US5443884A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Film-based composite structures for ultralightweight SDI systems
Assignee: Vencore Services and Solutions Inc
•
Filing: 1992-02-14
•
Granted: 1995-08-22
•
Expires: 2012-02-14
Abstract
Abstract Film-based composite structures meet the requirements of highly weight-efficient SDI space-based systems. These structures are rigid, lightweight, dimensionally stable, and possess a high degree of structural damping. Thin-walled structures (wall thickness less than 50 mu ) made from self-reinforced ordered-polymer films overcome drawbacks of fiber-reinforced composites, and provide resistance to microcracking, ply delamination and impact. They have high temperature capability (over 300 DEG C.), low temperature (cryogenic) capability and the capability for hardening and survivability. The modulus and dimensional stability of film-based ultralightweight honeycomb sandwich structures is better than currently possible with aluminum or fiber-reinforced composite materials. Other thin-walled structures such as tension web beams and thin facesheets also show similar stiffness-to-weight advantages over current materials.
Inventors
- 👤 Richard W. Lusignea
- 👤 Joseph J. Stanco
- 👤 Uday Kashalikar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:31
CPC Classifications
B; B32; B32B; B32B3/00; B32B3/10; B32B3/12; B29; B29D; B29D24/00; B29D24/002; B29D24/005; B29D99/00; B29D99/0089; B64; B64G; B64G99/00; C; C08; C08L; C08L63/00; C08L79/00; C08L79/04; C08L79/06; C08L79/08; C08L81/00; B32B2305/00; B32B2305/02; B32B2305/024; B32B2307/00; B32B2307/50; B32B2307/542; B32B2307/546; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1003; Y10T428/00; Y10T428/23; Y10T428/234; Y10T428/236; Y10T428/24; Y10T428/24149; Y10T428/24165
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
82 words
An ultralightweight (ULW) shaped structural member formed from a single-layer biaxially-oriented polymer film comprising an ordered rod-shaped extended chain polymer, wherein said polymer is an aromatic heterocyclic polymer selected from the group consisting of poly-(p-phenylene benzobisoxazole) and poly-(p-phenylene benzobisthiozole), wherein said polymer has a binder interpenetrated in the micro-infrastructure, the polymer being infiltrated with the binder to form a microcomposite of the polymer and binder, and wherein said structural member is a honeycomb structure comprising a honeycomb core formed from said film.
Claim 2
Dependent Claim
82 words
An ultralightweight (ULW) shaped structural member formed from a single-layer biaxially-oriented polymer film comprising an ordered rod-shaped extended chain polymer, wherein said polymer is an aromatic heterocyclic polymer selected from the group consisting of poly-(p-phenylene benzobisoxazole) and poly-(p-phenylene benzobisthiozole), wherein said polymer has a binder interpenetrated in the micro-infrastructure, the polymer being infiltrated with the binder to form a microcomposite of the polymer and binder, and wherein said structural member is a honeycomb structure comprising a honeycomb core formed from said film.
Claim 3
Dependent Claim
17 words
A structural member as in claim 1, wherein said film is less than about 0.25 mm thick.
Claim 4
Dependent Claim
17 words
A structural member as in claim 2, wherein said film is less than about 0.127 mm thick.
Claim 5
Dependent Claim
17 words
A structural member as in claim 3, wherein said film is less than about 0.05 mm thick.
Claim 6
Dependent Claim
17 words
A structural member as in claim 4, wherein said film is no more than 0.038±0.018 mm thick.
Claim 7
Dependent Claim
18 words
A structural member as in claim 5, wherein said film is no more than about 0.025 mm thick.
Claim 8
Dependent Claim
21 words
A structural member as in claim 5, wherein the cell size of said honeycomb core is less than about 3.8 mm.
Claim 9
Dependent Claim
18 words
A structural member as in claim 7, wherein said cell size is no more than about 3.175 mm.
Claim 10
Dependent Claim
39 words
A structural member as in claim 1, wherein the coefficient of thermal expansion in the cell axis direction of said honeycomb core is less than about 1 ppm/°C. over a range from about -50° C. to about +150° C.
Claim 11
Dependent Claim
20 words
A structural member as in claim 9, wherein said coefficient of thermal expansion is no more than about 0.3 ppm/°C.
Claim 12
Dependent Claim
23 words
A structural member as in claim 1, wherein said core material has a specific shear stiffness of at least about 863×10 3 m.
Claim 13
Dependent Claim
23 words
A structural member as in claim 11, wherein said core material has a specific shear stiffness of at least about 2.54×10 8 cm.
Claim 14
Dependent Claim
17 words
A structural member as in claim 1, further comprising a pair of facesheets applied to said core.
Claim 15
Dependent Claim
15 words
A structural member as in claim 13, wherein said facesheets comprise 2-ply uniaxial graphite/epoxy material.
Claim 16
Dependent Claim
18 words
A structural member as in claim 13, wherein said facesheets comprise the same material as said honeycomb core.
Claim 17
Dependent Claim
17 words
A structural member as in claim 15, wherein said facesheets are less than about 0.25 mm thick.
