Methods for forming macrocomposite bodies and macrocomposite bodies produced thereby
Assignee: Lanxide Technology Co LP
•
Filing: 1988-11-10
•
Granted: 1991-08-20
•
Expires: 2008-11-10
Abstract
Abstract The present invention relates to the formation of a macrocomposite body by spontaneously infiltrating a permeable mass of filler material or a preform with molten matrix metal and bonding the spontaneously infiltrated material to at least one second material such as a ceramic or ceramic containing body and/or a metal or metal containing body. Particularly, an infiltration enhancer and/or infiltration enhancer precursor and/or infiltrating atmosphere are in communication with a filler material or a preform, at least at some point during the process, which permits molten matrix metal to spontaneously infiltrate the filler material or preform. Moreover, prior to infiltration, the filler material or preform is placed into contact with at least a portion of a second material such that after infiltration of the filler material or preform, the infiltrated material is bonded to the second material, thereby forming a macrocomposite body.
Inventors
- 👤 Marc S. Newkirk
- 👤 Danny R. White
- 👤 Christopher R. Kennedy
- 👤 Alan S. Nagelberg
- 👤 Michael K. Aghajanian
- 👤 Robert J. Wiener
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 11:33
CPC Classifications
C; C22; C22C; C22C47/00; B; B22; B22D; B22D19/00; B22D19/14; C22C1/00; C22C1/10; C22C1/1005; C22C1/1015; C22C1/1036; C22C1/1057; C22C1/1063; C22C47/02; C22C47/06; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12007; Y10T428/12486
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
272 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that at least a portion of said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing a second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said second or additional body; heating said matrix metal to a temperature above the melting point of said matrix metal but below the melting point of said filler or preform and below the melting point of said second or additional body; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with at least a portion of said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with at least a portion of said second or additional body; and cooling said matrix metal to a temperature below the melting point of said matrix metal to form a body of excess matrix metal which is integrally attached to or bonded with a metal matrix composite body which is integrally attached or bonded to said second or additional body, said second or additional body having a greater coefficient of thermal expansion than said metal matrix composite body so that said second or additional body retains at least a portion of said metal matrix composite body under compression.
Claim 2
Independent Claim
272 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that at least a portion of said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing a second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said second or additional body; heating said matrix metal to a temperature above the melting point of said matrix metal but below the melting point of said filler or preform and below the melting point of said second or additional body; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with at least a portion of said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with at least a portion of said second or additional body; and cooling said matrix metal to a temperature below the melting point of said matrix metal to form a body of excess matrix metal which is integrally attached to or bonded with a metal matrix composite body which is integrally attached or bonded to said second or additional body, said second or additional body having a greater coefficient of thermal expansion than said metal matrix composite body so that said second or additional body retains at least a portion of said metal matrix composite body under compression.
Claim 3
Dependent Claim
26 words
The method of claim 1, wherein the volume of said metal matrix composite body is less than the volume of said body of excess matrix metal.
Claim 4
Dependent Claim
25 words
The method of claim 2, wherein said metal matrix composite body comprises a thin layer on the surface of said body of excess matrix metal.
Claim 5
Dependent Claim
26 words
The method of claim 1, wherein the volume of said metal matrix composite body is greater than the volume of said body of excess matrix metal.
Claim 6
Dependent Claim
25 words
The method of claim 4, wherein said body of excess matrix metal comprises a thin layer on the surface of said metal matrix composite body.
Claim 7
Dependent Claim
35 words
The method of claim 1, wherein said second or additional body comprises at least one body selected from the group consisting of ceramic bodies, ceramic matrix composite bodies, metal bodies and metal matrix composite bodies.
Claim 8
Dependent Claim
20 words
The method of claim 6, wherein said mass of filler or preform comprises an assemblage of at least two preforms.
Claim 9
Dependent Claim
41 words
The method of claim 1, wherein said second or additional body comprises an interconnected or bonded assemblage of at least two bodies selected from the group consisting of ceramic bodies, ceramic matrix composite bodies, metal bodies and metal matrix composite bodies.
