Process for making strain-compensated bonded silicon-on-insulator material free of dislocations
Assignee: Philips North America LLC
•
Filing: 1991-05-08
•
Granted: 1993-11-16
•
Expires: 2011-05-08
Abstract
Abstract A silicon-on-insulator material is formed by a method which includes the steps of forming a p-type silicon epitaxial layer, doped with boron and a higher concentration of germanium, on the surface of a semiconductor silicon substrate, forming an additional silicon epitaxial layer on the p-type silicon epitaxial layer, forming an oxide layer on the additional silicon epitaxial layer, forming an oxide layer on another semiconductor silicon substrate, forming a laminate by bringing into contact, at room temperature, the oxide layers thereby bonding together the substrates, etching the silicon substrate provided with the silicon epitaxial layers, with an isotropic etch to remove most of this silicon substrate, exposing the laminate to an anisotropic etch for this silicon substrate until the remainder of this silicon substrate is removed but only a part of the p-type epitaxial layer is removed and then exposing the resultant structure to an additional isotropic etch for the p-type epitaxial layer for a time sufficient only to remove only the remainder of the p-type epitaxial layer.
Inventors
- 👤 Ronald D. Pinker
- 👤 Emil Arnold
- 👤 Helmut Baumgart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 01:06
CPC Classifications
H; H10; H10P; H10P90/00; H10P90/19; H10P90/1904; H10P90/1906; H10P90/1914; H10W; H10W10/00; H10W10/10; H10W10/181
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
201 words
A method of forming a silicon-on-insulator material, said method comprising forming a boron doped p-type silicon epitaxial layer having a boron concentration above 8×10 19 B/cm 3 and a co-doped germanium concentration 6-8 times higher than the boron concentration on a surface of a first semiconductor silicon substrate, forming a second silicon epitaxial layer on said p type epitaxial layer, providing a first oxide layer on a surface of said second epitaxial layer, providing a second oxide layer on a second semiconductor silicon substrate, bringing into contact said first and second oxide layers at room temperature thereby bonding together said first and second semiconductor substrates to thereby form a laminated structure, exposing said structure to a first isotropic etch for said first silicon substrate to thereby remove most of said first silicon substrate, exposing said laminate to an anisotropic etch for said first silicon substrate until the remainder of said first silicon substrate is removed, but only a part of said p-type epitaxial layer is removed and exposing said resultant structure to a second isotropic etch for said p-type epitaxial layer for a time sufficient only to remove the remainder of the said p-type epitaxial layer thereby producing a silicon-on-insulator material.
Claim 2
Independent Claim
201 words
A method of forming a silicon-on-insulator material, said method comprising forming a boron doped p-type silicon epitaxial layer having a boron concentration above 8×10 19 B/cm 3 and a co-doped germanium concentration 6-8 times higher than the boron concentration on a surface of a first semiconductor silicon substrate, forming a second silicon epitaxial layer on said p type epitaxial layer, providing a first oxide layer on a surface of said second epitaxial layer, providing a second oxide layer on a second semiconductor silicon substrate, bringing into contact said first and second oxide layers at room temperature thereby bonding together said first and second semiconductor substrates to thereby form a laminated structure, exposing said structure to a first isotropic etch for said first silicon substrate to thereby remove most of said first silicon substrate, exposing said laminate to an anisotropic etch for said first silicon substrate until the remainder of said first silicon substrate is removed, but only a part of said p-type epitaxial layer is removed and exposing said resultant structure to a second isotropic etch for said p-type epitaxial layer for a time sufficient only to remove the remainder of the said p-type epitaxial layer thereby producing a silicon-on-insulator material.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein at least one of said oxide layers is provided by thermal oxidation.
Claim 4
Dependent Claim
36 words
The method of claim 2 wherein after exposure to said second isotropic etch, said structure is exposed to a nitric acid--HF etch to remove any staining passivation layer formed by exposure to said second isotropic etch.
Claim 5
Dependent Claim
18 words
The method of claim 2 wherein said first oxide layer has a thickness of at least 20 Å.
Claim 6
Dependent Claim
15 words
The method of claim 4 wherein said first oxide layer is formed by thermal oxidation.
