Method of making a multi-layered article
Assignee: Spectrum Control Inc
•
Filing: 1990-10-12
•
Granted: 1991-07-16
•
Expires: 2010-10-12
Abstract
Abstract A high speed process for forming a multi layered thin film structure in a vacuum wherein each film is less than about four microns thick and the total layers can reach upwards to 4,000 or more. The polymeric layers are formed of a cross linked component selected from the group consisting of polyfunctional acrylates and mixtures of polyfunctional acrylates and monocrylates with the component having a preferable molecular weight of between 200 and 300 and a vapor pressure preferably in excess of 1×10 -2 Torr. The polymeric layers may be interleaved with metal layers.
Inventors
- 👤 David G. Shaw
- 👤 Angelo Yializis
- 👤 Donald S. Strycker
- 👤 Mooyoung Ham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:56
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/56; B05D1/00; B05D1/60; B05D3/00; B05D3/06; B05D3/068; B05D7/24; H; H01; H01G; H01G13/00; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/14; H01G4/145; H01G4/30; H01G4/306; B05D3/14; B05D3/141; B05D3/145; B05D3/148; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31855; Y10T428/31909
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
276 words
A high-speed process for forming a multi layered article having a plurality of substantially delamination free, pin hole free and void free layers, comprising the following steps: (a) providing a vacuum chamber containing: i) a movable support, ii) at least one vapor outlet of a dielectric flash vaporizer mounted adjacent to an upstream portion of said support, iii) at least one curing means mounted adjacent to a downstream portion of said support, and, iv) means for maintaining said support at a temperature below that of said vaporizer; (b) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -4 Torr; (c) selecting a curable component comprising: i) polyfunctional acrylates, or ii) mixtures of monoacrylates and polyfunctional acrylates, said mixtures having an average of about two or more olefinic groups per molecule, said curable component having: i) an average molecular weight between 150 and 1,000, and ii) a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (d) metering a quantity of said curable component into an inlet portion of said vaporizer; (e) flash vaporizing said component within said vaporizer; (f) moving said support relative to said vapor outlet and said curing means at a rate of between about 1 cm/sec and 1,000 cm/sec; (g) condensing a film of vaporized component dispensed from said vapor outlet onto the surface of said support, said film having a thickness of 4 microns or less; (h) activating said curing means whereby a substantially cross linked polymer film is formed on said support; and, (i) repeating steps (c) through (h) whereby a multi layer article is formed.
Claim 2
Dependent Claim
276 words
A high-speed process for forming a multi layered article having a plurality of substantially delamination free, pin hole free and void free layers, comprising the following steps: (a) providing a vacuum chamber containing: i) a movable support, ii) at least one vapor outlet of a dielectric flash vaporizer mounted adjacent to an upstream portion of said support, iii) at least one curing means mounted adjacent to a downstream portion of said support, and, iv) means for maintaining said support at a temperature below that of said vaporizer; (b) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -4 Torr; (c) selecting a curable component comprising: i) polyfunctional acrylates, or ii) mixtures of monoacrylates and polyfunctional acrylates, said mixtures having an average of about two or more olefinic groups per molecule, said curable component having: i) an average molecular weight between 150 and 1,000, and ii) a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (d) metering a quantity of said curable component into an inlet portion of said vaporizer; (e) flash vaporizing said component within said vaporizer; (f) moving said support relative to said vapor outlet and said curing means at a rate of between about 1 cm/sec and 1,000 cm/sec; (g) condensing a film of vaporized component dispensed from said vapor outlet onto the surface of said support, said film having a thickness of 4 microns or less; (h) activating said curing means whereby a substantially cross linked polymer film is formed on said support; and, (i) repeating steps (c) through (h) whereby a multi layer article is formed.
Claim 3
Dependent Claim
282 words
A high-speed process for forming a multi layered article having a plurality of substantially delamination free, pin hole free and void free layers, comprising the following steps: (a) providing a vacuum chamber containing: i) a movable support, ii) at least one vapor outlet of a flash vaporizer mounted adjacent to an upstream portion of said support, iii) at least one curing means mounted adjacent to a downstream portion of said support, and iv) means for maintaining said support at a temperature below that of said vaporizer; (b) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -4 Torr; (c) selecting a curable component comprising: i) polyfunctional acrylates, or ii) mixtures of monoacrylates and polyfunctional acrylates, said mixtures having an average of about two or more olefinic groups per molecule, said curable component having: i) an average molecular weight between 150 and 1,000, and ii) a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (d) metering a quantity of said curable component into an inlet portion of said vaporizer; (e) flash vaporizing said component within said vaporizer; (f) moving said support relative to said vapor outlet and said curing means at a rate of between about 1 cm/sec and 1,000 cm/sec; (g) condensing a film of vaporized component dispensed from said vapor outlet onto the surface of said support, said film having a thickness of 4 microns or less; (h) repeating steps (c) through (g) whereby a plurality of films of said component are deposited; and, (i) activating said curing means whereby said films are cured to form a substantially cross linked polymer film on said support.
