Photo-anodic oxide surface passivation for semiconductors
Assignee: Raytheon Co
•
Filing: 1990-02-02
•
Granted: 1992-02-04
•
Expires: 2010-02-02
Abstract
Abstract A method is disclosed for passivating infrared detector arrays 50. A wafer 48 of indium antimonide (InSb) is subjected an anodization process while being illuminated by a bright incandescent lamp 66. In one embodiment, the photo-anodized layer 72 is used in an array 50 to passivate implanted diode regions 76,78 on the front side thereof, while employing an antireflective coating 74 on the backside anodized surface 70.
Inventors
- 👤 Ichiro Kasai
- 👤 Richard M. Wallach
- 👤 Bonnie A. Baumgratz
- 👤 Michael E. Boyd
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:40
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6312; H10P14/6324; H10P14/69; H10P14/692; Y; Y10; Y10S; Y10S257/00; Y10S257/912
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
111 words
A method of forming an indium-antimonide (InSb) infrared detector for the 3-5 micron range having substantially zero flatband voltage characteristics without requiring gated structures, said method comprising: placing an indium-antimonide substrate in a container filled with an aqueous solution; applying a positive electrical potential to the substrate; and illuminating the substrate with light having a wavelength of 4000-8000 Å and a preselected intensity for a sufficient period of time to grow an anodization layer thereon of desired thickness; forming a plurality of p-n junctions in the substrate so that said anodization layer covers and passivates the junctions; said anodization layer providing such improved passivation characteristics that gated structures are not required.
Claim 2
Independent Claim
111 words
A method of forming an indium-antimonide (InSb) infrared detector for the 3-5 micron range having substantially zero flatband voltage characteristics without requiring gated structures, said method comprising: placing an indium-antimonide substrate in a container filled with an aqueous solution; applying a positive electrical potential to the substrate; and illuminating the substrate with light having a wavelength of 4000-8000 Å and a preselected intensity for a sufficient period of time to grow an anodization layer thereon of desired thickness; forming a plurality of p-n junctions in the substrate so that said anodization layer covers and passivates the junctions; said anodization layer providing such improved passivation characteristics that gated structures are not required.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein the solution is a base.
Claim 4
Dependent Claim
11 words
The method of claim 1 wherein the solution is potassium hydroxide.
Claim 5
Dependent Claim
28 words
The method of claim 1 wherein the container is made of quartz whereby the container wall does not contaminate the aqueous base solution and thereby the substrate surface.
Claim 6
Dependent Claim
18 words
The method of claim 1 wherein an opposite surface of the substrate is provided with an antireflective layer.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein said light which illuminates the substrate has an intensity of about 10 lumens per square inch.
Claim 8
Dependent Claim
21 words
The method of claim 1 wherein the light illuminating said substrate contains photon energy having a strength of 1.5-3.1 electron volts.
Claim 9
Dependent Claim
49 words
The method of claim 1 wherein said light that illuminates the substrate is generated by the steps of: a) energizing a bright incandescent lamp; b) using a lens to filter ultraviolet radiation from the lamp; and c) using an infrared filter to filter near infrared radiation from the lamp.
Claim 10
Dependent Claim
112 words
An indium-antimonide infrared detector for the 3-5 micron range having substantially zero flatband voltage characteristics without requiring gated structures, said detector being fabricated according to the steps of: placing an indium-antimonide substrate in a container filled with an aqueous solution; applying a positive electrical potential to the substrate; and illuminating the substrate with light having a wavelength of 4000-8000 Å and a preselected intensity for a sufficient period of time to grow an anodization layer thereon of desired thickness; forming a plurality of p-n junctions in the substrate so that said anodization layer covers and passivates the junctions; said anodization layer providing such improved passivation characteristics that gated structures are not required.
Claim 11
Dependent Claim
112 words
An indium-antimonide infrared detector for the 3-5 micron range having substantially zero flatband voltage characteristics without requiring gated structures, said detector being fabricated according to the steps of: placing an indium-antimonide substrate in a container filled with an aqueous solution; applying a positive electrical potential to the substrate; and illuminating the substrate with light having a wavelength of 4000-8000 Å and a preselected intensity for a sufficient period of time to grow an anodization layer thereon of desired thickness; forming a plurality of p-n junctions in the substrate so that said anodization layer covers and passivates the junctions; said anodization layer providing such improved passivation characteristics that gated structures are not required.
Claim 12
Dependent Claim
22 words
The detector of claim 9 wherein said light which illuminates the substrate has an intensity of about 10 lumens per square inch.
Claim 13
Dependent Claim
21 words
The detector of claim 9 wherein the light illuminating said substrate contains photon energy having a strength of 1.5-3.1 electron volts.
Claim 14
Dependent Claim
49 words
The detector of claim 9 wherein said light that illuminates the substrate is generated by the steps of: a) energizing a bright incandescent lamp; b) using a lens to filter ultraviolet radiation from the lamp; and c) using an infrared filter to filter near infrared radiation from the lamp.
References Cited (Backward Citations)
US3217379A
Cited
US3554818A
Cited
US3977018A
Cited
US3882000A
Cited
US3982265A
Cited
US4119993A
Cited
US4157610A
Cited
US4297176A
Cited
US4502204A
Cited
US4507181A
Cited
US4569728A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-03 | 1995-08-05 | 1996-02-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-03 | 1999-08-05 | 2000-02-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-03 | 2003-08-05 | 2004-02-04 | $7700.00 | Window Closed / Lapsed |