Semiconductor field oxidation process
Assignee: Intel Corp
•
Filing: 1990-11-19
•
Granted: 1992-02-25
•
Expires: 2010-11-19
Abstract
Abstract Front end processing for a CMOS substrate resulting in the formation of n-wells, p-wells, channel stops and field oxide regions. Both the n-type and p-type dopant are implanted through silicon nitride members with one type dopant being first blocked by a first layer of photoresist and the second dopant by a second layer of photoresist. The field oxide regions are grown after the first dopant is implanted. Relatively low level ion implantation is used and additional threshold adjusting implants are not needed.
Inventors
- 👤 Mark T. Bohr
- 👤 Lawrence N. Brigham, Jr.
- 👤 Shahab Hossaini
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:46
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/10; H10W10/13; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0191; H10D84/02; H10D84/03; H10D84/038; H10P; H10P30/00; H10P30/20; H10P30/22; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/0126; H10W10/0127; H10D84/80; H10D84/82; H10D84/83; H10D84/85; H10D84/859
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
257 words
A process for forming field oxide regions and channel stops on a silicon substrate, comprising the steps of: forming a first and a second spaced-apart silicon nitride members on said substrate thereby defining an isolation region between said spaced-apart silicon nitride members; forming a first photoresist layer over said first member, said first photoresist layer extending on to and covering a first portion of said isolation region adjacent to said first silicon nitride member, a second portion of said isolation region adjacent to said second silicon nitride member being free of said first photoresist layer; subjecting said substrate to a first ion implantation step with a first conductivity dopant so as to implant ions of said first conductivity type into said substrate in said second portion of said isolation region and into said substrate beneath said second silicon nitride member; heating said substrate in a first heating step so as to form a field oxide region at said isolation region; forming a second photoresist layer generally over said second silicon nitride member and said second portion of said isolation region, said first silicon nitride member and said first portion of said isolation region being substantially free of said first and second layer of photoresist; subjecting said substrate to a second ion implantation step with a second conductivity type dopant to implant ions of said second conductivity type into said substrate beneath said first silicon nitride member and said first portion of said isolation region, said second ion implantation step being carried out after said first heating step.
Claim 2
Dependent Claim
257 words
A process for forming field oxide regions and channel stops on a silicon substrate, comprising the steps of: forming a first and a second spaced-apart silicon nitride members on said substrate thereby defining an isolation region between said spaced-apart silicon nitride members; forming a first photoresist layer over said first member, said first photoresist layer extending on to and covering a first portion of said isolation region adjacent to said first silicon nitride member, a second portion of said isolation region adjacent to said second silicon nitride member being free of said first photoresist layer; subjecting said substrate to a first ion implantation step with a first conductivity dopant so as to implant ions of said first conductivity type into said substrate in said second portion of said isolation region and into said substrate beneath said second silicon nitride member; heating said substrate in a first heating step so as to form a field oxide region at said isolation region; forming a second photoresist layer generally over said second silicon nitride member and said second portion of said isolation region, said first silicon nitride member and said first portion of said isolation region being substantially free of said first and second layer of photoresist; subjecting said substrate to a second ion implantation step with a second conductivity type dopant to implant ions of said second conductivity type into said substrate beneath said first silicon nitride member and said first portion of said isolation region, said second ion implantation step being carried out after said first heating step.
Claim 3
Dependent Claim
34 words
The process defined by claim 1 wherein said first heating step forms a well of a first conductivity type generally below said second silicon nitride member, said well extending beneath said field oxide region.
Claim 4
Dependent Claim
35 words
The process defined by claim 2 including a second heating step after said second ion implantation step thereby forming a second well of a second conductivity type dopant generally beneath said first silicon nitride member.
Claim 5
Dependent Claim
27 words
The process defined by claim 3 including the step of forming a silicon dioxide layer on said substrate prior to the formation of said silicon nitride members.
Claim 6
Dependent Claim
17 words
The process defined by claim 4 wherein said first ion implantation step comprises the implantation of phosphorus.
Claim 7
Dependent Claim
17 words
The process defined by claim 5 wherein said second ion implantation step comprises the implantation of boron.
