Polyacrylated oligomers in ultraviolet curable optical fiber coatings
Assignee: Stamicarbon BV
•
Filing: 1985-05-08
•
Granted: 1986-08-26
•
Expires: 2005-05-08
Abstract
Abstract An ultraviolet curing liquid coating composition is disclosed which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides buffer coatings for optical glass fiber having adequate strength at room or expected elevated temperature and stability at such elevated temperature, a high index of refraction above 1.48, and a low tensile modulus which remains low to resist microbending difficulties down to around -60° C. This coating composition consists essentially of a linear polyacrylate-terminated polyurethane or polyurea oligomer having a room temperature tensile modulus of at least 100 psi., and a tensile modulus at -60° C. which is less than 175,000 psi., when capped with 2-hydroxyethyl acrylate and cured with ultraviolet light, in admixture with a liquid acrylate-functional material which does not increase the low temperature hardness and which provides the liquidity needed for coating application. The oligomer is instead capped with a monohydric polyacrylate to provide improved cure speed without eliminating resistance to low temperature microbending.
Inventors
- 👤 Clive J. Coady
- 👤 John J. Krajewski
- 👤 Timothy E. Bishop
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 08:06
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/74; C08G18/75; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/106; C08F; C08F299/00; C08F299/02; C08F299/06; C08G18/08; C08G18/10; C08G18/28; C08G18/67; C08G18/671; C08G18/672; C08G18/673; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938; Y10T428/2964; Y10T428/31504; Y10T428/31551; Y10T428/31598; Y10T428/31601
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
109 words
An ultraviolet curing liquid coating composition which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber consisting essentially of a linear polyacrylate-terminated polyurethane or polyurea oligomer in admixture with a liquid acrylate-functional material which does not increase the low temperature hardness and which provides the liquidity needed for coating application, said polyacrylate-terminated polyurethane or polyurea oligomer having a room temperature tensile modulus of at least 100 psi., and a tensile modulus at -60° C. which is less than 175,000 psi., when capped with 2-hydroxyethyl acrylate and cured with ultraviolet light, said oligomer being capped with a monohydric polyacrylate.
Claim 2
Dependent Claim
109 words
An ultraviolet curing liquid coating composition which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber consisting essentially of a linear polyacrylate-terminated polyurethane or polyurea oligomer in admixture with a liquid acrylate-functional material which does not increase the low temperature hardness and which provides the liquidity needed for coating application, said polyacrylate-terminated polyurethane or polyurea oligomer having a room temperature tensile modulus of at least 100 psi., and a tensile modulus at -60° C. which is less than 175,000 psi., when capped with 2-hydroxyethyl acrylate and cured with ultraviolet light, said oligomer being capped with a monohydric polyacrylate.
Claim 3
Dependent Claim
26 words
A coating composition as recited in claim 1 in which said acrylate-functional liquid is a monoacrylate monomer having a glass transition temperature below about 0° C.
Claim 4
Dependent Claim
46 words
A coating composition as recited in claim 1 in which said acrylate-functional liquid is a linear aliphatic diacrylate in which the two acrylate groups are separated by a chain of at least 6 carbon atoms or by a molecular weight of from 400 to about 4000.
Claim 5
Dependent Claim
103 words
A coating composition as recited in claim 1 in which said diisocyanate includes a linear aliphatic chain containing at least 6 carbon atoms separating the two isocyanate groups, and this diisocyanate is reacted with a dihydric or diamino polyether or polyester containing alkylene groups having from 1 to 6 carbon atoms and a molecular weight in the range of 500 to 4000, to form a polyurethane or polyurea diisocyanate which is half end capped with said monohydric polyacrylate and reacted with a C 1 to C 4 oxyalkylene diamine having a molecular weight of from 100 to 600 to consume the isocyanate functionality.
Claim 6
Dependent Claim
19 words
A coating composition as recited in claim 4 in which said diisocyanate is provided by dimer fatty acid diisocyanate.
Claim 7
Dependent Claim
19 words
A coating composition as recited in claim 5 in which said dimer fatty acid diisocyanate contains 36 carbon atoms.
Claim 8
Dependent Claim
33 words
A coating composition as recited in claim 5 in which said diisocyanate is reacted with a polyether which is a polyoxyalkylene glycol having a molecular weight in the range of 1000 to 3000.
Claim 9
Dependent Claim
19 words
A coating composition as recited in claim 7 in which said oxyalkylene group contains 2 or 3 carbon atoms.
Claim 10
Dependent Claim
16 words
A coating composition as recited in claim 8 in which said monohydric polyacrylate is pentaerythritol polyacrylate.
Claim 11
Dependent Claim
32 words
A coating composition as recited in claim 1 in which said low glass transition temperature monomer is selected from the group consisting of ethoxyethoxyethyl acrylate, phenoxyethyl acrylate, butoxyethyl acrylate, and 2-hydroxyethyl acrylate.
Claim 12
Dependent Claim
113 words
An ultraviolet curing liquid coating composition which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber consisting essentially of a linear polyacrylate-terminated polyurea polyurethane oligomer in admixture with a liquid acrylate-functional material selected from the group consisting of ethoxyethoxyethyl acrylate, phenoxyethyl acrylate, butoxyethyl acrylate, and 2-hydroxyethyl acrylate to provide the liquidity needed for coating application, said polyacrylate-terminated polyurea polyurethane oligomer having a room temperature tensile modulus of at least 200 psi., and a tensile modulus at -60° C. which is less than 100,000 psi., when capped with 2-hydroxyethyl acrylate and cured with ultraviolet light, said oligomer being capped with a monohydric polyacrylate.
Claim 13
Dependent Claim
113 words
An ultraviolet curing liquid coating composition which, when cured with ultraviolet light in the presence of an appropriate photoinitiator, provides a buffer coating for optical glass fiber consisting essentially of a linear polyacrylate-terminated polyurea polyurethane oligomer in admixture with a liquid acrylate-functional material selected from the group consisting of ethoxyethoxyethyl acrylate, phenoxyethyl acrylate, butoxyethyl acrylate, and 2-hydroxyethyl acrylate to provide the liquidity needed for coating application, said polyacrylate-terminated polyurea polyurethane oligomer having a room temperature tensile modulus of at least 200 psi., and a tensile modulus at -60° C. which is less than 100,000 psi., when capped with 2-hydroxyethyl acrylate and cured with ultraviolet light, said oligomer being capped with a monohydric polyacrylate.
Claim 14
Dependent Claim
16 words
A coating composition as recited in claim 11 in which said monohydric polyacrylate is pentaerythritol polyacrylate.
Claim 15
Dependent Claim
15 words
An optical glass fiber coated with an ultraviolet-cured coating of the composition of claim 1.
Claim 16
Dependent Claim
15 words
An optical glass fiber coated with an ultraviolet-cured coating of the composition of claim 13.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-08-25 | 1990-02-24 | 1990-08-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-08-25 | 1994-02-24 | 1994-08-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-08-25 | 1998-02-24 | 1998-08-26 | $7700.00 | Window Closed / Lapsed |