Method of aligning and mounting solder balls to a substrate
Assignee: International Business Machines Corp
•
Filing: 1991-04-24
•
Granted: 1992-06-02
•
Expires: 2011-04-24
Abstract
Abstract A process for fabricating a plurality of solder joints from a low melting point solder paste and high melting point solder balls is described. An abbreviated process flow is as follows: First, the solder balls are placed into cavities in an alignment boat, a vacuum is initiated to hold the boat and solder balls in place. Second, an amount of solder paste is applied directly onto the solder balls in the boat. Third, an alignment plate is placed over the alignment boat to provide a means of roughly aligning the solder ball/solder paste combination to the substrate. Fourth, the substrate is placed through the alignment plate on top of the solder balls in the boat. Pressure is applied to wet the solder paste to the conductive pads on the substrate. Finally, the substrate and alignment boat assembly is processed through a furnace for solder paste reflow. No expensive alignment tools are necessary as the substrate can at least partially realign itself to the array of solder balls during reflow because of the surface tension exerted by the molten solder paste as it wets the entirety of each conductive pad on the substrate.
Inventors
- 👤 Carol Braun
- 👤 George C. Correia
- 👤 Sheila Konecke-Lease
- 👤 Richard W. Cummings
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 12:58
CPC Classifications
H; H10; H10P; H10P72/00; H10P72/04; H10P72/0444; B; B23; B23K; B23K1/00; B23K1/20; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3465; H05K3/3478; H10W; H10W70/00; H10W70/099; B23K2101/00; B23K2101/36; B23K2101/40; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/035; H05K2201/10; H05K2201/10613; H05K2201/10621; H05K2201/10734; H05K2203/00; H05K2203/01; H05K2203/0104; H05K2203/0113; H05K2203/0195; H05K2203/03; H05K2203/0338; H05K2203/04; H05K2203/041; H05K2203/043; H05K2203/08; H05K2203/082; H05K3/3485; H10W72/00; H10W72/01; H10W72/012; H10W72/01204; H10W72/01221; H10W72/01225
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
192 words
A method for fabricating a plurality of solder structures from a plurality of solder paste and solder ball combinations to a plurality of conductive pads on one surface of a substrate comprising the steps of: securing a plurality of solder balls into a set of aligning cavities in an aligning means, said cavities arranged in a pattern corresponding to a pattern of said conductive pads on said substrate; applying an amount of solder paste on each of said solder balls to form a plurality of solder paste pads the solder paste having a lower melting temperature than the solder balls; placing a substrate in rough alignment to said solder paste pads so that at least part of each of said solder paste pads will wet a corresponding conductive pad on said substrate; pressing said substrate into said solder paste with a minimum force; and, reflowing said solder paste to allow the surface tension generated by said solder paste to help bring said substrate into alignment with said solder balls; whereby said plurality of solder balls are fixed in place by said aligning means to maintain a desired spacing between the solder balls.
Claim 2
Independent Claim
192 words
A method for fabricating a plurality of solder structures from a plurality of solder paste and solder ball combinations to a plurality of conductive pads on one surface of a substrate comprising the steps of: securing a plurality of solder balls into a set of aligning cavities in an aligning means, said cavities arranged in a pattern corresponding to a pattern of said conductive pads on said substrate; applying an amount of solder paste on each of said solder balls to form a plurality of solder paste pads the solder paste having a lower melting temperature than the solder balls; placing a substrate in rough alignment to said solder paste pads so that at least part of each of said solder paste pads will wet a corresponding conductive pad on said substrate; pressing said substrate into said solder paste with a minimum force; and, reflowing said solder paste to allow the surface tension generated by said solder paste to help bring said substrate into alignment with said solder balls; whereby said plurality of solder balls are fixed in place by said aligning means to maintain a desired spacing between the solder balls.
Claim 3
Dependent Claim
55 words
The method as recited in claim 1 wherein each of said aligning cavities has a diameter slightly larger than said solder ball and is connected to a vacuum conduit having a diameter smaller than said solder ball at said aligning cavity; and, a vacuum is applied to said vacuum conduit to secure said solder ball.
Claim 4
Dependent Claim
22 words
The method as recited in claim 1 wherein said solder paste pads melt at a substantially lower temperature than said solder balls.
Claim 5
Dependent Claim
33 words
The method as recited in claim 3 wherein said solder paste is a eutectic composition of 37/63 weight percent Pb/Sn solder and said solder ball is comprised of 90/10 weight percent Pb/Sn solder.
Claim 6
Dependent Claim
47 words
The method as recited in claim 4 wherein said solder paste is heated for a period on the order of 13 minutes with a dwell time in the range of 1 to 4 minutes over 183° C. and a peak temperature of no more than 220° C.
Claim 7
Dependent Claim
38 words
The method as recited in claim 1 wherein a solder paste screen having a plurality of holes for responding to the position of said solder balls in said alignment cavities is used to apply said solder paste pads.
