Carbon-reinforced metal-matrix composites

Claim 2

A carbon fiber reinforced metal matrix comprising: (a) a continuous multifilament carbon fiber; (b) an oxide film operative to coat substantially surfaces of the multifilament carbon fiber; and (c) a metal matrix material infiltrated throughout and adhered to the multifilament carbon fiber.

Claim 3

The carbon fiber reinforced metal matrix as defined in claim 1 wherein the oxide is silicon-dioxide.

Claim 4

The carbon fiber reinforced metal matrix as defined in claim 1 wherein the metal matrix material is substantially magnesium.

Claim 5

The carbon fiber reinforced metal matrix as defined in claim 1 wherein the carbon fiber is substantially a graphite fiber.

Claim 6

A composite product comprising a plurality of carbon fibers each having a coating of an oxide formed with an element selected from the group consisting of silicon, titanium, vanadium, lithium, magnesium, sodium, potassium, zirconium, boron, or alloys thereof, said fibers being disposed in a substantially solid matrix of metal.

Claim 7

A composite product comprising a plurality of carbon fibers each having a coating of an oxide formed with an element selected from the group consisting of silicon, titanium, vanadium, lithium, magnesium, sodium, potassium, zirconium, boron, or alloys thereof, said fibers being disposed in a substantially solid matrix of metal.

Claim 8

A composite as defined in claim 5 wherein the thickness of said coating is within the range of approximately between seven hundred to fifteen hundred angstroms.

Claim 9

A composite as defined in claim 5 wherein the fibers are substantially graphite.

Claim 10

A composite as defined in claim 5 wherein the metal matrix is substantially magnesium.

Claim 11

A process for improving the wettability of multi-filament carbon fibers by molten metal by coating the fibers with an oxide comprising: (a) immersing the fibers in an ultrasonic bath containing an organic solvent solution having alkoxides therein at a predetermined temperature; and (b) flowing steam by the fibers to hydrolyze the alkoxides to oxide on the surface of the fiber to a predetermined thickness.

Claim 12

A process for improving the wettability of multi-filament carbon fibers by molten metal by coating the fibers with an oxide comprising: (a) immersing the fibers in an ultrasonic bath containing an organic solvent solution having alkoxides therein at a predetermined temperature; and (b) flowing steam by the fibers to hydrolyze the alkoxides to oxide on the surface of the fiber to a predetermined thickness.

Claim 13

The process as defined in claim 9 wherein the alkoxide in the immersing step comprises tetraethoxy silane.

Claim 14

The process as defined in claim 9 wherein the predetermined temperature in the immersing step may be within the range of approximately twenty to one hundred degrees centigrade.

Claim 15

The process as defined in claim 9 wherein the oxide in the flowing steam step has a predetermined thickness they may be within the range of approximately seven hundred to fifteen hundred angstroms.

Claim 16

The process as defined in claim 9 wherein the oxide in the flowing steam step comprises silicon-dioxide.

Claim 17

A process for improving the wettability of multifilament carbon fibers by molten metal by coating the fiber with an oxide comprising the steps of: (a) heating the fibers to a predetermined temperature to pyrolyze and vaporize the sizing; (b) immersing the fibers in a ultrasonic bath at a predetermined temperature containing an organic solvent solution having chlorides and alkoxides therein; (c) flowing steam by the fibers to hydrolyze the alkoxides to form an oxide on the surface of the fiber to a predetermined thickness; and (d) drying the fibers at a predetermined temperature in an inert atmosphere for vaporizing excess water and the organic solvent, and for pyrolyzing any unhydrolyzed compounds into the oxide.

Claim 18

A process for improving the wettability of multifilament carbon fibers by molten metal by coating the fiber with an oxide comprising the steps of: (a) heating the fibers to a predetermined temperature to pyrolyze and vaporize the sizing; (b) immersing the fibers in a ultrasonic bath at a predetermined temperature containing an organic solvent solution having chlorides and alkoxides therein; (c) flowing steam by the fibers to hydrolyze the alkoxides to form an oxide on the surface of the fiber to a predetermined thickness; and (d) drying the fibers at a predetermined temperature in an inert atmosphere for vaporizing excess water and the organic solvent, and for pyrolyzing any unhydrolyzed compounds into the oxide.

Claim 19

A process for improving the wettability of multifilament carbon fibers by molten metal by coating the fibers with an oxide comprising the steps of: (a) vaporizing off sizing on the fiber by heating it to a predetermined temperature; (b) immersing the fibers in an ultrasonic bath at a predetermined temperature containing an organic solvent solution having chlorides and alkoxides therein; (c) flowing steam by the fibers to hydrolyze the chlorides and alkoxides to an oxide on the surface of the fiber to a predetermined thickness; and (d) drying the fibers at a predetermined temperature in an inert atmosphere for vaporizing excess water and the organic solvent, and for pyrolyzing any unhydrolyzed compounds into the oxide.

Claim 20

A process for improving the wettability of multifilament carbon fibers by molten metal by coating the fibers with an oxide comprising the steps of: (a) vaporizing off sizing on the fiber by heating it to a predetermined temperature; (b) immersing the fibers in an ultrasonic bath at a predetermined temperature containing an organic solvent solution having chlorides and alkoxides therein; (c) flowing steam by the fibers to hydrolyze the chlorides and alkoxides to an oxide on the surface of the fiber to a predetermined thickness; and (d) drying the fibers at a predetermined temperature in an inert atmosphere for vaporizing excess water and the organic solvent, and for pyrolyzing any unhydrolyzed compounds into the oxide.

Claim 21

The process as defined in claim 15 wherein the predetermined temperature in the vaporizing step, is within the range of approximately three hundred fifty to four hundred fifty degrees centigrade.

Claim 22

The process as defined in claim 15 wherein the organic solvent in the immersing step is toluene.

Claim 23

The process as defined in claim 15 wherein the chloride in the organic solvent solution of the immersing step comprises silicon tetrachloride.

Claim 24

The process as defined in claim 15 wherein the alkoxide in the organic solvent solution in the immersing step comprises tetraethoxy silane.

Claim 25

The process as defined in claim 15 wherein the predetermined temperature in the immersing step is within the range of approximately twenty to one hundred degrees centigrade.

Claim 26

The process as defined in claim 15 wherein the oxide in the flowing steam step has a predetermined thickness that is within the range of approximately seven hundred to fifteen hundred angstroms.

Claim 27

The process as defined in claim 15 wherein the oxide in the flowing steam step comprises silicon-dioxide.

Claim 28

The process as defined in claim 15 wherein the predetermined temperature of the drying step is within the range of approximately three hundred to seven hundred fifty degrees centigrade.

Claim 29

The process as defined in claim 15 wherein the inert atmosphere of the drying step is substantially argon.

Claim 30

The process as defined in claim 15 wherein the compounds in the drying step are substantially silicon compounds.