Claim 10
Dependent Claim
20 words
The method of claim 8, wherein said mass of filler or preform comprises an assemblage of at least two preforms.
Claim 11
Independent Claim
227 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that at least a portion of said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; providing said mass of filler or preform with a support means which will enable said mass of filler or preform to maintain a three dimensionally interconnected geometry and sufficient porosity to permit the spontaneous infiltration of said matrix metal at a temperature where both said matrix metal and said filler or preform are molten; heating said matrix metal to a temperature above the melting point of both said matrix metal and said filler or preform but below the temperature at which said support means loses its ability to maintain said three-dimensionally interconnected geometry and said sufficient porosity; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with at least a portion of said matrix metal to form a metal matrix composite body; and cooling said matrix metal and said filler or preform to a temperature below the melting point of both said matrix metal and said filler or preform to form a body of excess matrix metal which is integrally attached to or bonded with said metal matrix composite body.
Claim 12
Independent Claim
227 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that at least a portion of said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; providing said mass of filler or preform with a support means which will enable said mass of filler or preform to maintain a three dimensionally interconnected geometry and sufficient porosity to permit the spontaneous infiltration of said matrix metal at a temperature where both said matrix metal and said filler or preform are molten; heating said matrix metal to a temperature above the melting point of both said matrix metal and said filler or preform but below the temperature at which said support means loses its ability to maintain said three-dimensionally interconnected geometry and said sufficient porosity; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with at least a portion of said matrix metal to form a metal matrix composite body; and cooling said matrix metal and said filler or preform to a temperature below the melting point of both said matrix metal and said filler or preform to form a body of excess matrix metal which is integrally attached to or bonded with said metal matrix composite body.
Claim 13
Dependent Claim
90 words
The method of claim 10, wherein a second or additional body is juxtaposed relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with said second or additional body and, upon cooling said matrix metal and said filler or preform to a temperature below their respective melting points, the metal matrix composite body is integrally attached or bonded to both said body of excess matrix metal and said second or additional body.
Claim 14
Independent Claim
210 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing at least one second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said at least one second or additional body; heating said matrix metal to a temperature above the melting point of said matrix metal but below the melting point of said filler or preform; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with at least a portion of said at least one second or additional body; and cooling said matrix metal to a temperature below its melting point to form a macrocomposite comprising said metal matrix composite body which is integrally attached to or bonded with said at least one second or additional body.
Claim 15
Independent Claim
210 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing at least one second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said at least one second or additional body; heating said matrix metal to a temperature above the melting point of said matrix metal but below the melting point of said filler or preform; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with at least a portion of said at least one second or additional body; and cooling said matrix metal to a temperature below its melting point to form a macrocomposite comprising said metal matrix composite body which is integrally attached to or bonded with said at least one second or additional body.
Claim 16
Dependent Claim
33 words
The method of claim 12, wherein said infiltrating atmosphere communicates with at least one of the matrix metal and the filler or preform for at least a portion of the period of infiltration.
Claim 17
Dependent Claim
39 words
The method of claim 12, further comprising the step of supplying at least one of an infiltration enhancer precursor and an infiltration enhancer to at least one of the matrix metal, the filler or preform, and the infiltrating atmosphere.
Claim 18
Dependent Claim
24 words
The method of claim 14, wherein said at least one of the infiltration enhancer precursor and infiltration enhancer is supplied from an external source.
Claim 19
Dependent Claim
13 words
The method of claim 14, wherein during infiltration, the infiltration enhancer precursor volatilizes.
Claim 20
Dependent Claim
27 words
The method of claim 16, wherein the volatilized infiltration enhancer precursor reacts to form a reaction product in at least a portion of the filler or preform.
Claim 21
Dependent Claim
22 words
The method of claim 17, wherein said reaction product is formed as a coating on at least a portion of said filler.
