Method for improving the electrical erase characteristics of floating gate memory cells by immediately depositing a protective polysilicon layer following growth of the tunnel or gate oxide

Claim 2

In a process for fabricating an array of floating gate memory devices which are erased by Fowler-Nordheim tunnelling of electrons from a floating gate to a silicon substrate, a method of improving the erase performance of said devices comprises the steps of: defining regions in said substrate for field oxide regions and a tunnel oxide region, wherein said tunnel oxide region is between said field oxide regions; thermally growing a tunnel oxide layer over said substrate in said tunnel oxide region; immediately depositing a first layer of polysilicon on said tunnel oxide layer to inhibit increased oxidation of said tunnel oxide layer within said tunnel oxide region adjacent to said field oxide regions; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said first polysilicon layer to form said floating gate of said device, thereby leaving said unexposed regions including a portion of said tunnel oxide layer and a portion of said first polysilicon layer that permanently remain over said substrate; after depositing said first polysilicon layer, forming source and drain regions within said substrate; and after depositing said masking layer, forming field oxide regions in said substrate.

Claim 3

The method of claim 1 further comprising the step of removing said masking layer.

Claim 4

The process in claim 2 further comprising, after said removing step, the step of depositing a second layer of polysilicon over said first polysilicon layer, making electrical contact thereto, wherein the floating gate of said devices are created.

Claim 5

The process of claim 3 wherein the thickness of said first polysilicon layer is greater than the thickness of said tunnel oxide and said first polysilicon layer is relatively thin when compared to said second polysilicon layer.

Claim 6

The method of claim 4 wherein said first polysilicon layer has a thickness in the range of about 200-700 Å.

Claim 7

The method of claim 5 wherein said first and second polysilicon layers form one continuous layer of polysilicon.

Claim 8

The method of claim 1 wherein said masking layer comprises silicon nitride.

Claim 9

The method of claim 6 wherein said source and drain regions are formed by ion implantation self-aligned to said gate.

Claim 10

The method of claim 8 wherein said tunnel oxide has a thickness in the range of approximately 80-200 Å.

Claim 11

The method of claim 2 further comprising, after said removing step, the step of depositing a second layer of polysilicon over said first polysilicon layer, such that one continuous polysilicon layer is formed creating the floating gate of said memory device.

Claim 12

The process of claim 10 wherein the thickness of said first polysilicon layer is greater than the thickness of said tunnel oxide and said first polysilicon layer is relatively thin when compared to said second layer polysilicon layer.

Claim 13

The method of claim 10 wherein said first polysilicon layer has a thickness in the range of about of 200-700 Å.

Claim 14

In a process for fabricating a field-effect device in a silicon substrate, a method of reducing the defect density in a thin gate oxide layer comprising the steps of: defining regions in said substrate for field oxide regions and a gate oxide region, wherein said gate oxide region is between said field oxide regions; thermally growing a gate oxide layer over said substrate in said gate oxide region; immediately capping said gate oxide layer with a first layer of polysilicon to protect it from contaminants which adversely affect said defect density of said gate oxide layer; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said first polysilicon layer, thereby leaving said unexposed regions including a portion of said gate oxide layer and a portion of said first polysilicon layer that permanently remain over said substrate; after depositing said masking layer, forming field oxide regions in said substrate; after depositing said first polysilicon layer, forming source and drain regions within said substrate; and removing said masking layer.

Claim 15

In a process for fabricating a field-effect device in a silicon substrate, a method of reducing the defect density in a thin gate oxide layer comprising the steps of: defining regions in said substrate for field oxide regions and a gate oxide region, wherein said gate oxide region is between said field oxide regions; thermally growing a gate oxide layer over said substrate in said gate oxide region; immediately capping said gate oxide layer with a first layer of polysilicon to protect it from contaminants which adversely affect said defect density of said gate oxide layer; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said first polysilicon layer, thereby leaving said unexposed regions including a portion of said gate oxide layer and a portion of said first polysilicon layer that permanently remain over said substrate; after depositing said masking layer, forming field oxide regions in said substrate; after depositing said first polysilicon layer, forming source and drain regions within said substrate; and removing said masking layer.