Claim 4
Dependent Claim
282 words
A high-speed process for forming a multi layered article having a plurality of substantially delamination free, pin hole free and void free layers, comprising the following steps: (a) providing a vacuum chamber containing: i) a movable support, ii) at least one vapor outlet of a flash vaporizer mounted adjacent to an upstream portion of said support, iii) at least one curing means mounted adjacent to a downstream portion of said support, and iv) means for maintaining said support at a temperature below that of said vaporizer; (b) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -4 Torr; (c) selecting a curable component comprising: i) polyfunctional acrylates, or ii) mixtures of monoacrylates and polyfunctional acrylates, said mixtures having an average of about two or more olefinic groups per molecule, said curable component having: i) an average molecular weight between 150 and 1,000, and ii) a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (d) metering a quantity of said curable component into an inlet portion of said vaporizer; (e) flash vaporizing said component within said vaporizer; (f) moving said support relative to said vapor outlet and said curing means at a rate of between about 1 cm/sec and 1,000 cm/sec; (g) condensing a film of vaporized component dispensed from said vapor outlet onto the surface of said support, said film having a thickness of 4 microns or less; (h) repeating steps (c) through (g) whereby a plurality of films of said component are deposited; and, (i) activating said curing means whereby said films are cured to form a substantially cross linked polymer film on said support.
Claim 5
Dependent Claim
310 words
A high-speed process for forming a multi layered article having a plurality of substantially delamination free, pin hole free and void free layers, comprising the following steps: (a) providing a vacuum chamber containing: i) a movable support, ii) at least one vapor outlet of a flash vaporizer mounted adjacent to an upstream portion of said support, iii) at least one curing means mounted adjacent to a downstream portion of said support, iv) means for maintaining said support at a temperature below that of said vaporizer; and v) means for depositing an inorganic material; (b) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -4 Torr; (c) selecting a curable component comprising: i) polyfunctional acrylates, or ii) mixtures of monoacrylates and polyfunctional acrylates, said mixtures having an average of about two or more olefinic groups per molecule, said curable component having: i) an average molecular weight between 150 and 1,000, and ii) a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (d) metering a quantity of said curable component into an inlet portion of said vaporizer; (e) flash vaporizing said component within said vaporizer; (f) moving said support relative to said vapor outlet and said curing means at a rate of between about 1 cm/sec and 1,000 cm/sec; (g) condensing a film of vaporized component dispensed from said vapor outlet onto the surface of said support, said film having a thickness of 4 microns or less; (h) activating said curing means whereby a substantially cross linked polymer film is formed on said support; (i) repeating steps (c) through (h) and, (j) depositing a layer of inorganic material on one or more substantially cured polymer films whereby a multi layered article comprising a plurality of polymer layers and at least one inorganic material layer is formed.
Claim 6
Dependent Claim
310 words
A high-speed process for forming a multi layered article having a plurality of substantially delamination free, pin hole free and void free layers, comprising the following steps: (a) providing a vacuum chamber containing: i) a movable support, ii) at least one vapor outlet of a flash vaporizer mounted adjacent to an upstream portion of said support, iii) at least one curing means mounted adjacent to a downstream portion of said support, iv) means for maintaining said support at a temperature below that of said vaporizer; and v) means for depositing an inorganic material; (b) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -4 Torr; (c) selecting a curable component comprising: i) polyfunctional acrylates, or ii) mixtures of monoacrylates and polyfunctional acrylates, said mixtures having an average of about two or more olefinic groups per molecule, said curable component having: i) an average molecular weight between 150 and 1,000, and ii) a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (d) metering a quantity of said curable component into an inlet portion of said vaporizer; (e) flash vaporizing said component within said vaporizer; (f) moving said support relative to said vapor outlet and said curing means at a rate of between about 1 cm/sec and 1,000 cm/sec; (g) condensing a film of vaporized component dispensed from said vapor outlet onto the surface of said support, said film having a thickness of 4 microns or less; (h) activating said curing means whereby a substantially cross linked polymer film is formed on said support; (i) repeating steps (c) through (h) and, (j) depositing a layer of inorganic material on one or more substantially cured polymer films whereby a multi layered article comprising a plurality of polymer layers and at least one inorganic material layer is formed.