Claim 22
Dependent Claim
14 words
The method of claim 12, wherein the filler comprises at least one ceramic material.
Claim 23
Dependent Claim
21 words
The method of claim 12, wherein the infiltrating atmosphere comprises an atmosphere selected from the group consisting of oxygen and nitrogen.
Claim 24
Independent Claim
190 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing at least one second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said at least one second or additional body; providing an infiltration enhancer precursor; spontaneously infiltrating at least a portion of said mass of filler or preform with said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with at least a portion of said at least one second or additional body; and cooling said matrix metal to a temperature below the melting point of said matrix metal to form a macrocomposite comprising said metal matrix composite body which is integrally attached to or bonded with said at least one second or additional body.
Claim 25
Independent Claim
190 words
A method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing at least one second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said at least one second or additional body; providing an infiltration enhancer precursor; spontaneously infiltrating at least a portion of said mass of filler or preform with said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with at least a portion of said at least one second or additional body; and cooling said matrix metal to a temperature below the melting point of said matrix metal to form a macrocomposite comprising said metal matrix composite body which is integrally attached to or bonded with said at least one second or additional body.
Claim 26
Independent Claim
58 words
The method of claims 11, 12 or 21, wherein said second or additional body has a greater coefficient of thermal expansion than said metal matrix composite body and, upon cooling the matrix metal to a temperature below its melting point, the second or additional body places at least a portion of the metal matrix composite body under compression.
Claim 27
Independent Claim
58 words
The method of claims 11, 12 or 21, wherein said metal matrix composite body has a greater coefficient of thermal expansion than said second or additional body and, upon cooling the matrix metal to a temperature below its melting point, the metal matrix composite body places at least a portion of the second or additional body under compression.
Claim 28
Independent Claim
101 words
The method of claims 1, 11, 12 or 21, wherein one or both of said metal matrix composite body and said second or additional body comprises notches, holes, slots, or any other surface irregularities which are matched with a corresponding inversely shaped surface irregularity on the surface to which the metal matrix composite body or the second or additional body is to be integrally attached or bonded and wherein said matching surface irregularities create a mechanical attachment or bond in addition to any attachment or bond which may exist between said metal matrix composite body and said second or additional body.
Claim 29
Independent Claim
15 words
The method of claims 12 or 21, wherein the infiltration occurs within defined barrier means.
Claim 30
Dependent Claim
22 words
The method of claim 25, wherein the barrier comprises a material selected from the group consisting of carbon, graphite and titanium diboride.
Claim 31
Independent Claim
39 words
The method of claims 12 or 21, wherein the filler comprises at least one material selected from the group consisting of powders, flakes, platelets, microspheres, whiskers, bubbles, fibers, particulates, fiber mats, chopped fibers, spheres, pellets, tubules and refractory cloths.
Claim 32
Independent Claim
38 words
The method of claims 14 or 21, wherein the matrix metal comprises aluminum, the infiltrating atmosphere comprises nitrogen and the infiltration enhancer precursor comprises at least one material selected from the group consisting of magnesium, strontium and calcium.
Claim 33
Independent Claim
25 words
The method of claims 14 or 21, wherein the matrix metal comprises aluminum, the infiltrating atmosphere comprises oxygen and the infiltration enhancer precursor comprises zinc.
Claim 34
Dependent Claim
11 words
The method of claim 21, further comprising providing an infiltrating atmosphere.
Claim 35
Dependent Claim
28 words
The method of claim 30, wherein said infiltration enhancer precursor is supplied to at least one of the matrix metal, the filler or preform and the infiltrating atmosphere.
Claim 36
Independent Claim
25 words
The method of claims 14 or 30, wherein the matrix metal comprises aluminum, the infiltrating atmosphere comprises nitrogen and the infiltration enhancer precursor comprises magnesium.
Claim 37
Dependent Claim
25 words
The method of claim 21, wherein said infiltration enhancer precursor is supplied to at least one of said matrix metal and said filler or preform.
