Novel sialon composition
Assignee: Benchmark Structural Ceramics Corp
•
Filing: 1990-06-07
•
Granted: 1991-07-09
•
Expires: 2010-06-07
Abstract
Abstract A novel composite mateial consisting of at least 70 weight percent of single-phase beta sialon and at least 20 weight percent of alpha-alumina is disclosed. The beta-sialon is of the formula Si 6-z Al z - z N 8-z , wherein z is from 2.5 to 3.5. The composite material contains no silicon nitride. Sintered products made from such composite material contain no glassy phase, contain no silicon nitride, and have superior thermal and mechanical properties.
Inventors
- 👤 George T. Hida
- 👤 Rodica S. Hida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:20
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/622; C04B35/64; C04B35/645; C04B35/71; C04B35/78; C04B35/80
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
95 words
A composite material consisting of (a) at least 70 weight percent of single-phase beta-sialon of the formula Si 6-z Al z O z N 8-z , wherein z is from about 2.5 to 3.5, and wherein said beta-sialon is comprised of from about 24.7 to 34.7 weight percent of silicon, from about 23.9 to 33.4 weight percent aluminum, from about 14.1 to 19.8 weight percent of oxygen, and from about 22.2 to 27.3 weight percent of nitrogen; (b) at least 20 weight percent of alpha-alumina; (c) 0 to 10 weight percent single phase silicon oxynitride;
Claim 2
Dependent Claim
95 words
A composite material consisting of (a) at least 70 weight percent of single-phase beta-sialon of the formula Si 6-z Al z O z N 8-z , wherein z is from about 2.5 to 3.5, and wherein said beta-sialon is comprised of from about 24.7 to 34.7 weight percent of silicon, from about 23.9 to 33.4 weight percent aluminum, from about 14.1 to 19.8 weight percent of oxygen, and from about 22.2 to 27.3 weight percent of nitrogen; (b) at least 20 weight percent of alpha-alumina; (c) 0 to 10 weight percent single phase silicon oxynitride;
Claim 3
Dependent Claim
55 words
The composite material as recited in claim 1, wherein at least about 20 volume percent of said single-phase beta-sialon is in the form of whiskers which have a length of from about 10 to 100 microns, a diameter of from about 3 to 7 microns, and as aspect ratio of from about 3 to 20.
Claim 4
Dependent Claim
119 words
A sintered ceramic material with a density of from about 2.94 to 3.20 grams per cubic centimeter, consisting of (a) at least 70 weight percent of single-phase beta-sialon of the formula Si 6-z Al z O z N 8-z , wherein z is from about 2.5 to 3.5, and wherein said beta-sialon is comprised of from about 24.7 to 34.7 weight percent of silicon, from about 23.9 to 33.4 weight percent of aluminum, from about 14.1 to 19.8 weight percent of oxygen, and from about 22.2 to 27.3 weight percent of nitrogen; (b) at least 20 weight percent of alpha alumina; (c) 0 to 20 weight percent single-phase silicon oxynitride; (d) said composite material: 1. contains no silicon nitride;
Claim 5
Dependent Claim
119 words
A sintered ceramic material with a density of from about 2.94 to 3.20 grams per cubic centimeter, consisting of (a) at least 70 weight percent of single-phase beta-sialon of the formula Si 6-z Al z O z N 8-z , wherein z is from about 2.5 to 3.5, and wherein said beta-sialon is comprised of from about 24.7 to 34.7 weight percent of silicon, from about 23.9 to 33.4 weight percent of aluminum, from about 14.1 to 19.8 weight percent of oxygen, and from about 22.2 to 27.3 weight percent of nitrogen; (b) at least 20 weight percent of alpha alumina; (c) 0 to 20 weight percent single-phase silicon oxynitride; (d) said composite material: 1. contains no silicon nitride;
Claim 6
Dependent Claim
67 words
contains no glassy phase; 3. has a density of from 2.94 to 3.20 grams per cubic centimeter; 4. has an elastic modulus of from about 300 to 650 GigaPascals; 5. has a flexural strength of from about 300 to 900 MegaPascals; 6. has a wear resistance of from about 28 to 20 cubic millimeters per 100 revolutions; and 7. has a porosity of less than 2 percent.
Claim 7
Dependent Claim
67 words
contains no glassy phase; 3. has a density of from 2.94 to 3.20 grams per cubic centimeter; 4. has an elastic modulus of from about 300 to 650 GigaPascals; 5. has a flexural strength of from about 300 to 900 MegaPascals; 6. has a wear resistance of from about 28 to 20 cubic millimeters per 100 revolutions; and 7. has a porosity of less than 2 percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-08 | 1995-01-07 | 1995-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-08 | 1999-01-07 | 1999-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-08 | 2003-01-07 | 2003-07-09 | $7700.00 | Window Closed / Lapsed |