Claim 8
Dependent Claim
306 words
The process for forming field oxide isolation regions with underlying channel stops on a silicon substrate, comprising the steps of: forming a first insulative layer on said substrate; forming a silicon nitride layer on said substrate; forming first and second spaced-apart silicon nitride members on said first insulative layer defining an isolation region between said spaced-apart silicon nitride members; forming a first photoresist layer over said first silicon nitride member, said first photoresist layer extended on to and covering a first portion of said isolation region adjacent to said first silicon nitride member, a second portion of said isolation region adjacent to said second silicon nitride member being free of said first photoresist layer; subjecting said substrate to a first ion implantation step with a first conductivity type dopant at a first energy level, said first energy level being not sufficient to cause ions to penetrate said first photoresist layer however, said first energy level being sufficient to cause ions to penetrate said second silicon nitride member and underlying first insulation layer; heating said substrate in a first heating step so as to form a field oxide region at said isolation region; forming a second photoresist layer over said second silicon nitride member and said second portion of said isolation region, said first silicon nitride member and the portion of the field oxide overlying said first portion of said isolation region being substantially free of said first and second layer of photoresist; subjecting said substrate to a second ion implantation step with a second conductivity type dopant at a second energy level, said second energy level being not sufficient to cause ions to penetrate said second photoresist layer, however said second energy level being sufficient to cause ions to penetrate said first silicon nitride member and underlying first insulation layer; and the exposed field oxide region.
Claim 9
Dependent Claim
306 words
The process for forming field oxide isolation regions with underlying channel stops on a silicon substrate, comprising the steps of: forming a first insulative layer on said substrate; forming a silicon nitride layer on said substrate; forming first and second spaced-apart silicon nitride members on said first insulative layer defining an isolation region between said spaced-apart silicon nitride members; forming a first photoresist layer over said first silicon nitride member, said first photoresist layer extended on to and covering a first portion of said isolation region adjacent to said first silicon nitride member, a second portion of said isolation region adjacent to said second silicon nitride member being free of said first photoresist layer; subjecting said substrate to a first ion implantation step with a first conductivity type dopant at a first energy level, said first energy level being not sufficient to cause ions to penetrate said first photoresist layer however, said first energy level being sufficient to cause ions to penetrate said second silicon nitride member and underlying first insulation layer; heating said substrate in a first heating step so as to form a field oxide region at said isolation region; forming a second photoresist layer over said second silicon nitride member and said second portion of said isolation region, said first silicon nitride member and the portion of the field oxide overlying said first portion of said isolation region being substantially free of said first and second layer of photoresist; subjecting said substrate to a second ion implantation step with a second conductivity type dopant at a second energy level, said second energy level being not sufficient to cause ions to penetrate said second photoresist layer, however said second energy level being sufficient to cause ions to penetrate said first silicon nitride member and underlying first insulation layer; and the exposed field oxide region.
Claim 10
Dependent Claim
34 words
The process defined by claim 7 wherein said first heating step forms a well of a first conductivity type generally below said second silicon nitride member, said well extending beneath said field oxide region.
Claim 11
Dependent Claim
35 words
The process defined by claim 8 including a second heating step after said second ion implantation step thereby forming a second well of a second conductivity type dopant generally beneath said first silicon nitride member.
Claim 12
Dependent Claim
14 words
The process defined by claim 9 wherein said first insulation layer comprises silicon dioxide.
Claim 13
Dependent Claim
17 words
The process defined by claim 10 wherein said first ion implantation step comprises the implantation of phosphorus.
Claim 14
Dependent Claim
17 words
The process defined by claim 11 wherein said second ion implantation step comprises the implantation of boron.
References Cited (Backward Citations)
US3920481A
Cited
US4013484A
Cited
JPS54122982A
Cited
JPS5817656A
Cited
US4426766A
Cited
US4422885A
Cited
JPS6038868A
Cited
US4578859A
Cited
US4707455A
Cited
US4906595A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-24 | 1995-08-26 | 1996-02-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-24 | 1999-08-26 | 2000-02-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-24 | 2003-08-26 | 2004-02-25 | $7700.00 | Window Closed / Lapsed |