Claim 8
Dependent Claim
71 words
The method as recited in claim 1 wherein said alignment means is a precisely machined graphhite boat having a plurality of aligning cavities machined therein in one surface in a pattern corresponding to a pattern of said conductive pads on said substrate, said alignment cavities having a diameter only slightly larger than the diameter of said solder balls and a depth only slightly smaller than the diameter of said solder balls.
Claim 9
Dependent Claim
51 words
The method as recited in claim 1 wherein said aligning cavities on said aligning means are arranged in a pattern corresponding to a plurality of substrates, a plurality of substrates are placed in rough alignment to said solder paste pads, and each of said substrates is pressed into said solder paste.
Claim 10
Dependent Claim
30 words
The method as recited in claim 1 wherein said substrate is a metallized ceramic substrate with at least one semiconductor chip bonded on a surface opposite to said solder balls.
Claim 11
Independent Claim
184 words
An apparatus for fabricating a plurality of solder structures from a plurality of solder paste pads and solder ball combinations to a plurality of conductive pads on one surface of a substrate comprising: a first aligning means for securing and fixing in place said plurality of solder balls in a pattern corresponding to a pattern of said conductive pads on said substrate; a means for applying a precise amount of solder paste on each of said secured solder balls to form said plurality of solder paste pads, the solder paste having a lower melting temperature than the solder balls; a second aligning means for placing said substrate in rough alignment to said solder paste so that at least part of each of said solder paste pads on its secured solder ball will wet a corresponding conductive pad on said substrate; and, pressure means to urge said substrate into said solder paste with a minimum force; whereby when said solder paste pads are reflowed, the surface tension generated by said molten solder paste helps bring said substrate into alignment with said plurality of solder balls.
Claim 12
Independent Claim
184 words
An apparatus for fabricating a plurality of solder structures from a plurality of solder paste pads and solder ball combinations to a plurality of conductive pads on one surface of a substrate comprising: a first aligning means for securing and fixing in place said plurality of solder balls in a pattern corresponding to a pattern of said conductive pads on said substrate; a means for applying a precise amount of solder paste on each of said secured solder balls to form said plurality of solder paste pads, the solder paste having a lower melting temperature than the solder balls; a second aligning means for placing said substrate in rough alignment to said solder paste so that at least part of each of said solder paste pads on its secured solder ball will wet a corresponding conductive pad on said substrate; and, pressure means to urge said substrate into said solder paste with a minimum force; whereby when said solder paste pads are reflowed, the surface tension generated by said molten solder paste helps bring said substrate into alignment with said plurality of solder balls.
Claim 13
Dependent Claim
22 words
The apparatus as recited in claim 10 wherein said solder paste pads melts at a substantially lower temperature than said solder balls.
Claim 14
Dependent Claim
33 words
The apparatus as recited in claim 11, wherein said solder paste is a eutectic composition of 37/63 weight percent Pb/Sn solder and said solder ball is comprised of 90/10 weight percent Pb/Sn solder.
Claim 15
Dependent Claim
47 words
The apparatus as recited in claim 12 wherein said solder paste is heated for a period in the order of 13 minutes with a dwell time in the range of 1 to 4 minutes over 183° C. and a peak temperature of no more than 220° C.
Claim 16
Dependent Claim
37 words
The apparatus as recited in claim 10 wherein a solder paste screen having a plurality of holes corresponding to the position of said solder balls in said alignment cavities is used to apply said solder paste pads.
Claim 17
Dependent Claim
71 words
The apparatus as recited in claim 10 wherein said alignment means is a precisely machine graphite boat having a plurality of aligning cavities machined therein in one surface in a pattern corresponding to a pattern of said conductive pads on said substrate, said alignment cavities having a diameter only slightly larger than the diameter of said solder balls and a depth only slightly smaller than the diameter of said solder balls.
Claim 18
Dependent Claim
51 words
The apparatus as recited in claim 10 wherein said aligning cavities on said aligning means are arranged in a pattern corresponding to a plurality of substrates, a plurality of substrates are placed in rough alignment to said solder paste pads, and each of said substrates is pressed into said solder paste.
Claim 19
Dependent Claim
29 words
The apparatus as recited in claim 10 where said substrate is a metallized ceramic substrate with at least one semiconductor chip bonded to a surface opposite said solder balls.
References Cited (Backward Citations)
US3871015A
Cited
US4067104A
Cited
US4565314A
Cited
JPS61242759A
Cited
US4836435A
Cited
US4722470A
Cited
US4739917A
Cited
US4752027A
Cited
US4759491A
Cited
US4831724A
Cited
EP0307591A2
Cited
US4871110A
Cited
US5022580A
Cited
JPH01256141A
Cited
US5024372A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-02 | 1995-12-02 | 1996-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-02 | 1999-12-02 | 2000-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-02 | 2003-12-02 | 2004-06-02 | $7700.00 | Window Closed / Lapsed |