Optical fiber coated with an ultraviolet cured topcoating
Assignee: Covestro Resins BV
•
Filing: 1983-11-10
•
Granted: 1985-06-11
•
Expires: 2003-11-10
Abstract
Abstract Buffer-coated and overcoated optical glass fiber is disclosed in which the topcoat has the high strength and high tensile modulus combined with good elongation and solvent resistance associated with extruded jacket coatings, but which is applied by ordinary coating procedures and cured by exposure to ultraviolet radiation. The coating compositions which enable this to be achieved comprise 30% to about 80% of linear diethylenic polyester polyurethanes which are the linear polyurethane reaction product of an organic diisocyanate with hydroxy-functional polyester formed by reacting a diol, such as ethylene glycol, with certain dicarboxylic acids, such as adipic acid. This polyurethane is end capped with a monoethylenically unsaturated monohydric alcohol. At least 50% of this diethylenic polyester polyurethane is combined with at least 5% of liquid diethylenic diester of a diglycidyl ether of a bisphenol, and at least 5% of liquid monoethylenically unsaturated monomer having a glass transition temperature above about 55 DEG C., these proportions being based on total reactive components.
Inventors
- 👤 Timothy E. Bishop
- 👤 George Pasternack
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:07
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/81; C08G18/8141; C08G18/815; C08G18/8158; C08G18/8175; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/1065; C08F; C08F299/00; C08F299/02; C08F299/06; C08G18/28; C08G18/30; C08G18/32; C08G18/3203; C08G18/3221; C08G18/67; C08G18/671; C08G18/672; C08G18/8108; C08G18/8116; Y; Y10; Y10S; Y10S525/00; Y10S525/92; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
189 words
A resin buffer-coated and topcoated optical glass fiber in which the topcoat is an ultraviolet cured coating of an ultraviolet curable coating composition which, when formed into a 3 mil cured test film, has a tensile modulus measured at room temperature of at least 150,000 psi. and an elongation at least about 15%, said composition comprising, based on total reactive components, from 30% up to about 80% of diethylenic polyester polyurethane having one of the following formulas: ##STR3## in which X is the residue of a monoethylenically unsaturated monohydric alcohol, Q is the residue of an organic diisocyanate, R is an alkylene group containing from 2-4 carbon atoms, R' is an alkylene group containing from 2-8 carbon atoms, and n is a number from about 1.8 to about 4; and ##STR4## in which the symbols have the above assigned meanings and Z is a monoisocyanate-functional monoethylenically unsaturated compound; at least 5% of total reactive components of liquid diethylenically unsaturated ester of a diglycidyl ether of a bisphenol, and at least 5% of total reactive components of liquid monoethylenically unsaturated monomer having a glass transition temperature above about 55° C.
Claim 2
Dependent Claim
189 words
A resin buffer-coated and topcoated optical glass fiber in which the topcoat is an ultraviolet cured coating of an ultraviolet curable coating composition which, when formed into a 3 mil cured test film, has a tensile modulus measured at room temperature of at least 150,000 psi. and an elongation at least about 15%, said composition comprising, based on total reactive components, from 30% up to about 80% of diethylenic polyester polyurethane having one of the following formulas: ##STR3## in which X is the residue of a monoethylenically unsaturated monohydric alcohol, Q is the residue of an organic diisocyanate, R is an alkylene group containing from 2-4 carbon atoms, R' is an alkylene group containing from 2-8 carbon atoms, and n is a number from about 1.8 to about 4; and ##STR4## in which the symbols have the above assigned meanings and Z is a monoisocyanate-functional monoethylenically unsaturated compound; at least 5% of total reactive components of liquid diethylenically unsaturated ester of a diglycidyl ether of a bisphenol, and at least 5% of total reactive components of liquid monoethylenically unsaturated monomer having a glass transition temperature above about 55° C.
Claim 3
Dependent Claim
18 words
A coated optical fiber as recited in claim 1 in which X is the residue of 2-hydroxyethyl acrylate.
Claim 4
Dependent Claim
30 words
A coated optical fiber as recited in claim 2 in which R is the ethylene radical, R' is an alkylene group containing 6 carbon atoms, and n is about 2.0.
Claim 5
Dependent Claim
33 words
A coated optical fiber as recited in claim 1 in which said monoethylenically unsaturated monomer is selected from the group consisting of dimethyl acrylamide, N-vinyl pyrrolidone, isobornyl acrylate, acrylic acid and dicyclopentenyl acrylate.
Claim 6
Dependent Claim
23 words
A coated optical fiber as recited in claim 4 in which said monomer is present in an amount not in excess of 45%.
Claim 7
Dependent Claim
22 words
A coated optical fiber as recited in claim 1 in which said diisocyanate is the residue of isophorone diisocyanate or 2,4-toluene diisocyanate.
Claim 8
Dependent Claim
28 words
A coated optical fiber as recited in claim 1 in which said buffer coating on said optical glass fiber has a room temperature tensile modulus below 10,000 psi.
Claim 9
Dependent Claim
28 words
A coated optical fiber as recited in claim 7 in which said buffer coating on said optical glass fiber has a room temperature tensile modulus below 2,000 psi.