Claim 38
Dependent Claim
23 words
The method of claim 12, wherein said infiltration enhancer precursor is supplied to both of said matrix metal and said filler or preform.
Claim 39
Independent Claim
26 words
The method of claims 12 or 21, wherein said metal matrix composite body comprises a thin layer on the surface of said second or additional body.
Claim 40
Independent Claim
26 words
The method of claims 12 or 21, wherein said second or additional body comprises a thin layer on the surface of said metal matrix composite body.
Claim 41
Independent Claim
37 words
The method of claims 12 or 21, wherein said second or additional body comprises at least one body selected from the group consisting of ceramic bodies, ceramic matrix composite bodies, metal bodies, and metal matrix composite bodies.
Claim 42
Independent Claim
273 words
The method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that at least a portion of said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing a second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said second or additional body; heating said matrix metal to a temperature above the melting point of said matrix metal but below the melting point of said filler or preform and below the melting point of said second or additional body; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with at least a portion of said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with said at least a portion of said second or additional body; and cooling said matrix metal to a temperature below the melting point of said matrix metal to form a body of excess matrix metal which is integrally attached to or bonded with a metal matrix composite body which is integrally attached or bonded to said second or additional body, said metal matrix composite body having a greater coefficient of thermal expansion than said second or additional body so that said metal matrix composite body retains at least a portion of said second or additional body under compression.
Claim 43
Independent Claim
273 words
The method for producing a macrocomposite comprising: juxtaposing a mass of filler or preform relative to a body of matrix metal such that at least a portion of said matrix metal, when molten, will spontaneously infiltrate said mass of filler or preform to form a metal matrix composite body; juxtaposing a second or additional body relative to said mass of filler or preform such that when said matrix metal spontaneously infiltrates said mass of filler or preform the matrix metal comes into contact with at least a portion of said second or additional body; heating said matrix metal to a temperature above the melting point of said matrix metal but below the melting point of said filler or preform and below the melting point of said second or additional body; providing an infiltrating atmosphere; spontaneously infiltrating at least a portion of said mass of filler or preform with at least a portion of said matrix metal to form a metal matrix composite body; continuing said spontaneous infiltration until said matrix metal comes into contact with said at least a portion of said second or additional body; and cooling said matrix metal to a temperature below the melting point of said matrix metal to form a body of excess matrix metal which is integrally attached to or bonded with a metal matrix composite body which is integrally attached or bonded to said second or additional body, said metal matrix composite body having a greater coefficient of thermal expansion than said second or additional body so that said metal matrix composite body retains at least a portion of said second or additional body under compression.
References Cited (Backward Citations)
US2951771A
Cited
US3031340A
Cited
US3149409A
Cited
US3364976A
Cited
US3396777A
Cited
US3547180A
Cited
US3608170A
Cited
US3915699A
Cited
US3718441A
Cited
US3970136A
Cited
US3864154A
Cited
US3868267A
Cited
US3969553A
Cited
US4082864A
Cited
DE2819076A1
Cited
US4232091A
Cited
US4802524A
Cited
US4677901A
Cited
US4404262A
Cited
US4376804A
Cited
US4376803A
Cited
US4473103A
Cited
JPS58144441A
Cited
EP0094353A2
Cited
US4450207A
Cited
EP0115742A1
Cited
US4570316A
Cited
US4559246A
Cited
GB2156718A
Cited
US4679493A
Cited
US4731298A
Cited
US4587177A
Cited
US4673435A
Cited
US4630665A
Cited
US4657065A
Cited
US4713111A
Cited
US4662429A
Cited
US4753690A
Cited
US4828008A
Cited
US4871008A
Cited
EP0340957A2
Cited
EP0364963A1
Cited
US4932099A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-19 | 1995-02-18 | 1995-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-19 | 1999-02-18 | 1999-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-19 | 2003-02-18 | 2003-08-20 | $7700.00 | Window Closed / Lapsed |