Method of fabricating epitaxially deposited ohmic contacts using group II-VI
Assignee: North Carolina State University
•
Filing: 1993-09-28
•
Granted: 1994-11-22
•
Expires: 2013-09-28
Abstract
Abstract An ohmic contact to a p-type zinc selenide (ZnSe) layer in a Group II-VI semiconductor device, includes a zinc telluride selenide (ZnTe x Se 1-x ) layer on the zinc selenide layer, a mercury selenide (HgSe) layer on the zinc telluride selenide layer and a conductor (such as metal) layer on the mercury selenide layer. The zinc telluride selenide and mercury selenide layers between the p-type zinc selenide and the conductor layer provide an ohmic contact by eliminating the band offset between the wide bandgap zinc selenide and the conductor. Step graded, linear graded, and parabolic graded layers of zinc telluride selenide may be provided. An integrated heterostructure is formed by epitaxially depositing the ohmic contact on the Group II-VI device. A removable overcoat layer may be formed on the Group II-VI device to allow room temperature atmospheric pressure transfer of the device from a zinc based deposition chamber to a mercury based deposition chamber, for deposition of the ohmic contact. A large area emitter may be formed by limiting the thickness of the mercury selenide layer so that optical radiation passes therethrough. A high efficiency optical emitter may be provided by using zinc telluride selenide or zinc sulfur telluride selenide to form an isoelectronic trap which produces broad and intense light output in the blue/green region.
Inventors
- 👤 Jan F. Schetzina
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:58
CPC Classifications
H; H10; H10H; H10H20/00; H10H20/80; H10H20/83; H10H20/832; B; B82; B82Y; B82Y20/00; H01; H01S; H01S5/00; H01S5/04; H01S5/042; H01S5/0421; H10D; H10D64/00; H10D64/01; H10D64/011; H10H20/01; H10H20/011; H10H20/012; H10H20/81; H10H20/822; H10H20/823; H01S5/02; H01S5/0206; H01S5/0215; H01S5/10; H01S5/18; H01S5/183; H01S5/30; H01S5/305; H01S5/3095; H01S5/32; H01S5/3211; H01S5/3215; H01S5/327; H01S5/34; H01S5/347; Y; Y10; Y10S; Y10S148/00; Y10S148/064; Y10S438/00; Y10S438/936
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
82 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device including a layer of p-type zinc selenide (ZnSe) or an alloy thereof, said ohmic contact forming method comprising the steps of: epitaxially forming a zinc telluride selenide (ZnTe x Se 1-x ) layer on said layer of p-type ZnSe or an alloy thereof, where 0<x<1; epitaxially forming a mercury selenide (HgSe) layer on said ZnTe x Se 1-x layer; and forming a conductor layer on said HgSe layer.
Claim 2
Independent Claim
82 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device including a layer of p-type zinc selenide (ZnSe) or an alloy thereof, said ohmic contact forming method comprising the steps of: epitaxially forming a zinc telluride selenide (ZnTe x Se 1-x ) layer on said layer of p-type ZnSe or an alloy thereof, where 0<x<1; epitaxially forming a mercury selenide (HgSe) layer on said ZnTe x Se 1-x layer; and forming a conductor layer on said HgSe layer.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein said zinc telluride selenide layer is epitaxially formed with x being constant to provide a step graded ZnTe x Se 1-x layer.
Claim 4
Dependent Claim
34 words
The method of claim 1 wherein said zinc telluride selenide layer is epitaxially formed with x decreasing from said ZnSe layer to said HgSe layer, to provide a graded ZnTe x Se 1-x layer.
Claim 5
Dependent Claim
36 words
The method of claim 3 wherein said zinc telluride selenide layer is epitaxially formed with x decreasing linearly from said ZnSe layer to said HgSe layer, to provide a linear graded ZnTe x Se 1-x layer.
Claim 6
Dependent Claim
36 words
The method of claim 3 wherein said zinc telluride selenide layer is epitaxially formed with x decreasing nonlinearly from said ZnSe layer to said HgSe layer, to provide a nonlinear graded ZnTe x Se 1-x layer.
Claim 7
Dependent Claim
36 words
The method of claim 5 wherein said zinc telluride selenide layer is epitaxially formed with x decreasing parabolically from said ZnSe layer to said HgSe layer, to provide a parabolic graded ZnTe x Se 1-x layer.
Claim 8
Dependent Claim
21 words
The method of claim 1 wherein at least a portion of said ZnTe x Se 1-x layer is epitaxially formed p-type.
Claim 9
Dependent Claim
31 words
The method of claim 7 wherein said ZnTe x Se 1-x layer is epitaxially formed p-type adjacent said ZnSe layer, and is epitaxially formed of neutral conductivity adjacent said HgSe layer.
