Abstract
Abstract Radial differential melt flow rate melt spun fiber, preparation thereof utilizing threadline oxidative chain scission degradation of hot fiber extruded from polyolefin polymer component(s) having a broad molecular weight distribution in conjunction with a delayed or slow quench step, and corresponding high strength nonwoven material obtained therefrom.
Inventors
- 👤 Randall E. Kozulla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:55
CPC Classifications
D; D01; D01F; D01F8/00; D01F8/04; D01F8/06; D01F6/00; D01F6/02; D01F6/04; D01F1/00; D01F1/02; D01F1/10; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2931; Y10T442/00; Y10T442/60; Y10T442/681
Claims Analysis
Total Claims: 77
Claim 1
Independent Claim
73 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to effect oxidative chain scission degradation of the surface to obtain at least one polypropylene containing fiber or filament.
Claim 2
Dependent Claim
73 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to effect oxidative chain scission degradation of the surface to obtain at least one polypropylene containing fiber or filament.
Claim 3
Dependent Claim
21 words
The process according to claim 1, wherein the polypropylene containing material has a molecular weight distribution of at least about 6.
Claim 4
Dependent Claim
21 words
The process according to claim 2, wherein the polypropylene containing material has a molecular weight distribution of at least about 7.
Claim 5
Dependent Claim
21 words
The process according to claim 3, wherein the polypropylene containing material has a molecular weight distribution of at least about 8.
Claim 6
Dependent Claim
28 words
The process according to claim 1, wherein the polypropylene containing material subjected to extrusion includes a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof.
Claim 7
Dependent Claim
26 words
The process according to claim 1, wherein the polypropylene containing material subjected to extrusion includes at least one of phenylphosphite and a N,N' bis-piperidinyl diamine derivative.
Claim 8
Dependent Claim
46 words
The process according to claim 1, wherein the polypropylene containing material is extruded from an extruder and includes a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof, in an effective amount to control chain scission degradation of polymeric components in the extruder.
Claim 9
Dependent Claim
48 words
The process according to claim 1, wherein the controlling quench of the at least one hot extrudate in an oxygen containing atmosphere to effect oxidative chain scission degradation of the surface of the at least one fiber or filament includes controlling rate of quenching of the hot extrudate.
Claim 10
Dependent Claim
20 words
The process according to claim 8, wherein the controlling quenching comprises delaying quenching of the at least one hot extrudate.
Claim 11
Dependent Claim
26 words
The process according to claim 9, wherein the oxygen containing quenching atmosphere comprises a cross-blow quench, and an upper portion of the cross-blow quench is blocked.
Claim 12
Dependent Claim
16 words
The process according to claim 10, wherein up to about 5.4% of the cross-blow is blocked.
Claim 13
Dependent Claim
25 words
The process according to claim 1, wherein the at least one polypropylene containing fiber or filament comprises a monocomponent or a bicomponent fiber or filament.
Claim 14
Dependent Claim
23 words
The process according to claim 1, wherein the polypropylene containing material is extruded at a temperature of about 250° C. to 325° C.
Claim 15
Dependent Claim
23 words
The process according to claim 13, wherein the polypropylene containing material is extruded at a temperature of about 275° C. to 320° C.
Claim 16
Dependent Claim
61 words
The process according to claim 1, wherein the controlling quench of the at least one hot extrudate in an oxygen containing atmosphere so as to effect oxidative chain scission of the surface comprises maintaining the temperature of the at least one hot extrudate above about 250° C. for a period of time to obtain oxidative chain scission degradation of the surface.
Claim 17
Dependent Claim
19 words
The process according to claim 15, wherein the controlling quenching includes blocking an upper portion of a cross-blow quench.
Claim 18
Dependent Claim
22 words
The process according to claim 15, wherein the controlling quenching includes passing the at least one hot extrudate through a blocked zone.
Claim 19
Dependent Claim
17 words
The process according to claim 17, wherein the blocked zone is open to the oxygen containing atmosphere.
