Method for manufacturing whisker preforms and composites
Assignee: Battelle Energy Alliance LLC
•
Filing: 1993-07-29
•
Granted: 1995-11-07
•
Expires: 2013-07-29
Abstract
Abstract A process for manufacturing Si 3 N 4 /SiAlON whiskers by mixing silicon carbide powder with aluminum nitride powder, adding impurities such as calcium oxide or potassium chloride to control whisker characteristics, forming the mixture in a boron nitrogen mold of desired shaped and hot isostatically pressing the formed mixture in a nitrogen environment to produce whiskers comprised substantially of SiAlON at the nucleating end of the whisker and Si 3 N 4 at the other end of the whisker. In one embodiment, reinforced composites are formed by impregnating the Si 3 N 4 /SiAlON whisker preform with a matrix material such as resin binders, liquid metals, intermetallics or ceramic materials.
Inventors
- 👤 Paul A. Lessing
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 17:35
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1005; C22C1/1015; C22C1/1021; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C04B35/16; C04B35/18; C04B35/185; C04B35/19; C04B35/195; C04B35/447; C04B35/46; C04B35/462; C04B35/478; C04B35/48; C04B35/486; C04B35/488; C04B35/495; C04B35/515; C04B35/56; C04B35/563; C04B35/565; C04B35/58; C04B35/5805; C04B35/58064; C04B35/58071; C04B35/58085; C04B35/58092; C04B35/581; C04B35/584; C04B35/597; C04B35/622; C04B35/62227; C04B35/62272; C04B35/62286; C04B35/62295; C04B35/626; C04B35/62605; C04B35/62645; C04B35/62675; C04B35/6268; C04B35/64; C04B35/645; C04B35/6455; C04B35/71; C04B35/78; C04B35/80; C22C47/00; C22C47/08; C22C47/12; C22C49/00; C22C49/02; C22C49/12; C30; C30B; C30B25/00; C30B25/005; C30B29/00; C30B29/10; C30B29/38; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3201; C04B2235/3205; C04B2235/3208; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/383; C04B2235/3834; C04B2235/3852; C04B2235/3865; C04B2235/44; C04B2235/444; C04B2235/46; C04B2235/48; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/524; C04B2235/5276; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/5445; C04B2235/5463; C04B2235/60; C04B2235/602; C04B2235/6021; C04B2235/6022; C04B2235/6027
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
99 words
A method for making a silicon nitride/SiAlON preform article, the method comprising the steps of: (a) mixing particulate silicon carbide with particulate aluminum nitride and a catalyzing agent, said catalyzing agent being selected from the group consisting of calcium oxide and potassium chloride, to form a mixture; (b) forming the mixture into a desired shape; (b) reacting the formed mixture with a gas at a sufficient temperature and pressure to impose free nitrogen to convert the formed mixture into a whisker composition, the individual whiskers consisting substantially of silicon nitride at one end, and SiAlON at the other end.
Claim 2
Independent Claim
99 words
A method for making a silicon nitride/SiAlON preform article, the method comprising the steps of: (a) mixing particulate silicon carbide with particulate aluminum nitride and a catalyzing agent, said catalyzing agent being selected from the group consisting of calcium oxide and potassium chloride, to form a mixture; (b) forming the mixture into a desired shape; (b) reacting the formed mixture with a gas at a sufficient temperature and pressure to impose free nitrogen to convert the formed mixture into a whisker composition, the individual whiskers consisting substantially of silicon nitride at one end, and SiAlON at the other end.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein the ratio of silicon nitride powder to aluminum nitride powder is in the range of from 95:5 to 50:50.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein the amount of catalyzing agent is in the range of from 0.1 to 5 wt % of the mixture.
Claim 5
Dependent Claim
10 words
The method of claim 1 wherein the gas is nitrogen.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein the temperature of the gas is in the range of from 1800° C. to 2000° C.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein the pressurized atmosphere is in the range of from 20,000 psia to 30,000 psia.
Claim 8
Dependent Claim
17 words
The method of claim 1 further comprising the step of adding an organic binder to the mixture.