Claim 7
Dependent Claim
20 words
A process in accordance with claim 3 wherein a plurality of inorganic material layers are interleaved between said polymer layers.
Claim 8
Dependent Claim
40 words
A process in accordance with claims 1, 2 or 3 and further including the placing of a removable substrate on said movable support prior to said vaporizing and curing whereby a plurality of polymer layers are deposited on said substrate.
Claim 9
Dependent Claim
32 words
A process in accordance with claim 5 and including the depositing of a release means on said substrate for releasing said article, said release means being deposited prior to said vaporizing step.
Claim 10
Dependent Claim
34 words
A process in accordance with claims 1, 2 or 3 and including the depositing of a release means on said movable support prior to said flash vaporizing step for releasing said multi layered article.
Claim 11
Dependent Claim
157 words
A process in accordance with claims 1, 2 or 3 and further including providing a plurality of said vapor outlets in said vacuum chamber; selecting curable components from the group consisting of polyfunctional acrylates and mixtures of monoacrylates and polyfunctional acrylates, said components having an average molecular weight between 150 and 1,000, and a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; metering a quantity of said curable components into at least two of said vapor outlets; vaporizing the components; moving said support relative to said vapor outlets and said curing means at a speed of between about 1 cm/sec. and 1,000 cm/sec. condensing one or more films of vaporized curable components dispensed from said vapor outlets on to the surface of said support, each film having a thickness of 4 microns or less; activating said curing means whereby substantially cross linked films are formed on said support.
Claim 12
Dependent Claim
40 words
A process in accordance with claim 8 and further including the steps of repeating of said metering, vaporizing, moving said support, condensing and operating said curing means to provide the desired number of films to form said multi layered article.
Claim 13
Dependent Claim
21 words
A process in accordance with claim 9 wherein said curable components metered into each of said vapor outlets are the same.
Claim 14
Dependent Claim
17 words
A process in accordance with claim 10 wherein said curable components selected from said group are different.
Claim 15
Dependent Claim
52 words
A process in accordance with claim 8 and further including the steps of placing a plurality of said curing means within said chamber, each curing means being located downstream of a vaporizer outlet; and, activating at least one curing means following the condensing of a film of vaporized component on said support.
Claim 16
Dependent Claim
31 words
A process in accordance with claim 12 including the step of sequentially condensing a film of curable component and activating one of said curing means to cross link said condensed component.
Claim 17
Dependent Claim
26 words
A process in accordance with claim 1, 2 or 3 and further including the step of removing gases from said curable component prior to said metering.
Claim 18
Dependent Claim
15 words
A process in accordance with claim 1, 2 or 3 wherein said support moves continuously.
Claim 19
Dependent Claim
15 words
A process in accordance with claim 1, 2 or 3 wherein said support is indexed.
Claim 20
Dependent Claim
17 words
A process in accordance with claim 1, 2 or 3 wherein said curable component is a diacrylate.
Claim 21
Dependent Claim
12 words
A process in accordance with claim 5 wherein said substrate is flexible.
Claim 22
Dependent Claim
19 words
A process in accordance with claims 1, 2 or 3 in which said movable support comprises a rotatable drum.
Claim 23
Dependent Claim
18 words
A process in accordance with claims 1, 2 or 3 in which said movable support comprises a disk.
Claim 24
Dependent Claim
19 words
A process in accordance with claims 1, 2 or 3 in which said movable support comprises a continuous belt.
Claim 25
Dependent Claim
20 words
A process in accordance with claims 1, 2 or 3 in which said curing is by means of electron beam.
Claim 26
Dependent Claim
34 words
A process in accordance with claims 1, 2 or 3 and further including the forming of a continuous multi layered strip on said movable support; and, removing said continuous strip from said movable support.
Claim 27
Dependent Claim
16 words
A process in accordance with claim 23 in which said movable support is a rotatable drum.
Claim 28
Dependent Claim
16 words
A multi layered article made in accordance with the process of claims 1, 2 or 3.
