Primary coatings for optical glass fibers including polyether acrylates
Assignee: DSM BV
•
Filing: 1993-01-26
•
Granted: 1994-08-09
•
Expires: 2013-01-26
Abstract
Abstract Photocurable liquid coating compositions adapted to provide primary coatings for optical glass fibers are disclosed. These compositions comprise an acrylate-terminated polyurethane, an acrylate of an unsubstituted or C1-C10 alkyl substituted phenol that is alkoxylated with a C2-C4 alkylene oxide and at least one alkylacrylate having a Tg below about -45 DEG C. Films produced from these ultraviolet light curable compositions are flexible and possess good water resistance and good wet adhesion.
Inventors
- 👤 Clive J. Coady
- 👤 Erwin S. Poklacki
- 👤 John M. Zimmerman
- 👤 Timothy E. Bishop
- 👤 John L. Derer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:03
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/30; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/106; C03C25/1065; C08F299/00; C08F299/02; C08F299/06; C08F299/065; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/81; C08G18/8141; C08G18/815; C08G18/8158; C08G18/8175; Y; Y10; Y10S; Y10S525/00; Y10S525/92; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2971
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
189 words
An optical fiber coated with a photocurable liquid coating composition adapted to provide a primary coating for an optical glass fiber comprising: (1) about 30 to about 80 weight percent, based on the total weight of the coating composition, of an acrylate-terminated polyurethane having a number average molecular weight of about 2,500 to about 8,000 daltons and being the reaction product of (i) a prepolymer having a number average molecular weight of about 700 to about 2,000 daltons wherein the prepolymer is selected from the group consisting of polycarbonates and mixtures of polycarbonates and polyethers having an average of at least two groups that are reactive with an isocyanate group, (ii) a diisocyanate and (iii) a hydroxy acrylate; (2) about 20 to about 60 weight percent of an acrylate of an unsubstituted or C 7 -C 10 alkyl substituted phenol that is alkoxylated with a C 2 -C 4 alkylene oxide and contains about 1 to about 5 moles of the oxide per mole of the phenol; and (3) about 5 to about 30 weight percent of at least one alkylacrylate having a T g below about -45° C.
Claim 2
Dependent Claim
189 words
An optical fiber coated with a photocurable liquid coating composition adapted to provide a primary coating for an optical glass fiber comprising: (1) about 30 to about 80 weight percent, based on the total weight of the coating composition, of an acrylate-terminated polyurethane having a number average molecular weight of about 2,500 to about 8,000 daltons and being the reaction product of (i) a prepolymer having a number average molecular weight of about 700 to about 2,000 daltons wherein the prepolymer is selected from the group consisting of polycarbonates and mixtures of polycarbonates and polyethers having an average of at least two groups that are reactive with an isocyanate group, (ii) a diisocyanate and (iii) a hydroxy acrylate; (2) about 20 to about 60 weight percent of an acrylate of an unsubstituted or C 7 -C 10 alkyl substituted phenol that is alkoxylated with a C 2 -C 4 alkylene oxide and contains about 1 to about 5 moles of the oxide per mole of the phenol; and (3) about 5 to about 30 weight percent of at least one alkylacrylate having a T g below about -45° C.
Claim 3
Dependent Claim
192 words
An optical glass fiber coated with a photocurable liquid coating composition adapted to provide a primary coating for an optical glass fiber comprising (1) about 30 to about 60 weight percent, based on the total weight of the coating composition, of an acrylate-terminated polyurethane having a number average molecular weight of about 2,500 to about 8,000 daltons and being the reaction product of (i) a prepolymer having a number average molecular weight of about 700 to about 2,000 daltons, the prepolymer being (a) a polycarbonate diol produced from an alkylene diol having about 2 to about 12 carbon atoms or (b) a polycarbonate copolymer of an alkylene oxide and the alkylene oxide diol, (ii) a diisocyanate and (iii) a hydroxy acrylate; (2) about 20 to about 60 weight percent of an acrylate of an unsubstituted or C 8 -C 9 alkyl substituted phenol that is alkoxylated with a C 2 -C 4 alkylene oxide and contains about 1 to about 10 moles of the oxide per mole of the phenol; and (3) about 5 to about 10 weight percent of at least one alkylacrylate having a T g below about -45° C.
Claim 4
Dependent Claim
192 words
An optical glass fiber coated with a photocurable liquid coating composition adapted to provide a primary coating for an optical glass fiber comprising (1) about 30 to about 60 weight percent, based on the total weight of the coating composition, of an acrylate-terminated polyurethane having a number average molecular weight of about 2,500 to about 8,000 daltons and being the reaction product of (i) a prepolymer having a number average molecular weight of about 700 to about 2,000 daltons, the prepolymer being (a) a polycarbonate diol produced from an alkylene diol having about 2 to about 12 carbon atoms or (b) a polycarbonate copolymer of an alkylene oxide and the alkylene oxide diol, (ii) a diisocyanate and (iii) a hydroxy acrylate; (2) about 20 to about 60 weight percent of an acrylate of an unsubstituted or C 8 -C 9 alkyl substituted phenol that is alkoxylated with a C 2 -C 4 alkylene oxide and contains about 1 to about 10 moles of the oxide per mole of the phenol; and (3) about 5 to about 10 weight percent of at least one alkylacrylate having a T g below about -45° C.
References Cited (Backward Citations)
US4255243A
Cited
US4264752A
Cited
US4624994A
Cited
US4932750A
Cited
US4608400A
Cited
US4608409A
Cited
US4690502A
Cited
US4690501A
Cited
US4741958A
Cited
US4798852A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-08 | 1998-02-07 | 1998-08-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-08 | 2002-02-07 | 2002-08-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-08 | 2006-02-07 | 2006-08-09 | $7700.00 | Window Closed / Lapsed |