Method of fabricating defect-free silicon on an insulating substrate
Assignee: International Business Machines Corp
•
Filing: 1994-04-11
•
Granted: 1995-10-31
•
Expires: 2014-04-11
Abstract
Abstract A method for fabricating silicon on insulator structures having a dislocation free silicon layer. The method utilizes low temperature UHVCVD to deposit a very heavily doped etch stop layer having a very steep doping profile onto a substrate and a lightly doped active layer onto the etch stop layer. An insulator is formed on the active layer and a carrier wafer is formed on the insulator layer. The original substrate is removed in a first etch and the etch stop layer is removed in a second etch resulting in a thin, uniform active layer. In one embodiment, a small percentage of germanium is added to the etch stop layer to produce a defect free epitaxial active layer.
Inventors
- 👤 Robert H. Dennard
- 👤 Bernard S. Meyerson
- 👤 Robert Rosenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 03:11
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10W; H10W10/00; H10W10/10; H10W10/181; Y; Y10; Y10S; Y10S148/00; Y10S148/012; Y10S148/135; Y10S438/00; Y10S438/97; Y10S438/977
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
106 words
Method of forming a silicon on insulator structure comprising the steps of: forming an etch stop layer of silicon very heavily doped with a p or n dopant on a silicon substrate, said etch stop layer containing a percentage of germanium sufficient to compensate for stress produced by the very heavy doping concentration; forming an active layer of lightly doped silicon on said etch stop layer; forming an insulator layer on said active layer; forming a carrier substrate on said insulator layer; removing said silicon substrate; and removing said etch stop layer thereby forming a substantially dislocation free, uniform silicon active layer on said insulator layer.
Claim 2
Dependent Claim
106 words
Method of forming a silicon on insulator structure comprising the steps of: forming an etch stop layer of silicon very heavily doped with a p or n dopant on a silicon substrate, said etch stop layer containing a percentage of germanium sufficient to compensate for stress produced by the very heavy doping concentration; forming an active layer of lightly doped silicon on said etch stop layer; forming an insulator layer on said active layer; forming a carrier substrate on said insulator layer; removing said silicon substrate; and removing said etch stop layer thereby forming a substantially dislocation free, uniform silicon active layer on said insulator layer.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein said etch stop layer is formed by epitaxially growing SiGe by UHVCVD.
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein said active layer is a compound semiconductor of SiGe.
Claim 5
Dependent Claim
17 words
The method of claim 3 wherein said active layer is formed by epitaxially growing SiGe by UHVCVD.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein said active layer is formed by epitaxially growing silicon by UHVCVD.
Claim 7
Dependent Claim
19 words
The method of claim 1 wherein said insulator layer is one of a silicon oxide and a silicon nitride.
Claim 8
Dependent Claim
18 words
The method of claim 1 where said insulator layer is formed by depositing an insulator material by PECVD.
Claim 9
Dependent Claim
14 words
The method of claim 1 wherein said insulator layer is formed by thermal oxidation.
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein said carrier substrate is comprised of polysilicon and said forming step includes depositing said polysilicon by PECVD.
Claim 11
Dependent Claim
26 words
The method of claim 1 wherein said step of forming a carrier substrate on said insulator layer includes bonding a carrier wafer to said insulator layer.
Claim 12
Dependent Claim
57 words
The method of claim 10 wherein said bonding step includes forming a layer of polysilicon on said insulator layer, forming a layer of germanium on said polysilicon layer, forming a layer of germanium on a silicon wafer, contacting the germanium layers and exposing said layers to temperatures sufficient to bond the carrier substrate to said insulator layer.
Claim 13
Dependent Claim
14 words
The method of claim 10 wherein said carrier wafer is a glass ceramic material.
Claim 14
Dependent Claim
45 words
The method of claim 12 wherein said bonding step includes forming a layer of SiO 2 on said carrier wafer and said insulator layer, contacting the SiO 2 layers and exposing said layers to temperatures sufficient to bond the carrier substrate to said insulator layer.
Claim 15
Dependent Claim
43 words
The method of claim 12 wherein said bonding step includes forming a layer of sol-gel on said carrier substrate and said insulator layer, contacting the sol-gel layers and exposing said layers to temperatures sufficient to bond the carrier substrate to said insulator layer.
Claim 16
Dependent Claim
17 words
The method of claim 1 wherein said etch stop layer is formed with a steep doping profile.
Claim 17
Dependent Claim
17 words
The method of claim 15 wherein said doping profile is approximately as that shown in FIG. 10.
Claim 18
Dependent Claim
18 words
The method of claim 15 wherein said doping profile is about 1 nm per decade of doping concentration.
Claim 19
Dependent Claim
25 words
The method of claim 15 wherein said etch stop layer is formed with a doping concentration level of about 10 21 cm -3 or greater.
Claim 20
Dependent Claim
16 words
The method of claim 1 wherein said etch stop layer is formed by low temperature CVD.
Claim 21
Dependent Claim
15 words
The method of claim 19 wherein said CVD is performed at 550° C. or less.
Claim 22
Dependent Claim
18 words
The method of claim 1 wherein said etch stop layer is formed to a thickness of 2,000 angstroms.
Claim 23
Dependent Claim
23 words
The method of claim 1 wherein said active layer is formed to a thickness in the range of about 500 to 1,000 angstroms.
Claim 24
Dependent Claim
16 words
The method of claim 1 wherein the percentage of germanium is in the range of 1-8%.
Claim 25
Dependent Claim
13 words
The method of claim 1 wherein the percentage of germanium is about 2%.
Claim 26
Dependent Claim
20 words
The method of claim 1 wherein said etch stop layer and said active layer are formed by low temperature CVD.
Claim 27
Dependent Claim
29 words
The method of claim 1 wherein the p dopant in said etch stop layer is boron, and wherein the concentration of germanium is higher than the concentration of boron.
Claim 28
Dependent Claim
17 words
The method of claim 26 wherein the concentration of boron is about 10 21 cm -3 .
Claim 29
Dependent Claim
18 words
The method of claim 26 wherein the amount of germanium in the etch stop layer is about 2%.
Claim 30
Dependent Claim
26 words
The method of claim 1 wherein the p dopant in said etch stop layer is boron in a concentration of about 10 21 cm -3 .
Claim 31
Dependent Claim
43 words
The method of claim 26 wherein said step of forming a carrier substrate on said insulator includes the steps of forming an insulator layer on a silicon carrier wafer and bonding together the insulating layers on said carrier wafer and said active layer.
Claim 32
Dependent Claim
59 words
The method of claim 30 wherein said steps of removing the silicon substrate and removing said etch stop layer are effected by chemical etching in one or more steps in which the etching solution utilized in at least one etching step is selected from the group consisting of KOH and a mixture of HF, nitric acid and acetic acid.
Claim 33
Dependent Claim
12 words
The method of claim 30 wherein both insulator layers are oxide layers.
References Cited (Backward Citations)
US3293087A
Cited
US3455748A
Cited
US4000020A
Cited
US4351856A
Cited
US4861393A
Cited
US4534804A
Cited
US4601779A
Cited
US5013681A
Cited
US5261999A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-10-30 | 1999-05-01 | 1999-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-10-30 | 2003-05-01 | 2003-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-10-30 | 2007-05-01 | 2007-10-31 | $7700.00 | Window Closed / Lapsed |