Claim 20
Dependent Claim
142 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface, the polypropylene containing material including a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof, in an effective amount to at least substantially limit chain scission degradation of polymeric components in the extruder; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to effect oxidative chain scission degradation of the surface, the controlling quenching including maintaining the at least one hot extrudate at a temperature for a sufficient period of time to permit oxidative chain scission degradation of the surface of the hot extrudate to obtain at least one polypropylene containing fiber or filament.
Claim 21
Dependent Claim
142 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface, the polypropylene containing material including a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof, in an effective amount to at least substantially limit chain scission degradation of polymeric components in the extruder; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to effect oxidative chain scission degradation of the surface, the controlling quenching including maintaining the at least one hot extrudate at a temperature for a sufficient period of time to permit oxidative chain scission degradation of the surface of the hot extrudate to obtain at least one polypropylene containing fiber or filament.
Claim 22
Dependent Claim
99 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to obtain at least one polypropylene containing fiber or filament having a decreasing weight average molecular weight towards the surface of the at least one fiber or filament, and an increasing melt flow rate towards the surface of the at least one fiber or filament.
Claim 23
Dependent Claim
99 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to obtain at least one polypropylene containing fiber or filament having a decreasing weight average molecular weight towards the surface of the at least one fiber or filament, and an increasing melt flow rate towards the surface of the at least one fiber or filament.
Claim 24
Dependent Claim
30 words
The process according to claim 20, wherein the at least one fiber or filament comprises an inner zone including a weight average molecular weight of about 100,000 to 450,000 grams/mole.
Claim 25
Dependent Claim
22 words
The process according to claim 21, wherein the inner zone comprises a weight average molecular weight of about 100,000 to 250,000 grams/mole.
Claim 26
Dependent Claim
18 words
The process according to claim 21, wherein the inner zone comprises a melt flow rate of 5-25 dg/min.
Claim 27
Dependent Claim
45 words
The process according to claim 21, wherein the at least one fiber or filament comprises an outer zone including the surface of the at least one fiber or filament, and the outer zone comprises a weight average molecular weight of less than about 10,000 grams/mole.
Claim 28
Dependent Claim
22 words
The process according to claim 24, wherein the outer zone comprises a weight average molecular weight of about 5,000 to 10,000 grams/mole.
Claim 29
Dependent Claim
19 words
The process according to claim 24, wherein the outer zone comprises a melt flow rate of about 25-1000 dg/min.
Claim 30
Dependent Claim
37 words
The process according to claim 24, including an intermediate zone positioned between the inner zone and the outer zone having a weight average molecular weight and melt flow rate intermediate the inner zone and the outer zone.
Claim 31
Dependent Claim
22 words
The process according to claim 24, wherein the inner zone has a high birefringence, and the outer zone has a low birefringence.
Claim 32
Dependent Claim
50 words
The process according to claim 20, wherein the polypropylene containing material is extruded from an extruder and includes a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof, in an effective amount to control chain scission degradation of polymeric components of the hot extrudate in the extruder.
Claim 33
Dependent Claim
23 words
The process according to claim 20, wherein the at least one fiber or filament comprises a monocomponent or a bicomponent fiber or filament.
Claim 34
Dependent Claim
21 words
The process according to claim 20, wherein the polypropylene containing material has a molecular weight distribution of at least about 6.
Claim 35
Dependent Claim
21 words
The process according to claim 31, wherein the polypropylene containing material has a molecular weight distribution of at least about 7.
Claim 36
Dependent Claim
21 words
The process according to claim 32, wherein the polypropylene containing material has a molecular weight distribution of at least about 8.
Claim 37
Dependent Claim
186 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface, the polypropylene containing material including a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof, in an effective amount to control chain scission degradation of polymeric components in the hot extrudate in the extruder; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to obtain at least one polypropylene containing fiber or filament having a decreasing weight average molecular weight towards the surface of the at least one fiber or filament, and an increasing melt flow rate towards the surface of the at least one fiber or filament, the at least one fiber or filament comprising an inner zone including a weight average molecular weight of about 100,000 to 450,000 grams/mole, and an outer zone, including the surface of the at least one fiber or filament, including a weight average molecular weight of less than about 10,000 grams/mole.
Claim 38
Dependent Claim
186 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding polypropylene containing material having a molecular weight distribution of at least about 5.6 to form at least one hot extrudate having a surface, the polypropylene containing material including a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof, in an effective amount to control chain scission degradation of polymeric components in the hot extrudate in the extruder; and controlling quenching of the at least one hot extrudate in an oxygen containing atmosphere so as to obtain at least one polypropylene containing fiber or filament having a decreasing weight average molecular weight towards the surface of the at least one fiber or filament, and an increasing melt flow rate towards the surface of the at least one fiber or filament, the at least one fiber or filament comprising an inner zone including a weight average molecular weight of about 100,000 to 450,000 grams/mole, and an outer zone, including the surface of the at least one fiber or filament, including a weight average molecular weight of less than about 10,000 grams/mole.
Claim 39
Dependent Claim
21 words
The process according to claim 34, wherein the polypropylene containing material has a molecular weight distribution of at least about 6.
Claim 40
Dependent Claim
21 words
The process according to claim 35, wherein the polypropylene containing material has a molecular weight distribution of at least about 7.
Claim 41
Dependent Claim
21 words
The process according to claim 36, wherein the polypropylene containing material has a molecular weight distribution of at least about 8.
Claim 42
Dependent Claim
127 words
A process for preparing at least one polyolefin polymer containing fiber or filament, comprising: extruding a mixture comprising a broad molecular weight distribution polyolefin polymer and an effective amount of a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof under conditions to control oxidative chain scission degradation of polymeric components within the mixture prior to entering an oxygen containing atmosphere as a hot extrudate; and exposing the hot extrudate to an oxygen containing atmosphere under conditions to effect oxidative chain scission degradation of a surface of the hot extrudate to obtain at least one polyolefin polymer containing fiber or filament having a highly degraded surface zone of lower molecular weight, and lowered melting point compared to an inner zone of the hot extrudate.
Claim 43
Dependent Claim
127 words
A process for preparing at least one polyolefin polymer containing fiber or filament, comprising: extruding a mixture comprising a broad molecular weight distribution polyolefin polymer and an effective amount of a member selected from the group consisting of antioxidants, stabilizers, and mixtures thereof under conditions to control oxidative chain scission degradation of polymeric components within the mixture prior to entering an oxygen containing atmosphere as a hot extrudate; and exposing the hot extrudate to an oxygen containing atmosphere under conditions to effect oxidative chain scission degradation of a surface of the hot extrudate to obtain at least one polyolefin polymer containing fiber or filament having a highly degraded surface zone of lower molecular weight, and lowered melting point compared to an inner zone of the hot extrudate.
Claim 44
Dependent Claim
46 words
The process according to claim 38, comprising controlling quenching of the resulting partially degraded extrudate to obtain a fiber or filament having a degraded surface zone of lower molecular weight and lower melting point, and the inner zone having higher molecular weight and higher melting point.
Claim 45
Dependent Claim
22 words
The process according to claim 39, wherein the mixture contains polypropylene, and has a molecular weight distribution of at least about 5.5.
Claim 46
Dependent Claim
19 words
The process according to claim 40, wherein the mixture has a molecular weight distribution of at least about 5.6.
Claim 47
Dependent Claim
19 words
The process according to claim 41, wherein the mixture has a molecular weight distribution of at least about 6.
Claim 48
Dependent Claim
19 words
The process according to claim 42, wherein the mixture has a molecular weight distribution of at least about 7.
Claim 49
Dependent Claim
19 words
The process according to claim 43, wherein the mixture has a molecular weight distribution of at least about 8.
Claim 50
Dependent Claim
57 words
The process according to claim 38, wherein the exposing of the hot extrudate to an oxygen containing atmosphere so as to effect oxidative chain scission of the surface comprises maintaining the temperature of the at least one hot extrudate above about 250° C. for a period of time to obtain oxidative chain scission degradation of the surface.
Claim 51
Dependent Claim
19 words
The process according to claim 45, wherein the controlling quenching includes blocking an upper portion of a cross-blow quench.
Claim 52
Dependent Claim
22 words
The process according to claim 45, wherein the controlling quenching includes passing the at least one hot extrudate through a blocked zone.
Claim 53
Dependent Claim
17 words
The process according to claim 47, wherein the blocked zone is open to the oxygen containing atmosphere.
Claim 54
Dependent Claim
112 words
A process for preparing at least one fiber or filament comprising: extruding a broad molecular weight distribution polyolefin containing material at a temperature and an environment under conditions minimizing oxidative chain scission degradation of polymeric components within the extruder; exposing resulting hot extrudate to an oxygen containing atmosphere to permit oxygen diffusion into the hot extrudate to obtain oxidative chain scission degradation of a surface of the resulting hot extrudate; and quenching the resulting hot extrudate to obtain at least one fiber or filament having a surface zone of lower molecular weight and lowered melting point, and an inner zone having higher molecular weight and higher melting point than the surface zone.
Claim 55
Dependent Claim
112 words
A process for preparing at least one fiber or filament comprising: extruding a broad molecular weight distribution polyolefin containing material at a temperature and an environment under conditions minimizing oxidative chain scission degradation of polymeric components within the extruder; exposing resulting hot extrudate to an oxygen containing atmosphere to permit oxygen diffusion into the hot extrudate to obtain oxidative chain scission degradation of a surface of the resulting hot extrudate; and quenching the resulting hot extrudate to obtain at least one fiber or filament having a surface zone of lower molecular weight and lowered melting point, and an inner zone having higher molecular weight and higher melting point than the surface zone.
Claim 56
Dependent Claim
16 words
The process according to claim 49, wherein the inner zone is substantially not degraded by oxygen.
Claim 57
Dependent Claim
24 words
The process according to claim 49, wherein the polyolefin containing material contains polypropylene, and has a molecular weight distribution of at least about 5.5.
Claim 58
Dependent Claim
21 words
The process according to claim 51, wherein the polyolefin containing material has a molecular weight distribution of at least about 5.6.
Claim 59
Dependent Claim
21 words
The process according to claim 52, wherein the polyolefin containing material has a molecular weight distribution of at least about 6.
Claim 60
Dependent Claim
21 words
The process according to claim 53, wherein the polyolefin containing material has a molecular weight distribution of at least about 7.
Claim 61
Dependent Claim
21 words
The process according to claim 54, wherein the polyolefin containing material has a molecular weight distribution of at least about 8.
Claim 62
Dependent Claim
109 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding a broad molecular weight distribution polypropylene containing material at a temperature and an environment under conditions minimizing oxidative chain scission degradation of polymeric components within the extruder; exposing resulting hot extrudate to an oxygen containing atmosphere to permit oxygen diffusion into the hot extrudate to obtain oxidative chain scission degradation of a surface of the resulting hot extrudate; and quenching the resulting hot extrudate to obtain a degraded at least one polypropylene containing fiber or filament having an average melt flow rate increase of about 20-200% in comparison to corresponding substantially non-oxidized fiber or filament.
Claim 63
Dependent Claim
109 words
A process for preparing at least one polypropylene containing fiber or filament, comprising: extruding a broad molecular weight distribution polypropylene containing material at a temperature and an environment under conditions minimizing oxidative chain scission degradation of polymeric components within the extruder; exposing resulting hot extrudate to an oxygen containing atmosphere to permit oxygen diffusion into the hot extrudate to obtain oxidative chain scission degradation of a surface of the resulting hot extrudate; and quenching the resulting hot extrudate to obtain a degraded at least one polypropylene containing fiber or filament having an average melt flow rate increase of about 20-200% in comparison to corresponding substantially non-oxidized fiber or filament.
Claim 64
Dependent Claim
42 words
The process according to claim 56, wherein the at least one fiber or filament comprises a surface zone of lower molecular weight and lowered melting point, and an inner zone having higher molecular weight and higher melting point than the surface zone.
Claim 65
Dependent Claim
16 words
The process according to claim 51, wherein the inner zone is substantially not degraded by oxygen.
Claim 66
Dependent Claim
24 words
The process according to claim 56, wherein the polyolefin containing material contains polypropylene, and has a molecular weight distribution of at least about 5.5.
Claim 67
Dependent Claim
19 words
The process according to claim 59, wherein the polyolefin containing material has a molecular weight distribution of about 5.6.
Claim 68
Dependent Claim
21 words
The process according to claim 60, wherein the polyolefin containing material has a molecular weight distribution of at least about 6.
Claim 69
Dependent Claim
21 words
The process according to claim 61, wherein the polyolefin containing material has a molecular weight distribution of at least about 7.
Claim 70
Dependent Claim
21 words
The process according to claim 62, wherein the polyolefin containing material has a molecular weight distribution of at least about 8.
Claim 71
Dependent Claim
25 words
The process according to claim 8, wherein the controlling quenching includes immediately blocking an area as the at least one hot extrudate exits a spinnerette.
Claim 72
Dependent Claim
25 words
The process according to claim 15, wherein the controlling quenching includes immediately blocking an area as the at least one hot extrudate exits a spinnerette.
Claim 73
Dependent Claim
26 words
The process according to claim 20, wherein the at least one fiber or filament comprises an inner zone having a melt flow rate of 5-25 dg/min.
Claim 74
Dependent Claim
27 words
The process according to claim 20, wherein the at least one fiber or filament comprises an outer zone having a melt flow rate of about 25-1000 dg/min.
Claim 75
Dependent Claim
19 words
The process according to claim 49, wherein the resulting hot extrudate is immediately exposed to an oxygen containing atmosphere.
Claim 76
Dependent Claim
19 words
The process according to claim 56, wherein the resulting hot extrudate is immediately exposed to an oxygen containing atmosphere.
Claim 77
Dependent Claim
42 words
The process according to claim 34, wherein the fiber or filament includes an intermediate zone positioned between the inner zone and the outer zone having a weight average molecular weight and melt flow rate intermediate the inner zone and the outer zone.
References Cited (Backward Citations)
US2335922A
Cited
US2715075A
Cited
US2715077A
Cited
US2715076A
Cited
GB738474A
Cited
LU34908A1
Cited
FR1142065A
Cited
US2985995A
Cited
US3428506A
Cited
US3516899A
Cited
US3364537A
Cited
US3509013A
Cited
US3533904A
Cited
US3663675A
Cited
US3484916A
Cited
US3616168A
Cited
US3505164A
Cited
US3597268A
Cited
US3693341A
Cited
US3862265A
Cited
US3807917A
Cited
US3907957A
Cited
US3898209A
Cited
US3907057A
Cited
US4134882A
Cited
US4195051A
Cited
US4115620A
Cited
US4193961A
Cited
US4303606A
Cited
US4259399A
Cited
US4251200A
Cited
US4347206A
Cited
US4438238A
Cited
US4480000A
Cited
US4511615A
Cited
US4500384A
Cited
GB2121423A
Cited
US4592943A
Cited
US4717325A
Cited
US4578414A
Cited
US4634739A
Cited
US4680156A
Cited
US4632861A
Cited
US4626467A
Cited
US4828911A
Cited
US4874666A
Cited
US4770925A
Cited
EP0279511A2
Cited
US4804577A
Cited
US4842922A
Cited
US4830904A
Cited
US4840847A
Cited
US5009951A
Cited
US4883707A
Cited
US4909976A
Cited
US5066723A
Cited
JPH0392416A
Cited
EP0445536A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-06 | 1997-12-06 | 1998-06-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-06 | 2001-12-06 | 2002-06-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-06 | 2005-12-06 | 2006-06-07 | $7700.00 | Window Closed / Lapsed |