Claim 10
Dependent Claim
174 words
A resin buffer-coated and topcoated optical glass fiber in which the buffer coating has a room temperature tensile modulus of less than 10,000 psi, and the topcoat is an ultraviolet cured coating which, in a 3 mil test film, has a tensile modulus measured at room temperature of at least 175,000 psi. and an elongation of at least 15%, said topcoat comprising from 40% up to about 70% of total reactive components of diacrylate polyester polyurethane having the formula: ##STR5## in which X is the residue of a monohydric monoacrylate, Q is the residue of an organic diisocyanate, R is an alkylene group containing from 2-4 carbon atoms, R' is an alkylene group containing from 2-8 carbon atoms, and n about 2, at least 8% of total reactive components of liquid diacrylate of a diglycidyl ether of bisphenol A having a molecular weight of 350-400, and at least 15% of total reactive components of monoethylenically unsaturated monomer selected from the group consisting of dimethyl acrylamide, N-vinyl pyrrolidone, isobornyl acrylate, acrylic acid and dicyclopentenyl acrylate.
Claim 11
Dependent Claim
174 words
A resin buffer-coated and topcoated optical glass fiber in which the buffer coating has a room temperature tensile modulus of less than 10,000 psi, and the topcoat is an ultraviolet cured coating which, in a 3 mil test film, has a tensile modulus measured at room temperature of at least 175,000 psi. and an elongation of at least 15%, said topcoat comprising from 40% up to about 70% of total reactive components of diacrylate polyester polyurethane having the formula: ##STR5## in which X is the residue of a monohydric monoacrylate, Q is the residue of an organic diisocyanate, R is an alkylene group containing from 2-4 carbon atoms, R' is an alkylene group containing from 2-8 carbon atoms, and n about 2, at least 8% of total reactive components of liquid diacrylate of a diglycidyl ether of bisphenol A having a molecular weight of 350-400, and at least 15% of total reactive components of monoethylenically unsaturated monomer selected from the group consisting of dimethyl acrylamide, N-vinyl pyrrolidone, isobornyl acrylate, acrylic acid and dicyclopentenyl acrylate.
Claim 12
Independent Claim
205 words
A method of topcoating resin buffer-coated optical glass fiber to provide a topcoat having the high strength and modulus combined with good elongation and solvent resistance associated with extruded jacket coatings, but which is applied by ordinary coating procedures and cured by exposure to ultraviolet radiation comprising, applying to resin buffer-coated optical glass fiber an ultraviolet-curable coating composition comprising, based on total reactive components, from 30% up to about 80% of diethylenic polyester polyurethane having one of the following formulas: ##STR6## in which X is the residue of a monoethylenically unsaturated monohydric alcohol, Q is the residue of an organic diisocyanate, R is an alkylene group containing from 2-4 carbon atoms, R' is an alkylene group containing from 2-8 carbon atoms, and n is a number from about 1.8 to about 4; and ##STR7## in which the symbols have the above assigned meaning and Z is a monoisocyanate-functional monoethylenically unsaturated compound; at least 5% of total reactive components of liquid diethylenically unsaturated ester of a diglycidyl ether of a bisphenol, and at least 5% of total reactive components of liquid monoethylenically unsaturated monomer having a glass transition temperature above about 55° C., and then exposing the wet-coated fiber to ultraviolet light to cure the coating.
Claim 13
Independent Claim
205 words
A method of topcoating resin buffer-coated optical glass fiber to provide a topcoat having the high strength and modulus combined with good elongation and solvent resistance associated with extruded jacket coatings, but which is applied by ordinary coating procedures and cured by exposure to ultraviolet radiation comprising, applying to resin buffer-coated optical glass fiber an ultraviolet-curable coating composition comprising, based on total reactive components, from 30% up to about 80% of diethylenic polyester polyurethane having one of the following formulas: ##STR6## in which X is the residue of a monoethylenically unsaturated monohydric alcohol, Q is the residue of an organic diisocyanate, R is an alkylene group containing from 2-4 carbon atoms, R' is an alkylene group containing from 2-8 carbon atoms, and n is a number from about 1.8 to about 4; and ##STR7## in which the symbols have the above assigned meaning and Z is a monoisocyanate-functional monoethylenically unsaturated compound; at least 5% of total reactive components of liquid diethylenically unsaturated ester of a diglycidyl ether of a bisphenol, and at least 5% of total reactive components of liquid monoethylenically unsaturated monomer having a glass transition temperature above about 55° C., and then exposing the wet-coated fiber to ultraviolet light to cure the coating.
Claim 14
Dependent Claim
26 words
A method as recited in claim 10 in which said buffer coating on said optical glass fiber has a room temperature tensile modulus below 10,000 psi.
Claim 15
Dependent Claim
30 words
A method as recited in claim 11 in which said coating composition contains up to 45% of said monoethylenically unsaturated monomer having a glass transition temperature above about 55° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-10 | 1988-12-10 | 1989-06-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-10 | 1992-12-10 | 1993-06-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-10 | 1996-12-10 | 1997-06-11 | $7700.00 | Window Closed / Lapsed |