Claim 16

The method of claim 13 further comprising the step of depositing a second layer of polysilicon over said first polysilicon layer, making electrical contact thereto.

Claim 17

The method of claim 13 wherein the thickness of said first polysilicon layer is greater than the thickness of said gate oxide and said first polysilicon layer is relatively thin when compared to said second polysilicon layer.

Claim 18

The method of claim 15 wherein said first polysilicon layer has a thickness in the range of about 200-700 Å.

Claim 19

The method of claim 16 wherein said first and second polysilicon layers form one continuous layer of polysilicon.

Claim 20

The method of claim 17 wherein said masking layer comprises silicon nitride.

Claim 21

The method of claim 18 wherein said source and drain regions are formed by ion implantation self-aligned to said gate.

Claim 22

The method of claim 19 wherein said gate oxide has a thickness in the range of approximately 80-200 Å.

Claim 23

In a process for fabricating an array of floating gate memory devices which are erased by Fowler-Nordheim tunnelling of electrons from a floating gate to a silicon substrate, a method of improving the erase performance of said devices comprises the steps of: defining regions in said substrate for field oxide regions and a tunnel oxide region, wherein said tunnel oxide region is between said field oxide regions; thermally growing a tunnel oxide layer over said substrate in said tunnel oxide region; immediately depositing a first layer of polysilicon to inhibit increased oxidation in those areas of said tunnel oxide region adjacent to said field oxide regions, the thickness of said first polysilicon layer being greater than the thickness of said tunnel oxide layer, said first polysilicon layer being relatively thin when compared to said second polysilicon layer, said first polysilicon layer having a thickness in the range of about 200-700 Å; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said first polysilicon layer and the underlying tunnel oxide layer to form said floating gate of said device; forming source and drain regions within said substrate; forming field oxide regions in said substrate; removing said masking layer; and depositing a second layer of polysilicon over said first polysilicon layer, making electrical contact thereto, wherein the floating gate of said devices are created.

Claim 24

In a process for fabricating an array of floating gate memory devices which are erased by Fowler-Nordheim tunnelling of electrons from a floating gate to a silicon substrate, a method of improving the erase performance of said devices comprises the steps of: defining regions in said substrate for field oxide regions and a tunnel oxide region, wherein said tunnel oxide region is between said field oxide regions; thermally growing a tunnel oxide layer over said substrate in said tunnel oxide region; immediately depositing a first layer of polysilicon to inhibit increased oxidation in those areas of said tunnel oxide region adjacent to said field oxide regions, the thickness of said first polysilicon layer being greater than the thickness of said tunnel oxide layer, said first polysilicon layer being relatively thin when compared to said second polysilicon layer, said first polysilicon layer having a thickness in the range of about 200-700 Å; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said first polysilicon layer and the underlying tunnel oxide layer to form said floating gate of said device; forming source and drain regions within said substrate; forming field oxide regions in said substrate; removing said masking layer; and depositing a second layer of polysilicon over said first polysilicon layer, making electrical contact thereto, wherein the floating gate of said devices are created.

Claim 25

The method of claim 21 wherein said first and second polysilicon layers form one continuous layer of polysilicon.

Claim 26

The method of claim 21 wherein said masking layer comprises silicon nitride.

Claim 27

The method of claim 22 wherein said source and drain regions are formed by ion implantation self-aligned to said gate.

Claim 28

The method of claim 24 wherein said tunnel oxide has a thickness in the range of approximately 80-200 Å.