Claim 10
Dependent Claim
45 words
The method of claim 6 wherein a first half of said ZnTe x Se 1-x layer adjacent said ZnSe layer is epitaxially formed p-type, and a second half of said ZnTe x Se 1-x layer adjacent said HgSe layer is of epitaxially formed neutral conductivity.
Claim 11
Dependent Claim
26 words
The method of claim 1 wherein said zinc telluride selenide layer forming step further comprises the step of p-type modulation doping said zinc telluride selenide layer.
Claim 12
Dependent Claim
34 words
The method of claim 1 wherein the following step is performed between said epitaxially forming steps: epitaxially forming a layer of zinc telluride (ZnTe) between said layers of ZnTe x Se 1-x and HgSe.
Claim 13
Independent Claim
98 words
A method of forming a Group II-VI compound semiconductor device comprising the steps of: forming in a first chamber, a first heterostructure of zinc-based Group II-VI compound semiconductor materials including a top layer of zinc telluride; forming in said first chamber, an overcoat layer on said top layer of zinc telluride; transferring said first heterostructure including said overcoat layer to a second chamber; removing said overcoat layer in said second chamber; and forming in said second chamber, a second heterostructure of at least one mercury based Group II-VI compound semiconductor material on said top layer of zinc telluride.
Claim 14
Independent Claim
98 words
A method of forming a Group II-VI compound semiconductor device comprising the steps of: forming in a first chamber, a first heterostructure of zinc-based Group II-VI compound semiconductor materials including a top layer of zinc telluride; forming in said first chamber, an overcoat layer on said top layer of zinc telluride; transferring said first heterostructure including said overcoat layer to a second chamber; removing said overcoat layer in said second chamber; and forming in said second chamber, a second heterostructure of at least one mercury based Group II-VI compound semiconductor material on said top layer of zinc telluride.
Claim 15
Dependent Claim
27 words
The method of claim 12 wherein said first heterostructure forming step comprises the step of epitaxially depositing said first heterostructure in a first molecular beam epitaxy chamber.
Claim 16
Dependent Claim
27 words
The method of claim 12 wherein said second heterostructure forming step comprises the step of epitaxially depositing said second heterostructure in a second molecular beam epitaxy chamber.
Claim 17
Dependent Claim
24 words
The method of claim 12 wherein said overcoat layer forming step comprises the step of forming a selenium overcoat layer on said first heterostructure.
Claim 18
Dependent Claim
16 words
The method of claim 12 wherein said transforming step occurs at room temperature and atmospheric pressure.
Claim 19
Independent Claim
83 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device including a layer of p-type zinc selenide (ZnSe) or an alloy thereof, said ohmic contact forming method comprising of steps of: epitaxially forming a zinc mercury selenide (Zn x Hg 1-x Se) layer on said layer of p-type ZnSe or an alloy thereof, where 0<x<1; epitaxially forming a mercury selenide (HgSe) layer on said Zn x Hg 1-x Se layer; and forming a conductor layer on said HgSe layer.
Claim 20
Independent Claim
83 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device including a layer of p-type zinc selenide (ZnSe) or an alloy thereof, said ohmic contact forming method comprising of steps of: epitaxially forming a zinc mercury selenide (Zn x Hg 1-x Se) layer on said layer of p-type ZnSe or an alloy thereof, where 0<x<1; epitaxially forming a mercury selenide (HgSe) layer on said Zn x Hg 1-x Se layer; and forming a conductor layer on said HgSe layer.
Claim 21
Dependent Claim
29 words
The method of claim 17 wherein said zinc mercury selenide layer is epitaxially formed with x being constant to provide a step graded Zn x Hg 1-x Se layer.
Claim 22
Dependent Claim
35 words
The method of claim 17 wherein said zinc mercury selenide layer is epitaxially formed with x decreasing from said ZnSe layer to said HgSe layer, to provide a graded Zn x Hg 1-x Se layer.
Claim 23
Dependent Claim
38 words
57. The method of claim 19 wherein said zinc mercury selenide layer is epitaxially formed with x decreasing linearly from said ZnSe layer to said HgSe layer, to provide a linear graded Zn x Hg 1-x Se layer.
Claim 24
Dependent Claim
37 words
The method of claim 19 wherein said zinc mercury selenide layer is epitaxially formed with x decreasing nonlinearly from said ZnSe layer to said HgSe layer, to provide a nonlinear graded Zn x Hg 1-x Se layer.
Claim 25
Dependent Claim
37 words
The method of claim 21 wherein said zinc mercury selenide layer is epitaxially formed with x decreasing parabolically from said ZnSe layer to said HgSe layer, to provide a parabolic graded Zn x Hg 1-x Se layer.
Claim 26
Dependent Claim
22 words
The method of claim 17 wherein at least a portion of said Zn x Hg 1-x Se layer is epitaxially formed p-type.