Claim 29
Dependent Claim
23 words
A multi layered article made in accordance with the process of claims 1 or 2 wherein said product comprises at least 1,000 layers.
Claim 30
Dependent Claim
24 words
A multi layered article made in accordance with the process of claim 3 wherein said product comprises at least 1,000 layers of cured component.
Claim 31
Dependent Claim
22 words
A multi layered article made in accordance with the process of claims 3 or 4 wherein said inorganic material is a metal.
Claim 32
Dependent Claim
63 words
A process in accordance with claims 1, 2 or 3 wherein said polyfunctional acrylate has the formula: ##STR6## wherein: R 1 is an aliphatic, alicyclic or mixed aliphatic-alicyclic radical derived from a compound of the formula R 1 (OH) m ; R 2 is a hydrogen, methyl, ethyl, propyl, butyl or pentyl; n is from 2 to 4; m is 2 or more.
Claim 33
Dependent Claim
52 words
A process in accordance with claims 1, 2 or 3 in which said monoacrylate has the formula: ##STR7## wherein: R 2 , r and 2 are defined above; x 1 is H or: ##STR8## X 3 is CN or COOR 3 wherein R 3 is an alkyl radical containing 1-4 carbon atoms.
Claim 34
Dependent Claim
39 words
A process in accordance with claims 1, 2 or 3 wherein said polyfunctional acrylate comprises a diacrylate of the formula: ##STR9## wherein: r and s are each 7 or 8 and the sum of r and s is 15.
Claim 35
Dependent Claim
43 words
A process in accordance with claims 1, 2 or 3 wherein said polyfunctional acrylate is selected from the group consisting of: (i) 1,6-hexane diol diacrylate; (ii) alkoxylated cyclohexane dimethanol diacrylates; wherein the alkoxy group contains 1 to 4 carbon atoms and (iii) ##STR10##
Claim 36
Dependent Claim
30 words
A process in accordance with claims 1, 2 or 3 wherein said movable support is maintained at a temperature in the range of about -7° C. to about 80° C.
Claim 37
Dependent Claim
36 words
A process in accordance with claims 1, 2 or 3 wherein said movable support comprises a rotating drum and said drum passes said vapor outlet and said curing means at a speed of about 100 cm/sec.
Claim 38
Dependent Claim
21 words
A process in accordance with claims 1, 2 or 3 in which said curing means comprises a gas discharge electron beam.
Claim 39
Dependent Claim
20 words
A process in accordance with claim 8 in which said vaporizers are flash vaporizers and said components are flash vaporized.
References Cited (Backward Citations)
US2734478A
Cited
CA789746A
Cited
US1873548A
Cited
GB550419A
Cited
US2389420A
Cited
US2614524A
Cited
US2590906A
Cited
GB762953A
Cited
CH313676A
Cited
US2820934A
Cited
US2971862A
Cited
US3081201A
Cited
US3024394A
Cited
US3252830A
Cited
GB970865A
Cited
US3068510A
Cited
US3123490A
Cited
US3237273A
Cited
US3326718A
Cited
US3457614A
Cited
US3244953A
Cited
GB1104172A
Cited
GB1168641A
Cited
US3547683A
Cited
US3466719A
Cited
US3520987A
Cited
GB1253124A
Cited
US3743532A
Cited
US3654532A
Cited
US3617834A
Cited
US3819990A
Cited
US4076866A
Cited
US4121537A
Cited
DE2641232A1
Cited
US4153925A
Cited
US4301580A
Cited
US4207836A
Cited
DE2737509A1
Cited
DE2759118A1
Cited
JPS5527455A
Cited
GB2033355A
Cited
US4376329A
Cited
US4508049A
Cited
US4294194A
Cited
US4277516A
Cited
US4301765A
Cited
US4261798A
Cited
US4379182A
Cited
US4290384A
Cited
US4434452A
Cited
US4403381A
Cited
US4414722A
Cited
US4378382A
Cited
WO1982000542A1
Cited
US4329419A
Cited
GB2085755A
Cited
US4363162A
Cited
US4543275A
Cited
US4387113A
Cited
JPS5874701A
Cited
DE3231576A1
Cited
US4502095A
Cited
JPS59177365A
Cited
US4571316A
Cited
US4453199A
Cited
US4490774A
Cited
US4533710A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-15 | 1995-01-14 | 1995-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-15 | 1999-01-14 | 1999-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-15 | 2003-01-14 | 2003-07-16 | $7700.00 | Window Closed / Lapsed |