Silicidation method for contactless EPROM related devices
Assignee: Intel Corp
•
Filing: 1993-05-24
•
Granted: 1995-11-28
•
Expires: 2013-05-24
Abstract
Abstract A process for fabricating contactless electrically programmable and electrically erasable memory cells of the flash contactless EPROM or EEPROM type. The array of memory cells in these devices have elongated, parallel source and drain regions disposed beneath field oxide regions. The word lines are elongated, parallel strips of polysilicon. A series of SiO 2 depositions using TEOS chemistry in a PECVD process, and etches using sputter etch and plasma processes, is performed. After deposition and etchback, the polysilicon word lines remain exposed while all previous exposed substrate regions between source and drain are covered with SiO 2 . A metal deposition and silicidation are performed forming a silicide on the exposed silicon word lines thereby lowering the resistance of the word lines. Since the substrate regions between source and drain is covered between SiO 2 prior to metal deposition and silicidation no silicide is formed in these regions. Therefore the word lines are silicidized in a self aligned process with no need for a photolithographic step after SiO 2 deposition.
Inventors
- 👤 Been-Jon Woo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:21
CPC Classifications
H; H10; H10B; H10B41/00; H10B41/30
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
152 words
A process for forming a silicide on an array of floating gate memory devices, said array having first regions of exposed silicon where silicide is to be formed and having second regions of exposed silicon where no silicide is to be formed, said process comprising the steps of: depositing an oxide on said array; etching said oxide from said first regions while leaving at least a portion of said oxide in said second regions, said steps of depositing said oxide and etching said oxide from said first regions while leaving at least a portion of said oxide in said second regions being performed without use of a masking layer; depositing metal on said array in said first regions and on said unetched portion of said oxide in said second regions; forming a metal silicide in said first regions; and removing said metal from all regions of said array except said first regions.
Claim 2
Dependent Claim
152 words
A process for forming a silicide on an array of floating gate memory devices, said array having first regions of exposed silicon where silicide is to be formed and having second regions of exposed silicon where no silicide is to be formed, said process comprising the steps of: depositing an oxide on said array; etching said oxide from said first regions while leaving at least a portion of said oxide in said second regions, said steps of depositing said oxide and etching said oxide from said first regions while leaving at least a portion of said oxide in said second regions being performed without use of a masking layer; depositing metal on said array in said first regions and on said unetched portion of said oxide in said second regions; forming a metal silicide in said first regions; and removing said metal from all regions of said array except said first regions.
Claim 3
Dependent Claim
45 words
The process as in claim 1 wherein said process of depositing metal on said array, forming a metal silicide in said first regions, and removing said metal from all regions of said array except said first regions is performed without use of a masking layer.
Claim 4
Dependent Claim
18 words
The process as in claim 1 wherein said metal comprises titanium and said metal silicide comprises titanium silicide.
Claim 5
Dependent Claim
73 words
The process as in claim 1 wherein said deposition and said etch of said oxide comprise the steps of: depositing a first oxide layer by PECVD using TEOS as a precursor; etching some of said first layer by sputter etch; depositing a second oxide layer by PECVD using TEOS as a precursor; and, etching said first and said second oxide layers from said first regions while leaving some oxide in said second regions.
Claim 6
Dependent Claim
53 words
The process as in claim 4 wherein the thickness of said first oxide layer is in the range of 1000 to 5000Å, said etching of said first layer by sputter etch removes 500 to 4000Å of said first oxide layer, and said second oxide layer is deposited to a thickness of 1-4 microns.
Claim 7
Dependent Claim
24 words
The process as in claim 1 wherein the thickness of oxide remaining in said second regions after said etch is at least 200 Å.
Claim 8
Dependent Claim
24 words
The process as in claim 4 wherein the thickness of oxide remaining in said second regions after said etch is at least 200 Å.
Claim 9
Dependent Claim
24 words
The process as in claim 5 wherein the thickness of oxide remaining in said second regions after said etch is at least 200 Å.
Claim 10
Dependent Claim
17 words
The process as in claim 1 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 11
Dependent Claim
17 words
The process as in claim 2 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 12
Dependent Claim
17 words
The process as in claim 3 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 13
Dependent Claim
17 words
The process as in claim 4 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 14
Dependent Claim
17 words
The process as in claim 5 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 15
Dependent Claim
17 words
The process as in claim 6 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 16
Dependent Claim
17 words
The process as in claim 7 wherein said first regions of exposed silicon comprise polysilicon word lines.
Claim 17
Dependent Claim
17 words
The process as in claim 8 wherein said fast regions of exposed silicon comprise polysilicon word lines.
Claim 18
Dependent Claim
52 words
The process as described in claim 1 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 19
Dependent Claim
52 words
The process as described in claim 3 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 20
Dependent Claim
52 words
The process as described in claim 4 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 21
Dependent Claim
52 words
The process as described in claim 5 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 22
Dependent Claim
52 words
The process as described in claim 6 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 23
Dependent Claim
52 words
The process as described in claim 7 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 24
Dependent Claim
52 words
The process as described in claim 8 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
Claim 25
Dependent Claim
52 words
The process as described in claim 9 wherein said array of floating gate memory devices comprises elongated spaced apart diffusion regions, and elongated, spaced apart conductive regions disposed above and substantially perpendicular to said diffusion regions, and wherein said second regions are disposed between said diffusion regions and between said conductive regions.
References Cited (Backward Citations)
DE3222805A1
Cited
US4635347A
Cited
US4746219A
Cited
US4784971A
Cited
US4886765A
Cited
US5051796A
Cited
US5160986A
Cited
US5081056A
Cited
US4997790A
Cited
US5089442A
Cited
US5069747A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-27 | 1999-05-29 | 1999-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-27 | 2003-05-29 | 2003-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-27 | 2007-05-29 | 2007-11-28 | $7700.00 | Window Closed / Lapsed |