Claim 18
Dependent Claim
17 words
A structural member as in claim 16, wherein said facesheets are less than about 0.127 mm thick.
Claim 19
Dependent Claim
17 words
A structural member as in claim 17, wherein said facesheets are less than about 0.05 mm thick.
Claim 20
Dependent Claim
17 words
A structural member as in claim 18, wherein said facesheets are no more than 0.038±0.018 mm thick.
Claim 21
Dependent Claim
18 words
A structural member as in claim 19, wherein said facesheets are no more than substantially 0.025 mm thick.
Claim 22
Dependent Claim
19 words
A structural member as in claim 2, wherein the flexural stiffness of said structure is at least 70,000 psi.
Claim 23
Dependent Claim
21 words
A structural member as in claim 21, wherein the core density of said core is no more than about 5 pcf.
Claim 24
Dependent Claim
21 words
A structural member as in claim 22, wherein the core density of said core is no more than about 3 pcf.
Claim 25
Dependent Claim
21 words
A structural member as in claim 2, wherein the core density of said core is no more than about 5 pcf.
Claim 26
Dependent Claim
21 words
A structural member as in claim 24, wherein the core density of said core is no more than about 3 pcf.
Claim 27
Dependent Claim
141 words
A process for thermally shaping a honeycomb core which comprises a plurality of substantially hexagonal cells each defining a common cell axis direction, said process comprising the steps of: providing a mold having two mold halves which together define a plurality of substantially hexagonal mold cells; placing two sheets of thermally shapable material between said two mold halves and within said plurality of mold cells; placing a plurality of thermally expandable rods between said two sheets and respectively within said plurality of mold cells; and heating said mold, said sheets, and said rods so as to expand said rods so as to force said sheets to conform to the hexagonal shape of said mold cells, and to cure said sheets, thereby obtaining two thermally shaped sheets which together define said plurality of hexagonal cells each extending in said cell axis direction.
Claim 28
Dependent Claim
141 words
A process for thermally shaping a honeycomb core which comprises a plurality of substantially hexagonal cells each defining a common cell axis direction, said process comprising the steps of: providing a mold having two mold halves which together define a plurality of substantially hexagonal mold cells; placing two sheets of thermally shapable material between said two mold halves and within said plurality of mold cells; placing a plurality of thermally expandable rods between said two sheets and respectively within said plurality of mold cells; and heating said mold, said sheets, and said rods so as to expand said rods so as to force said sheets to conform to the hexagonal shape of said mold cells, and to cure said sheets, thereby obtaining two thermally shaped sheets which together define said plurality of hexagonal cells each extending in said cell axis direction.
Claim 29
Dependent Claim
56 words
A process as in claim 26, wherein said material is a polymer film comprising an ordered rod-shaped extended chain aromatic heterocyclic polymer selected from the group consisting of poly-(p-phenylene benzobisoxazole) and poly-(p-phenylene benzobisthiozole), having a binder interpenetrated in the micro-infrastructure, the polymer being infiltrated with the binder to form a microcomposite of the polymer and binder.
Claim 30
Dependent Claim
13 words
A process as in claim 27, wherein said thermally expandable rods comprise polytetrafluoroethylene.
Claim 31
Dependent Claim
13 words
A process as in claim 28, wherein said mold is coated with polytetrafluoroethylene.
Claim 32
Dependent Claim
61 words
A process as in claim 26, further comprising a step of forming a hexagonal cellular sheet by bonding said two thermally shaped sheets together by a primary bonding step of applying an adhesive material between respective facing surfaces of said sheets, while retaining said rods within said cells so as to interfere with any running of said adhesive into said cells.
Claim 33
Dependent Claim
104 words
A process as in claim 30, further comprising cutting said hexagonal cellular sheet along cut lines transverse to said cell axis direction to form a plurality of hexagonal cellular strips; stacking a plurality of said cellular strips along a plane transverse to said cell axis direction; and bonding said cellular strips by a secondary bonding step of applying an adhesive between respective facing surfaces of said cellular strips which define a secondary bonding plane, while retaining polytetrafluoroethylene rods within secondary cells which are defined between said cellular strips along said secondary bonding plane, to interfere with any running of adhesive into said secondary cells.
Claim 34
Dependent Claim
14 words
A process as defined in claim 31, wherein said adhesive is a bisphenol-A-based epoxy.
Claim 35
Dependent Claim
39 words
A process according to claim 26, wherein said material is a polymer film comprising a polybenzazole having a binder interpenetrated in the microinfrastructure, the polymer being infiltrated with the binder to form a microcomposite of the polymer and binder.
References Cited (Backward Citations)
US3356555A
Cited
US4554119A
Cited
US4606875A
Cited
US4845150A
Cited
EP0240302A2
Cited
WO1987006186A1
Cited
US4716067A
Cited
US4966806A
Cited
EP0284848A2
Cited
US4937125A
Cited
JPH01192536A
Cited
US4957577A
Cited
US5135783A
Cited
US4898924A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-08-21 | 1999-02-20 | 1999-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-08-21 | 2003-02-20 | 2003-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-08-21 | 2007-02-20 | 2007-08-22 | $7700.00 | Window Closed / Lapsed |