Claim 29

A process for fabricating on a silicon substrate a floating gate memory device having enhanced erase performance characteristics, said floating gate device being of the type which relies upon Fowler-Nordheim tunnelling of electrons from the floating gate to said substrate comprising the steps of: defining regions in said substrate for field oxide regions and a tunnel oxide region, wherein said tunnel oxide region is between said field oxide regions; growing a tunnel oxide layer over said substrate; immediately depositing a first layer of polysilicon over said tunnel oxide layer to inhibit increased oxidation in those areas of said tunnel oxide region adjacent to said field oxide regions, said first polysilicon layer being a thickness in the range of about 200-700 Å; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said polysilicon layer and the underlying tunnel oxide layer to form said floating gate of said device; forming field oxide regions in said substrate; forming source and drain regions in said substrate; removing said making layer; and after said removing step, depositing a second layer of polysilicon over said first polysilicon layer, such that one continuous polysilicon layer is formed creating the floating gate of said memory device.

Claim 30

A process for fabricating on a silicon substrate a floating gate memory device having enhanced erase performance characteristics, said floating gate device being of the type which relies upon Fowler-Nordheim tunnelling of electrons from the floating gate to said substrate comprising the steps of: defining regions in said substrate for field oxide regions and a tunnel oxide region, wherein said tunnel oxide region is between said field oxide regions; growing a tunnel oxide layer over said substrate; immediately depositing a first layer of polysilicon over said tunnel oxide layer to inhibit increased oxidation in those areas of said tunnel oxide region adjacent to said field oxide regions, said first polysilicon layer being a thickness in the range of about 200-700 Å; depositing a masking layer over said first polysilicon layer; patterning said masking layer to form exposed and unexposed regions of said first polysilicon layer; etching said exposed regions of said polysilicon layer and the underlying tunnel oxide layer to form said floating gate of said device; forming field oxide regions in said substrate; forming source and drain regions in said substrate; removing said making layer; and after said removing step, depositing a second layer of polysilicon over said first polysilicon layer, such that one continuous polysilicon layer is formed creating the floating gate of said memory device.

Claim 31

The process of claim 26 wherein the thickness of said first polysilicon layer is greater than the thickness of said tunnel oxide and said first polysilicon layer is relatively thin when compared to said second layer polysilicon layer.

Claim 32

In a process for fabricating field-effect devices in a silicon substrate, a method of reducing the defect density in thin gate oxides comprising the steps of: defining regions in said substrate for field oxide regions and a gate oxide region, wherein said gate oxide region is between said field oxide regions; thermally growing a gate oxide layer over said substrate in said gate oxide region; immediately capping said gate oxide layer with a first layer of polysilicon to protect it from contaminants which adversely affect said defect density of said gate oxide, the thickness of said first polysilicon layer being greater than the thickness of said gate oxide layer and said first polysilicon layer being relatively thin when compared to said second polysilicon layer, said first polysilicon layer having a thickness in the range of about 200-700 Å; forming source and drain regions within said substrate; and depositing a second layer of polysilicon over said first polysilicon layer, making electrical contact thereto.

Claim 33

In a process for fabricating field-effect devices in a silicon substrate, a method of reducing the defect density in thin gate oxides comprising the steps of: defining regions in said substrate for field oxide regions and a gate oxide region, wherein said gate oxide region is between said field oxide regions; thermally growing a gate oxide layer over said substrate in said gate oxide region; immediately capping said gate oxide layer with a first layer of polysilicon to protect it from contaminants which adversely affect said defect density of said gate oxide, the thickness of said first polysilicon layer being greater than the thickness of said gate oxide layer and said first polysilicon layer being relatively thin when compared to said second polysilicon layer, said first polysilicon layer having a thickness in the range of about 200-700 Å; forming source and drain regions within said substrate; and depositing a second layer of polysilicon over said first polysilicon layer, making electrical contact thereto.

Claim 34

The method of claim 28 wherein said first and second polysilicon layers form one continuous layer of polysilicon.

Claim 35

The method of claim 29 wherein said masking layer comprises silicon nitride.

Claim 36

The method of claim 30 wherein said source and drain regions are formed by ion implantation self-aligned to said gate.

Claim 37

The method of claim 31 wherein said gate oxide has a thickness in the range of approximately 80-200 Å.