Abstract
Abstract A local interconnect system for VLSI integrated circuits. After titanium is deposited for self-aligned silicidation of exposed moat and gate regions in a nitrogen atmosphere, a hardmask is deposited and patterned over the titanium. When a conductive titanium nitride layer is formed overall, it will already be patterned according to this hardmask.
Inventors
- 👤 Thomas C. Holloway
- 👤 Thomas E. Tang
- 👤 Che-Chia Wei
- 👤 Roger A. Haken
- 👤 David A. Bell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:17
CPC Classifications
H; H10; H10B; H10B10/00; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4437; H10W20/4441
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
163 words
An integrated circuit local interconnect product fabricated by a process comprising the steps of: (a) providing a partially fabricated integrated circuit structure including a plurality of moat regions separated from one another by oxide regions, said moat regions incorporating active devices therein; (b) depositing a thin layer of metal consisting predominantly of titanium overall; (c) depositing a relatively inert material over said metal layer in locations defining local interconnect pathways thereunder; (d) reacting said partially fabricated structure in an atmosphere containing a high portion of nitrogen so that the portions of said metal layer over moat regions are converted to a first layer predominantly of titanium silicide covered by a second layer predominantly of titanium nitride, and so that the portions of said metal layer over oxide regions are converted predominantly to titanium nitride; and (e) etching away portions of said metal layer not covered by said relatively inert material so that local interconnects of titanium nitride remain in said local interconnect pathways.
Claim 2
Dependent Claim
163 words
An integrated circuit local interconnect product fabricated by a process comprising the steps of: (a) providing a partially fabricated integrated circuit structure including a plurality of moat regions separated from one another by oxide regions, said moat regions incorporating active devices therein; (b) depositing a thin layer of metal consisting predominantly of titanium overall; (c) depositing a relatively inert material over said metal layer in locations defining local interconnect pathways thereunder; (d) reacting said partially fabricated structure in an atmosphere containing a high portion of nitrogen so that the portions of said metal layer over moat regions are converted to a first layer predominantly of titanium silicide covered by a second layer predominantly of titanium nitride, and so that the portions of said metal layer over oxide regions are converted predominantly to titanium nitride; and (e) etching away portions of said metal layer not covered by said relatively inert material so that local interconnects of titanium nitride remain in said local interconnect pathways.
Claim 3
Dependent Claim
21 words
The product of claim 1, wherein said step (c) of depositing a relatively inert material comprises plasma-assisted deposition of silicon oxides.
Claim 4
Dependent Claim
32 words
The product of claim 1, wherein said step (c) of depositing a relatively inert material comprises plasma-assisted deposition of silicon oxides to a thickness in the range between 1000 and 2500 Angstroms.
Claim 5
Dependent Claim
20 words
The product of claim 1, wherein said etching step (e) is performed entirely as an etch at approximately atmospheric pressure.
Claim 6
Dependent Claim
17 words
The product of claim 1, wherein said etching step (e) is performed entirely as a wet etch.
Claim 7
Dependent Claim
27 words
The product of claim 1, further comprising the additional step, subsequent to said reacting step (d), of (f) annealing said titanium silicide regions to lower their resistivity.
Claim 8
Dependent Claim
45 words
The product of claim 6, wherein said reacting step (d) is performed at a temperature in the range of 500 to 750 degrees C., and said subsequent annealing step (f) is performed at a higher temperature in the range of 700 to 875 degrees C.
Claim 9
Dependent Claim
17 words
The product of claim 6, wherein said reacting step (d) is performed as a transient heating step.
Claim 10
Dependent Claim
56 words
The product of claim 6, wherein said relatively inert material is removed after said heating step (d) and before said annealing step (f), and wherein said annealing step (f) is performed in an atmosphere comprising nitrogen so that unconverted titanium remaining in said local interconnects after said reacting step (d) are converted predominantly to titanium nitride.
Claim 11
Dependent Claim
19 words
The product of claim 1, wherein said titanium metal is applied to a thickness of less than 2000 Angstroms.
Claim 12
Dependent Claim
24 words
The product of claim 1, wherein said reacting step (d) is performed at a temperature in the range of 500 to 750 degrees Centigrade.
Claim 13
Dependent Claim
15 words
The product of claim 1, wherein said depositing step (c) follows said reacting step (d).
Claim 14
Dependent Claim
15 words
The product of claim 1, wherein said depositing step (c) precedes said reacting step (d).
Claim 15
Dependent Claim
59 words
The product of claim 1, wherein the process further comprises: (f) subsequent to said reacting step (d) and prior to said etching step (e), depositing a second metal layer consisting predominantly of titanium overall; and (g) subsequent to said depositing step (f) and prior to said etching step (e), reacting said partially fabricated structure in an atmosphere comprising nitrogen.
Claim 16
Dependent Claim
15 words
The product of claim 14, wherein said depositing step (c) follows said reacting step (g).
Claim 17
Dependent Claim
15 words
The product of claim 14, wherein said depositing step (c) precedes said reacting step (d).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-24 | 1991-11-23 | 1992-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-24 | 1995-11-23 | 1996-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-24 | 1999-11-23 | 2000-05-24 | $7700.00 | Window Closed / Lapsed |