Abstract
Abstract Buffer-coated and overcoated optical glass fiber is disclosed in which the topcoat has the high strength and high tensile modulus combined with good elongation and solvent resistance associated with extruded jacket coatings, but which is applied by ordinary coating procedures and cured by exposure to ultraviolet radiation. The coating compositions which enable this to be achieved comprise an ultraviolet curable coating composition comprising, based on total reactive components, from about 60% up to about 85% of a diepoxide polyacrylate combined with at least about 15% of an monacrylate-functional monomer having a glass transition temperature below 0 DEG C. to provide desired coating viscosity. The diepoxide is a diglycidyl ether of a bisphenol having a molecular weight in the range of about 560 to about 2000 and contains at least 1.8 oxirane groups per molecule, substantially all of these oxirane groups being consumed in the polyacrylate.
Inventors
- 👤 Timothy E. Bishop
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:42
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/1065; C08; C08F; C08F290/00; C08F290/02; C08F290/06; C08F290/064; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
144 words
An organic buffer-coated and topcoated optical glass fiber in which the topcoat is an ultraviolet-cured coating composition which, when formed into a 3 mil cured test film, has a tensile strength of at least about 2500 psi, a tensile modulus measured at room temperature of at least 50,000 psi. and an elongation at least about 25%, said composition consisting essentially of, based on total reactive components, from about 60% up to about 85% of a diepoxide polyacrylate combined with at least about 15% up to 40% of a monoacrylate-functional monomer having a glass transition temperature below 0° C. to provide desired coating viscosity, said diepoxide being a diglycidyl ether of a bisphenol having a molecular weight in the range of about 560 to about 2000 and at least 1.8 oxirane groups per molecule, substantially all of said oxirane groups being consumed in said polyacrylate.
Claim 2
Dependent Claim
144 words
An organic buffer-coated and topcoated optical glass fiber in which the topcoat is an ultraviolet-cured coating composition which, when formed into a 3 mil cured test film, has a tensile strength of at least about 2500 psi, a tensile modulus measured at room temperature of at least 50,000 psi. and an elongation at least about 25%, said composition consisting essentially of, based on total reactive components, from about 60% up to about 85% of a diepoxide polyacrylate combined with at least about 15% up to 40% of a monoacrylate-functional monomer having a glass transition temperature below 0° C. to provide desired coating viscosity, said diepoxide being a diglycidyl ether of a bisphenol having a molecular weight in the range of about 560 to about 2000 and at least 1.8 oxirane groups per molecule, substantially all of said oxirane groups being consumed in said polyacrylate.
Claim 3
Dependent Claim
28 words
A coated optical fiber as recited in claim 1 in which said buffer coating on said optical glass fiber has a room temperature tensile modulus below 10,000 psi.
Claim 4
Dependent Claim
28 words
A coated optical fiber as recited in claim 1 in which said buffer coating on said optical glass fiber has a room temperature tensile modulus below 2,000 psi.
Claim 5
Dependent Claim
152 words
An organic buffer-coated and topcoated optical glass fiber in which the buffer coating has a room temperature tensile modulus of less than 10,000 psi, and the topcoat is an ultraviolet cured coating which, in a 3 mil test film, has a tensile strength of at least about 2500 psi, a tensile modulus measured at room temperature of at least 75,000 psi. and an elongation at least about 25%, the composition of said topcoat consisting essentially of, based on total reactive components, from about 65% up to about 80% of a diepoxide diacrylate combined with 20% to 35% of monoacrylate-functional monomer selected from phenoxyethyl acrylate, tetrahydrofurfuryl acrylate, and C 2 -C 4 alkoxyethyl acrylates, and mixtures thereof, to provide desired coating viscosity, said diepoxide being a diglycidyl ether of bisphenol A having a molecular weight in the range of 700 to 1200, substantially all of said oxirane groups being consumed in said diacrylate.
Claim 6
Dependent Claim
152 words
An organic buffer-coated and topcoated optical glass fiber in which the buffer coating has a room temperature tensile modulus of less than 10,000 psi, and the topcoat is an ultraviolet cured coating which, in a 3 mil test film, has a tensile strength of at least about 2500 psi, a tensile modulus measured at room temperature of at least 75,000 psi. and an elongation at least about 25%, the composition of said topcoat consisting essentially of, based on total reactive components, from about 65% up to about 80% of a diepoxide diacrylate combined with 20% to 35% of monoacrylate-functional monomer selected from phenoxyethyl acrylate, tetrahydrofurfuryl acrylate, and C 2 -C 4 alkoxyethyl acrylates, and mixtures thereof, to provide desired coating viscosity, said diepoxide being a diglycidyl ether of bisphenol A having a molecular weight in the range of 700 to 1200, substantially all of said oxirane groups being consumed in said diacrylate.
Claim 7
Dependent Claim
75 words
A method of topcoating buffer-coated optical glass fiber in which the topcoat has the high strength and modulus combined with good elongation and solvent resistance associated with extruded jacket coatings, but which is applied by ordinary coating procedures and cured by exposure to ultraviolet radiation comprising, applying to organic buffer-coated optical glass fiber an ultraviolet-curable coating composition as described in claim 1, and then exposing the wet-coated fiber to ultraviolet light to cure the coating.
Claim 8
Dependent Claim
26 words
A method as recited in claim 5 in which said buffer coating on said optical glass fiber has a room temperature tensile modulus below 10,000 psi.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-05-03 | 1991-11-02 | 1992-05-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-05-03 | 1995-11-02 | 1996-05-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-05-03 | 1999-11-02 | 2000-05-03 | $7700.00 | Window Closed / Lapsed |