Claim 27
Dependent Claim
32 words
The method of claim 23 wherein said Zn x Hg 1-x Se layer is epitaxially formed p-type adjacent said ZnSe layer, and is epitaxially formed of neutral conductivity adjacent said HgSe layer.
Claim 28
Dependent Claim
47 words
The method of claim 22 wherein a first half of said Zn x Hg 1-x Se layer adjacent said ZnSe layer is epitaxially formed p-type, and a second half of said Zn x Hg 1-x Se layer adjacent said HgSe layer is of epitaxially formed neutral conductivity.
Claim 29
Dependent Claim
26 words
The method of claim 17 wherein said zinc mercury selenide layer forming step further comprises the step of p-type modulation doping said zinc mercury selenide layer.
Claim 30
Independent Claim
61 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device, said ohmic contact forming method comprising the steps of: epitaxially forming a ternary compound Group II-VI semiconductor material on said Group II-VI semiconductor device; epitaxially forming a Group II-VI semimetal on said ternary compound Group II-VI semiconductor material; and forming a conductor on said Group II-VI semimetal.
Claim 31
Independent Claim
61 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device, said ohmic contact forming method comprising the steps of: epitaxially forming a ternary compound Group II-VI semiconductor material on said Group II-VI semiconductor device; epitaxially forming a Group II-VI semimetal on said ternary compound Group II-VI semiconductor material; and forming a conductor on said Group II-VI semimetal.
Claim 32
Dependent Claim
17 words
The method of claim 27 wherein said ternary compound Group II-VI semiconductor material is zinc mercury selenide.
Claim 33
Dependent Claim
13 words
The method of claim 27 wherein said Group II-VI semimetal is mercury selenide.
Claim 34
Dependent Claim
11 words
The method of claim 27 wherein said conductor is a metal.
Claim 35
Independent Claim
56 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device including a layer of p-type zinc selenide (ZnSe) or an alloy thereof, said ohmic contact forming method comprising the steps of: epitaxially forming a mercury selenide (HgSe) heterostructure on said p-type ZnSe layer; and forming a conductor layer on said HgSe heterostructure.
Claim 36
Independent Claim
56 words
A method of forming an ohmic contact for a Group II-VI compound semiconductor device including a layer of p-type zinc selenide (ZnSe) or an alloy thereof, said ohmic contact forming method comprising the steps of: epitaxially forming a mercury selenide (HgSe) heterostructure on said p-type ZnSe layer; and forming a conductor layer on said HgSe heterostructure.
Claim 37
Dependent Claim
13 words
The method of claim 31 wherein said conductor layer is a metal layer.
Claim 38
Independent Claim
82 words
A method of forming a Group II-VI compound semiconductor device comprising the steps of: forming in a first chamber, a first heterostructure of zinc-based Group II-VI compound semiconductor materials; forming in said first chamber, an overcoat layer on said first heterostructure; transferring said first heterostructure including said overcoat layer to a second chamber; removing said overcoat layer in said second chamber; and forming in said second chamber, a second heterostructure of mercury based Group II-VI compound semiconductor materials on said first heterostructure.
Claim 39
Independent Claim
82 words
A method of forming a Group II-VI compound semiconductor device comprising the steps of: forming in a first chamber, a first heterostructure of zinc-based Group II-VI compound semiconductor materials; forming in said first chamber, an overcoat layer on said first heterostructure; transferring said first heterostructure including said overcoat layer to a second chamber; removing said overcoat layer in said second chamber; and forming in said second chamber, a second heterostructure of mercury based Group II-VI compound semiconductor materials on said first heterostructure.
Claim 40
Dependent Claim
26 words
The method of claim 33 wherein said first heterostructure forming step comprises the step of epitaxially depositing said first heterostructure in a first molecular epitaxy chamber.
Claim 41
Dependent Claim
27 words
The method of claim 33 wherein said second heterostructure forming step comprises the step of epitaxially depositing said second heterostructure in a second molecular beam epitaxy chamber.
Claim 42
Dependent Claim
24 words
The method of claim 33 wherein said overcoat layer forming step comprises the step of forming a selenium overcoat layer on said first heterostructure.
Claim 43
Dependent Claim
16 words
The method of claim 33 wherein said transforming step occurs at room temperature and atmospheric pressure.
References Cited (Backward Citations)
US4315796A
Cited
US4123295A
Cited
US4273596A
Cited
US4620058A
Cited
US4685979A
Cited
US4801984A
Cited
US4893154A
Cited
US4755663A
Cited
US4887274A
Cited
US5008891A
Cited
US5045897A
Cited
EP0475606A2
Cited
US5213998A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-11-21 | 1998-05-23 | 1998-11-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-11-21 | 2002-05-23 | 2002-11-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-11-21 | 2006-05-23 | 2006-11-22 | $7700.00 | Window Closed / Lapsed |