words
A steel substrate having a surface bearing a hard and corrosion resistant layer having a thickness of about 50 to 100 microns, and containing iron and tin in amounts corresponding substantially to the formula FeSn.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |