Polyethylene fibers and spunbonded fabric or web
Assignee: Dow Chemical Co
•
Filing: 1987-10-27
•
Granted: 1989-06-27
•
Expires: 2007-10-27
Abstract
Abstract Blends of high molecular weight linear polyethylene and low molecular weight linear polyethylene provide improved fiber-forming capabilities over that found with either polymer taken alone. Preferably at least one of the polymers used in the blend is a linear low density polyethylene, LLDPE, which is a linear polyethylene comprising ethylene copolymerized with an amount of a higher alpha-olefin which causes the density of the copolymer to be less than that of a homopolymer made using the same process and catalyst. The higher alpha-olefin can be at least one in the C 3 -C 12 range, preferably in the C 4 -C 8 range.
Inventors
- 👤 Stephen P. Krupp
- 👤 Edward N. Knickerbocker
- 👤 John O. Bieser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:19
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; B; B01; B01F; B01F33/00; B01F33/30; C08L23/08; C08L23/0807; C08L23/0815; D; D01; D01F; D01F6/00; D01F6/02; D01F6/04; D01F6/44; D01F6/46; D04; D04H; D04H3/00; D04H3/08; D04H3/16; C08L2205/00; C08L2205/02; C08L2205/025; Y; Y10; Y10S; Y10S264/00; Y10S264/26; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24826; Y10T442/00; Y10T442/60; Y10T442/681
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
132 words
A spunbonded fabric of web prepared from a blend of linear polyethylenes suitable for spunbonding at throughput rates of about 1.0 to about 1.2 grams/minute/hole, at linear spinning velocities of at least about 3500 meters per minute, to produce fiber sizes of less than 3.0 denier/filament, said blend comprising high molecular weight linear polyethylenes having a MFR value within the range between about 0.5 to 25 g/10 min. and a density above about 0.91 g/cm 3 , and low molecular weight linear polyethylene having a MFR value within the range of greater than 25 to about 300 g/10 min. and a density above about 0.91 g/cm 3 , said spunbonded fabric or web being prepared therefrom and exhibiting improved properties over that similarly prepared from the high molecular weight linear polyethylene alone.
Claim 2
Dependent Claim
132 words
A spunbonded fabric of web prepared from a blend of linear polyethylenes suitable for spunbonding at throughput rates of about 1.0 to about 1.2 grams/minute/hole, at linear spinning velocities of at least about 3500 meters per minute, to produce fiber sizes of less than 3.0 denier/filament, said blend comprising high molecular weight linear polyethylenes having a MFR value within the range between about 0.5 to 25 g/10 min. and a density above about 0.91 g/cm 3 , and low molecular weight linear polyethylene having a MFR value within the range of greater than 25 to about 300 g/10 min. and a density above about 0.91 g/cm 3 , said spunbonded fabric or web being prepared therefrom and exhibiting improved properties over that similarly prepared from the high molecular weight linear polyethylene alone.
Claim 3
Dependent Claim
57 words
The spunbonded fabric or web of claim 1 wherein the ratio of the high molecular weight linear polyethylene and low molecular weight linear polyethylene is sufficient to provide a blend having a MFR value in the range of about 25 to about 100 g/10 min. and a density of about 0.91 to about 0.96 g/cm 3 .
Claim 4
Dependent Claim
73 words
The spunbonded fabric or web of claim 1 wherein the high molecular weight linear polyethylene is LLDPE having a MFR value within the range between about 0.5 and 25 g/10 min., the low molecular weight linear polyethylene is LLDPE having a MFR value within the range of greater than to about 300 g/10 min., and wherein the blend has a MFR value in the range of about 25 to about 100 g/10 min.
Claim 5
Dependent Claim
28 words
The spunbonded fabric or web of claim 1 wherein each of the linear polyethylenes comprises a copolymer of ethylene with at least one C 3 -C 12 olefin.
Claim 6
Dependent Claim
28 words
The spunbonded fabric or web of claim 1 wherein each of the linear polyethylenes comprises a copolymer of ethylene with at least one C 4 -C 8 olefin.
Claim 7
Dependent Claim
23 words
The spunbonded fabric or web of claim 1 wherein at least one of the linear polyethylenes is a copolymer of ethylene and octene.
Claim 8
Dependent Claim
21 words
The spunbonded fabric or web of claim 1 wherein each of the linear polyethylenes is a copolymer of ethylene and octene.
Claim 9
Dependent Claim
121 words
In a process wherein molten LLDPE polymer is spunbonded to make a web or fabric, the improvement wherein the LLDPE comprises a blend of high molecular weight LLDPE and low molecular weight LLDPE spunbondable at a throughput rate of about 1.0 to about 1.2 grams/minute/hole, using a linear spinning velcocity of at least about 3500 meters per minute, and at a fiber size of smaller than 3 denier/filament, thereby producing a web or fabric having improved strength over that obtained by similarly spunbonding a web or fabric of the high molecular weight LLDPE alone, wherein said high molecular weight LLDPE has a MFR below 25 g/10 min., and wherein said low molecular weight LLDPE has a MFR above 25 g/10 min.
Claim 10
Dependent Claim
121 words
In a process wherein molten LLDPE polymer is spunbonded to make a web or fabric, the improvement wherein the LLDPE comprises a blend of high molecular weight LLDPE and low molecular weight LLDPE spunbondable at a throughput rate of about 1.0 to about 1.2 grams/minute/hole, using a linear spinning velcocity of at least about 3500 meters per minute, and at a fiber size of smaller than 3 denier/filament, thereby producing a web or fabric having improved strength over that obtained by similarly spunbonding a web or fabric of the high molecular weight LLDPE alone, wherein said high molecular weight LLDPE has a MFR below 25 g/10 min., and wherein said low molecular weight LLDPE has a MFR above 25 g/10 min.
Claim 11
Dependent Claim
30 words
The process of claim 8 wherein the high molecular weight LLDPE has a MFR below about 20 and the low molecular weight LLDPE has a MFR greater than about 40.
References Cited (Backward Citations)
US4076698A
Cited
US4076698B1
Cited
US4429079A
Cited
JPS5759943A
Cited
US4438238A
Cited
US4584347A
Cited
EP0154197A2
Cited
US4578414A
Cited
US4644045A
Cited
US4705829A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-26 | 1992-12-26 | 1993-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-26 | 1996-12-26 | 1997-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-26 | 2000-12-26 | 2001-06-27 | $7700.00 | Window Closed / Lapsed |