Claim 9
Independent Claim
110 words
A method for making a silicon nitride/SiAlON blend whisker reinforced composite, said method comprising the steps of: (a) mixing particulate silicon carbide with particulate aluminum nitride and a catalyzing agent, said catalyzing agent being selected from the group consisting of calcium oxide and potassium chloride, to form a mixture; (b) compacting the mixture to a desired shape; (c) reacting said compacted mixture with a gas at a sufficient temperature and pressure to impose free nitrogen to convert the compacted mixture to a silicon nitride and SiAlON whisker composition; (d) impregnating said whisker blend composition with a matrix material; and (e) solidifying said matrix material to form said whisker reinforced composite.
Claim 10
Independent Claim
110 words
A method for making a silicon nitride/SiAlON blend whisker reinforced composite, said method comprising the steps of: (a) mixing particulate silicon carbide with particulate aluminum nitride and a catalyzing agent, said catalyzing agent being selected from the group consisting of calcium oxide and potassium chloride, to form a mixture; (b) compacting the mixture to a desired shape; (c) reacting said compacted mixture with a gas at a sufficient temperature and pressure to impose free nitrogen to convert the compacted mixture to a silicon nitride and SiAlON whisker composition; (d) impregnating said whisker blend composition with a matrix material; and (e) solidifying said matrix material to form said whisker reinforced composite.
Claim 11
Dependent Claim
10 words
The method of claim 8 wherein the gas is nitrogen.
Claim 12
Dependent Claim
22 words
The method of claim 8 wherein the temperature of the gas is in the range of from 1800° C. to 2000° C.
Claim 13
Dependent Claim
20 words
The method of claim 8 wherein the pressurized atmosphere is in the range of from 20,000 psia to 30,000 psia.
Claim 14
Dependent Claim
42 words
The method of claim 8 wherein said matrix material is selected from the group consisting of a resin binder, a liquid metal, a colloidal suspension, an ionic solution and at least one gaseous material capable of being solidified to form a matrix.
Claim 15
Dependent Claim
33 words
The method of claim 8 further comprising the step of treating said liquid metal with a wetting agent prior to the impregnating step to facilitate the wetting of said whiskers by said metal.
Claim 16
Independent Claim
91 words
A method of forming individual silicon/SiAlON whiskers, said method comprising the steps of: (a) mixing particulate silicon carbide with particulate aluminum nitride and a catalyzing agent, said catalyzing agent being selected from the group consisting of calcium oxide and potassium chloride, to form a mixture; (b) compacting the mixture; (c) reacting the compacted mixture with a gas at a sufficient temperature and pressure to impose free nitrogen to convert said mixture into a silicon nitride/SiAlON whiskers composition; (d) crushing the silicon nitride/SiAlON whiskers composition to form a silicon nitride/SiAlON whisker powder.
Claim 17
Independent Claim
91 words
A method of forming individual silicon/SiAlON whiskers, said method comprising the steps of: (a) mixing particulate silicon carbide with particulate aluminum nitride and a catalyzing agent, said catalyzing agent being selected from the group consisting of calcium oxide and potassium chloride, to form a mixture; (b) compacting the mixture; (c) reacting the compacted mixture with a gas at a sufficient temperature and pressure to impose free nitrogen to convert said mixture into a silicon nitride/SiAlON whiskers composition; (d) crushing the silicon nitride/SiAlON whiskers composition to form a silicon nitride/SiAlON whisker powder.
Claim 18
Dependent Claim
10 words
The method of claim 14 wherein the gas is nitrogen.
Claim 19
Dependent Claim
22 words
The method of claim 14 wherein the temperature of the gas is in the range of from 1800° C. to 2000° C.
Claim 20
Dependent Claim
20 words
The method of claim 14 wherein the pressurized atmosphere is in the range of from 20,000 psia to 30,000 psia.
Claim 21
Dependent Claim
24 words
The method of claim 14 further comprising the step of mixing the silicon nitride/SiAlON whisker powder with a matrix material to form a composite.
Claim 22
Dependent Claim
24 words
The method of claim 8 wherein the amount of catalyzing agent is in the range of 0.1 to 5 wt % of the mixture.
Claim 23
Dependent Claim
25 words
The method of claim 14 wherein the amount of catalyzing agent is in the range of from 0.1 to 5 wt % of the mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-06 | 1999-05-08 | 1999-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-06 | 2003-05-08 | 2003-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-06 | 2007-05-08 | 2007-11-07 | $7700.00 | Window Closed / Lapsed |