Compound semiconductor single crystals and the method for making the crystals, and semiconductor devices employing the crystals
Assignee: Eneos Corp
•
Filing: 1989-02-23
•
Granted: 1993-06-15
•
Expires: 2009-02-23
Abstract
Abstract PCT No. PCT/JP89/00183 Sec. 371 Date Oct. 20, 1989 Sec. 102(e) Date Oct. 20, 1989 PCT Filed Feb. 23, 1989 PCT Pub. No. WO89/08158 PCT Pub. Date Sep. 8, 1989.According to the present invention, an ingot of the compound semiconductor single crystal grown by the LEC method or the HB method, or a block/blocks or wafers cut from the ingot is subjected to a high temperature annealing at any temperature in the range not less than 1100 DEG C. and not more than the melting point, and then the ingot is cooled at the cooling rate of 15 DEG DIFFERENCE 30 DEG C./min. This method ensures that the egg-shape etch pit density revealed in the single crystal by AB etchant is 5x104 cm-2 or less, preferably 5x103 cm-2 or less. As a result, the device employing the single crystal as its substrate can be possessed of homogeneous property.
Inventors
- 👤 Haruhito Shimakura
- 👤 Gaku Kano
- 👤 Hiromasa Yamamoto
- 👤 Osamu Oda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:14
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/40; C30B29/42; C30B33/00; Y; Y10; Y10S; Y10S148/00; Y10S148/084; Y10T; Y10T428/00; Y10T428/21; Y10T428/24; Y10T428/24479; Y10T428/24612; Y10T428/31
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
94 words
A method for producing a compound semiconductor single crystal grown from gallium arsenide having a melting point of 1238° C. by a liquid encapsulated Czochralski method having an egg-shaped etch pit density revealed in said crystal by an AB etchant of less than 5×10 4 cm -2 , wherein said grown compound semiconductor single crystal is heat-treated at a temperature in a range between not less than 1100° C. and not more than the melting point and then said crystal is cooled at a cooling rate between 15° C. to 30° C. per minute.
Claim 2
Independent Claim
94 words
A method for producing a compound semiconductor single crystal grown from gallium arsenide having a melting point of 1238° C. by a liquid encapsulated Czochralski method having an egg-shaped etch pit density revealed in said crystal by an AB etchant of less than 5×10 4 cm -2 , wherein said grown compound semiconductor single crystal is heat-treated at a temperature in a range between not less than 1100° C. and not more than the melting point and then said crystal is cooled at a cooling rate between 15° C. to 30° C. per minute.
Claim 3
Dependent Claim
29 words
The method for producing a compound semiconductor single crystal according to claim 1, wherein said single crystal is formed in an ingot or a block/blocks cut from the ingot.
Claim 4
Dependent Claim
22 words
The method for producing a compound semiconductor single crystal according to claim 1, wherein said single crystal is formed in a wafer.
Claim 5
Dependent Claim
37 words
A compound semiconductor gallium arsenide single crystal grown by the liquid encapsulated Czochralski method having an egg-shaped etch pit density revealed in said single crystal by an AB etchant of less than 5×10 4 cm -2 .
Claim 6
Dependent Claim
37 words
A compound semiconductor gallium arsenide single crystal grown by the liquid encapsulated Czochralski method having an egg-shaped etch pit density revealed in said single crystal by an AB etchant of less than 5×10 4 cm -2 .
Claim 7
Dependent Claim
22 words
A semiconductor device wherein a wafer of said single crystal according to claim 4 is used as a substrate for said device.
Claim 8
Dependent Claim
22 words
The compound semiconductor single crystal according to claim 4, wherein the egg-shape etch pit density is 5×10 3 cm -2 or less.
Claim 9
Dependent Claim
22 words
A semiconductor device wherein a wafer of said single crystal according to claim 6 is used as a substrate for said device.
Claim 10
Independent Claim
101 words
A method of heat treating a gallium arsenide semiconductor single crystal grown by a liquid-encapsulated Czochralski method having an egg-shaped etch pit density revealed in said single crystal by an AB etchant of less than 5×10 4 cm -2 to reduce the egg-shaped etch pit density, comprising: subjecting said gallium arsenide single crystal to an annealing heat treatment in a temperature range of not less than 1100° C. and not more than its melting point of 1238° C.; and cooling said crystal at a cooling rate between 15° C. and 30° C. per minute for reducing the density of the pits.
Claim 11
Independent Claim
101 words
A method of heat treating a gallium arsenide semiconductor single crystal grown by a liquid-encapsulated Czochralski method having an egg-shaped etch pit density revealed in said single crystal by an AB etchant of less than 5×10 4 cm -2 to reduce the egg-shaped etch pit density, comprising: subjecting said gallium arsenide single crystal to an annealing heat treatment in a temperature range of not less than 1100° C. and not more than its melting point of 1238° C.; and cooling said crystal at a cooling rate between 15° C. and 30° C. per minute for reducing the density of the pits.
Claim 12
Dependent Claim
25 words
The method of claim 8, wherein the annealing heat treatment is at a temperature just below the melting point of 1238° C. of said crystal.
Claim 13
Dependent Claim
33 words
The method of claim 8, wherein the crystal is a cut piece of the ingot and the lower temperature is 138° C. lower than the melting point of 1238° C. of the crystal.
Claim 14
Dependent Claim
21 words
The method of claim 8, including maintaining the temperature of said crystal between 1100° C. and 1235° C. for five hours.
Claim 15
Dependent Claim
21 words
The method of claim 9, including maintaining the temperature of said crystal between 1100° C. and 1235° C. for five hours.
References Cited (Backward Citations)
US3737282A
Cited
US4016006A
Cited
JPS5628375A
Cited
US4885257A
Cited
JPS6055612A
Cited
JPS60118687A
Cited
US4897141A
Cited
US4713354A
Cited
JPS61222999A
Cited
US4750969A
Cited
US5051376A
Cited
US4889493A
Cited
US4851358A
Cited
US4929564A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-06-14 | 1996-12-14 | 1997-06-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-06-14 | 2000-12-14 | 2001-06-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-06-14 | 2004-12-14 | 2005-06-15 | $7700.00 | Window Closed / Lapsed |