Method of manufacturing composite materials
Assignee: UK Secretary of State for Defence
•
Filing: 1975-03-14
•
Granted: 1976-07-20
•
Expires: 1995-03-14
Abstract
Abstract A process for forming a composite material comprising a metal matrix incorporating fibrous reinforcement having a pre-determined pattern of fibre orientation which includes the steps of providing in a mould substantially parallel fibre arrays in which each array consists of a sheet of substantially coplanar fibres, providing a reservoir of molten matrix metal between at least some of the fibre arrays and applying pressure to the mould contents sufficient to force molten metal to surround substantially all the fibres.
Inventors
- 👤 John Corjeag Cannell
- 👤 Rodney Seymour Leaper
- 👤 Noel James Parratt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:29
CPC Classifications
B; B22; B22D; B22D19/00; B22D19/14; C; C22; C22C; C22C47/00; C22C47/08; Y; Y10; Y10S; Y10S428/00; Y10S428/922; Y10S428/9335; Y10S428/939; Y10T; Y10T428/00; Y10T428/12; Y10T428/1234; Y10T428/12486
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
122 words
A process for forming a composite material comprising a metal matrix incorporating non-metallic fibrous reinforcement having a predetermined pattern of fiber orientation which includes the steps of: a. providing in a mold a plurality of layers of fibers formed from at least one array of substantially coplanar fibers, b. providing reservoirs of molten matrix metal between at least some of the layers of fibers, and c. forcing said molten metal to penetrate said layers and intimately to surround substantially each of the fibers by applying pressure to the mold contents, sufficient matrix metal reservoirs being provided for the separation between neighboring reservoirs to be within twice the distance that the molten metal can penetrate before solidification under the applied temperature and pressure.
Claim 2
Dependent Claim
122 words
A process for forming a composite material comprising a metal matrix incorporating non-metallic fibrous reinforcement having a predetermined pattern of fiber orientation which includes the steps of: a. providing in a mold a plurality of layers of fibers formed from at least one array of substantially coplanar fibers, b. providing reservoirs of molten matrix metal between at least some of the layers of fibers, and c. forcing said molten metal to penetrate said layers and intimately to surround substantially each of the fibers by applying pressure to the mold contents, sufficient matrix metal reservoirs being provided for the separation between neighboring reservoirs to be within twice the distance that the molten metal can penetrate before solidification under the applied temperature and pressure.
Claim 3
Dependent Claim
17 words
A process according to claim 1 wherein the coplanar fibers in any fiber array are unidirectionally aligned.
Claim 4
Dependent Claim
34 words
A process according to claim 1 and in which the matrix metal reservoirs are formed in situ by melting solid phase matrix metal previously positioned between at least some of the layers of fibers.
Claim 5
Dependent Claim
34 words
A process according to claim 3 and in which the solid matrix metal is melted to form the matrix metal reservoirs before the fiber arrays and molten matrix metal are introduced into the mold.
Claim 6
Dependent Claim
18 words
A process according to claim 3 and in which the solid matrix metal is melted within the mold.
Claim 7
Dependent Claim
30 words
A process according to claim 3 wherein the solid matrix metal is provided in the form of sheets of matrix metal inserted between and parallel to the layers of fibers.
Claim 8
Dependent Claim
48 words
A process according to claim 6 and in which the layers of fibers are constituted by a roll formed from an array of aligned fibers, and the solid matrix metal is provided in the form of one or more sheets of solid matrix metal interposed within the roll.
Claim 9
Dependent Claim
25 words
A process according to claim 3 wherein the solid matrix metal is provided in the form of matrix metal particles dispersed throughout each fiber array.
Claim 10
Dependent Claim
16 words
A process according to claim 8 wherein the matrix metal particles are equant, substantially spherical, particles.
Claim 11
Dependent Claim
16 words
A process according to claim 8 wherein the mean particle size is at least 60 microns.
Claim 12
Dependent Claim
48 words
A process according to claim 1 and in which said molten metal reservoirs are provided in desired positions by forcing molten metal to flow, under the initial application of pressure to the mold contents, along paths of low flow resistance between the layers of fibers to said positions.
Claim 13
Dependent Claim
19 words
A process according to claim 11 and in which the layers of fibers are preconsolidated to improve their packing.
Claim 14
Dependent Claim
84 words
A process according to claim 11 and in which the molten matrix metal, is poured on to substantially parallel layers of fibers arranged in the mold transverse to the direction of approach of the mold closure and incompletely filling the transverse cross section of the molds so that a catchment volume substantially free of fibers is formed in the mold from which molten metal may flow directly between the layers of fibers to the desired reservoir positions without passing through the layers of fibers.
Claim 15
Dependent Claim
52 words
A process according to claim 13 wherein the catchment volume in the mold for molten matrix metal represents a fraction of the total volume of the mold prior to compression which approximates to the compression ratio to be applied to fully consolidate the fiber arrays and molten metal into a composite material.
Claim 16
Dependent Claim
19 words
A process according to claim 13 and in which the layers of fibers are preconsolidated to improve their packing.
Claim 17
Dependent Claim
77 words
A process according to claim 13 and in which a cylinder of composite material is formed by arranging a stack of annular layers of fibers in the mold to provide an axial catchment volume in the center of the stack, pouring the molten matrix metal into the catchment volume and pressing the layer of fibers and molten matrix metal to force the metal between the annular layer of fibers and thence around the fibers in each layer.
Claim 18
Dependent Claim
32 words
A process according to claim 1 in which the layers of fibers are formed from a rolled array of fibers and are forced into the mold which already contains molten matrix metal.
Claim 19
Dependent Claim
39 words
A process according to claim 1 and in which the fibres are selected from the group consisting of carbon and boron fibers in semi-continuous or staple form, glass, silica, asbestos and whiskers of silicon carbide, silicon nitride and alumina.
Claim 20
Dependent Claim
35 words
A process according to claim 1 and in which the matrix metal is selected from the group consisting of aluminum, magnesium, titanium, copper, nickel, lead, tin and alloys containing at least one of these metals.
Claim 21
Dependent Claim
31 words
A process according to claim 9 and in which the matrix metal is selected from the group consisting of aluminum, magnesium, titanium and alloys containing at least one of these metals.
Claim 22
Dependent Claim
34 words
A process according to claim 20 and in which the fibers are selected from the group consisting of boron fibers in staple or continuous form and whiskers of silicon carbide, silicon nitride and alumina.
Claim 23
Dependent Claim
30 words
A process according to claim 1 and in which the said parallel layers of fibers are arranged in the mold parallel to the direction of approach of the mold closure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-07-20 | 1980-01-19 | 1980-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-07-20 | 1984-01-19 | 1984-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-07-20 | 1988-01-19 | 1988-07-20 | $7700.00 | Window Closed / Lapsed |