Claim 7
Dependent Claim
32 words
The method of claim 5 wherein said second oxide layer has a thickness of about 0.5-2.5 μm and wherein said oxide layers are subjected to treatment with nitrogen ions prior to bonding.
Claim 8
Dependent Claim
25 words
The method of claim 6 wherein the laminated structure is annealed in an oxidizing atmosphere at a temperature of 800° C.-900° C. prior to etching.
Claim 9
Dependent Claim
56 words
The method of claim 7 wherein said first isotropic etch comprises a mixture of nitric acid, hydrofluoric acid and acetic acid, the anisotropic etch comprises a mixture of ethylene diamine, pyrazine, pyrocatechol and water and the second isotropic etch comprises a mixture of nitric acid, hydrofluoric acid, hydrogen peroxide and acetic acid in a major amount.
Claim 10
Dependent Claim
87 words
The method of claim 8 wherein the first isotropic etch consists essentially of about 12 parts of nitric acid, 2 parts of hydrofluoric acid and 5 parts of acetic acid, the anisotropic etch consists essentially of a mixture of about 17 parts of ethylene diamine, 3 parts of pyrocatechol, 8 parts of water and 10 parts pyrazine and the second isotropic etch consists essentially of about 3 parts of nitric acid, 1 part of hydrofluoric acid, 12 parts of acetic acid and 0.01 parts of hydrogen peroxide.
Claim 11
Dependent Claim
31 words
The method of claim 9 wherein, after exposure to said second isotropic etch, the structure is exposed to a 200:1 mixture of acetic acid and hydrofluoric acid buffered with ammonium fluoride.
Claim 12
Independent Claim
214 words
A method of forming a silicon-on-insulator material, said method comprising forming an in-situ boron doped p-type silicon epitaxial layer having a boron concentration above 8×10 19 B/cm 3 and a co-doped germanium concentration 6-8 times higher than the boron concentration on a surface of a first semiconductor silicon substrate, forming a second silicon epitaxial layer on said p-type epitaxial layer, providing a first oxide layer on a surface of said second epitaxial layer, providing a second oxide layer on a second semiconductor silicon substrate, hydrolyzing said oxide layers and subjecting said oxide layers to treatment with nitrogen ions, bringing into contact said first and second oxide layers at room temperature thereby bonding together said first and second semiconductor substrates to thereby form a laminated structure, exposing said structure to a first isotropic etch for said first silicon substrate to thereby remove most of said first silicon substrate, exposing said laminate to an anisotropic etch for said first silicon substrate until the remainder of said first silicon substrate is removed, but only a part of said p-type epitaxial layer is removed, and exposing said resultant structure to a second isotropic etch for said p-type epitaxial layer for a time sufficient only to remove the remainder of said p-type epitaxial layer thereby producing a silicon-on-insulator material.
Claim 13
Independent Claim
214 words
A method of forming a silicon-on-insulator material, said method comprising forming an in-situ boron doped p-type silicon epitaxial layer having a boron concentration above 8×10 19 B/cm 3 and a co-doped germanium concentration 6-8 times higher than the boron concentration on a surface of a first semiconductor silicon substrate, forming a second silicon epitaxial layer on said p-type epitaxial layer, providing a first oxide layer on a surface of said second epitaxial layer, providing a second oxide layer on a second semiconductor silicon substrate, hydrolyzing said oxide layers and subjecting said oxide layers to treatment with nitrogen ions, bringing into contact said first and second oxide layers at room temperature thereby bonding together said first and second semiconductor substrates to thereby form a laminated structure, exposing said structure to a first isotropic etch for said first silicon substrate to thereby remove most of said first silicon substrate, exposing said laminate to an anisotropic etch for said first silicon substrate until the remainder of said first silicon substrate is removed, but only a part of said p-type epitaxial layer is removed, and exposing said resultant structure to a second isotropic etch for said p-type epitaxial layer for a time sufficient only to remove the remainder of said p-type epitaxial layer thereby producing a silicon-on-insulator material.
References Cited (Backward Citations)
US5013681A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-15 | 1997-05-17 | 1997-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-15 | 2001-05-17 | 2001-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-15 | 2005-05-17 | 2005-11-16 | $7700.00 | Window Closed / Lapsed |